Effect of Sintering Time for Aluminum / Stainless Steel Composite on Mechanical Properties
تأثير زمن التلبيد لمركب الألمنيوم / الصلب اللامصديء على الخواص الميكانيكية

Author: Saheb Mohammed Mahdi صاحب محمد مهدي
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 1 Pages: 154-161
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The effect of sintering time on mechanical properties of two powder composition containing 25 wt% and 12.5 wt% 316L Austenitic Stainless Steel and the balance is Aluminum has been studied, at two sintering temperatures 500 and 530 Co for sintering time (30,60,90,120,180) minutes. Results of compression tests showed that compression strength and yield strength increase with sintering time, reaches a maximum value and then decreases gradually, for both compositions and sintering temperatures used. Hardness showed a similar relation with sintering time for both compositions and sintering temperatures, microstructure of the sintered parts showed a two phase structure, one phase was identified using XRD technique as FeAl3 , the other phase is Al matrix.

تم في هذا البحث دراسة تأثير زمن التلبيد على الخواص الميكانيكية لخليط مشكل بطريقة متالورجيا المساحيق ، يتكون من 25% و 12.5% وزناً صلب لامصديء نوع (316L) والباقي معدن الألمنيوم ، عند درجتي حرارة تحميص هي 500 و 530 oم لزمن تلبيد (180,120,90,60,30) دقيقة. بينت نتائج اختبارات الضغط ان مقاومة الضغط ومقاومة الخضوع ازدادت مع زيادة زمن التلبيد ، حتى قيمة قصوى ثم تنخفض تدريجياً .لكل من الخليط المعدني ولدرجتي حرارة التلبيد المستخدمة. وقد اظهر اختبار الصلادة نفس التصرف وايضا لكل من تركيب الخليط المعدني ولدرجتي حرارة التلبيد.ان التركيب ألمجهري للعينات التي جرى لها تلبيد أظهرت وجود طورين ، حيث تم تحديد احد الطورين باستخدام حيود أشعة X وكان عبارة عن) (FeAl3 وكان الطور الأخر هو الأساس معدن الألمنيوم .


Article
Reinforcing of Aluminum-Silicon Alloy with Nano Composites

Authors: Ali. M --- Mohsen O.S.
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2013 Volume: 9 Issue: 2 Pages: 25-30
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

The microstructures of composites were examined using optical microscopy (OM) and transmission electron microscopy (TEM). Microscopic observations of the microstructures revealed that the dispersion of the particles was uniform. The tensile strength (yield strength and ultimate tensile strength) and the Young's modulus improve with the addition of nano particles although some reduction in ductility is observed. The highest yield strength and UTS was obtained by 3.5 vol. % of SiC nano-particles. A relatively ductile fracture in tensile fractured samples was observed by fractography examination.


Article
The Study of Dielectric and Microstructure Properties for Iraqi Kaolin Under the Effects of Binder and Calcinations.
دراسة الخواص العزلية والتركيبية للكاؤؤلين العراقي تحت تأثيرالمادة الرابطة وعمليات الكلسنة

Authors: F. A. Rasin فاضل عبد رسن --- R. S. Al-Khafaji رغد صبحي الخفاجي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2013 Volume: 54 Issue: 2 Pages: 333-339
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The calcination treatments and a binder of poly acrylic acid PAA (1wt%) effects on kaolinite particles were investigated through dielectric properties at 1MHz ,quantitative analysis of X-ray diffraction and microstructure. The calcinated samples at 850°C/3hr and fired at 1350°C/2hr were revealed decrease in broadening (Full Width at half maximum) FWHM and increase of dielectric constant.

ان المعاملة تحت تأثيرعمليات الكلسنة (التحميص) والمادة الرابطة بولي أكرلك أسد ((1wt% على حبيبات الكاؤؤلينيت تمت دراستها من خلال الفحوصات التشخيصية للاشعة السينية والمجهرية والقياسات العزلية وتبين ان العينة المكلسنة عند 850م˚لمدة 3ساعات والملبدة الى 1350 م˚لمدة ساعتين امتازت بنقصان في التعريض عند منتصف الشدة (FWHM) وزيادة في ثابت العزل.


Article
THEORETICAL AND EXPERIMENTAL INVESTIGATION OF FRICTION STION STIR WELDING FOR COPPER ALLOY
دراسة نظرية وعملية للحام الاحتكاكي لسبائك النحاس

Authors: Nabeel Shallal Thamer --- Ahmed Hadi Abood --- Dr. Hani Aziz Ameen
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2013 Volume: 6 Issue: 3 Pages: 332-351
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Friction stir welding (FSW) is a relatively new solid-state joining process. Thisjoining technique is energy efficient. In particular, it can be used to join highstrengthaerospace aluminum alloys and other metallic alloys that are hard to weldby conventional fusion welding. In this paper the investigation is made on frictionstir welding process for joining of copper alloy. Friction stir welding experimentswas performed using different pins (pin with straight boundary and pin with curvedboundary). Welding joints efficiencies were found for each set. Mechanical andmicrostructural analysis has been performed experimentally on the welding zone.Non- linear numerical models was built in ANSYS software to simulate thethermal history of a workpiece undergoing friction stir welding by a movingheating source. An accurate prediction of temperature fields is evident. Exclusiveresult for effect of rotating a friction stir tools with respect to boundary conditionson stress-strain curves is presented. The results shown that the friction stir weldingwith pin of curved boundary is more efficient than that of straight boundary

تعتبر عملية اللحام الاحتكاكي من اكفأ عمليات اللحام والتي تستعمل لربط المعادن مثل الالمينيوم والمعادن)FSW( الاخرى والتي من الصعوبة لحامها بالطرق التقليدية . في هذه الدراسة تم تطبيق الحام الاحتكاكيلسبائك النحاس من خلال تصميم وتصنيع نوعين من الأدوات )الدبوس بحواف مستقيمة والدبوس بحوافمنحنية(. وقد وجد ان كفاءة اللحام جيدة لكلا الحالتين وقد تم إجراء تحاليل ميكانيكية ومجهرية على منطقةاللحام . وقد تم انشاء موديل غير خطي ببرنامج الانسز لمحاكاة التأثيرات الحرارية خلال عملية اللحامباستخدام مصدر حراري متنقل . وقد تم الحصول على نتائج الخواص الميكانيكة منحنى )الاجهاد-الانفعال (لكلا الاوادت التي تم تصنيعها. وقد بينت النتائج ان اللحام باستخدام دبوس بحواف منحنية هو اكثر كفاءة منالحواف المستقيمة .


Article
The Influence of Microstructure on the Corrosion Rate of Carbon Steels
تأثير البنية المجهرية على معدلات تأكل الفولاذ الكربوني

Authors: Sami I. Al-rubaiey --- Eman A. Anoon --- Mahdi M. Hanoon
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 10 Part (A) Engineering Pages: 1825-1836
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper presents the influence of carbon steel microstructure on the corrosion rates. Four types of microstructures have obtained by quenching and tempering and iso-thermal annealing. These microstructures are: banded ferrite/pearlite microstructure, fine ferrite/pearlite microstructure, coarse ferrite/pearlite microstructure and tempered martensite microstructure. General corrosion and localized corrosion (penetration rates) were determined via mass loss and optical microscopy. The different microstructures of steels investigated in this paper revealed corrosion rate variations of 0.8– 3.2 mm y-1 and 3.3–6.4 - mm y-1 for the general and localized forms, respectively. The corrosion stability of the various microstructures may arise from variations of phases within the steel. A banded ferrite/pearlite microstructures have worse general corrosion properties, while tempered martensite worse microstructures have localized pitting corrosion properties. Coarse ferrite/pearlite microstructures have better localized pitting corrosion resistances compared to others investigated microstructures This paper has demonstrated that, microstructure is an important consideration when selecting carbon steel for an industrial corrosion resistance application.

يهدف البحث الحالي إلى دراسة تأثير بنية الفولاذ الكربوني على معدلات التآكل . تمت دراسة بنى مجهرية مختلفة, قسمت إلى أربعة مجاميع هي :حزم من الفرايت / البيرلايت ,المجموعة الثانية : الفرايت / البيرلايت الناعم, الفرايت / البيرلايت الخشن , المارتنزايت المراجع. تم كشف التآكل وحساب معدلاته بواسطة الفقدان بالوزن والمجهر الضوئي . بينت النتائج ان اختلاف البنى المجهرية يؤدي إلى تغير في معدلات التآكل من 0.8- 3.2 مم / سنة ومن 3.2 – 6.4 مم / سنة لكل من التآكل العام والتآكل الموضعي على التوالي. إن استقرارية التآكل تأتي من اختلاف البنى المجهرية . تمتلك حزم الفرايت / بيرلايت على مقاومة تأكل عام قليلة , بينما تمتلك بنية المارتنزايت المراجع مقاومة تأكل موضعي قليلة قيما تمتلك بنية الفرايت / البيرلايت الخشن على أفضل مقاومة تأكل موضعي مقارنة بالبني المجهرية المفحوصة الأخرى. أكدت نتائج البحث إن البنية المجهرية عامل مهم في اختيار الفولاذ الكربوني في التطبيقات الصناعية التي تتطلب مقاومة تأكل عالية .


Article
Study the Efffect of Adding Cu on Some Mechanical and Structural Properties of the Ag-Sn Alloy
دراسة تأثير إضافة النحاس على بعض الخصائص التركيبية والميكانيكية لسبيكة فضة-قصدير

Authors: Mohammed Obaid Kadhim --- Hassan Juma Abd --- Huda Khailed Hameed
Journal: Iraqi Journal of Science and Technology المجلة العراقية للعلوم والتكنولوجيا ISSN: 18136893 Year: 2013 Volume: 4 Issue: 3 Pages: 134-141
Publisher: Ministry of science and technology وزارة العلوم والتكنولوجيا

Loading...
Loading...
Abstract

In this Research, four high-copper amalgam alloys have been prepared by melting at 1050oC in an inert atmosphere, with copper content ranging from (14 to 26wt. %). Heat treatment processes were carried out to increase phases homogeneity and to reduce residual stresses, then, the alloys were mixed with mercury with a ratio of (1:1.2). Several structural measurements were carried out such as x-ray diffraction and microstructure analysis and some mechanical tests such as micro-hardness and compressive strength. X-ray diffraction results show that the amalgams and amalgams alloys have a variety of phases which depends on the copper content in the alloys. On the other hand, results of micro-hardness and compressive strength show that there is a linear increment in the mechanical properties with increasing copper in the amalgam, the results of D (Cu 26%) amalgam was comparable to those measured for the commercial amalgam of ANA that have high mechanical properties.

حضرت أربع سبائك ملغم عالية النحاس بصهرها عند درجة حرارة 1050oC في أجواء خاملة. وقد تراوحت نسب النحاس في السبائك بين (14~26wt.%) , تم إجراء معالجات حرارية لتحسين التجانس الطوري في السبائك وإزالة الإجهادات، أُجريت عملية الملغمة بخلط السبائك مع الزئبق بنسبة (1:1.2) ,أُجري عدد من القياسات التركيبية مثل تحليلات حيود الأشعة السينية وتحليلات البنية الدقيقة وبعض الخواص الميكانيكية المهمة مثل الصلادة ومقاومة الأنضغاط. وبينت تحليلات حيود الأشعة السينية وجود عدد من الأطوار الرئيسية في السبائك والملاغم تعتمد نسبها وتوزيعها على محتوى النحاس في السبيكة. بينما أظهرت نتائج قياسات الصلادة ومقاومة الانضغاط حصول زيادة خطية في الخصائص الميكانيكية مع زيادة النحاس في الملاغم. وكانت نتائج الملغم D (%26 Cu) مقاربة للقيم المقاسة للملغم التجاري ANA والذي يمتلك خصائص ميكانيكية عالية


Article
Fatigue Test of Coated Mild Steel with Nickel and Aluminum
فحص الكلال للصلب الطري المطلي بالنيكل والألمنيوم

Authors: Moyad A. Mohammad مؤيد عبد لله محمد --- Nawal E. Matti نوال ايشوع متي
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2013 Volume: 24 Issue: 1A Pages: 84-97
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

In this research, we try to study the fatigue resistance of coated mild steel 1020 AISI. The alloy was coated with Al in single process using pack cementation technique and Ni using electrodeposition technique. Both processes were also used for coating the same alloy (double layer coating). The fatigue resistance of these coating was compared with the base alloy and with those subjected to a heat treatment at the same conditions of time and temperature. The aim of this study was to understand the effect of the temperature and coating type on the fatigue life. The results obtained, based on XRD, Fatigue test, optical microstructure and hardness measurement, that the temperature of heat treatment played the major rule of fatigue life reduction. This can be attributed to the phase transformation of α­ ferrite steel to pearlite ( ferrite + cementite). The results also showed that the coating types have a very important effect on fatigue life. The coatings performed at high temperature (aluminizing) revealed a negative effect on the fatigue life. This is due to the formation of a new brittle and less ductility of Fe-Al phase on the alloy surface. The electrodeposition of Ni leads to a positive effect which is due to an improvement in surface conditions of the alloys via filling the voids or other defects which are present at the surface. The double layer coating (Ni-Al) applied to some specimens shows some improvement in fatigue resistance, in comparison with a single aluminized specimen. This was attributed to the formation of multiphase layer consisting of Fe-Al and Ni-Al intermetallic compound.

تم في هذا البحث دراسة مقاومة الكلال لسبيكة الصلب الطري ( Mild Steel) المطلية بطلاءات منفردة هما الألمنيوم (بتقنية السمنتة) مع النيكل بطريقة الترسيب الكهربائي إضافة إلى طلاءات مزدوجة هي النيكل والألمنيوم كلاهما معا. تم مقارنة النتائج البحثية بالسبيكة الأساس قبل وبعد معاملتها حراريا بشروط الزمن ودرجات الحرارة نفسها وذلك لمعرفة مدى تأثير كلًٍّ من درجة الحرارة و نوعية الطلاء على عمر الكلال.أثبتت نتائج البحث العلمي بالاعتماد على نتائج الأشعة السينية، فحص الكلال، الفحص ألمجهري، قياس الصلادة بأن درجة الحرارة تلعب الدور الأهم في تناقص عمر الكلال، كما أثبتت النتائج العملية أن لنوع الطلاء تأثيرا" مهما على عمر الكلال حيث الطلاء الذي ينجز في درجات حرارية عالية مثل الطلاء بالألمنيوم (الالمنة) له تأثير سلبي على عمر الكلال، في حين إن الطلاء بالترسيب الكهربائي مثل الطلاء بالنيكل يكون له تأثير ايجابي إذ يحسنَ من حالة سطح السبيكة عن طريق ملء الفجوات أو العيوب الأخرى المتواجدة على السطح. أما الطلاء المزدوج (نيكل-ألمنيوم) فقد اظهر تحسنا" لمقاومة الكلال مقارنة بالألمنيوم المنفرد بسبب اشتراك الحديد-ألمنيوم ونيكل-ألمنيوم في تكوين طبقة الطلاء.


Article
The Effect of Tool Path Strategy on Mechanical Properties of Brass (65-35) in Single Point Incremental Sheet Metal Forming (SPIF)
تأثير مسار العدة على الخواص الميكانيكية في التشكيل النقطي التزايدي لسبيكة البراص35-65

Authors: Qasim Mohammed Doos Al-Attaby قاسم محمد دوس --- Tahseen Fadhel Abaas تحسين فاضل عباس --- Aqeel Sabree Bedan عقيل صبري بدن
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 5 Pages: 629-636
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this paper, three tool paths strategies; iso-planar, helical and adaptive have been implemented to investigates their effect on the mechanical properties of Brass 65-35 formed by single point incremental sheet metal forming process. To response this task, a fully digital integrated system from CAD modeling to finished part (CAD/CAM) for SPIF process has been developed in this paper.The photo-micrographs shows an identical grain formation due to the plastic deformation of the incremental forming process, change in the grain shape and size was observed. It's found that the adaptive tool path play a significant role to increase the hardness of the formed specimen from (48 to 90 HV) and the grain texture of the formed specimen found as round shape, while the hardness is increased in little amount from (48 to 74 HV) in the specimen formed using helical and it’s grain texture was found as needle shape

تم في هذا البحث اعتماد ثلاثة طرق لمسار العدة في دراسة تاثيرها على الخواص الميكانيكية لسبيكة البراص (65-35) عند تشكيلها بطريقة التشكيل النقطي التزايدي وباستخدام نظام تصميم وتصنيع متكامل تم تطويره لانجاز هذا البحث, تبين من خلال الفحص المجهري للعينات المنجزة بان البنية المجهرية قد تغيرت من ناحية الشكل والحجم نتيجة التشكيل اللدن من جراء التشكيل واستنتج بان مسارات العدة لها اثر كبير في تغير الخواص من ناحية الصلادة والبنية المجهرية حيث تبين بان مسار العدة المحسن (Adaptive) رفع من صلادة النماذج المشكلة (48-90) وحافظ على الشكل الدائري للبنية المجهرية للبراص في حين ان مساري العدة (Isoplaner and Helical) قد رفعا الصلادة بمقدار اقل من الاول(48-74) بينما تغيرت البنية المجهرية للنماذج المشكلة حيث تم الحصول على بنية مجهرية طولية الشكل.


Article
Evaluation Of Future Performance of Northern Fatha Storage System
دراسة تأثير الضغط المسلط على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 باستخدام السباكة بالعصر

Author: د. فاروق منصور مهدي د. نجيب سلمان عبطان سعد رمضان احمد
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2013 Volume: 20 Issue: 4 Pages: 11-17
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This present study shows ,the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Alumium alloy A380 was studied .From fig(5) its clear that ,the microstructure of prepare casting samples consist of two phases hard eutectic (Al-Si) and Primary α-Al.The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84)MP

تم في هذا البحث دراسة تاثير الضغط المسلط ضمن المدى (10-84) ميكاباسكال خلال عملية السباكة بالعصر المباشر على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 من الخردة , تبين من خلال البنية المجهرية ان البنية تتكون من طورين هما طور اليوتكتك الصلد وطور الالمنيوم الاولي وكذلك وجدنا من خلال علاقة الضغط المسلط وكسر المساحة لطور اليوتكتك ان نسبة كسر المساحة تزداد عند الضغوط (68,84) ميكاباسكال بينما قلت هذه النسبة عند الضغوط (10,17,34) ميكاباسكال . ومن خلال دراسة العلاقة بين الضغط المسلط بمدياته الخمسة والكثافة الحقيقية نلاحظ زيادة الكثافة بزيادة الضغط المسلط (10-17) ميكاباسكال وكذلك عند الضغط (84) ميكاباسكال.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (5)

Arabic (3)

Arabic and English (1)


Year
From To Submit

2013 (9)