Antibacterial Activity of Gold and Silver Nanoparticles against Pathogen Species, E. coli and S. aureus

Authors: Odai N. Salman --- Mohammed O. Dawood --- Duha S. Ahmed
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2017 Volume: 13 Issue: 3 Pages: 19-22
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

Gold and silver nanoparticles (NPs) have been prepared by pulsed laser ablation in liquid (PLAL) operated at 532 nm wavelength with energy density about 17 J/cm2 and 10 J/cm2 for gold (Au) and silver (Ag), respectively, immersed in aqueous solvent with addition 5 mM sodium dodecyl sulfate (SDS) as surfactant. Transmission electron microscopy (TEM) revealed the spherical shape morphology of Ag nanoparticles and Au nanoparticles in the presence of surfactant and grain size of the Ag nanoparticles and Au nanoparticles was found to vary between 20 and 100 nm. Absorption spectra of Au and Ag colloidal confirmed the formation of nanoparticles and improve the addition of (SDS) as surfactant during PLAL method. Finally, the antibacterial activity of Au and Ag nanoparticles against bacterial species E. coli and S. aureus demonstrates that these nanoparticles were more active against Gram negative bacteria than Gram positive bacteria and this was attributed to change in the bacterial cell membranes composition.


Article
Surface Plasmon Resonance study of Ag nanoparticles colloidal
دراسة رنين بلازمون السطح لسائل الفضة الجسيمات النانوية الغروية

Authors: Waleed k. Mahmood وليد خالد محمود --- Rawa k. Ibrahim روى خليل ابراهيم --- Asama N. Naje اسامه ناطق ناجي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2017 Volume: 58 Issue: 4B Pages: 2090-2097
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Silver nanoparticles (Ag-NPs) have been prepared using the electro-chemical method. The experimental setup of this technique consist of two electrodes of pure silver (99.2 %), the applied voltage on the electrodes is 20 V and the current through the colloidal was about 0.4 Amp. The silver nanoparticles crystallization has been studied; the crystalline structure appears Face center Cubic. The optical properties of silver nanoparticles are strongly affected by the Local Surface Plasmon Resonance (LSPR). The wavelength of maximum absorption band for an Ag NPs have a range (~350nm-550nm).

تم تحضير الجسيمات الفضة النانوية باستخدام الطريقة الكهروكيميائية. الإعداد العملي لهذه التقنية يتكون من قطبين من الفضة النقية (99,2%), والفولتية المسلطة على القطبين 20 فولت والتيار المار خلال الغراء بحدود (0,4 امبير). وقد تمت دراسة تبلور جسيمات الفضة النانوية ، ويظهر التركيب البلوري مكعب متمركز الوجه. الخصائص البصرية لجسيمات الفضة النانوية تتأثر بقوة بالرنين الموضعي لبلازمون السطح ,والطول الموجي لأقصى امتصاص لجسيمات الفضة النانوية يقع ضمن المدى (350-550 ) نانومتر.


Article
Synthesis and Characteristics of Ag, Cu/Au Core/Shell Nanoparticles Produced by Pulse Laser Ablation
تحضير وخصائص الجسيمات النانوية لAg,Cu/Au (لب- قشرة) المستحصلة بواسطة استئصال الليزر النبضي

Author: Isam M. Ibrhim عصام محمد ابراهيم
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2017 Volume: 58 Issue: 3C Pages: 1651-1659
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Colloidal dispersions of mono Au, Ag , Cu and bimetallic Ag/Au and Cu/Au core/shell nanoparticles are synthesized by pulsed laser ablation of metals targets immersed in 5 ml distilled water (DW). Surface Plasmon resonance (SPR) and particle sizes are characterized by UV-VIS and HRTEM, the X-ray diffraction shows the structure of core/shell. The Surface Plasmon resonance of the produced nanoparticles solutions for silver nanoparticles about 402 nm and copper nanoparticles about 636 nm. While for the core-shell observed two peaks of SPR, Ag/Au core/shell at (406-516) nm, and Cu/Au core/shell observed one peak at 565nm, because the region of gold and copper close together. The shape and particle size have been confirmed by HRTEM measurement, average size is around 12nm for Ag NPs, and 14nm for Cu NPs, while the average size is around 11nm for Ag/Au core/shell NPs and around 13nm for Cu/Au core/shell NPs. Zeta potential (ZP) results proved the silver nanoparticle is more stabilizing (-23.11 mV) than other noble metal nanoparticles,while Ag/Au core/shell is more stabilizing(-27.77mV) with comparison with Cu/Au core/shell which less stabilizing.

تم تحضير السائل الغروي للعناصر Au، Ag و Cu والمعادن الثنائية Ag/Au و Cu/Au (لب/قشرة) للجسيمات النانوية بطريقة الليزر النبضي لاقراص هذه المعادن المغموره في 5ml من الماء المقطر . تم اجراء فحوصات طيف UV-VIS وفحوصات الاشعة السينية لايجاد التركيب البلوري ل(لب/قشرة), وكذلك فحوصات المجهر الالكتروني النافذ ذو الدقة العالية HRTEM)) لحساب حجم الجسيمات وكذلك ايجاد سطح البلازمون الرنيني(SPR) . كان قمة البلازمون الرنيني لجسيمات الفضة حوالي 402nm ولجسيمات النحاس النانوية 636nm . بينما كانت هناك قمتين للبلازمون الرنيني. لAg/Au(لب/قشرة) حيث كانت عند (406-516nm) ولCu/Au (لب/قشرة) كانت هناك قمة واحدة عند 565nm وذلك لكون قمة النحاس والذهب قريبة من بعضها . شكل وحجم الجسيمات النانوية تم تاكيدها بواسطة المجهر الالكتروني النافذ ذو الدقة العالية حيث كانت معدل حجم الجسيمات للفضة هي 12nm ولجسيمات النحاس 14nm وكان الحجم حوالي 11nm ﻟAg /Au (لب/قشرة) بينما كانت ل Cu/Au (لب/قشرة) هي 13nm .فحص جهد زيتا (Zeta potential) اثبت ان جسيمات الفضة النانوية اكثر استقرارا (-23.11mV) من بين العناصر النانوية للمعادن بينما كانت للمركب Ag/Au (لب/قشرة) اكثر استقرارا (-27.77mV) بالمقارنة مع Cu/Au (لب/قشرة) النانوية.