Article
Physical behavior of polypropylene/low density polyethylene blends

Authors: Balkees M. Aldabbagh --- Hanaa Sh. Mahmood
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2015 Issue: 3 Pages: 289-300
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Blends of polypropylene (PP) and low-density polyethylene (LDPE) may contribute to make recycling more economically attractive. The aim of this work was to make LDPE /PP blends (0/100, 10/90, 25/75, 50/50 w/w) via injection molding carried out under 170 o C injection temperatures and to evaluate their physical properties including :(Shore D hardness, Density, Tensile strength , elongate to break , Fracture toughness ,impact strength, weight gain and thermal conductivity properties . The blend behavior dependent on its composition, especially regarding elongation at break and the presence of necking . The optimum sample was (10:90 w/w) (PP/LDPE).This sample has the optimum elongation to break, optimum fracture toughness, optimum thermal conductivity, and other properties.Increasing of PP contents over the optimum value leads to decreasing of the properties of blend.Weight gain of these samples increasing with increasing of the Immersion time in oil and benzene liquid but the sample not affected when exposed water.

تم تحضير خليط من البولي اثلين الواطئ الكثافة والبولي بروبلين لعمل خليط بوليميري اقل كلفةمن الناحية الاقتصادية. الهدف من البحث هو عمل خليط بوليميري من البولي اثيلين بطريقة القولبةبدرجه حراره (0/100, 10/90, 25/75, 50/50 w/w) والبولي بروبلين الواطي الكثافة بنسب170 درجه مئويه بطريقة القولبة بالبثق لغرض دراسة الخواص الفيزيائية المتضمنة) الاستطالة صلاده شور ، الكثافة ، مقاومة الشد ، الزياده بالوزن والتوصيلية الحرارية ( ، افضل عينة كانتبنسبه ) 10 : 90 ( ) بولي بروبلين : بولي اثيلين ( واطئي الكثافة : اظهرت النتائج ان العينة التيتحتوي 10 % بولي بروبلين تظهر زيادة في جميع الخواص وبزياة نسبه البولي بروبلين يؤدي الىتدني الخواص الفيزيائية للخليط .الزيادة في وزن العينات اظهرت زيادة في مع زيادة زمن الغمرفي النفط والبنزين فيما اظهرت النتائج ان الماء لايؤثر على الخليط البوليميري .


Article
الموصلية الكهربائية لراتنج البولي أثلين المقوى بدقائق السليكا

Author: سعد محمد حمزة
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 1 Pages: 84-87
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Electrical conductivity of low density polyethylene resin reinforced by variety weight fracture (1%,2%,3%,4%,5%) from silica particles with (8µm) grain particles has been studied in this paper before and after reinforcement . The experimental results obtained through measurement of resistivity by (Keithly electrometer type (616 ºC)) and then converted to conductivity show that decreased electrical conductivity of resin after adding silica particles, where the electrical conducting was decreased from 5 ×10-14 (ohm.cm)-1 before adding silica to 8.7 ×10-17 (ohm.cm)-1 after addition (5%) from silica at (40ºC).

الموصلية الكهربائية لراتنج البولي أثلين واطئ الكثافة المقوى بكسر وزني متنوع(1%،2%،3%،4% ،5%) من دقائق السليكا بحجم حبيبي (8µm) تم دراستها في هذا البحث قبل وبعد التقوية . النتائج العملية التي تم الحصول عليها من خلال قياس المقاومية بواسطة Keithly electrometer type (616 ºC))) وتحويلها بعد ذلك إلى الموصلية ، أظهرت إنخفاض الموصلية الكهربائية للراتنج بعد إضافة دقائق السليكا ، حيث إنخفض معدل التوصيل الكهربائي من 5 ×10-14 (ohm.cm)-1 قبل إضافة السليكا إلى 8.7 ×10-17 (ohm.cm)-1 بعد إضافة (5%) من السليكا عند درجة حرارة (40 ºC).


Article
The Energy of Break or Deformation in Some Semi- Crystalline Polymers
طاقة الكسر أو التلف لبعض البولیمرات شبھ – بلوریة

Author: Widad H. Jassim وداد حمدي جاسم
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042 Year: 2015 Volume: 28 Issue: 1 Pages: 24-32
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of the current study is the investigation of tensile behavior of the semi -crystalline polymers : polypropylene (PP ) , high density polyethylene(HDPE) and lowdensity polyethylene (LDPE) .The energy to break or deformation was determined as a function of extension rates ,( PP) was break at extension rate (5) mm/min but (HDPE) break at higher extension rates(25) mm/min while( LDPE) not break even at very high extension rates but it is deformationor failure

ان الهدف من الدراسة الحالية , هو البحث في طبيعة العلاقة ( القوة – الاستطالة ) للبوليمرات شبه-بلورية مثل البولي بروبلين(pp) ،البولي أثيلين عالي الكثافة و البولي أثيلين واطى الكثافة. وأنجزت فحوصات الشد لقياس طاقة الكسر أو فشل الأنموذج دالة لمعدل السحب ،ينكسر البولي بروبلين بمعدل سحب 5)mm/min) ولكن البولي أثيلين عالي الكثافة ينكسر عند معدلات عالية جدا للسحب 25)mm/min) ، بينما لا ينكسر البولي أثيلين واطى الكثافة حتى عند المعدلات العالية جدا للسحب ولكنه يتلف .