Effect of amount of amonia on Optical Properties of Nano (ZnS) Film prepared by CBD Technique
تأثير كمية الأمونيا على الخواص البصرية لغشاء (ZnS) النانوي المحضر بأستخدام تقنية الترسيب بالحمام الكيميائي(CBD)

Loading...
Loading...
Abstract

The research includes the study of the effect of the amount of ammonia (2, 5 and 8) ml on the optical properties of the membrane zinc sulfide (ZnS) nanoscale . Nanofilms attended using a chemical bath deposition method . The included optical properties: transmittance , absorbance , reflectivity , absorption coefficient , refractive index , extinction coefficient , the optical energy gap and the dielectric constant partially real and imaginary . It has been observed that increasing the amount of ammonia led to increased values of forbidden energy gap , has been prepared all models in concentration (0.05 M) and temperature (70 OC) and the time of deposition (30 min) where these conditions are optimal conditions for obtained on nanofilm by (CBD ) . It was to increase the amount of ammonia , clear effect on the thickness of the film were obtained on nanofilm in thickness (100nm) when the amount of ammonia (8ml). Was also noted that increase of ammonia may change clearly the rest of the optical properties.

تضمن البحث دراسة تأثير كمية الأمونيا ml (2 , 5 and 8) على الخواص البصرية لغشاء كبريتيد الخارصين (ZnS) النانوي . الأغشية النانوية حضرت بأستخدام طريقة ترسيب الحمام الكيميائي . وقد تضمنت الخواص البصرية: النفاذية، الأمتصاصية، الأنعكاسية ، معامل الأمتصاص، معامل الأنكسار، معامل الخمود، فجوة الطاقة البصرية وثابت العزل الكهربائي بجزئيه الحقيقي والخيالي. وقد لوحظ أن زيادة كمية الأمونيا أدى الى زيادة قيم فجوة الطاقة الممنوعة ، وقد تم تحضير جميع النماذج بتركيز(0.05 M) ودرجة حرارة (70 OC) وزمن ترسيب (30 min) حيث كانت هذه الظروف هي الظروف المثلى للحصول على غشاء نانوي بطريقة (CBD). وكان لزيادة كمية الأمونيا تأثير واضح على سمك الغشاء حيث تم الحصول على الغشاء النانوي بسمك (100nm) عند كمية أمونيا (8ml) .كما لوحظ أن زيادة الأمونيا قد أثر وبشكل واضح على بقية الخواص البصرية .


Article
Electrical properties of Nano crystalline ZnxCd1-xS thin films prepared by CBD technique
الخصــــــائــــص الكهربــائيـــــة لأغشيـــــــــة ZnxCd1-xS النانــــويـــــــة المحضــــــرة بتقنيـــــة الترسيـــب بالحمـــام الكيميـــائــي

Authors: Jamal F. Mohammad --- Hamed. S. Al-jumaili
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 7 Part (B) Scientific Pages: 1267-1272
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Nanocrystalline zinc cadmium sulfide (ZnxCd1-xS) thin films were deposited on glass substrate by chemical bath deposition (CBD) technique using the mixed aqueous solution of zinc chloride ((ZnCl2), cadmium chloride (CdCl2), thiourea (CS(NH2)2) and ammonia solution (NH4OH). The as deposited films were characterized by high quality instrument type (HMS-3000). The results show that all the prepared films have n-type conductivity; this is concluded from the Hall measurements. The electrical conductivity is found to decrease with increasing x, while the activation energies are found to be increasing from (0.458 to 0.860 eV) as x increase from ( 0.1to 0.9).

تم ترسيب اغشية كبريتيد خارصين- كادميوم (ZnxCd1-xS) النانوية على ارضيات زجاجية بتقنية الترسيب بالحمام الكيميائي باستخدام محلول كلوريد الخارصين (ZnCl2) ، كلوريد الكادميوم (CdCl2) ، الثايوريا (CS(NH2)2) ومحلول الامونيا (NH4OH). تم فحص الاغشية المحظرة باستخدام جهاز نوع (HMS-3000) حيث بينت النتائج باستخدام جهاز هول ان الاغشية المحظرة ذات توصيلية من النوع السالب (n-type) وان التوصيلية الكهربائية تتناقص كلما زادت قيمة x ، بينما طاقات التنشيط تزداد من 0.458 الى 0.860 الكترون- فولط عندما تزداد قيمة x من 0.1 الى 0.9


Article
Study the Structural, Optical and Electrical Conductivity Properties of Copper Oxide Thin Films Prepared by Chemical Bath Deposition
دراسة الخواص التركيبية والبصرية والتوصيلية الكهربائية لأغشية اوكسيد النحاس المحضر بتقنية الترسيب الكيميائي

Loading...
Loading...
Abstract

Copper oxide thin films were prepared on glass substrate by using chemical bath deposition (CBD) method, with thickness of 0.23μm. In this study, aqueous solutions of copper oxide at low temperature were used. The structural (nano structure) of the film was studied by using X-ray diffraction (XRD), optical examination microscopic and Scanning electron micrographs (SEM). Also electrical conductivity and optical properties by were studied. The band gap energy was ~2.6eV.

في هذا البحث حضر اوكسيد النحاس بسمك 0.23 μm بتقنية الترسيب الكيميائي (CBD) على قواعد زجاجية. كما وحددت في هذه الدراسة المحاليل المائية لأوكسيد النحاس بدرجة حرارة منخفضة ، ودرست الخصائص التركيبية (التركيب النانوية) باستخدام فحوصات حيود الاشعة السينية(XRD) ومجهر الفحص البصري و الماسح الضوئي (SEM), وكذلك درست التوصيلية الكهربائية والخصائص البصرية للأغشية المحضرة. وجد ان فجوة الطاقة كانت (~2.6 eV).