Indium doping effects on growth and preparation of spray pyrolysis deposited Cd0.6Zn0.4S thin films
تأثير التطعيم بالانديوم على نمو وخصائص أغشية Cd0.6Zn0.4S الرقيقة المرسبة بطريقة الرش الكيميائي

Loading...
Loading...
Abstract

Pure and Indium doped in Cadmium Zinc Sulfide Cd0.6Zn0.4S thin films were deposited onto glass substrate at different substrate temperature (275-375)C0 , at different Indium doping concentration (1-10) ml by spray pyrolysis technique , using precursor solution of Cadmium Chloride , Zinc Chloride , and Thiourea as Cadmium , Zinc and Sulfide source respectively The effect of Indium doping on the structure and morophology of prepared thin films have been investigeted .X-ray diffraction (XRD) , scanning electron microscope (SEM) have been used examining these samples .XRD studies , have revealed that the films are polycrystalline , with preferentid orientation of the crystallites in film grown producing a strong hexagonal (002)or cubic (111) peak . the grain sizes were found in the rang of (175-339.68)nm and (214-258) nm depending on Indium dopinconcentration and annelingtemperature. And these results have been confirmed by scanning electron microscope .The best crystallinity of the films was obtained at the substrate temperature of 350 C0 and Indium doping concentration of5ml.

تم ترسيب اغشية رقيقة للمركب Cd0.6Zn0.4S النقي والمطعم بالانديوم وذلك بطريقة الرش وعلى أرضية زجاجية بدرجات حرارية C0(375-275) وبتراكيز ml (10 -1) من الانديوم وذلك بأستخدام محلول من CdCl2 , ZnCl2, S على التوالي .تم أستقصاء تأثير التطعيم بالانديوم على تركيب هذه الاغشية. استخدم طريقة حيود الاشعة السينية (XRD) والمجهر الالكتروني الماسح SEM)).ووجدت أن هذه الاغشية ذات تركيب متعدد البلورات مع قمة عند (002) سداسية التركيب و (111) مكعب التركيب . حجم الحبيبات وجدت عند مديات nm(175 - 339 ) وnm(258- 214) معتمدا على نسبة الانديوم ودرجة حرارة التلدين على التوالي .تم الحصول على أفضل خصائص تركيبية ذلك عند درجات حرارة C0 (350) وعند تركيز (5)mlللأنديوم.


Article
Effect of Indium Tin Oxide (ITO) Nanoparticles on the Optical Properties Of PMMA Polymer
دراسة تأثير إضافة (ITO) كجسيمات نانوية على الخصائص البصرية للبوليمر بولي مثيل مثيكولايت

Authors: Asama Natik.Naje --- Salma M. Hasan --- Estabrak Talib
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Issue: المؤتمر العلمي الثالث لكلية العلوم Pages: 17-23
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work the optical properties of the PMMA polymer doped with different concentrations of ITO nanoparticles had been studied. All samples were prepared by casting technique with thickness of 1 mm. The optical properties ((absorption, transmission, absorption coefficient, extinction coefficient and refractive index) had been investigated. The doped composites have shown shifted toward the visible region. Whereas measured energy gap for pure and doped polymer shows decreases in the energy gap from 5.5eV to 3.5eV. The refractive index of pure polymer decreases as wavelength increase, where the refractive index of the doped polymer increases with increasing ITO concentrations.

في هذا العمل تمت دراسة الخصائص البصرية للبوليمر PMMA الذي تم تطعيمه مع تراكيز مختلفه ل ITO للجسيمات النانويه التي تمت يواسطة تقنية الطلاء مع سمك 1 ملم . تم دراسة الخصائص البصريه ( الامتصاصيه ,النفاذيه,معامل الامتصاص,معامل الانكسار, معامل الاخماد) , لوحظ ازاحة المركبات المطعمه باتجاه المنطقه المرئيه . كما لوجظ ان فجوه الطاقه المقاسه للبوليمرات المطعمه تتناقص من 5.5 الى.eV3.5 بينت الدراسه ان معامل الانكسار للبوليمر النقي يقل بزيادة الطول الموجي, وعند تطعيم البوليمر مع تراكيز مختلفه من الجسيمات النانويه ITO (0.01, 0.03, 0.05) معامل الانكسار يزداد.