Article
Effect of Medium Quenching and Temperature on Corrosion Behavior of Aluminum Alloy 6061

Authors: Abbad Kassouha --- Sami Entakly
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2017 Volume: 20 Issue: 3 Pages: 498-504
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In the present work the effect of heat treatment processes at different temperatures and in different quenching media on mechanical properties in addition to corrosion behavior in different pH solutions of aluminum alloy 6061 was achieved.The alloy was received as fabricated and the solution heat treatment processes was achieved at temperatures (490,530,570 °C), then quenching for every degree was done in two media (water, oil) to obtain on six samples. The artificial aging was done on every sample at temperature (160°C) for one hour. The microstructure was examined to show Mg2Si in every sample. The results of hardness test showed that the hardness of alloy increased with increasing heat treatment temperatures, and at the same temperature the quenched specimens in oil had higher hardness.On the other hand, the tension tests showed that the strength of alloy increased with increasing of heat treatment temperature, and at the same temperature the quenched specimens in water had higher hardness.The results of corrosions test showed that the heat treatment operations improved corrosion resistance, and the lower value was get upon treating at 530°C.

في هذا البحث تمت دراسة تأثير عمليات المعالجة الحرارية عند درجات حرارة وفي أوساط سقاية مختلفة على الخصائص الميكانيكية وسلوك التآكل في أوساط مائية ملحية مختلفة بدرجة الحموضة PH لسبيكة الألمنيوم 6061. تم إحضار السبيكة كما تم تشكيلها وتم إجراء عمليات المعالجة الحرارية المحلولية عند درجات حرارة (490,530,570°C ), وأجريت السقاية عند كل درجة في وسطين مختلفين (الماء, الزيت) للحصول على ستة نماذج. تم التحقق من البنية المجهرية لكل نموذج وتوزع سيليسيدات المغنزيوم ضمن كل نموذج.أظهرت نتائج اختبارات القساوة أن السبيكة تزداد قساوتها مع ازدياد درجة حرارة المعالجة الحرارية, وعند نفس الدرجة أبدت العينات المسقاة بالزيت قساوة أعلى.أما نتائج اختبار الشد أظهرت أن السبيكة تزداد متانتها مع ازدياد درجة حرارة المعالجة الحرارية, لكن العينات المسقاة بالماء عند نفس الدرجة كان لها المتانة الأعلى.أظهرت نتائج اختبارات التآكل أن العينة المعالجة عند 530°C والمسقاة بالماء تبدي أقل معدل للتآكل في وسط مائي ملحي حمضي, بينما العينة المعالجة عند 530°C والمسقاة بالزيت تبدي أقل معدل للتآكل في وسط مائي ملحي معتدل, أما في الوسط المائي الملحي القلوي فالعينة المعالجة عند 570°C والمسقاة بالماء تملك أقل معدل تآكل.


Article
The effects of Heat Treatment (T6) Technique and Some Centrifugal Casting Parameters on the Fatigue behavior of the Composite Material (A380/Al2O3)

Authors: Salah F. AbdulJabbar --- Thaer F.A. ALSultan --- Faris H. --- Mohand A. Hamid
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2017 Volume: 24 Issue: 3 Pages: 34-41
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Aluminum alloys composite is one of the most common types of composite materials and are used a lot in the recent years. In this paper, it had been dealt with the effects of the heat treatment techniques and some centrifugal casting parameters on the fatigue behavior of the composite material (A380/Al2O3) for high-cycle fatigue resistance which is one of the most important property for the automotive industry. It has been used aluminum alloy A380 with alumina particles Al2O3 to form composite materials through the process of centrifugal casting. The proportions were 10% and 20% with a grain size 63μm. After there, it has been manufactured Thirty-two models of composite material (A380/ Al2O3). Half of them are examined directly without treatment while the other half was treated with (T6) and then examined. The results showed that adding the amount of alumina 20% without heat treatment will increase relatively resistant composite material for the fatigue resistance by 17% percentage. And adding 10% alumina to the composite material and them cause distortion of the surface structure samples had been by blisters with completely discolored. A high Alumina content improves the fatigue behavior of the composite material (A380/Al2O3).


Article
Dry Sliding Wear Behavior of EN25 Steel Treated by Different Quenching Media
سلوك البلى الانزلاقي الجاف للفولاذ En 25 المعالج بأوساط تقسية مختلفة

Author: Bassam Ali Ahmed بسام علي أحمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 10 Pages: 72-84
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The present investigation aims to study the effect of heat treatment by quenching in different quenching media (salt water, water and oil) following by tempering on wear resistance of EN25 steel. EN25 steel is an alloy of medium carbon low alloy steel which is used for many applications requiring high tensile strength and wear resistance such as connecting rods, adapters and in power sectors extensively. The specimens are machined to 20 mm in length and 10 mm in diameter. This study is done by two stages: The first stage is done by austenitizing EN25 steel to 850℃ for 1 hr by quenching the specimens in three different quenching media and then tempered at 300℃ in air. While the second stage is performed by wear test. Dry sliding wear test is done by using pin –on-disc technique by varying the loads as 5, 10, 15, 20 and 25 N, also varying the time as 5, 10, 15, 20, 25 and 30 min respectively. The microstructure examination, hardness and followed roughness tests are also done for the specimens before and after wear test. The results of this work showed that an improving in wear resistance and hardness for the specimen quenched by salt water more than for water and oil. At the same time the roughness decreasing for the specimen quenched by salt water more than for water and oil.

يهدف البحث الحالي لدراسة تأثير المعاملة الحرارية بالتقسية في اوساط مختلفة (ماء مالح، ماء، زيت) على مقاومة البلى للفولاذ En 25 . الفولاذ En 25 هو سبيكة من فولاذ متوسط الكاربون منخفض السبائكية يستخدم في عدة تطبيقات التي تتطلب مقاومة شد ومقاومة بلى عاليتين مثل اذرع التوصيل ،المحولات وقاطعات القدرة. تم تشغيل العينات بطول 20 ملم وقطر 10 ملم . اجريت هذه الدراسة بمرحلتين: الاولى تم فيها تقسية العينات بثلاث اوساط تقسية مختلفة عند درجة حرارية 850 مo ولمدة 1 ساعة، بعد ذلك تتم عملية المراجعة عند 300 مo ولمدة 1 ساعة ومن ثم التبريد في في الهواء. بينما في المرحلة الثانية اجري اختبار البلى. تم اختبار البلى الانزلاقي الجاف باستخدام تقنية المسمار- على- القرص وذلك بتغير الاحمال 25،20،15،10،5 نيوتن، كذلك تم تغير الزمن بمقدار 30،25،20،15،10،5 دقيقة على التوالي. وكذلك تم فحص البنية المجهرية واجريت اختبارات الصلادة والخشونة قبل وبعد اختبار البلى.اظهرت نتائج البحث تحسن في مقاومة البلى والصلادة للعينة المقساة بالماء المالح اكثر مما هو عليه للعينات المقساة بالماء والزيت. وبنفس الوقت نقصان الخشونة للعينة المقساة بالماء المالح اكثر مما هو عليه للعينات المقساة بالماء والزيت


Article
EFFECT OF HEAT TREATMENT ON CORROSION BEHAVIOR OF 2205 DUPLEX STAINLESS STEEL IN ORTHODONTIC APPLICATIONS
تأثير المعاملة الحرارية على تصرف التاكل لسبيكة الفولاذ المقاوم للصدأالمزدوج في تطبيقات تقويم الاسنان

Loading...
Loading...
Abstract

The heat treatment is necessary for 2205 duplex stainless steel to remove or dissolve intermetallic phases, removed segregation and to relieve any residual thermal stress in DSS which may be formed during production processes. In the present study, the corrosion resistance of a 2205 DSS in artificial saliva was studied by SEM, XRD, HV test and potentiodynamic measurements. The results indicated that the corrosion resistance mainly effected by ferrite /austenite ratio. The best result was obtained with the treatment at 900°C for 2 min. The austenite phase has corrosion resistance higher than ferrite.

المعالجة الحرارية ضرورية لل2205 للفولاذ المقاوم للصدأ المزدوج لإزالة أوتذويب أطوار المركبات المعدنية و إزالة الانعزال وكذلك توهين الإجهادات الحرارية المتبقية في الفولاذ المقاوم للصدأ المزدوج والتي تتكون أثناء عمليات الإنتاج. في هذه الدراسة تمت دراسة مقاومة التآكل لل2205 الفولاذ المقاوم للصدأ المزدوج في اللعاب الاصطناعي بواسطة المجهر الاكتروني الماسح، حيود الأشعة السينية، صلادة فيكرز وأختبار التأكل الكهروكيمياوي وتشير النتائج إلى أن مقاومة التآكل تتأثر بصورة رئيسية لوجود أطوار الثانوية (طور سيكما ( ونسبة الفرايت / الأوستينايت. تم الحصول على أفضل النتائج مع المعالجة الحراريه عند 900 درجة سيليزية لمدة 2 دقيقة. طور الأستينايت يمتلك مقاومة للتآكل أعلى من الفرايت و طور سيكما له تأثير ضار على سلوك التآكل لل 2205 الفولاذ المقاوم للصدأ المزدوج .


Article
STRUCTURE-PROPERTIES RELATIONSHIPS IN HEAT TREATED LOW CARBON STEEL

Author: Heider Yasser Thamir Alyasiri
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2017 Volume: 10 Issue: 4 Pages: 486-495
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The samples of AISI 1018 Low carbon steel were heated to austenite zone then cooled in different mediums with different cooling rates. Mechanical tests show increase in hardness, yield strength, tensile strength, modulus of elasticity, and yield/tensile ratio as cooling rate is increase. Ductility has inverse proportionality to cooling rate. The resulting microstructures show decreasing in grains sizes accompanying to cooling rate increase. The relations between mechanical properties and grains size are opposites of relations between mechanical properties with cooling rates. Hardness, yield strength, tensile strength, modulus of elasticity, and yield/tensile ratio increase as grains size decreases, while ductility decreases.


Article
Development the Mechanical Properties of (AL-Li-Cu) Alloy
تطوير الخواص الميكانيكية لسبيكة ألمُنيوم– ليثيوم– نحاس

Authors: Awatif Mustafa Ali عواطف مصطفى علي --- Ihsan Kadhom AlNaimi إحسان كاظم عباس النعيمي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 11 Pages: 43-55
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of this research is to develop mechanical properties of a new alloy aluminum-lithium-copper which is prepared by casting under control atmosphere in a permanent metal mold. The mechanical properties (impact, elasticity modulus, tensile strength, and fatigue) with microstructure were examined before and after heat treatment. The research outcome showed that the modulus of elasticity of the prepared alloy is higher than standard alloy about 2%. While the alloy that was heat treated for 6 h and cooled in water, showed a higher ultimate tensile stress comparing with as-cast alloy. The homogenous heat treatment gives best fatigue behavior compared with as-cast and other heat treatment alloys. Also, the impact test illustrates that the homogeneous heat treatment alloy gives the highest value.

الهدف من هذا البحث هو تطوير الخواص الميكانيكية لسبيكة جديدة من ألمُنيوم- ليثيوم- نحاس. هذه السبيكة حضرت بطريقة السباكة بقالب معدني دائمي تحت ظروف جوية مسيطر عليها. تم فحص التركيب المجهري وأجريت الفحوصات الميكانيكية للسبيكة قبل وبعد المعاملة الحرارية لدراسة تأثير المعاملة الحرارية على خواصها الميكانيكية والتي تتضمن: معامل مرونة، مقاومة الشد، مقاومة الصدمة، وجهد الكلال. وقد بينت النتائج زيادة في معامل المرونة للسبيكة المحضرة مقارنةً مع السبيكة القياسية بمقدار 2% تقريباً. بينما أعطت السبيكة المعاملة حرارياً لمدة 6 ساعات ومبردة بالماء مقداراً أعلى لمقاومة الشد الأقصى مقارنة مع السبيكة قبل المعاملة. إن السبيكة التي أجريت عليها معاملة المجانسة أعطت سلوك كلال أفضل مقارنة مع السبيكة قبل المعاملة والسبائك الأخرى المعاملة حرارياً. أيضاً إن فحص الصدمة بيّن إن السبيكة المعاملة حرارياً بطريقة المجانسة قد أعطت أعلى قيمة.


Article
EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE
تأثير النسب الوزنية لمادة الزجاج والمعاملة الحرارية على الخواص الميكانيكية ومعدل البلى لمتراكبات الألمنيوم - 2% كرافيت

Author: Hashim Shukur Hammood هاشم شكر حمود الكرغولي
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2017 Volume: 10 Issue: 4 Pages: 33-41
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research studied the effect of the Heat Treatment on the Mechanical Properties and the Wear Rate of the pure Aluminum with a particle size of (≤53μm). The Aluminum is reinforced by graphite with a particle size of (≤63μm) with an addition of glass particles with different weight ratios of (3, 6, 9, and 12) Wt. % and a particle size was (≤ 53μm).Powder metallurgy technique has been used to manufactured the samples, where the samples are pressed uniaxial at room temperature with (500 Map), then sintering at (550 C0) for (2 hr.). After that, heat treatment is applied on the samples at (500 OC) for one hour and Quenched in water.There was a great improvement of the mechanical properties such as the hardens and the compressive strength. This improvement was proportional with the Weight ratio of the glass particles before and after the Heat Treatment.On the other hand, there was a decrease of the wear rate versus the increase of the Weight ratio of the glass particles and heat treatment.

يهدف هذا البحث الى دراسة تأثير اضافة دقائق الزجاج بنسب وزنية مختلفة Wt%(3,6,9,12) بحجم (≤53 μm) مع اضافة نسبة وزنية ثابتة % 2 من كرافيت بحجم جسيمي(≤ 63 μm) وتأثير المعاملة الحرارية على الخواص الميكانيكية ومعدل البلى للالمنيوم النقي وبحجم جسيمي (≤53 μm) .استُخدمت تقانة ميتالورجيا المساحيق لتصنيع النماذج اذ كبست النماذج على البارد بضغط كبس ( Mpa500) تم تلبيدها بدرجة حرارة (550 Co) ولمدة ساعتين ثم سُخنتْ النماذج الى درجة حرارة (500 Co) لمدة ساعة واحدة ثم بردت بالماء.بعدَ اجراء فحص الصلاده ومقاومة الانضغاط اظهرت النتائج حدوث تحسن كبير في الصلاده ومقاومة الانضغاط مع زيادة نسب اضافة دقائق الزجاج الى المتراكب قبل وبعد المعاملة الحرارية.تبين من خلال اختبار البلى حدوث انخفاض واضح مع زيادة نسب الاضافة قبل وبعد المعاملة الحرارية.


Article
Reinforcing a metal-based composite with a percentage of MgO particale to improve some of its properties and its relationship to conventional heat treatment
تدعيم متراكب ذات أساس معدني بنسب من دقائق أوكسيد المغنسيوم لتحسين بعض من خواصه وعلاقتها بالمعالجة الحرارية التقليدية

Author: Shaymaa M.F. شيماء محمد فياض
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2017 Volume: 22 Issue: 11 Pages: 71-78
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This research involved the manufacture of three compounds using powdered metallurgy technology through the reinforcement of the AlNi with addition percentage (40%), (35%) and 30% (MgO) ceramic reinforce phase to compound of A , B and C respectively and thermally treated In the traditional way In order to study the effect of the MgO addition and heat treatment, the mechanical tests (Diametrical compressive strength and hardness) were conducted.In order to determine the possibility of using the models produced for the attenuation of β particles, The linear attenuation coefficient and half thickness were examined for all models, The mechanical properties and the linear attenuation coefficient of all compounds have been improved, It was observed that the effect of the chemical composition was greater on the properties under study. We obtained the value of the compressive compressive strength of C (29) MPa before the a heat treatment, while the same compound had the MPa ( 32) After the heat treatment, in case of change in the addition ratio, we obtained the highest values of the mechanical properties and the linear attenuation coefficient of C, (29) MPa, (39) and (19.6)cm-1 respectively., And the lowest value given to the thickness of half (0.035)cm compared with (0.078) given by the A compound with the lowest mechanical properties and the linear attenuation coefficient (26.5)Mpa, (34.5) and (8.8)cm-1respectively before thermal treatment.

تضمن هذا البحث تصنيع ثلاث مركبات بتقانة ميتالورجيا المساحيق من خلال تدعيم طور الأساس المعدني (AlNi) بنسب أضافة (40%) , (35%) و(30%) من طور التدعيم السيراميكي MgO لتكوين المركبات A,B,C على التوالي ومعالجتها حراريا بالطريقة التقليدية, ولدراسة تأثير نسبة اضافة MgO والتلدين تم اجراء الفحوصات الميكانيكية (مقاومة الانضغاط القطرية والصلادة) ولتحديد امكانية استخدام النماذج المنتجة لغرض توهين جسيمات بيتا تم اجراء فحص معامل التوهين الخطي وسمك النصف لكافة النماذج. تم التوصل الى امكانية تحسن الخواص الميكانيكية ومعامل التوهين الخطي لكافة المركبات بالتلدين, لكن تم ملاحظة ان تأثير التكوين الكيميائي كان أكبر من التلدين على الخواص قيد الدراسة فحصلنا على قيمة مقاومة الانضغاط القطري للمركب C MPa(29) قبل التلدين بينما امتلك نفس المركب القيمة MPa(32) بعد التلدين بنما في حالة تغير نسبة الاضافة حصلنا على اعلى قيم للخواص الميكانيكية ومعامل التوهين الخطي للمركب C وهي MPa(29), (39) وcm-1(19.6) على التوالي, واقل قيمة اعطاها لسمك النصف cm(0.035) بالمقارنة مع القيمة cm (0.078) التي اعطاها المركب A الذي امتلك اقل قيم للخواص الميكانيكية ومعامل التوهين الخطي MPa(26.5) , (34.5) و cm-1(8.8) على التوالي قبل المعالجة الحرارية .


Article
Study of Differential Scanning Calorimetry on Phase Precipitation in Various Heat Treatments of AlZnMgCu Aluminum Alloys
دراسة مسعر المسح التبايني على أطوار الترسيب في معاملات حرارية متنوعة لسبائك الألمنيوم (الألمنيوم-زنك-مغنيسيوم-نحاس)

Author: Haider Tawfiq Naeem
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2017 Volume: 5 Issue: 1 Pages: 10-15
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

Powers compensation of the differential scanning calorimetry (DSC) have been utilized to revealed ‎and analyze the phases of precipitations in the complex quaternary of Zinc (6.7wt. %) _ Magnesium (2.8 wt. %) _ Copper (1.8 wt. %) _Aluminum alloys ‎manufactured by the process of the Semi-Direct Chill Casting. The casted Al-Zn-Mg-Cu alloys slabs were homogenizing at the different temperatures. Firstly under treatment 450°C for 2 hours follow by treatment 470°C for 1 day and then treatment at 480°C for 40 minutes, then all casted samples have quenched in cold water after each step. The treated homogenized Al-Zn-Mg-Cu samples that were underwent the artificial ageing at 120 °C for 1 day, and then retrogression at 180°C for 2400sec. and then re-ageing at 120°C for 1 day. The outcomes proved that the X-ray diffraction (XRD) analyses confirmed information of the DSC thermal analyses which were obtained through various heat treatments of the three samples AlZnMgCu alloy. The outcomes have explained that the DSC data are helping in understanding the changes the peaks of temperatures as well the enthalpy values for the forming and dissolution the equilibrium phase’s and precipitation compounds within the artificial againg (with the pea-temper) and the Retrograession and Re-Againg-(RRA) treatments were conducting for Al_Zn_Mg_Cu alloy samples.

في هذه الدراسة تم استخدام معادلة القدرة التفاضلية لمسعر المسح التبايني (Differential Scanning Calorimetry-DSC) لكشف وتحليل مركبات الترسيب في الرباعية معقدةالالمنيوم- 6.7٪ الزنك -2.8٪ المغنيسيوم- 1.8٪ النحاس سبائك , التي تنتجها عملية السباكة ذات التبريد السريع شبه المباشر.خضعت ألواح مسبوكة من خلائط آلامنيوم - الزنك- المغنيسيوم- النحاس الى معاملة المجانسة الحرارية عند درجات حرارة مختلفة .كانت هذه اولى تحت 450 درجة مئوية لمدة 2 ساعة يتبعها 470 درجة مئوية لمدة 24 ساعة واخيرا 480 درجة مئوية لمدة 40 دقيقة، بعدها تم اخماد العينات في الماء البارد بعد كل خطوة من عمليات التجانس. بالاضافة الى ذلك خضعت الواح السبيكة لمعاملة التعتيق الصناعي عند درجة حرارة 120 مئوية لمدة 24 ساعة ، وايضا على حرارة 180 درجة مئوية لمدة 40 دقيقة ثم إعادة التعتيق عند 120 درجة مئوية لمدة 24 ساعة خضعت كل العينات الى التبريد بالماء البارد بعد كل عملية حرارية. أثبتت النتائج أن معلومات تحليل حيود الأشعة السينية (XRD) تؤكد المعلومات الحاصلة من التحاليل الحرارية للمسعر المسح التبايني ((DSC لعينات الالمنيوم الخاضعة للمعالجات الحرارية المختلفة.من جانب اخر اوضحت النتائج ان البيانات الحرارية للمسعر المسح التبايني ((DSC ساعدت في فهم المتغيرات و قيم المحتوى الحراري لاطوارومركبات الترسيب عند التشكيل والانحلال الناتجة بتاثير التعتيق الصناعي عند 120 درجة مئوية وايضا عند عملية اعادة التعتيق في 120 درجة مئوية وثم عند 180 درجة مئوية تليها عند 120 درجة مئوية.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (8)

Arabic (1)


Year
From To Submit

2017 (9)