Frequency Dependent Capacitance –Voltage and Current Density Characteristic of Al/PS/p-Si Heterojunction
إعتماد التردد على خصائص السعة – فولتية وكثافة التيار للمفرق الهجين Al/PS/p-Si

Authors: Hassan Juma Abd حسن عبد الصاحب هادي --- Hasan Abdulsaheb Hadi حسن جمعه عبد
Journal: Iraqi Journal of Science and Technology المجلة العراقية للعلوم والتكنولوجيا ISSN: 18136893 Year: 2014 Volume: 5 Issue: 1 Pages: 89-96
Publisher: Ministry of science and technology وزارة العلوم والتكنولوجيا

Loading...
Loading...
Abstract

In this paper, formation of microstructures porous silicon layer (PS) on c-Si substrate p-type with resistivity’s10 Ω.cm which was prepared by the electrochemical etching (ECE) is presented. The etching current densities (40 and 50 mA.cm-2) were used in the electrochemical etching procedure leading to the formation of 1.08 µm and 1.34µm thick porous layers respectively at constant etching time 300sec. From the current – voltage characteristics of the PS/p-Si, the potential barrier were determined and found to be (0.54 and 0.53 eV) respectively. C-V measurements performed on metal/porous silicon/crystalline silicon structures with different etching current densities and frequency depended

في هذا البحث تم تشكيل التركيب المايكروي لطبقة السيليكون المسامي(PS) على القاعدة السيليكونية من النوع الموجب ذي المقاومية 10 Ω.cm المحضر بطريقة التنميش الكهروكيميائية . ان قيم كثافات تيار التنميش في الطريقة المستخدمة للحصول على سمكي طبقة السيليكون المسامي 1.08 µm و 1.34µm هي على التوالي (40 mA.cm-2 و 50 mA.cm-2) بثبات زمن التنميش عند القيمة 300 ثانية. من خصائص تيار –فولتية للتركيب PS/p-Si تم حساب قيمة حاجز الجهد والذين هما 0.54 ev و 0.53 ev لكلا التركيبين على التوالي. دراسة خصائص السعة – فولتية لتركيب المعدن/ السيليكون المسامي/السيليكون البلوري والتي اعتمدت على كل من كثافة تيار التنميش والتردد


Article
Preparation of Barium Ferrite Powder and Studying the Effect of Glucose Concentration on the Coefficient of Magnetic Viscosity
تحضير مسحوق الباريوم فرايت ودراسة تاثير تراكيز الكلوكوز على معامل اللزوجة المغناطيسي

Loading...
Loading...
Abstract

The preparation of Barium Ferrite powder doped with Cobalt (Co) and Titanium (Ti) to produce , where (x= 0.5), is made by using Glass crystallization method. The effect of the presence of Glucose, at different concentration, on the coefficient of magnetic viscosity (S) of the doped compound by using Vibrating Sample Magnetometer (VSM). The results indicated that the coefficient of magnetic viscosity (S) increased with the increase of the applied magnetic field (Ha) and reached a maximum at the Remanence Coercivity magnetic field (Hcr), and it started to decrease. Also, increasing of the Glucose concentration tends to decrease the coefficient of magnetic viscosity (S) due to the decline of Barium ferrite particles in the system.

حضرت عينات من الباريوم فرايت (BaFe12-2xCoxTixO19 ) المطعمة بشوائب من الكوبلت والتيتانيوم بنسبة (x=0.5) بطريقة التبلور الزجاجي، درس تأثير تركيز الكلوكوز على معامل اللزوجة المغناطيسي لهذه العينات باستخدام جهاز المقياس المغناطيسي (VSM)، وقد تبين أن قيمة معامل اللزوجة المغناطيسي (S) تزداد مع زيادة المجال المغناطيسي المطبق (Ha) ويصبح لها قيمة عظمى عند المجال المغناطيسي القسري المتبقي (Hcr) ثم تبدأ بالتناقص بعد ذلك مع زيادة المجال المغناطيسي المطبق، كما تبين أن الزيادة بتركيز الكلوكوز تؤدي الى تناقص قي قيمة معامل اللزوجة المغناطيسي بسبب انخفاض تركيز جسيمات الباريوم فرايت داخل النظام