تحضير ودراسة وصلات معدنية تستخدم في أنظمة التبريد الكهروحراري باستخدام تقنية ميتالورجيا المساحيق

Authors: نبأ ستار راضي --- براء حسن هادي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 1 Pages: 204-214
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The electrothermic cooling system, proposed by German scientist ( Altnkerh ) in 1934 , the latest cooling systems known . The electrothermic cooling system is built on the property semiconductor materials which absorb heat during the cold and links to expel heat through hot links as a result of the different electromotive force of the semiconductor material in the joints. Was prepared test specimens in a manner powder metallurgy, where used powders with particles size convergent for the purpose of obtaining agglutination good between atoms, mixed powders for a period of five and a half hours for the purpose of obtaining the homogeneity of mixing prepared, then create part of the powder for the purpose of conducting the process of pressing pressure different then sintered powder at (450°C) at this stage will interfere components with each other so as to obtain compounds of the elements used then underwent a series of tests necessary for the alloy , such as measuring the thermal conductivity and checking the electrical resistance and examine the X-ray diffraction (XRD), and the results obtained is to increase the coefficient of thermal conductivity increase applied pressure and the time of sintering as well as increase the electrical resistance increase the time of sintering, where up to resistance (0.09Ω) when using sintering time two hours and a half .

يعتبر نظام التبريد الكهروحرارى, الذى اقترحه العالم الألمانى (التنكرش) عام 1934,أحدث أنظمة التبريد المعروفة. يبنى نظام التبريد الكهروحرارى على خاصية المواد الشبه موصلة وهى امتصاص الحرارة خلال الوصلات الباردة وطرد الحرارة خلال الوصلات الساخنة نتيجة اختلاف القوة الدافعة الكهربائية للمواد الشبه موصلة عند الوصلات. تم تحضير عينات الاختبار بطريقة ميتالورجيا المساحيق, حيث استخدمت مساحيق بحجوم حبيبة متقاربه لغرض الحصول على تراص جيد بين الذرات, خلطت المساحيق لفترة خمس ساعات ونصف لغرض الحصول على تجانس للخلطه المحضره,بعدها يهيئ جزء من المسحوق لغرض أجراء عملية الكبس بضغوط مختلفة ثم يلبد المسحوق بدرجة (C°450) في هذه المرحلة سوف تتداخل المكونات مع بعضها بحيث يتم الحصول على مركبات للعناصر المستخدمه ثم اجريت مجموعه من الاختبارات الضرورية للسبيكة مثل قياس الموصلية الحرارية وفحص المقاومة الكهربائية وفحص حيود الاشعه السينية (XRD), ومن النتائج المحصلة هو زيادة معامل التوصيل الحراري بزيادة الضغط المسلط وزمن التلبيد وكذلك زيادة المقاومة الكهربائية بزيادة زمن التلبيد حيث تصل المقاومة الى (0.09Ω) عند استخدام زمن تلبيد ساعتين ونصف .


Article
EFFECT OF ALUMINA POWDER ADDITION ON WEAR RESISTANCE OF Zn-4Al ALLOY PREPARED BY POWDER METALLUGY METHOD
تأثير إضافة مسحوق الألومينا على مقاومة البلى لسبيكة Zn-4Al المصنعة بطريقة ميتالورجيا المساحيق

Author: Ali Mezher Resen علي مزهر رسن
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2015 Volume: 8 Issue: 3 Pages: 20-33
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research is aimed to produce Zn-4Al alloys by using powder metallurgy technique. Zinc and aluminum powders were thoroughly mixed to obtain Zn-4 wt% Al. Alumina powder with different weight percents 2, 3 and 4 then added to Zn-4 wt% Al mixture. Careful mixings were applied to guarantee homogeneous distribution of alumina in the zinc-aluminum powder mixture. Cold pressings at 6.5 t using cylindrical die were done. Sintering of samples at 335 ¬oC for a period of 1 hr using argon gas as an inert gas were made. Grinding, polishing and etching were applied to the sintered samples in order to study the microstructure and hardness. Green density, true density, X-ray diffraction and wear resistance were also investigated. Results obtained showed that increasing the volume fraction of alumina increased the green density after pressing while the true density increased after sintering as compare with green density. Both the size of porosity and its percentage decrease because the formation of hard phases from zinc and aluminum. This is lead to increase the Vickers hardness and enhance the wear resistance of samples due to the formation of second phase of Al4Zn6 and also to the presence of alumina powder.

يهدف هذا البحث الى تحضير سبائك الزنك-المنيوم (Zn-4Al) بطريقة ميتالورجيا المساحيق. حيث تم العمل في هذا البحث أستخدام مسحوقي الزنك والألومنيوم بعد عملية الخلط للمسحوقين وبنسبة Zn-4Al. وبعدها تم ايضا اضافة مسحوق الألومينا وبنسب وزنية 2، 3، 4% وبعدها اجريت عملية المزج لضمان تجانس مسحوق الألومينا (Al2O3) مع الخليط للخارصين-المنيوم. تم إجراء عملية الكبس على البارد عند 6.5 ton وبقالب اسطواني. وبعدها تم إجراء عملية التلبيد للعينات عند335 °C ولمدة ساعة واحدة وباستخدام غاز الأركون كغاز خامل. تم تحضير العينات للفحص ألمجهري وقياس الصلادة بواسطة التنعيم والصقل. كذلك تم فحص الكثافة الخضراء و الكثافة الحقيقية وفحص حيود الأشعة السينية ومقاومة البلى. بينت النتائج ان زيادة نسبة مسحوق الألومينا تؤدي الى زيادة الكثافة الخضراء بعد الكبس أما الكثافة الحقيقية فانها تزداد بعد التلبيد مقارنة مع الكثافة الخضراء. كذلك تم النقصان في حجم المسامات ونسبة المسامية بسبب تكوين اطوار صلدة من مركبات الزنك والألومينا. أدى ذلك بالنتيجة الى زيادة قيم صلادة فيكرز المايكروية ومقاومة البلى للمكبوسات بسبب تكوين الطور الثانوي الصلد (Al4Zn6) ووجود حبيبات مسحوق الألومينا.