Article
Mechanical Properties of Epoxy Reinforced with different percentage of ceramic particle weights
الخواص الميكانيكية للايبوكسي المدعم بنسب وزنية مختلفة من جسيمات سيراميكية مختلفة

Loading...
Loading...
Abstract

In this research work, mechanical behavior of reinforced epoxy (quick mast 105) composites filled with varying concentration of aluminum oxide Al2O3 and Silicon carbide SiC has been investigated. Composites were prepared by standard method. The objective of this work was to study the mechanical properties such as impact strength, hardness and flexural strength of the prepared composite. the results shows that the composites with 40% of SiC and Al2O3 concentration exhibit maximum hardness strength , the impact strength of SiC filled composite increases with increasing concentration, while Al2O3 filled composite impact strength decreases with increasing concentration . Modulus of elasticity of SiC filled composite decreases with increasing concentrated while Al2O3 filled composite elasticity increases.

في هذا العمل تم بحث السلوك الميكانيكية لراتنج الايبوكسي المدعم بتراكيز مختلفه من اوكسيد الالمنيوم(Al2O3) وكاربيد السليكا(SiC). تم تحضير المركبات بوساطة الطرق الكلاسيكية, ان الهدف من هذه الدراسة هو دراسة الخواص الميكانيكية مثل قوة الصدمة وقوة المرونة للمركبات المحضرة. اظهرت النتائج أن المركبات ذات تركيز 40% من اوكسيد الالمنيوم(Al2O3) وكاربيد السليكا(SiC) تمتلك اعظم قوة صلابة, وان قوة الصدمة للمركب المدعم بكاربيد السليكا(SiC) تزداد مع زيادة التركيز بينما المركب المدعم باوكسيد الالمنيوم(Al2O3) تتناقص قوة الصدمة له مع تزايد التركيز، كما يتناقص معامل المرونة للمركبات المدعمة (SiC) مع زيادة التركيز بينما المركبات المدعمة (Al2O3) يزداد معامل المرونة بزيادة التركيز.


Article
Investigation of Physical Properties of Polymeric Nanocomposite Material Used in Structural Applications
الاستقصاء عن الخصائص الفيزيائية للمواد المتراكبة النانوية البوليمرية المستخدمة في التطبيقات الهيكلية

Authors: Sihama Issa Salih سهامه عيسى صالح --- Wleed Bdaiwi Salih وليد بديوي صالح --- Salam Obaid Abdulghani سلام عبيد عبد الغني
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2017 Volume: 13 Issue: 1 - part 2 Pages: 60-71
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

In the current research were prepared composite materials, from thermoplastic polymer (PMMA) as a matrix materials by used the hand lay-out technique. The composite material was prepared from two sets of composites materials the first set consists of a poly methyl Methacrylate (PMMA) resin as matrix material reinforced by nanoparticle of aluminum Oxide (Al2O3) with average size (53.60) nm once and the second group is composed of poly methyl Methacrylate resin reinforced by nanoparticle of Magnesium Oxide (MgO) with average size (52.54) nm. The research includes the study of the influence of the selected volumetric fraction ratios of (0.5, 1, 1.5%) for the reinforce materials, on the properties of the prepared composite materials. Number of physical tests which included (density, Thermal Conductivity, specific heat and thermal diffusivity, and DSC) . which all test were done at room temperature. Result of the work shows that the values of Thermal Conductivity, Specific Gravity, Tg and Tm) increase with the increase of volume fraction of nanoparticle for both groups of polymeric Nano composites material. Whereas decreased the specific heat values with the increase of volume fraction of nanoparticle for both groups of polymeric Nano composites material Moreover the poly methyl Methacrylate Nano composite material reinforced with nanoparticle of aluminum Oxide possesses physical properties higher than those of Article composites reinforced with nanoparticle of Magnesium Oxide .

اجرية في البحث تحضیر مواد متراكبة ذات أساس مادة مطاوعة للحرارة بطريقة الصب الیدوي وقد حضرت مجموعتین من المواد المتراكبة النانوية المجموعة الأولى تتكون من راتنج البولي مثیل میثا اكريلیت (PMMA) كمادة أساس مدعمة بدقائق أوكسید الألمنیوم النانوية (Al2O3) ذات معدل حجم حبیبي (53,60 nm) نانو متر مرة والمجموعة الثانیة تتكون من راتنج البولي مثیل میثا اكريلیت (PMMA) كمادة أساس مدعمة بدقائق أوكسید المغنیسیوم النانوية (MgO) ذات معدل حجم حبیبي (52,54 nm). تضمن البحث دراسة تأثیر الكسر الحجمي المختار (0.5 ، 1 ، 1.5)% لدقائق مادتا التقوية على خصائص المواد المتراكبة المحضرة . وقد أجريت مجموعة من الإختبارات الفیزيائیة المتمثلة بالكثافة والتوصیلیة الحرارية والإنتشارية الحرارية والحرارة النوعیة والمسعر الماسح التفاضلي و المجهر الألكتروني الماسح ) ، وجمیع هذه الإختبارات تم إجراؤها عند درجة حرارة الغرفة . وقد أظهرت نتائج البحث إن قیم (التوصیلیة الحرارية والإنتشارية الحرارية والكثافة) تزداد مع زيادة الكسر الحجمي لدقائق مادتي التقوية في المادة المتراكبة . بینما قلت قیم (الحرارة النوعیة) مع زيادة الكسر الحجمي لدقائق مادتي التقوية .. وإن البولي مثیل میثا اكريلیت (PMMA) المدعم بدقائق أوكسید الألمنیوم النانوي يمتلك خصائص فیزيائیة أعلى من مثیلاتیها للمادة المتراكبة المدعمة بدقائق أوكسید المغنیسیوم النانويه كما بینت الدراسة زيادة درجة حرارة التحول الزجاج مع زيادة الكسر الحجمي لمادتي التقوية .