STUDYING PROPERTIES OF AL-12WT%SI ALLOY REINFORCED WITH CeO2 NANO POWDERS PREPARED BY POWDER METALLURGY
دراسة خواص سبيكة Al-12%Si المقواة بمسحوق نانوي من CeO2 والمحضرة بطريقة ميتالورجيا المساحيق

Loading...
Loading...
Abstract

In this paper, Aluminum – 12wt% Silicon alloys reinforced by cerium oxide (CeO2) nano powder with a different percentage (1, 2, and 3 wt.%) were prepared by powder technology method. Wear, porosity, apparent density tests were conducted for composite materials and reference alloy. The results showed that there is a slight change in the density and increases in the porosity of nanocomposite materials compared to reference alloy. The wear rate decreases with the increase in the proportion of the reinforced particles for the reference alloy as well as the wear rate increases with increased applied load.

في هذا البحث تم تحضير مواد متراكبة ذات اساس من سبيكة المنيوم – 12% سليكون ومقواة بمسحوق نانوي من مادة سيراميكية اوكسيد السيريوم (CeO2) بنسب مختلفة (1, 2, 3%) بطريقة تكنولوجيا المساحيق. تم اجراء اختبارات البلى, المسامية وكذلك الكثافة الظاهرية على المواد المتراكبة والسبيكة الاساس. اظهرت النتائج ان هنالك تغيير طفيف في الكثافة وزيادة في المسامية للمواد المتراكبة النانوية مقارنة بالسبيكة غير المقواة . اما معدل البلى فيقل مع زيادة نسبة الدقائق المقواة بالنسبة الى السبيكة غير المقواة وكذلك يزداد معدل البلى مع زيادة الحمل المسلط .


Article
Fabrication And Studies Of structural, Dielectrical Properties Of (Ni0.95-xCoxCu0.05Fe2O4) Composites by Powder Technology Method
تصنيع ودراسة الخصائص التركيبية والعزلية للمتراكب (Ni0.95-xCoxCu0.05Fe2O4) بطريقة تقانة المساحيق

Loading...
Loading...
Abstract

In this paper, the preparation of compounds, Ni0.95CoxCu0.05Fe2O4) by using powder technology method where (X = 0, 0.01, 0.02, 0.03, 0.04,and 0.05) annealing at 1100 C temperature for four hours. A series of samples were carried out for the study of structural properties by measuring x-ray diffraction (XRD). It included the study of the lattice constant (a), the particle size (D), the porosity (P) and the virtual density by x-ray diffraction, (x-ray density) as well as the study of Dielectric properties using the LCR , the study of the loss of dielectric meter tand and the electric conductivity (Ϭac). The results of X-ray diffraction showed that all samples had a crystalline,) and also showed that the Lattice constant (a) increases as the content of cobalt increases the density of the particles calculated by X-ray diffraction increases with the cobalt content, while the porosity and particles size decreases as the cobalt content increases, and the electrical show that the real and imaginary dielectric and electrical conductivity using current decreases as frequency increases, the real electrical dielectric constant increases as the cobalt content increases, while the imaginary part of dielectric constant and electrical conductivity decreases as the cobalt content increases.

تم في هذا البحث تحضير مركبات نيكل –كوبالت – نحاس فرايت ذات الصيغة الكيميائية Ni0.95CoxCu0.05Fe2O4)) باستخدام طريقة تكنولوجيا المساحيق حيث X=0.00,0.01,0.02,0.03,0.04,0.05)) عند درجة حرارة التلدين 1100) ₒC) لمدة أربع ساعات. حيث تم اجراء مجموعة من الفحوصات لدراسة الخواص التركيبية وذلك عن طريق قياس حيود الأشعة السينية XRD)) فقد تضمنت دراسة ثابت الشبيكة (a) والحجم الحبيبي (Dμm) والمسامية والكثافة الظاهرية بدلالة حيود الأشعة السينية, وكذلك دراسة الخواص العزلية باستخدام جهاز LCR)) اذ تضمنت الدراسة قياس ثابت العزل الكهربائي الحقيقي ('Ɛ) وثابت العزل الكهربائي الخيالي ("Ɛ) ودراسة خسارة العازل tan δ)) والتوصيلية الكهربائية Ϭ ac)). لقد أظهرت نتائج حيود الأشعة السينية أن جميع النماذج ذات تركيب بلوري متمركز الاوجه (FCC) من خلال الحصول على خواص نظام FCC)) وهي ((β=ɣ=α و(a=b=c) وكذلك أظهرت أن ثابت الشبيكة a)) يزداد كلما زاد تركيز الكوبالت والكثافة الظاهرية التي تم حسابها عن طريق حيود الأشعة السينية تزداد مع زيادة تركيز الكوبالت أما المسامية والحجم الحبيبي ينخفضان كلما زاد تركيز الكوبالت. كما أظهرت الفحوصات العزلية أن ثابت العزل الكهربائي الحقيقي والخيالي والتوصيلية الكهربائية باستخدام تيار متناوب تنخفض كلما زاد التردد أما تأثير تركيز الكوبالت فأنه يؤدي إلى زيادة ثابت العزل الحقيقي وانخفاض قيم ثابت العزل الخيالي والتوصيلية الكهربائية


Article
EFFECT OF SINTERING TEMPERATURE ON PHYSICAL PROPERTIES AND CORROSION BEHAVIOR OF COMPACT (AL-4.5%CU- 1.5%MG) ALLOY
دراسة تأثير درجة حرارة التلبيد عل الخواص الفيزياوية والسلوك التاكلي لمكبوسة من سبيكة ( ألمنيوم-4.5% نحاس –1.5% مغنيسيوم)

Loading...
Loading...
Abstract

This work aims to study the effect of sintering temperatures on physical properties (density and porosity) and corrosion behavior of compact(Al-4.5%Cu-1.5%Mg) alloy in 3.5% NaCl solution at room temperature using cyclic polarization method. Powder technology was used to prepare this alloy by mechanical mixing of Al, Cu and Mg powders in a ball mill for 6 hours to ensure a homogenous distribution of powders in the mixture. Mixed powder was compacted by using single action pressing at (450 MPa) then followed directly by sintering process at different temperatures (520,540,560,580 and 600ºC) for one hour in vacuum furnace under the effect of inert gas condition. Density ,porosity and microhardness measurements were performed to find the best sintering temperature. Tafel extrapolation method and cyclic polarization tests were conducted for all sintered samples. It was shown that the highest density and micro hardness were at sintering temperature 560ºC. It was found that the pitting corrosion resistance enhances with increasing sintering temperature up to 560ºC and afterword it drops again at higher temperatures (580 and 600ºC).

يهدف هذا البحث الى دراسة تأثير درجة حرارة التلبيد على الخواص الفيزياوية (الكثافة والمسامية) والسلوك التاكلي لسبيكة مكبوسة من ( ألمنيوم –4.5% نحاس-1.5% مغنيسيوم) في محلول 3.5% كلوريد الصوديوم في درجة حرارة الغرفة بطريقة الاستقطاب الحلقي ( الدوري ) باستخدام جهاز المجهاد الساكن . حيث تم خلط المساحيق من الألمنيوم ,النحاس ،المغنيسيوم بواسطة طاحونة الكرات لمدة 6 ساعات للحصول على مسحوق متجانس. تم كبس الخليط بعدها بضغط أحادي الاتجاه تحت ضغط (450MPa ) بواسطة مكبس هيدروليكي . لبدت المكبوسات بدرجات حرارة مختلفة ولمدة ساعة واحدة لكل درجة حرارية في فرن كهربائي مفرغ (في جو غاز الاركون). تم قياس الكثافة والمسامية والصلادة الدقيقة للعينات وكذلك اجري فحص التآكل بطريقة تافل للاستقطاب والاستقطاب الدوري للعينات. لوحظ أن أعلى كثافة حقيقية وصلادة مجهرية كانت عند درجة تلبيد (560 ºC). وكذلك لوحظ ان مقاومة التآكل النقري للسبيكة الملبدة تتحسن مع زيادة درجة حرارة التلبيد إلى حد (560ºC) ثم تنخفض بعد ذلك عند الدرجات الحرارية الأعلى منها .


Article
Comparison the Physical and Mechanical Properties of Composite Materials (Al /SiC and Al/ B4C) Produced by Powder Technology
مقارنة الخواص الفيزياوية والميكانيكية لمواد مركبة (المنيوم/ كاربيد السليكون، المنيوم/ كاربيد البورون) منتجة بطريقة تكنولوجيا المساحيق

Author: Khansaa Dawood Salman خنساء داود سلمان
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 10 Pages: 85-96
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this investigation, metal matrix composites (MMCs) were manufactured by using powder technology. Aluminum 6061 is reinforced with two different ceramics particles (SiC and B4C) with different volume fractions as (3, 6, 9 and 12 wt. %). The most important applications of particulate reinforcement of aluminum matrix are: Pistons, Connecting rods etc. The specimens were prepared by using aluminum powder with 150 µm in particle size and SiC, B4C powder with 200 µm in particle size. The chosen powders were mixed by using planetary mixing setup at 250 rpm for 4hr.with zinc stearate as an activator material in steel ball milling. After mixing process the powders were compacted by hydraulic unidirectional press type (Leybold Harris No. 36110) at 250 Kg/cm2 according to (ASTM-D 618). Finally the green compacts were sintered at 500 ℃ for 3 hr. by using electrical furnace with argon atmosphere. There are many examinations and tests were done for the produced metal matrix composites (MMCS), (Al/ SiC and Al/B4C) such as examination of the microstructure, mechanical tests (hardness and compressive strength), physical tests (density test before and after sintering, also porosity test). The results of this investigation showed that improving the physical properties (theoretical density, experimental density, porosity) and mechanical properties (Rockwell hardness and compressive strength).

في هذا البحث تم تصنيع مادة مركبة بطريقة تكنولوجيا المساحيق. تمت تقوية الألمنيوم 6061 بنوعين مختلفين من الدقائق السيراميكية ( كاربيد السليكون ، كاربيد البورون) بنسب حجمية مختلفة 3، 6، 9، و12 % . من أهم تطبيقات التقوية بالدقائق لأرضية من الألمنيوم هي: المكابس، أذرع التوصيل . . الخ. تم تحضير العينات بأستخدام مسحوق الألمنيوم بحجم حبيبي 150 مايكرون ومساحيق كاربيد السليكون و كاربيد البورون بحجم حبيبي 200 مايكرون. تم خلط المساحيق المستخدمة باستخدام خلاط كوكبي بسرعة 250 دورة / دقيقة لمدة 4 ساعات مع مادة سترات الزنك كمادة منشطة مع كرات طحن من الفولاذ. بعد عملية الخلط تم تدميج المساحيق بمكبس هيدروليكي أحادي الأتجاه نوع (Leybold Harris No. 36110) بمقدار 250 كغم/ سم2 بموجب المواصفة (ASTM-D 618). أخيرآ تم تلبيد المدمجات الخضراء عند درجة حرارة 500مo لمدة 3 ساعات بأستخدام فرن كهربائي في جو من الآركون. أجريت العديد من الأختبارات والفحوصات للمواد المركبة المنتجة (ألمنيوم / كاربيد السليكون ، ألمنيوم/ كاربيد البورون ) مثل فحص البنية المجهرية ، أختبارات الصلادة ومقاومة الضغط، أختبارات الكثافة قبل وبعد التلبيد، كذلك أجري أختبار المسامية. أظهرت نتائج هذا البحث تحسن واضح في الخواص الفيزياوية (الكثافة النظرية ، الكثافة التجريبية، المسامية ) والخواص الميكانيكية (صلادة روكويل، مقاومة الأنضغاط).

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2017 (4)