Shear Behavior of Self Compacting Concrete Deep Beams

Loading...
Loading...
Abstract

This study deals with shear behavior of self compacting concrete (SCC) deep beams. The experimental work includes testing eight reinforced concrete simply supported deep beams cast using SCC. All tested beams have dimensions of 100×330×1050 mm and have been subjected to two point loads. The parameters considered are shear span to effective depth ratio (a/d), concrete compressive strength (fʹc) and vertical web reinforcement ratio (v). Test results indicated that the increase in (a/d) ratio from 0.6 to 1 leads to decreases in cracking and ultimate shear strengths by average ratios of 28.6 % and 23.3 % respectively. Increasing (fʹc) from 32.84 MPa to 64.65 MPa leads to increases in the cracking and ultimate shear strengths by average ratios of 11.7 % and 38.8 % respectively. Increasing the vertical web reinforcement ratio (v) from 0.25 % to 0.57 % leads to an increase in the ultimate shear strength by average ratio of 10.1 %. The analytical work includes derivation of new method for predicting ultimate shear strength of SCC deep beams depending on modified strut and tie model with adoption of a circular failure interaction relation. The new method gives high agreement with the experimental results by comparison with the ACI-2011 Code method.

تتناول هذه الدراسة سلوك القص للعتبات العميقة المصنوعة من الخرسانة ذاتية الرص. يتضمن البرنامج فحص ثمانية من العتبات الخرسانية المسلحة العميقة ذات الاستناد البسيط المصبوبة باستخدام الخرسانة ذاتية الرص. جميع العتبات كانت بإبعاد 100×330 ×1050 ملم ومعرضة لحملين مركزين. المتغيرات المعتبرة في هذه الدراسة هي نسبة فضاء القص الى العمق الفعال (a/d)، مقاومة انضغاط الخرسانة (fʹc) ونسبة تسليح القص العمودي (v). نتائج الفحص اظهرت ان الزيادة في نسبة (a/d) من 0.6 الى 1 تؤدي إلى نقصان في مقاومة التشقق والمقاومة القصوى بمعدل نسب 28.6 % و 23.3 % على التوالي. الزيادة في (fʹc) من 32.84 MPaالى 64.65 MPa يؤدي إلى الزيادة في مقاومة التشقق والمقاومة القصوى بمعدل نسب 11.7 % و 38.8 % على التوالي. زيادة نسبة تسليح القص العمودي (v) من0.25 % إلى 0.57 % يؤدي إلى زيادة في مقاومة القص القصوى بمعدل نسب 10.1 %. الجزء التحليلي من هذه الدراسة تضمن اشتقاق طريقة جديدة لاحتساب مقاومة القص القصوى لهذا النوع من العتبات بناءا ً على الطريقة المطورة لتقنية (strut and tie model) باعتماد علاقة خط الفشل الدائري. الطريقة الجديدة تعطي توافق عالي مع النتائج العملية بالمقارنة مع الطريقة المعتمدة من قبل (ACI-2011 Code).


Article
Shear Behavior of Fibrous Self Compacting Concrete Deep Beams
سلوك القص لعتبات الخرسانة ذاتية الرص العميقة المسلحة بالألياف

Loading...
Loading...
Abstract

Self compacting concrete (SCC) is a relatively new generation of concrete that is characterized by its liquid nature that makes it appropriate for cast the narrow members such as deep beams without vibration. The work aims to investigate the behavior of SCC deep beams and evaluate their shear capacity especially when steel fibers are used in their construction. The experimental work includes testing twelve reinforced concrete simply supported deep beams cast using self compacting concrete (SCC) with steel fibers to evaluate their shear behavior and strength. All tested beams have dimensions of (100×330×1050) mm and have been subjected to two point loads. The parameters considered are shear span to effective depth ratio (a/d), concrete compressive strength (fʹc) and steel fiber volumetric ratio (Vf). Test results indicated that the increase in (a/d) ratio from 0.6 to 1 leads to decreases in cracking and ultimate shear strengths by average ratios of 25.1 % and 20.6 % respectively. Increasing (fʹc) to the twice of the origin value leads to increases in the cracking and ultimate shear strengths by average ratios of 13.9 % and 48.1 % respectively. Using steel fibers in SCC deep beams improves cracking and ultimate shear strength by average ratios of 33.1 % and 11.4 % respectively when 0.4 % of steel fibers is used while they improve these shear strengths by average ratios of 64.4 % and 23 % when 0.8 % of steel fibers is used. The analytical work includes derivation of new equation for predicting ultimate shear strength of fibrous SCC deep beams depending on regression analysis of test results. The new proposed equation gives good agreement with the experimental results by comparison with the ACI318M-1999 Code equation and Rao-2012 Equation.

الخرسانة ذاتية الرص عبارة عن جيل جديد نسبيا ً من الخرسانة التي تتميز بطبيعتها السائلة والتي تجعلها ملائمة لصب الاعضاء الانشائية الضيقة كالعتبات العميقة بدون الحاجة الى عملية الرص. يهدف العمل الى تحري السلوك الانشائي للعتبات العميقة المصنعة من هذا النوع من الخرسانة وتقييم تحملها لقوى القص خصوصا ً عند استخدام الياف الحديد في انشاءها. يتضمن الجزء فحص اثنى عشر من العتبات الخرسانية المسلحة العميقة ذات الاستناد البسيط المصبوبة باستخدام الخرسانة ذاتية الرص مع استخدام الياف الحديد للتعرف على سلوك ومقاومة هذا النوع من العتبات. جميع العتبات كانت بإبعاد (100×330 ×1050) ملم ومعرضة لحملين مركزين. المتغيرات المعتبرة في هذه الدراسة هي نسبة فضاء القص الى العمق الفعال (a/d) ومقاومة انضغاط الخرسانة (fʹc) والنسبة الحجمية لالياف الحديد (Vf). نتائج الفحص دلت ان الزيادة في نسبة (a/d) من 0.6 الى 1 تؤدي إلى نقصان في مقاومة التشقق والمقاومة القصوى بمعدل نسب 25.1 % و 20.6 % على التوالي. الزيادة في (fʹc) الى ضعف القيمة الاصلية يؤدي إلى الزيادة في مقاومة التشقق والمقاومة القصوى بمعدل نسب 13.9 % و 48.1 % على التوالي. استخدام ألياف الحديد في العتبات العميقة المعدة باستخدام الخرسانة ذاتية الرص يحسن مقامة التشقق والمقاومة القصوى بمعدل نسب 33.1 % و 11.4 % على التوالي عند استخدام نسبة 0.4 % من ألياف الحديد بينما يحسن هذه المقاومات بمعدل نسب 64.4 % و 23 % عند استخدام نسبة 0.8 % منها. الجزء التحليلي من هذه الدراسة يتضمن اشتقاق معادلة جديدة لاحتساب مقاومة القص القصوى لهذا النوع من العتبات اعتمادا على التحليل الرجعي للنتائج العملية. المعادلة الجديدة المقترحة تعطي توافق جيد مع النتائج العملية بالمقارنة مع معادلة الكود الامريكي (ACI318M-1999 Code) ومعادلة مقترحة حديثا من قبل احد الباحثين (Rao-2012 Equation).


Article
Experimental Study on the Behavior of Normal and High Strength Self-compacting Reinforced Concrete Corbels
دراسة عملية لسلوك الكتائف الخرسانية المسلحة والمصنوعة من الخرسانة الذاتية الرص ذات المقاومة الاعتيادية والعالية

Loading...
Loading...
Abstract

The main purpose of this experimental study is to investigate the behavior and strength of self-compacting reinforced concrete corbels with and without steel fibers. The program included (10) specimens, in which the shear span to effective depth ratio (a/d), the amount of steel fiber (Vf), and compressive strength(f'c)of self-compacting concrete were varied. All specimens had the same length, thickness and main reinforcement and they were subjected to concentrated vertical loads only.It was found that the addition of steel fibers delays the formation of the cracking of fibrous corbel relative to nonfibrous corbels and the cracking load and ultimate load for Normal strength self-compacting concrete(NSCC) corbels increase by 31.5% and 25.3% when the volume of steel fibers increases from 0% to 0.4%. While the cracking and ultimate loads increases by 7.3% and 3.1% when the volume of steel fibers increases from 0.4% to 0.8% and the increase in volume of steel fibers from 0% to 0.8% results in increasing the cracking load and ultimate load by about 41.1% and 29.1% respectively.

يهدف البحث لدراسة سلوك ومقاومة الكتائف الخرسانية المسلحة ذاتية الرص والرص والمعززة بالالياف او بدونها ويتضمن برنامج البحث (10 ) نماذج ذات ابعاد وكمية حديد تسليح رئيسة ثابتة ،والمتغيرات التي تم تناولها في البحث نسبة فضاء القص الى العمق الفعال ( 0,3 ، 0,45 ، 0,6 ) ونسبة الالياف الحديدية ( 0 ، 0,4 ، 0,8 ) % ومقاومة الانضغاط.لقد وجد من خلال البحث ان اضافة الالياف الحديدية يؤخر تكون حمل التشقق في الكتائف الخرسانية المسلحة ، كما وجد ان حمل التشقق والحمل الاقصى يزداد بنسبة ( 31,5 ، 23,3 )% عندما تزداد نسبة الالياف الحديدية من ( 0 الى 0,4 )% , وان زيادة نسبة الالياف الحديدية من (0,4 الى 0,8 )% يؤدي الى زيادة حمل التشقق والحمل الاقصى بنسبة (7,3 ،3,1 ) % ، كما ان زيادة نسبة الالياف الحديدية من ( 0 الى 0,8 ) % تؤدي الى زيادة حمل التشقق والحمل الاقصى بنسبة (41,1 ، 29,1 ) % على التوالي.


Article
EFFECT OF HYBRID MICRO STEEL-POLYPROPYLENE FIBERS ON HIGH STRENGTH CONCRETE WITH MICRO SILICA FUME
تأثير هجين الياف الحديد الدقيقة-البولي بروبلين على الخرسانة عالية المقاومة الحاوية على غبار السلكا الدقيقة

Author: Othman Hameed Zinkaah عثمان حميد زنكاح
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2014 Volume: 3 Issue: 1 Pages: 90-102
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

The present investigations consider the effect of hybrid micro steel- polypropylene fibers on high strength concrete. The fractions of steel and polypropylene fibers are 1% and 0.5% by volume respectively. Many mixes have been investigation by combination between steel fibers and polypropylene fibers with different percentages it is (0%S.F-100%P.P.F), (100%S.F-0%P.P.F), (25%S.F, 75%P.P.F), (50%S.F-50%P.P.F), (75%S.F-25%P.P.F) in addition to reference mix. Properties of high strength concrete such as compressive strength, splitting strength, flexural strength, static modulus of elasticity, and absorption have been studied. The results showed that, the compressive strength decrease by about 28% when adding (0%S.F-100%P.P.F), and there are a small increasing with adding (100%S.F-0%P.P.F). However the results showed that there are an inverse relationship between compressive strength and the amount of polypropylene fibers. Experimental work also showed that adding (0%S.F-100%P.P.F)decrease the splitting strength by about 16%, while using hybrid fibers increase the splitting strength but less than its increasing when adding (100%S.F-0%P.P.F). It can be concluded that, the maximum effect of hybrid fibers is on the flexural strength, it is reach to 128% more than reference mix. Furthermore absorption increases by using polypropylene fibers.

هذا البحث أخذ بنظر الاعتبار تأثير مزيج الألياف الحديدية وألياف البولي بروبلين على الخرسانة عالية المقاومة. إن نسبة ألياف الحديد والبولي بروبلين هي 1% و0,5% على التوالي. عدة خلطات تم الاستقصاء عنها وذلك بالمزج بين ألياف الحديد والبولي بروبلين بنسب مختلفة وهي (0% ألياف حديد-100% ألياف البولي بروبلين), (100% ألياف حديد-0% ألياف البولي بروبلين), (25% ألياف حديد-75% ألياف البولي بروبلين), (50% ألياف حديد-50% ألياف البولي بروبلين), (75% ألياف حديد-25% ألياف البولي بروبلين) بالإضافة إلى الخلطة المرجعية. مواصفات الخرسانة العالية المقاومة تم دراستها كمقاومة الانضغاط و مقاومة الانشطار ومعامل الإنحاء ومعامل المرونة ونسبة الامتصاص. النتائج أظهرت إن مقاومة الانضغاط تقل بنسبة 28% بإستخدام (0% ألياف حديد-100% ألياف البولي بروبلين) وعند استخدام (100% ألياف حديد-0% ألياف البولي بروبلين) تزداد مقاومة الانضغاط بنسبة صغيرة . لكن النتائج أظهرت إن هناك علاقة عكسية بين زيادة نسبة ألياف البولي بروبلين ومقاومة الانضغاط. النتائج العملية أظهرت أيظا إن إضافة (0% ألياف حديد-100% ألياف البولي بروبلين) تقلل من مقاومة الانشطار بنسبة 16% ولكن استخدام مزيج الألياف يزيد من مقاومة الانشطار ولكن هذه الزيادة أقل من الزيادة الناتجة من استخدام (100% ألياف حديد-0% ألياف البولي بروبلين). ويمكن الاستنتاج إن أكثر تأثير لمزيج الألياف هو على مقاومة الانحناء حيث تصل الزيادة إلى 128% أكثر من الخلطة المرجعية. بالإضافة إلى إن نسبة الامتصاص تزداد بإستخدام ألياف البولي بروبلين.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic and English (3)

English (1)


Year
From To Submit

2014 (4)