The Effects of Adding Waste Plastic Fibers (WPFs) on Some Properties of Self Compacting Concrete using Iraqi local Materials
تأثير اضافة الياف الفضلات البلاستيكية على خواص الخرسانة ذاتية الرص المصنعة من مواد محلية الصنع

Loading...
Loading...
Abstract

This study presents an experimental research of Self-Compacting Concrete (SCC) properties containing waste plastic fibers (WPF). Adding waste plastics which resulting from cutting PET bottles as fibers to SCC with aspect ratio (l/d) equal to (28). To illustrate the effects of WPFs on the SCC, the current study was divided into two parts, the first part shows the effect of adding plastic fibers on the properties of fresh SCC, which include the ability flow, spread, passing and resistance to segregation, and the second part to evaluate the properties of hardened (mechanical) destructive and non-destructive, which include compression strength, flexural strength and ultrasonic pulse velocity test. One reference concrete mix was conducted and eight mixes contain WPF has been producing self-compacting concrete mixers containing a different volumetric ratio of plastic fibers (Vf) % percentages (0.25, 0.5, 0.75, 1, 1.25, 1.5, 1.75, 2) %. Three cubes samples were prepared for testing the compressive strength, three prisms were prepared for the test modules of rupture, one cylinder were prepared testing the modulus of elasticity.The experiments show that adding plastic fibers to SCC leads to an increase in the compression strength and modulus of rupture at 28-day as follows (42.30)% and (73.12)% respectively for mix ratio (1.5)% in comparison with the reference mix, which represent the best ratio of fibers, as such the results of testing the fresh concrete containing waste fibers showed that adding these fibers led a reduction in workability for SCC.

تقدم هذة الدراسة بحثاً عملياً لخواص الخرسانة ذاتية الرص المسلحة والمحتوية على ألياف الفضلات البلاستيكية. تم أضافة نواتج التقطيع اليدوي للقناني البلاستيكية (المستخدمة في حفظ المشروبات الغازية) حيث تم تقطيعها بنسبة باعية (الطول/العرض) (28). لتوضيح تأثير الألياف البلاستيكية على سلوك الخرسانة الذاتية الرص, تم تقسيم الدراسة الحالية إلى جزئين, الجزء الأول يوضح تاثير الألياف البلاستيكية على الخواص الطرية للخرسانة ذاتية الرص والتي تشمل قابلية الأنسياب, الأنتشار, المرور ومقاومة الانعزال, في حين كان الجزء الثاني يشمل تقييم الخواص المتصلبة (الميكانيكية) الأتلافية وغير الأتلافية والتي تشمل مقاومة الأنضغاط, الأنثناء (معامل الكسر) والموجات فوق الصوتية.تم تصميم خلطة مرجعية واحدة في هذا البحث والتي تم أعتمادها كأساس لتطوير الخلطات الأخرى، في حين تم صب (8) خلطات خرسانية ذاتية الرص محتوية على نسب حجمية مختلفة من الألياف البلاستيكية % (fV) ، حيث كانت تلك النسب (0.25, 0.5, 0.75, 1.0, 1.25, 1.5, 1.75 و 2)% لغرض المقارنة مع الخلطة المرجعية. تم صب ثلاث (3) مكعبات لفحص مقاومة الأنضغاط وثلاث (3) مواشير لفحص معاير الكسر و (1) أسطوانة لفحص معامل المرونة.أوضحت نتائج الفحوصات العملية للدراسة الحالية أن إضافة الألياف البلاستيكية إلى الخرسانة ذاتية الرص كان لها تأثير إيجابي في زيادة مقاومة الأنضغاط ومقاومة الأنثناء، حيث كان مقدار الزيادة بعمر (28) يوم يساوي (42.30%) و(73.12%) على التوالي عند نسبة المزج (1.5 %) بالمقارنة مع الخلطة المرجعية والتي تمثل أفضل نسبة حجمية للألياف, كما بينت نتائج الفحوصات الطرية للخلطات الخرسانية الحاوية على الألياف البلاستيكية بأن أضافة الألياف يؤدي إلى أنخفاض في قابلية التشغيل للخرسانة الذاتية الرص.


Article
FLEXURAL BEHAVIOR OF HIGH STRENGTH RC SLABS WITH OPENING STRENGTHENING WITH WIRE MISH AND STEEL FIBERS
تصرف الانحناء للبلاطات الخرسانية عالية المقاومة المسلحة مع الفتحات والمقواة بالمشبكات السليكة والياف الصلب

Authors: Aqeel H. Chkheiwer عقيل حاتم جخيور --- Mazen D. Abdullah مازن ديوان عبد الله
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2017 Volume: 8 Issue: 3 Pages: 103-118
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

This paper consists of experimental study on ability of use of wire mish strengthening and steel fiber to recover the flexural strength of the slab after configuring openings cut out with different shapes. 15 slabs (800*800*95 mm) made of high strength concrete were prepared and tested, these slabs were divided to gropes, the first group was with square openings, the second group with was rectangular openings. For each group, two different strengthening techniques were used wire mish (with different layers and widths) strips around openings and steel fibers (with four contents of 0, 0.5, 1.0 and 1% by volume fraction). The results showed that the two strengthening techniques increased the load-carrying capacities of the slabs with openings compared with the slabs without strengthening. The wire mish was more effective than the steel fibers technique. Wire mish and steel fiber reduced the cracks at the inside faces of opening and also wire mish prevent it at the inside corners.

تتضمن هذا البحث دراسة التجريبية على قدرة استخدام التقوية بالمشبكات السلكية والياف الحديد لاستعادة مقاومة الانحناء )ملم مصنوعة 95 * 800 * 800( من ألبلاطات المربعة بابعاد 15 لبلاطة بعد قطع فتحات فيها بأشكال مختلفة .تم إعداد وكانت المجموعة الأولى مع فتحات مربعة، ، من الخرسانة عالية المقاومة واختبارها، تم تقسيم هذه البلاطات إلى مجموعتين وكانت المجموعة الثانية مع فتحات مستطيلة .في كل مجموعة، واستخدمت اثنين من التقنيات التقوية الاولى بالمشبكات من ٪1 و 1.0 ،0.5 ،0 السلكية (مع طبقات مختلفة وعرض )حول الفتحات والثانية بالألياف الفولاذية (مع أربعة محتويات حجم جزء .)وأظهرت النتائج أن تقنياتي التقوية الاثنين ساهمت في زيادة قدرة تحمل البلاطات مع فتحات و كانت المشبكات السلكية أكثر فعالية من الألياف الفولاذية .المشبكات السلكية والياف الحديد قللت التشققات في الاوجهة الداخلية للفتحات والمشبكات السلكية منعت حدوث تشققات في داخل زوايا الفتحات.


Article
Compressive Strength of Bottle-Shaped Compression Fields of Fiber Reinforced Concrete Members
مقاومة الانضغاط للمجال الانضغاطي على شكل قنينة للاعضاء الخرسانية المسلحة بالالياف

Authors: Zinah Asaad زينة اسعد --- Ghzwan Ghanim غزوان غانم --- Hussein Al-Quraishi حسين القريشي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 11 Pages: 56-69
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Applying load to a structural member may result in a bottle-shaped compression field especially when the width of the loading is less than the width of bearing concrete members. At the Building and Construction Department – the University of Technology-Iraq, series tests on fibre reinforced concrete specimens were carried out, subjected to compression forces at the top and bottom of the specimens to produce compression field. The effects of steel fibre content, concrete compressive strength, transverse tension reinforcement, the height of test specimen, and the ratio of the width of loading plate to specimen width were studied by testing a total of tenth normal strength concrete blocks with steel fibre and one normal strength concrete block without steel fibres. Based on experimental results; all the test specimens failed with the splitting of concrete directly under the loading plate. Increased the uniaxial compressive strength of concrete increases the maximum bearing capacity of compressive stresses. The load-transverse deformation initially behaves linearly and shows some nonlinearity before failure. Addition of steel fibre to normal strength concrete or presence of transverse reinforcement, delay the reaching of maximum compressive stress after the presence of the first crack.

عند تسليط الحمل على العضو الانشائي يمكن ان ينتج مجال انضغاطي على شكل قنينة وخاصة في حالة كون عرض التحميل هو اقل من عرض العضو الانشائي الساند. في مختبر قسم هندسة البناء والانشاءات- الجامعة التكنولوجية سلسلة من الفحوصات المختبرية قد تمت لنماذج خرسانية متعرضة الى قوى انضغاط لتكوين مجال انضغاطي. المتغيرات المأخوذة هي محتوى الالياف, مقاومة الانضغاط للخرسانة, تسليح الشد العرضي, ارتفاع النموذج, نسبة عرض بليتة التحميل الى عرض النموذج. تم دراسة تأثير هذه المتغيرات على قابلية الاسناد لمحتوى الانضغاط الذي يكون على شكل قنينة. تم فحص تسعة نماذج , ثمانية منها مسلحة بالالياف وواحد فقط غير مسلح بالالياف.بالاعتماد على نتائج الفحوصات المختبرية ، كل النماذج المفحوصة فشلت بالانشطار تحت بليتة التحميل مباشرة . زيادة مقاومة الانضغاط للخرسانة يزيد اجهادات الاسناد للانضغاط. العلاقة بين القوة والتشوه العرضي يتصرف بالبداية خطي ولكنه يكون غير خطي قبل الفشل. اضافة الياف الحديد للخرسانة العادية او اضافة تسليح عرضي يؤخر الوصول الى اعلى اجهاد الاضغاط بعد ظهور التشقق الاولي.