Mechanical Properties for Polymer Hybrid Composites Reinforced by Fibers and Particles
الخواص الميكانيكية لمتراكبات بوليمرية هجينة مقواةبالالياف والدقائق

Author: Ruaa Haitham Abdel-Rahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 3 Part (A) Engineering Pages: 635-643
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The Mechanical properties of hybrid composites based on epoxy resin (ER) filled with metal powders (Al) and Glass fibers (GF) are studied. The specimens are prepared using hand lay-up techniques according to ASTM standard for different volume fractions of fiber, particles& matrix material. Glass fibers (GF) are one of the most useful filler materials in composites, its major use being the manufacture of components in the aerospace, automotive, and leisure industries. The epoxy was reinforced with GF:( metal powders)in the ratio 10%:40%, 20%:30%, 30%:20%, and 40%:10%. It was observed that in the ratio 40%:10% has the maximum(UTS), fracture strength, flexural strength, fracture toughness and hardness increase with the increase of volume fraction of fibers when compared to unfilled epoxy.

تم في هذا البحث دراسة الخواص الميكانيكية من متراكبات هجينة ذات اساس راتنج الايبوكسي مقواة بدقائق معدنية من الالمنيوم والياف الزجاج.العينات حضرت بطريقة الصب اليدوي وفقا لمعيار ASTM لكسورحجميةمختلفة منالألياف والدقائقوالمادة الاساس.الألياف الزجاجية(GF) هي واحدة منموادحشوالأكثر فائدةفي المواد المتراكبة، وتدخل في كثير من الصناعات منهاصناعة الطائرات والسيارات، والصناعاتالترفيهية. الايبوكسي كانت تقويته مع GF: MPفي نسبة10٪: 40٪، 20٪: 30٪، 30٪: 20٪، و 40٪: 10٪. لوحظأنه نسبة 40%:10% تمتلك اقصى اجهاد شد, مقاومة كسر,مقاومة انحناء,متانة كسر وصلادة ونلاحظ تزداد مع زيادة الكسر الحجمي للالياف مقارنة مع الايبوكسي الغير مدعم .


Article
MECHANICAL PROPERTIES OF EPOXY BASED HYBRID COMPOSITES REINFORCED BY GLASS FIBERS AND SiC PARTICLES.
الخواص الميكانيكية لمتراكبات هجينة اساس ايبوكسي مقواة بواسطةالياف الزجاج ودقائق السليكون كاربيد

Loading...
Loading...
Abstract

In the present study mechanical properties of pure epoxy and hybrid composites were studied. Pure epoxy and hybrid composites were prepared by Hand lay-up molding and investigated. The composites constituents were epoxy resin as the matrix, 4% and 8% volume fractions of glass fibers as reinforcement and 4% and 8% of silicon carbide as filler particles. The investigated mechanical properties were hardness, tensile properties (ultimate tensile strength (UTS), fracture strength), and impact properties (impact strength, fracture toughness). The experimental results showed that the mechanical properties, Hybrid composite with (Epoxy +8%GF+8% SiC) has the maximum hardness of (82) shore D, Hybrid composites with (Epoxy +8%GF+4% SiC) has the maximum (UTS), fracture strength, impact strength (Gc) & fracture toughness (Kc) of (107) MPa, (108) MPa, (9900) J/m2, (27. 487) MPa.m-1/2 respectively

تم في هذا البحث دراسة الخواص الميكانيكية لمتراكبات هجينة ذات اساس من الايبوكسي. تم تحضير المتراكبات الهجينة وراتنج الايبوكسي بواسطة المقالبة اليدوية وتم فحصها. مكونات المواد المتراكبة كانت راتنج الايبوكسي كماده اساس و(4%، 8%) كسر حجمي من الياف الزجاج كمادة تقوية و (4%، 8%) من كاربيد السليكون كدقائق تقوية.الخواص الميكانيكيه التي تم فحصها كانت ( الصلادة , الشد (اقصى مقاومة شد , مقاومة الكسر ) والصدمة ( مقاومة الصدمة ومتانة الكسر). أظهرت النتائج التجريبية بالنسبه للخواص الميكانيكية فأن المتراكبات الهجينة الحاوية على ( ايبوكسي/8%الياف زجاج %8%سليكون كاربيد ) اعطت اعلى صلادة شور مقدارها (82) شور D , والمتراكبات الهجينة مع (ايبوكسي /8%الياف زجاج/ 4%سليكون كاربيد) كانت لها اعلى مقاومة شد , مقاومة كسر, مقاومة الصدمة , متانة كسر من (107 MPa) , (108MP)و (9900 J/m2) , (27. 487 MPa. m-0.5) على التوالي .


Article
Effect of Nature Materials Powders on Mechanical and Physical Properties of Glass Fiber / Epoxy Composite
تأثير مساحيق اساسها مواد طبيعية على الخواص ميكانيكية وفيزياوية لمواد مركبة من ايبوكسي والياف زجاج

Authors: Aseel Basim Abdul-Hussein --- Emad Saadi AL-Hassani --- Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (A) Engineering Pages: 175-197
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as the matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% of nature material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Density, water absorption, hardness test, flexural strength, shear stress measurements and tests were conducted to reveal their values for each type of composite. True density results had shown an incremental increase with volume fraction increasing and water absorption, hardness, flexural strength and shear stress results had shown an incremental increase with volume fraction increasing with smaller particle size.

تم في هذا البحث تحضير مواد متراكبه بواسطة طريقة القولبة اليدوية. المواد المتراكبة مكونة من راتنج الايبوكسي كماده اساس وبألياف الزجاج بكسر حجمي 6% وكذلك 3% و 6 % كحشوة من المواد الطبيعية ( رماد قشور الارز , مسحوق الجزر , بودرة خشب جاوي ) . تم اجراء قياسات وفحوصات الكثافة وامتصاصية الماء وفحص الصلادة, مقاومة الانحناء , اجهاد القص للكشف عن قيمها لكل نوع من المواد المتراكبة . عند اجراء اختبارات الكثافة فان النتائج اظهرت بان الكثافة تزداد مع زيادة الكسر الجحمي والنتائج اظهرت بان امتصاصية الماء والصلادة ومقاومة الانحناء واقصى اجهاد قص يزداد مع زياد الكسر الجحمي و مع اصغر حجم حبيبي .


Article
Numerically and Theoretically Studying of the Upper Composite Complete Prosthetic Denture
دراسة تحليلية ونظرية لطقم الاسنان الاصطناعي الكامل المتراكب العلوي

Authors: Sihama I. Salih --- Jawad K. Oleiwi --- Qahtan A. Hamad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (A) Engineering Pages: 1023-1037
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current study focused on the manufacturing and development properties of upper prosthesis complete denture from composite materials with the basis cold cured resin of poly methyl methacrylate as new fluid resin and reinforced materials by two different types of particles (nano-hydroxyapatite (nHA), micro zirconia (ZrO2)), that added with different volume fractions of (1%, 2% and 3%), and the different types of woven fibers (Glass fiber, Kevlar fiber), it were added with a fixed volume fraction of (5%) to PMMA composites.Specimens’ consist of a six groups where prepared by using (Hand Lay-Up) method from the composites materials and hybrid laminated composites materials. This research includes theoretical and numerical studies by using finite element method to confirming the experimental results of the effect of selected volume fractions of theseparticles and fibers on the (total deformation distribution, equivalent elastic strain and equivalent Von Mises stress) of the composite prosthetic dentures.The theoretical part included calculations the values of theoretical safety factor and Poisson's ratio. While the numerical part based on finite element method (F.E.M), which was performed by using program (ANSYS-15) to analyze the prepared of denture composite materials and evaluate its characteristics which represent total deformation distribution, equivalent stress and equivalent elastic strain. This was performed by obtaining twenty one models for the PMMA composite dental prostheses which were treated as three dimension structure. The numerical results of the F.E.A showed coincided with some of the experimental results.

في هذا البحث تم التركيز على تصنيعوتطوير مواصفات طقم أسنان أصطناعي كامل علوي من مواد متراكبة. وقد حضرت هذه المواد المتراكبة من راتنج البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية تم اضافتهما بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج والياف الكفلر والتي تمت اضافتها الى المواد المتراكبةبكسر حجمي ثابت هو (%5)الى المواد المتراكبة. تتكون العينات من ستة مجاميع تم تحضيرها باستخدام طريقة الصب اليدوي تمثل مواد متراكبة ومواد متراكبة طبائقية هجينية. تضمن البحث دراسة نظرية وتحليلية باستخدام طريقة العناصر المحددة للتاكد من النتائج العمليةلتأثير الكسور الحجمية المختارة لهذه الألياف والدقائق على (توزيع التشوه الكلي، الانفعال المرن المكافيء والاجهاد المكافيء) لأطقام الاسنان الأصطناعية المتراكبة.تضمنتنتائج الجانب النظري حساب قيم معامل الامان النظريونسبة بويزن. أما الجانب التحليلي فيتضمن أستخدام أستخدام طريقة العناصر المحددة والتي أنجزت بأستخدام برنامج(ANSYS-15) لغرض تحليل المواد المتراكبة المحضرة لطقم الأسنان وحساب خصائصه والتي تمثل (توزيع التشوه الكلي، الاجهاد المكافيء والانفعال المرن المكافيء)، وقد تم انجاز ذلك عن طريق الحصول على واحد وعشرون موديل لطقم الاسنان الأصطناعي باعتبارها أطقام أسنان متراكبة مكونة من راتنج البولي مثيل ميثا اكريليت ذات هيكل ثلاثي الابعاد، وقد أظهرت النتائج التحليلية لطريقة العناصر المحددة تطابق مع بعض النتائج العملية.


Article
COMPARATIVE STUDY THE FLEXURAL PROPERTIES AND IMPACT STRENGTH FOR PMMA REINFORCED BY PARTICLES AND FIBERS FOR PROSTHETIC COMPLETE DENTURE BASE
دراسة مقارنة حول خصائص الانحناء ومقاومة الصدمة للبولي مثيل ميثا اكريليت المقوى بالدقائق والألياف لمادة قاعدة طقم أسنان أصطناعي كامل

Loading...
Loading...
Abstract

In the present search, attempts are made to develop the properties of PMMA resin that used for upper and lower prosthesis complete denture, by addition two different types of particles, which included: nano-hydroxyapatite (nHA) particles and micro-zirconia (ZrO2) particles that added with different volume fractions of (1%, 2% and 3%) to poly methyl methacrylate (PMMA) cold cured resin as new fluid resin matrix. Also woven glass fiber kind (E-glass) and woven Kevlar fiber kind (49), it were added with a fixed volume fraction of (5%) to PMMA composites. In this work the composite prosthetic dentures specimens preparation was done by using (Hand Lay-Up) method as six groups which includes: the first group consists of PMMA resin reinforced by nHA particles, the second group consists of PMMA resin reinforced by ZrO2 particles, the third group consists of (PMMA-nHA) and glass fiber layer as laminated composite , the fourth group consists of (PMMA-ZrO2) and glass fiber layer, the fifth group consists of (PMMA-nHA) and Kevlar fiber layer and the sixth group consists of (PMMA-ZrO2) and Kevlar fiber layer.The experimental part of this study included performing many mechanical tests which, includes (Flexural, Maximum Shear Stress and Impact) tests. The result of this study showed the values of most properties increased with increasing of the volume fraction of (nHA and ZrO2) particles in polymer composite materials. While, the impact strength decreased. The ZrO2 particle and woven mat Kevlar fiber had shown greater values for the most composite materials properties for all groups’ specimens except the flexural strain.Also the results showed the maximum values for hybrid laminated composite properties (flexural modulus and impact strength) were obtained in hybrid laminated composite materials for sixth group specimens. While, the maximum value for properties (flexural strength and max shear stress) were obtained in hybrid laminated composite materials for fourth group specimens.

تم في هذا البحث أجراء عدة محاولات لغرض تطوير مواصفات راتنج البولي مثيل ميثا اكريليت المستخدم كطقم أسنان أصطناعي كامل علوي أو سفلي. وقد حضرت هذه المواد المتراكبة من البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية اضيفت بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج نوع (E-GLASS) والياف الكفلر نوع (49) وقد اضيفت الى المواد المتراكبة بكسر حجمي ثابت هو (%5). في هذا البحث حضرت عينات من أطقام الاسنان الأصطناعية المتراكبة بطريقة (الصب اليدوي) على شكل ستة مجاميع هي: المجموعة الاولى تضم راتنج البولي مثيل ميثا اكريليت ودقائق الهيدروكسي اباتايت النانوية، المجموعة الثانية تضم راتنج البولي مثيل ميثا اكريليت ودقائق الزركونيا، المجموعة الثالثة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الهيدروكسي اباتايت النانوية، المجموعة الرابعة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الزركونيا، المجموعة الخامسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الهيدروكسي اباتايت النانوية، المجموعة السادسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الزركونيا.يتضمن الجزء العملي من هذا البحث اجراء العديد من الاختبارات الميكانيكية والتي شملت فحوصات (الانحناء، اجهاد القص الأعظم والصدمة(. وقد بينت النتائج بان قيم اغلب الخواص ازدادت مع زيادة الكسر الحجمي لدقائق الهيدروكسي أباتايت النانوية ودقائق الزركونيا، بينما قلت مقاومة الصدمة. وان دقائق الزركونيا والياف الكفلر الحصيرية تعطي قيم أعلى لاغلب خواص المواد المتراكبة ولكافة مجاميع العينات ماعدا الانفعال الأنحنائي. كذلك أظهرت النتائج بان اعلى قيم لخصائص (معامل الانحناء ومقاومة الصدمة) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة السادسة. بينما اعلى قيم لخصائص (مقاومة الانحناء واجهاد القص الأقصى) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة الرابعة.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2015 (5)