The Rheological Properties of Isothermal Curing of DGEBA/ TETA Epoxy System
دراسة الخواص الريولوجية بثبوت درجة الحرارة لعملية تقسية راتنج الايبوكسي بأستخدم مادة تراي اثلين تترا امين

Authors: Adnan A. Abdul Razak --- Najat j. Saleh --- Maryem Emad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (A) Engineering Pages: 1095-1112
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study viscosity (η) of diglycidyl ether of bisphenol A / triethylenetetramine (DGEBA/TETA) system were measured through curing using a Brookfield viscometer at four different temperatures (30, 45, 60 and 80) °C. The measurements were carried out for two hardener/resin ratios (13 and 20) phr. The gel time was calculated for each hardener/resin ratio formulation; from the viscosity experimental data. The results showed that the gel time decrease with increasing curing temperature for each hardener/resin ratio formulation. Viscosity profiles were described by a model based on the Boltzmann function. The fitted results agreed well with the experimental values.

في هذا البحث تم قياس اللزوجة لنظام مكون من (DGEBA/TETA ) خلال عملية الانضاج بأستخدام مقياس اللزوجة من نوع Brookfieldفي اربع درجات مختلفة (30,45,60,80) م0 . تم أخذ القياسات باستخدام نسبتين للراتنج / المصلد وهما (13) و(20) جزء من المائة .تم حساب زمن التصلب gel time)) لكل نسبة من الراتنج/ المصلد من قياسات اللزوجة . أظهرت النتائج بان زمن التصلد يزداد مع زيادة درجة الانضاج لكل نسبة من نسب الراتنج/ المصلد . تم وصف منحنى اللزوجة بموديل يعتمد على موديل (Boltzman) وتم مطابقة النتائج المستخلصة من الموديل مع النتائج المختبرية وظهر تطابق كبير بينهما .

Keywords

Epoxy Resin --- Curing --- Rheology --- Hardener