Studying the Corrosion Resistance of Anodized Low Carbon Steel in Alkaline Solution

Author: Sami A.Ajeel
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2015 Volume: 8 Issue: 2 Pages: 159-170
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Low carbon steels are widely used materials in industrial application due to its availability and properties. Therefore it always needs to improve its properties especially corrosion resistance. One of the most important methods for improving its corrosion resistance is anodizing process. This study involves anodized of low carbon steels in 1 M sodium hydroxide (alkaline) electrolyte for 30 minute, using constant current technique at a range of (20-620) mA/cm2.Atomic force microscope (AFM) used to investigate the topography and anodic film parameters, it was found that the roughness of the anodic film is mainly depend on the anodizing current density and its increase from 0.9 (as polished) to (0.281-0.598) nm after anodizing. Coating thickness also increases with an increase in current density supply to the range of (2.5-13.3) μm. The corrosion behaviors of anodized and non-anodized of low carbon steel specimens in sea water are obtained. The corrosion current density and corrosion rate are decreased with an increase in anodic current density which increases anodic film thickness.

يستخدم الصلب الكاربوني بشكل واسع في التطبيقات الصناعية لوفرته وخواصه الجيدة، لذلك تبرز حاجة دائمية لتحسين خواصهوخاصة خواص التآكل. احد الطرق المهمة لتحسين مقاومة التآكل هي عملية الأنودة حيث تتضمن هذه الدراسة انودة الصلب- الكاربوني في مول واحد من محلول هيدروكسيد الصوديوم بزمن قدره 03 دقيقة بأستخدام تقنية التيار الثابت بمدى 003 03. امبير/سم 0تم استخدام جهاز القوة الذرية ) AFM ( لدراسة طبوغرافية سطح الأنودة، لقد وجد بأن خشونة طبقة الأنودة تعتمد بصورة رئيسيةعلى كثافة تيار الأنودة حيث تزداد من ) 0.09 nm للمعدن الصقيل( الى 0.598 nm) ( بعد الأنودة. سمك التغطية يزداد كذلكمع الزيادة في كثافة التيار المسلط الى ) 13.3 μm (. تم الحصول على سلوك التآكل للصلب الكاربوني قبل وبعد عملية الأنودةبأختلاف تيار التآكل حيث تم ملاحظة ان معدل التآكل يتناقص مع زيادة كثافة التيار الذي بدوره يزيد من سمك طبقة الأنودة.


Article
Heat Treatment Effect on Anodizing Corrosion Resistance of Low Carbon Steel
تأثير المعاملات الحرارية على مقاومة التآكل للصلب الكاربوني المنخفض المؤنود

Author: Sami A. Ajeel سامي ابو النون عجيل
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2015 Volume: 18 Issue: 2 Pages: 250-258
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This work involves studying heat treatment effect on anodized low carbon steel using electrochemical measurements. Heat treatments of low carbon steel before anodizing were applied by anodizing at different temperatures of 650, 900, and1000°C for one hour. Anodizing process was used for non-annealed and annealed low carbon steel at the above temperatures in KOH solution. The electrochemical behavior of low carbon steel, anodized low carbon steel, and anodized annealing low carbon steel at the above temperatures in 3.5 wt% NaCl solution using potentiostat device. Corrosion rates for the above conditions were measured. The corrosion rates measured results indicate an improvement in corrosion resistance of anodized annealing low carbon steel. Surface characterization of anodic film on low carbon steel was examined anodic film on low carbon steel using Atomic force microscopy (AFM) and optical microscopy used to examine the specimens before and after corrosion test. the practical results indicate the best conditions to obtain higher corrosion resistance are for anodized low carbon steel annealed the steel before anodizing at 1000 °C.

يتضمن البحث دراسة تأثير المعاملات الحرارية لانودة الصلب الكربوني باستخدام القياسات الكهروكيميائية . أجريت معاملة حرارية للصلب الكربوني المنخفض قبل الانودة بالتلدين عند درجات الحرارة (1000,900,650) م˚ لمدة ساعة واحدة ثم انودة سطح الصلب الكربوني المنخفض غير الملدن والملدن بالدرجات الحرارية اعلاة في محلول هيدروكسيد الصوديوم . يتم دراسة السلوك الكهروكيميائي للصلب الكربوني المنخفض , الصلب الكربوني المنخفض بعد الانودة و الصلب الكربوني المنخفض الملدن بالدرجات الحرارية أعلاه المؤنود في (3.5 wt% NaCl) محلول كلوريد الصديوم بأستخدام المجهاد الساكن . معدلات التآكل للمواد أعلاه تم قياسها . تشير نتائج معدلات التأكل المقاسة الى تحسين في مقاومة التأكل للصلب الكربوني المنخفض الملدن بالدرجات الحرارية اعلاة بعد الانودة . تم فحص خصائص السطحية لطبقة الانودة باستخدام مجهر القوة الذرية (AFM) والمجهر الضوئي لفحص العينات قبل وبعد أختبار التآكل . تشير النتائج العملية بأن أفضل ظروف للحصول على أعلى مقاومة تأكل هو للصلب الكربوني المنخفض المؤنود عند التلدين عند درجة حرارة 1000م˚.