Article
Effect of Hydrocarbon Solutions on Polymer Concrete

Authors: Sanaa Abdul Hadi --- Mustafa Hassan Omar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 2 Part (B) Scientific Pages: 234-242
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The damaging effect of oil products on concrete besides the high permeability of concretehave made researchers try to improve the properties of concrete exposed to oil products, hence improving the durability and serviceability of oil concrete structures.Polymer concrete exposed to oil products is one of a new field that deals with the enhancement of concrete durability. In the present work polyester resin concrete was used and then immersed in different types of oil exposure liquids (gasoline, gas oil and kerosene) compared with reference concrete which left in the air.Polyester resin concrete is used as a new type in this field, it is noteworthy that the use of this concrete gives good test results that raise the values of the mechanical properties, so we did the SEM test in an attempt to study the microstructure of this concrete after soaking for 90 days in oil products.


Article
Preparation and studying of some properties of polymer composites reinforced with natural and artificial fibers
تحضير ودراسة بعض الخواص لمتراكبات بوليمرية مسلحة بالياف طبيعية وصناعية

Authors: Awham M. Hameed أوهام محمد حميد --- Saad Ali Fouad سعد علي فؤاد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 138-147
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work concerns the thermal and sound insulation as well as the mechanical properties of polymer matrix composite reinforced with glass fibers. These fibers may have dangerous effect during handling, for example the glass fibers might cause some damage to the eyes, lungs and even skin. For this reason the present work, investigates the behavior of polymer composite reinforced with natural fibers (Plant fibers) as replacement to glass fibers. Unsaturated Polyester resin was used as matrix material reinforced with two types of fibers, one of them is artificial (Glass fibers) and the other type is natural (Jute, Fronds Palm and Reed Fibers) by hand lay-up technique. All fibers are untreated with any chemical solvent. The Percentage of mixing was (90 wt. %) of the matrix while the weight fraction of each type of fibers was fixed (10 wt. %). The mechanical tests included impact and flexural strength tests. The results showed that the impact strength and flexural strength of the composites reinforced with Jute fibers is higher than that of Glass fibers and other natural fibers. The coefficients of thermal conductivity of the composites were measured by Lee's disc apparatus, the results show that the thermal insulation of the composite reinforced with jute fibers is higher than that of glass fibers and other natural fibers.The acoustic insulation of the composites reinforced with Jute fibers showed excellent result in insulation compared with glass fibers and other natural fibers.

أهتمت العديد من البحوث في دراسة الخواص العزل الحراري والصوتي و الخواص الميكانيكية لمتراكبات بوليمرية مسلحة بالياف الزجاج علما بأن هذه الالياف لها مضار عند التعامل معها فهي قد تضر بالعينين والرئتين وكذلك الجلد لذا ارتأينا اجراء دراسة خواص لمتراكبات البوليمر المقواة بألياف طبيعية (نباتية) كبدائل عن الياف الزجاج ومقارنة خواص كليهما وتحديد النتائج.استخدم راتنج البولي استر غير المشبع كمادة اساس وتم تسلسحه مع نوعين من الالياف, صناعية (الياف الزجاج) وطبيعية (الياف الجوت, وسعف النخيل, والياف القصب) جميع الالياف استخدمت بدون معاملة كيميائية, بواسطة تقنية الصب اليدوي. الكسر الوزني للرتنج كانت 90% نسبة وزنية بينما كان الكسر الوزني لجميع للأياف ثابت وهو 10% نسبة وزنية, الاختبارات الميكانيكية الي تم اجرائها هي اختبار الصدمة بطريقة جاربي واختبار مقاومة الكسر لحساب قيمة مقاومة الصدمة ومقاومة الكسر لهذه المتراكبات, النتائج اضهرت ان المتراكبات المسلحة بالياف الجوت (الطبيعية) لها مقاومة صدمة ومقاومة كسر اعلى من الياف الزجاج والاياف الطبيعية الاخرى. كذلك تم اجراء فحص التوصيلية الحرارية لهذه المتراكبات باستخدام جهاز(قرص لي) واوضحت نتائج اختبار التوصيلية الحرارية بأن العزل احراري للمتراكبات المسلحة بألياف الجوت اعلى من المتراكبات المسلحة بألياف الزجاج وكذلك اعلى من الالياف الطبيعية الاخرى, بينما نتائج فحص العزل الصوتي للمتراكبات المسلحة بألياف الجوت كانت ممتازة مقارنة بالمتراكبات المسلحة بالياف الزجاج وكذلك المتراكبات المسلحة بالاياف الطبيعيه الاخرى.


Article
Preparation of Unsaturated Polyester Nanocomposites and Studying Their Mechanical Properties Using some Inorganic Additives
تحضير متراكبات البولي استر غير المشبع النانوية ودراسة خواصها الميكانيكية باستعمال بعض المضافات اللاعضوية

Authors: Jalil Raheef Ugal جليل رهيف عكال --- Raghad Mohammed Hasson رغد محمد حسون
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2016 Volume: 13 Issue: 2ملحق ابحاث المؤتمر الوطني الثاني للكيمياء Pages: 10-18
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study three inorganic nano additives, namely; CaCO3, Al2O3 and SiO2 were used to prepare nanocomposites of unsaturated polyester in order to modify their mechanical properties, i.e. tensile strength, elongation, impact and hardness. The results indicated that all the three additives were effective to improve the mechanical properties up to 4% by weight. The effectiveness of them follows the order :CaCO3 > Al2O3 > SiO2This is due to their particle size in which CaCO3 (13nm), Al2O3 (20-30nm) and SiO2 (15-20nm).

استعملت في هذا البحث ثلاثة مضافات لاعضوية نانوية هي, كربونات الكالسيوم, واوكسيد الالمنيوم, واوكسيد السَليكون لتحضير متراكبات البولي استر غير المشبع وذلك لغرض تحسين خواصها الميكانيكية ؛ وقوة الشد والاستطالة وقوة الصدم والصلادة .أشارت النتائج بان المضافات الثلاثة كانت فعالة في تحسين الخواص الميكانيكية عند استعمال المضافات بنسب تصل الى 4% وزنا˝ وكانت كفاءة هذه المضافات تتبع التسلسل الاتي :CaCO3 > Al2O3 >SiO2 وذلك بسبب الحجم الحبيبي لكل منها ؛ كربونات الكالسيوم (13 نانوميتر) واوكسيد الالمنيوم (20-30 نانوميتر) واوكسيد السَليكون (15-20 نانوميتر) .


Article
Electrical Insulation Breakdown Strength and Thermal Conductivity of Different Blended Nanocomposites of New Epoxy Resins
قوة انهيار العزل الكهربائي والتوصيل الحراري لمختلف السبائك النانوية المتراكبة لراتنج الايبوكسي الجديد

Loading...
Loading...
Abstract

This research studies the development and synthesis of blended nanocomposites filled with Titanium dioxide (TiO2). Blended nanocomposites based on unsaturated polyester resin (UPR) and epoxy resins were synthesized by reactive blending. The optimum quantity from nano partical of titanium dioxide was selected and different weight proportions 1%, 3%, 5%, and 7% ratios of new epoxy are blended with UPR resin. The dielectric breakdown strength and thermal conductivity properties of the blended nanocomposites were compared with those of the basis material (UPR and 3% TiO2).The results show good compatibility epoxy resins with the UPR resin on blending, dielectric breakdown strength values are higher while thermal conductivity values of blends nanocomposites are significantly lower compared to that of the(UPR and 3% TiO2), semi-interpenetrating UPR/Epoxy blends (semi-IPNs) for one type of new epoxy [P2]was prepared and noticed the blend nanocomposites show higher dielectric breakdown strength than the semi- IPNs (UPR/Epoxy) at low loading of new epoxies but the thermal conductivity is a higher than the semi- IPNs UPR/Epoxy at all loading. Thermogravimetric analysis (TGA) was employed to study the thermal properties of the blended nanocomposites.

يكشف هذا البحث عن تحضيروتطوير عشرة مخاليط متراكبة ومليئة بجسيمات نانويه وهي ثاني أوكسيد التيتانيوم (TiO2). تم تحضير شبكات البوليمر المتراكبة النانويه على أساس راتنج البوليستر غير المشبعة (UPR) وراتنجات ايبوكسي جديدة مختلفه عن طريق مزج فعال .أذ تم اختيار النسبه المثلى من الجسيمات النانويه لثاني أوكسيد التيتانيوم (3%) وهي نسبة مختارة من نتائج مزجها بنسب مختلفة مع راتنج البولي استر غير مشبع. ومن ثم مزجت النسبة المثلى (3%) من(TiO2) مع بولي استرالغير مشبع مع نسب مختلفه من مركبات الايبوكسي الجديدة 1 ٪ , 3٪ , 5٪ و 7٪ من وزن راتنج البولي استر غير مشبع. وتمت مقارنة خصائص قوة انهيار العزل الكهربائي والتوصيل الحراري للمتراكبات النانويه المقساة مع تلك المواد الأساس (UPR و 3٪ TiO2). تظهر الاولى قوة انهيار العزل الكهربائي اعلى في حين التوصيل الحراري هي اقل وكما تم تحضيرمخاليط لاحد تراكيب الايبوكسي رقم ( 2) وبالنسب المذكورة نفسها (UPR و (Epoxy و مقارنتها مع مخلوط المتراكبة النانويه لوحظه ان قوة انهيار العزل الكهربائي للمخلوط المتراكبة النانويه هو الاعلى عند نسب التحميل الواطئة للإيبوكسي رزن وكما اظهرت التوصيلية الحرارية عالية مقارنة بما اظهرته مخاليط من ( UPR Epoxy/) .اجري التحليل الحراري الوزني (TGA) لدراسة الخواص الحرارية للمخاليط المتراكبة النانويه .


Article
Effect of Al2O3 Powder on Some Mechanical and Physical Properties for Unsaturated Polyester Resin Hybrid Composites Materials Reinforced by Carbon and Glass Fibers

Author: Reem Alaa Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 12 Part (A) Engineering Pages: 2371-2379
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research is a study of the effect of Al2O3 powder on physical and mechanical properties of the polymer hybrid composites based on unsaturated polyester resin reinforced with carbon and glass fibers. The samples were made by a hand lay-up method according to ASTM standard for various volume fractions of additives. The polymer composites materials reinforced with carbon and glass fibers are the most used in manufacture of components such as pip, part of aerospace, and leisure industries and automotive.The polyester resin matrixwas strengthened with 3% carbon and glass fibers with 1%, 3%, 5%, 7% Al2O3 powders. The water absorption, hardness (shore D), impact test, and flexural strength properties are studied. The results show the specimens (UP+3%C.F+7%Al2O3) and(UP+3%G.F+7%Al2O3) had the maximum hardness (shore D) and water absorptionwhen compared withunfilledpolyester resinspecimen, it can be observed that the specimens(UP+3%C.F+5%Al2O3) and (UP+3%G.F+5%Al2O3) have maximum impact strength and flexural strengthcompared with specimens (UP+3%C.F+7%Al2O3)and (UP+3%G.F+7%Al2O3) .


Article
Mechanical and physical properties of carbon nanotubes with Kevlar fiber reinforced with polyester resin
الخواص الميكانيكية و الفيزيائية لانابيب الكاربون النانوية مع الياف الكفلر المقواة مع راتنج البولي استر

Loading...
Loading...
Abstract

In this research study Hardness (shore D), Water absorption, Flexural, Impact Test, and Fracture Toughness of polymer nano composites.The polymer nano composites based on unsaturated polyester resin reinforced with Kevlar fibers (K.F). The samples are attended by hand lay – up method according to (Rule mixture) for various volume fractions of unsaturated polyester resin, fiber and carbon nanotube. The polyester resin was matrix strengthened with 3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%( volume fractions of carbon nanotube. The water absorption, hardness (shore D), flexural test, impact testand toughness fracture properties were studied. Results showed that the water absorption increase with volume fraction increase of fiber with Carbon Nanotube, the sample (polyester+3%K.F+0.5% CNTs) has lower water absorption than other samples. The hardness (shore D), flexural test, impact testand toughness fracture for the sample (polyester+3%C.F+0.5% CNTs) has higher value for Nano- composites. Nano composites, Carbon nanotube, Kevlar fiber, Hardness (shore D), Water absorption, Flexural Strength, Impact Test, Toughness Fracture.

تم في هذا البحث دراسة الصلادة (شورD), امتصاصية الماء, مقاومة الكسر, اختبار الصدمة و متانة الكسر لمتراكبات نانوية ذات اساس راتنج البولي استر غير المشبع مقواة بألياف الكفلر. العينات جهزت بطريقة الصب اليدوي وفقالقاعدة الخلط لكسور حجمية مختلفة من راتنج البولي استر غير المشبع والالياف وانابيب الكاربون النانوية. راتنج البولي استر كان ارضية مقواة مع 3%كسر حجمي من الياف الكفلر و (0.5 ,1 ,1.5 , 2 ) % كسر حجمي لانابيب الكاربون النانوية. تم دراسة خواص امتصاصية الماء, صلادة (شور(D, اختبار الصدمة ومقاومة الكسر. اظهرت النتائج بان امتصاصيه الماء تزداد مع زيادة الكسر الحجمي للالياف مع انابيب الكاربون النانوية, العينه (بولي استر + 3% الياف كفلر + 0.5 % انابيب اكاربون النانوية) تمتلك اقل امتصاصية ماء من العينات الاخرى. الصلادة (شورD), فحص الكسر, فحص الصدمة ومتانة الكسر للعينه (بولي استر +3% الياف كفلر + 0.5 %انابيب الكاربون انانوية) تمتلك اعلى قيمه للمتراكبات النانوية.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (4)

Arabic (1)

Arabic and English (1)


Year
From To Submit

2016 (6)