Evaluation of the Corrosion Rate of Different Types of Marine Ship Steel using Potentiostatic Test Method in Arabian Gulf Sea Water

Authors: R. A. Hussain --- H. H. Jassim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 7 Part (A) Engineering Pages: 709-716
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The effect of flow velocity and chemical composition of Arab gulf sea water on the corrosion behavior of three different types of steel (DNV/EH40, AB/FH32 and ABS DQ47) used in building of marine ship hull structures investigated by using electrochemical Potentiostatic test method was. The results indicate that the general corrosion rate under flow condition is larger than that obtained under static case. Increasing the velocity of sea water leads to increase the corrosion rates for certain limit and then began to decrease. NV/EH40 steel exhibited a significantly lower values of corrosion rate, ABS DQ47 steel has larger values and AB/FH32 marine steel plates has moderate values.


Article
CORROSION BEHAVIOR OF DISSIMILAR FRICTION STIR WELDED FOR ALUMINUM ALLOYS (5052 H34 AND 7075 T6)
سلوك التآكل لوصلات ملحومة بالخلط الاحتكاكي لسببكتي الالمنيوم (5052 H34 و7075 T6)

Author: Ahmed A. Zainulabdeen
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 2 Pages: 205-215
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Friction stir welding was used widely in joining of dissimilar Aluminum alloys joints which used in aerospace applications due to high specific strength and superior corrosion resistance. Aluminum alloys 5052 H34 and 7075 T6 was successfully welded at tool rotation speed (400) rpm and travel speed (187) mm/min with using adjustable scrolled pin tool. Corrosion behavior of this joint was investigated using potentiostat in two medias “0.5% HCl, 0.5% NaOH” to show the polarization resistance and calculate the corrosion rate from data of “Tafel extrapolation method”. The microstructures of different zones of FSW joint have been investigated. Cyclic polarizations were done to measure the resistance of specimens to pitting corrosion. From the results obtained, it has been shown that best corrosion resistance of welded joint was noticed in 0.5% NaOH comparing with 0.5% HCl. The corrosion rate of FSW welded joint was higher than base alloys in 0.5% NaOH, while it's lower than base alloys in 0.5% HCl. The Base metal alloys susceptible to pitting corrosion while friction stir welded joint exhibit good general and pitting corrosion resistance in NaOH and HCl media.

استخدمت طريقة اللحام بالخلط الاحتكاكي بشكل واسع في ربط سبائك الالمنيوم المختلفة المستخدمة في التطبيقات الفضائية وذلك لخفة وزنها وارتفاع مقاومتها النوعية ومقاومتها العالية للتآكل. تم لحام سبائك الالمنيوم 5052 H34 و7075 T6 بنجاح عن سرعة دورانية 400 دورة/دقيقة وسرعة لحام 187 ملم/دقيقة وباستعمال اداة ذات مسمار مسنن. كما تمت دراسة سلوك التآكل لها باستخدام "المجهاد الساكن" بوسطين هما: 0.5% حامض الهيدروكلوريك 0.5 % هيدروكسيد الصوديوم لبيان مقاومة الاستقطاب وحساب معدل التآكل من قيم طريقة "تافل الاستقرائية. كما تم فحص البنية المجهرية عند مناطق لحام مختلفة من الوصلة. الاستقطاب الحلقي تم اجراءه لقياس مقاومة التآكل النقري للعينات. من النتائج التي تم الحصول عليها تبين ان أفضل مقاومة تآكل لوصلة اللحام عند الغمر بمحلول هيدروكسيد الصوديوم بتركيز) 0.5%) بالمقارنة مع حامض الهيدروكلوريك بتركيز (0.5%). ان معدل التآكل لوصلة اللحام عند الغمر بمحلول هيدروكسيد الصوديوم أعلى منه بالنسبة للمعدن الأساس بينما يكون معدل الـتآكل لوصلة اللحام أوطأ من المعدن الأساس عند الغمر بمحلول حامض الهيدروكلوريك. لقد بينت النتائج ان سبائك المعدن الأساس يكون عرضة للتآكل النقري مقارنة بوصلة اللحام التي أبدت مقاومة تآكل جيدة ضد التآكل النقري والتآكل العام عند الغمر بمحلول هيدروكسيد الصوديوم وحامض الهيدروكلوريك بتركيز (0.5%).