STUDY THE EFFECT OF NANO MATERIALS ADDITION ON SOME PROPERTIES OF CEMENT MORTAR

Authors: Fadhil A. Rasin --- Laith K. Abbas --- Mohammed J. Kadhim
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 5 Pages: 159-170
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This study involves nano-materials addition and interaction with cement mortar behavior for many mortar samples under variable curing time with constant water to cement ratio (W/C = 0.5). In this research some properties such as (hardness and water absorption test), were affected by adding small ratios of nano-particles (SiO2 or Al2O3) as replacements to the Ordinary Portland Cement (OPC) / type (I). The percentages of nano materials additives replacement on the mixture of mortar include (1, 2, 3, 4 and 5%) for both nano materials with constant (W/C) ratio. Also the amount of the fine aggregate used was three times the amount of cement. The results showed that, the hardness of the mortars for both nano materials gives better properties than mortar without nano materials in all tests. Best enhancements in properties for mortars with nano silica were achieved with (3%) additives while were achieved with nano alumina at (2%) additives.

تتضمن الدراسة اضافة المواد النانوية وتداخلاتها مع سلوك مونة الاسمنت لكثير من العينات تحت تاثير اوقات متغيرة للمعالجة مع نسبة ثابة للماء وبنسبة (W/C = 0.5). في البحث الحالي بعض الخواص الميكانيكية(اختبارخاصية الصلادة) والفيزياوية (اختبار امتصاص الماء) ، تأثرت من خلال اضافة نسب صغيرة من جسيمات نانوية (SiO2 or AL2O3) وكأضافات الى الأسمنت البورتلاندي العادي (OPC) نوع (I). النسبة المئوية للمواد النانوية المضافة الى خليط من عينات مونة الاسمنت كانت (1، 2، 3، 4، 5%) لكلا المواد النانوية المضافة ، كما استخدم الركام الناعم بثلاثة أضعاف كمية من الاسمنت المستخدم. اضهرت النتائج تحسن وارتفاع صلادة مونة الاسمنت لكل العينات الحاوية على مواد نانوية بالمقارنة مع العينات بدون المواد النانوية المضافة ولكل الأختبارات. تم الوصول الى افضل تحسن في الخصائص للعينات المضاف اليها النانو السيليكا عند نسبة (3%) بالمقارنة مع العينات المضاف اليها النانو الومينا والذي تحقق بنسبة (2%) مواد نانوية مضافة.


Article
Study the Characterizations of Cement Mortar by Nano Pozzolanic Materials Additions
دراسة الخصائص لمونة الاسمنت باضافة مواد بوزلانية نانوية

Authors: Mohammed J. Kadhim محمد جواد كاظم --- Laith K. Abbas ليث قيس عباس --- Fadhil A. Rasin فاضل عبد رسن
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2017 Volume: 13 Issue: 4 Pages: 152-163
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study involves adding nano materials and interaction with cement mortar behavior for several mortar samples under variable curing time with constant water to cement ratio (W/C = 0.5). The effects of adding nano materials on the microstructure of cement mortar were studied by (Scanning Electronic Microscopy (SEM) and X-Ray (for samples at different curing time 28 and 91 days. Small ratio replacements of nano particles (SiO2 or Al2O3) were added to Ordinary Portland Cement (OPC) type (I). The percentage of nano materials additives replacement by weight of ordinary Portland cement includes (1, 2, 3, 4 and 5%) for both types of nano materials with constant (W/C) ratio, also the amount of the fine aggregate used was three times the amount of cement. The results showed that, the mortar consist of both nano materials had better microstructure than mortar without nano materials in all test. Best enhancements in properties and microstructure for mortars with nano silica were achieved with (3%) additives while were achieved with nano alumina at (2%) additives.

تتضمن هذه الدراسة اضافة المواد النانوية وتداخلاتها مع سلوك مونة الاسمنت لكثير من عينات المونة تحت تاثير اوقات معالجة متغيرة مع نسبة ثابتة من الماء/ الأسمنت تبلغ (W / C = 0.5).تم دراسة تأثير اضافة المواد النانوية على التركيب المجهري لعينات مونة الأسمنت باستخدام المجهر الماسح الالكتروني والأشعة السينية للعينات وبفترات زمنية مختلفة للمعالجة (28 و91 يوما). نسبة استبدال صغيرة من جسيمات النانو سيليكا او النانو الومينا (SiO2 AL2O3) اضيفت الى الأسمنت بعد استبدالها بوزن من الاسمنت البورتلاندي الاعتيادي (OPC) والنسب المئوية للمواد النانونية المضافة لخليط مونة الأسمنت تضمنت (1 ، 2 ، 3 ، 4 ، 5 %) لكلا النوعين مع نسبة ثابتة من (الماء / الأسمنت) ، كذلك تم استخدام كمية من الركام الناعم بثلاثة أضعاف كمية الاسمنت المستخدم. اظهرت النتائج أن البنية المجهرية لمونة الاسمنت للعينات الحاوية على مواد نانوية تكون افضل من العينات التي لاتحتوي على المواد النانوية وفي جميع الأختبارات. تم الوصول الى افضل تحسن في الخصائص والبنية المجهرية للعينات المضاف اليها النانو السيليكا عند نسبة (3%) بالمقارنة مع العينات المضاف اليها النانو الومينا والذي تحقق بنسبة (2%) مواد نانوية مضافة.