Article
Study optical and structural properties of copper oxide nanoparticles prepared by pulse laser ablation technology in (LC/MS) water
دراسة الخواص البصرية والتركيبية لجسيمات أوكسيد النحاس النانوية المحضرة بتقنية الاستئصال بالليزر النبضي في ماء (LC/MS)

Loading...
Loading...
Abstract

Copper oxide nanoparticles (CuO NPs) were prepared by pulse laser (Nd: YAG Q-switch, λ=1064nm, frequency=6 Hz) ablation technology for copper target in height purity water type liquid chromatography / mass spectrometry (LC/MS), at energy (200) mJ and different pulses (100, 200, 300, 400) pulse to formation colloidal solution. Found surface Plasmon resonance (SPR) at (200) mJ and (100) pulses is (625) nm, when increases in pulses the (SPR) is nearly constant. The indirect optical energy gab for these solution (4, 2.7, 2.75, 2.5) respectively, with the increase in number of pulses, the energy gap by using Fluorescence Spectrophotometer (3.543) eV.

حضرت جسيمات أوكسيد النحاس النانوية (CuO NPs) بتقنية الاستئصال بواسطة ليزر النيدميوم-ياك النبضي لهدف من النحاس في ماء عالي النقاء نوع (LC/MS water)، عند طاقة mJ (200)، ونبضات مختلفة (100، 200، 300، 400) لتكوين محلول عالق. تم حساب رنين بلازمون السطح (SPR)، عند طاقة mJ (200) تساوي nm (625) وعند زيادة عدد النبضات تكون تقريبا ثابتة. تم حساب فجوة الطاقة البصرية المباشرة لهذه المحاليل النانوية، تكون eV (4، 2.7، 2.75، 2.5) على التوالي مع زيادة عدد النبضات، تكون فجوة الطاقة باستخدام مطياف التألق eV (3.543).


Article
Synthesis and Characteristics of Ag, Cu/Au Core/Shell Nanoparticles Produced by Pulse Laser Ablation
تحضير وخصائص الجسيمات النانوية لAg,Cu/Au (لب- قشرة) المستحصلة بواسطة استئصال الليزر النبضي

Author: Isam M. Ibrhim عصام محمد ابراهيم
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2017 Volume: 58 Issue: 3C Pages: 1651-1659
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Colloidal dispersions of mono Au, Ag , Cu and bimetallic Ag/Au and Cu/Au core/shell nanoparticles are synthesized by pulsed laser ablation of metals targets immersed in 5 ml distilled water (DW). Surface Plasmon resonance (SPR) and particle sizes are characterized by UV-VIS and HRTEM, the X-ray diffraction shows the structure of core/shell. The Surface Plasmon resonance of the produced nanoparticles solutions for silver nanoparticles about 402 nm and copper nanoparticles about 636 nm. While for the core-shell observed two peaks of SPR, Ag/Au core/shell at (406-516) nm, and Cu/Au core/shell observed one peak at 565nm, because the region of gold and copper close together. The shape and particle size have been confirmed by HRTEM measurement, average size is around 12nm for Ag NPs, and 14nm for Cu NPs, while the average size is around 11nm for Ag/Au core/shell NPs and around 13nm for Cu/Au core/shell NPs. Zeta potential (ZP) results proved the silver nanoparticle is more stabilizing (-23.11 mV) than other noble metal nanoparticles,while Ag/Au core/shell is more stabilizing(-27.77mV) with comparison with Cu/Au core/shell which less stabilizing.

تم تحضير السائل الغروي للعناصر Au، Ag و Cu والمعادن الثنائية Ag/Au و Cu/Au (لب/قشرة) للجسيمات النانوية بطريقة الليزر النبضي لاقراص هذه المعادن المغموره في 5ml من الماء المقطر . تم اجراء فحوصات طيف UV-VIS وفحوصات الاشعة السينية لايجاد التركيب البلوري ل(لب/قشرة), وكذلك فحوصات المجهر الالكتروني النافذ ذو الدقة العالية HRTEM)) لحساب حجم الجسيمات وكذلك ايجاد سطح البلازمون الرنيني(SPR) . كان قمة البلازمون الرنيني لجسيمات الفضة حوالي 402nm ولجسيمات النحاس النانوية 636nm . بينما كانت هناك قمتين للبلازمون الرنيني. لAg/Au(لب/قشرة) حيث كانت عند (406-516nm) ولCu/Au (لب/قشرة) كانت هناك قمة واحدة عند 565nm وذلك لكون قمة النحاس والذهب قريبة من بعضها . شكل وحجم الجسيمات النانوية تم تاكيدها بواسطة المجهر الالكتروني النافذ ذو الدقة العالية حيث كانت معدل حجم الجسيمات للفضة هي 12nm ولجسيمات النحاس 14nm وكان الحجم حوالي 11nm ﻟAg /Au (لب/قشرة) بينما كانت ل Cu/Au (لب/قشرة) هي 13nm .فحص جهد زيتا (Zeta potential) اثبت ان جسيمات الفضة النانوية اكثر استقرارا (-23.11mV) من بين العناصر النانوية للمعادن بينما كانت للمركب Ag/Au (لب/قشرة) اكثر استقرارا (-27.77mV) بالمقارنة مع Cu/Au (لب/قشرة) النانوية.