Mechanical Properties And Flexural Behavior of reinforced Polymer Modified Concrete beams enhanced by Waste Plastic Fibers (WPF)
الخواص الميكانيكية وسلوك الانحنا للخرسانة المحورة بالبوليمر والمعززة بالياف الفضلات البلاستيكية

Authors: Dr.Abdulkader Ismail Al- Hadithi1 عبدالقادر اسماعيل الحديثي --- Shahad Younus Thabet Al-Waysi
Journal: Iraqi Journal of Civil Engineering المجلة العراقية للهندسة المدنية ISSN: 19927428 Year: 2017 Volume: 11 Issue: 2 Pages: 16-32
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This research include the study of flexural behavior of polymer modified concrete beams containing waste plastic fiber (WPF). Fifteen reinforced concrete beams are moulded of (100*150*1300) mm dimension with different steel reinforcement ratio (ρ). These steel reinforcement ratio were (0.0038, 0.0207 & 0.0262). Styrene Butadine Rubber (SBR) was added as cement replacement by weight equal to (5%). Reinforced concrete beams classified in to five groups, each contains three beams with different (ρ) value. The first group conducted of reference concrete mix , the second group made with SBR modified concrete, while the three remaining groups were make by PMC containing (WPF) with volumetric ratio equal to (0.75, 1.25 & 1.75)%.This study includes compressive and flexural tests for concrete which was used in this research, load deflection relationships, the moment at mid-span with deflection and ductility were established.The results prove that, polymer modified concrete wich content waste plastic fiber has compressive and flexural strengths more than reference mixes as well as the PMC beams wich content waste plastic fiber have a stiffer response in terms of structural behaviour, more ductility and lower cracking deflection than those made by reference concretes and that refer to good role of styrene Butadiene Rubber (SBR) polymer and plastic fiber on the properties and behaviour of reinforced concrete beams.

يتضمن هذا البحث دراسة السلوك الانشائي للعتبات الخرسانية المطورة بالبوليمر والمزودة بألياف الفضلات البلاستيكية. حيث تم صب 15 عتبة خرسانية بابعاد (1300*100 *150) ملم بنسب تسليح مختلفة (ρ). وهذه النسب كانت (0.003, 0.0207,0.0262). تم اضافة بوليمر ستايرين بيوتادين ربر( (SBRبنسبة 5% من وزن الاسمنت. العتبات الخرسانية المسلحة قسمت الى خمس مجاميع, كل مجموعة تحتوي على ثلاث عتبات بتلاث نسب تسليح مختلفة (ρ). المجموعة الاولى تمثل الخلطة المرجعية, والمجموعة الثانية معدلة ببوةليمر ,(SBR) بينما المجاميع الثلاثة المتبقية اعدت من الخرسانة المعدلة بالبوليمر وحاوية على الياف بلاستيكية بنسب حجمية مساوية ل (0.75, 1.25, 1.75)%. تضمنت الدراسة اجراء فحوصات مقاومة الانضغاط والانثناء للخرسانة موضوع البحث, فحص العتيات للانثناء ومن ثم ايجاد علاقات (الحمل- الأود), العلاقة مابين العزم والأود في منتصف العتبة والمطيلية. أثبتت النتائج ان الخرسانة المعدلة بالبوليمر والحاوية على نسبة معينة من الياف بلاستيكية ذات مقاومة انضغاط وانثناء اعلى مقارنة بالخرسانة المرجعية وأظهرت العتبات الخرسانية المسلحة المعدلة بالبوليمر والحاوية على الياف بلاستيكية تصرفا اكثر صلابة , أكثر مطيلية وأقل أود من مثيلاتها المصنعة من الخرسانة المرجعية مما يدل على تأثير بوليمر الستايرين بيوتادين ربر((SBR ودور الالياف المهم في تحسين خواص وسلوك العتبات الخرسانية المسلحة.


Article
Mechanical Properties of Light Weight Polymer Modified Concrete Made with Chopped Rubber Tires

Author: Hassanien Mohammed Thiyab
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 4 Pages: 1169-1178
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Lightweight concrete is highly used as loaded and unloaded parts in structures. The low values of compressive strength leads to the production of lightweight concrete blocks that can be used in partitions and the types that have more than 17 MPa and in some structural members that are not highly loaded. This research includes study of mechanical properties of this type of concrete which produced from the waste materials ( chopped rubber tires ) that are used as a percentage from coarse aggregates by the replacing method. The replacement was as 10%, 20%, 30%, 40% and 50% by weight of coarse aggregates. The mixes were modified by using the styrene butadiene rubber (SBR) to increase the values of the mechanical properties and durability. The aim of this investigation is to product special mixes of concrete with a low density and good mechanical properties to reduce the dead load and more economic construction . This study proof the CRT effect on compressive strength whereas it dropped from 62.5 Mpa to 40.8 Mpa by increase percentage of the CRT from 10% to 50%, but in the same time the density lowered up to 33%. The mixes with 10%, 20%, 30% can be regarded as a structural lightweight concrete (exceeded 17 MPa) and the other mixes can be used for the production of lightweight blocks used in partitions.

تستخدم الخرسانة الخفيفة الوزن بشكل واسع في الأجزاء المحملة وغير المحملة للمنشات. تؤدي القيم المنخفضة لمقاومة الانضغاط الى أستخدام الخرسانة الخفيفة الوزن في القواطع والأنواع التي لها مقاومة أنضغاط اكبر من 17 ميكا باسكال كما يمكن أستخدامها في بعض أجزاء المنشات المحملة والتي لا تكون معرضة الى أحمال عالية.هذا البحث يتضمن دراسة الخواص الميكانيكية للخرسانة خفيفة الوزن التي تنتج من فضلات المواد ( مفروم الإطارات المطاطية) والتي تستخدم كنسب من الركام الخشن بواسطة الاستبدال. هذا الاستبدال بنسبة 10%, 20% ,30% , 40% و 50% من وزن الركام الخشن. الخلطات تم تطويرها بأستخدام (SBR) لزيادة قيم الخواص الميكانيكية والديمومة. أن الهدف من الدراسة هو لأنتاج خلطات خاصة من الخرسانة بكثافة قليلة وخواص ميكانيكية جيدة لتقليل الاحمال ولتكون أكثر اقتصادية. برهنت الدراسة على تأثير مفروم الأطارات المطاطية على مقاومة الأنضغاط حيث تنخفض مقاومة الانضغاط من 62.23 ميكا باسكال الى 40.89 ميكا باسكال بزيادة نسبة مفروم الإطارات المطاطية من 10%الى 50%,ولكن في نفس الوقت تنخفض الكثافة الى 33%. الخلطات ذات النسب 10% , 20 و30% يمكن أعتبارها كمنشات خفيفة الوزن (مقاومة الانضغاط أكبر من 17 ميكا باسكال) والخلطات الأخرى يمكن أستخدامها في أنتاج خرسانة خفيفة الوزن تستخدم كقواطع.


Article
Improving Mechanical Properties of Polymer Modified Concrete Using Micro-Steel Fiber and Silica Fume

Author: Muhammad Abed Attiya
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 1 Pages: 212-223
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The use of Steel Fiber Reinforced Concrete (SFRC) is to improve the structural behavior such as increasing the resistance to cracking and crack propagation. This work has been made to study the properties of polymer modified concrete when micro-steel fiber is incorporated at different volumetric percentages from 0.1 % to 2 %. Two mixes (1:1.5:2 and 1:2:4) have been used and modified with styrene butadiene rubber resin (SBR) and silica fume with maintaining water cement ratio at 0.45. It has been found that increasing steel fiber content in concrete has a significant influence on the increase compressive, tensile, flexural strength, modulus of elasticity and stress- strain relationship. Flexural strength increases from 4.14 MPa (for 0% steel fiber) to 11.83 MPa (for 2% steel fiber). Whereas, the modulus of elasticity is improved by about 77% (for 1:1.5:2 mixes) and 91% (for 1:2:4 mixes).

تستعمل الخرسانة المسلحة بألياف الحديدِ (SFRC) لتحسّينَ السلوكَ الإنشائي مثل زيَاْدَة مقاومة التَصَدُّع والحد من تمدد التشققات. في هذا البحث تم دراسة تأثير إضافة ألياف الحديد (micro-steel fiber) كنسب مئوية حجميه مختلفة تتراوح من 0.1 % إلى 2 % على خواص الخرسانة المعدلة باستخدام مضافات البوليمرات (polymer modified concrete). حيث تم استخدام نوعين من الخلطات ((1:1.5:2 و1:2:4) ومع نوعين من المضافات هما styrene butadiene rubber resin (SBR) و silica fume مع بقاء نسبة الماء/ سمنت ثابته (0.45). وُجِدَ إن زيادة محتوى ألياف الحديد في الخرسانةِ لَهُ تأثير واضح على زيادة مقاومة الانضغاط، الشد والانثناء. وكذلك زيادة قيم معامل المرونة وتحسن علاقةِ الإجهادِ-الانفعال stress-strain relationship. ِلوحظ خلال هذه الدراسة إن مقاومة الانثناء ازدادت من 4.14 MPa بدون استخدام ألياف الحديد (0% steel fiber) إلى 11.83 MPa باستخدام ألياف الحديد بنسبة (2% steel fiber). كذلك معامل المرونة تحسن بنسبة 77% للخلطة (1:1.5:2 ) و بنسبة 91% للخلطة (1:2:4).