Article
STUDY THE EFFECT OF NANO MATERIALS ADDITION ON SOME PROPERTIES OF CEMENT MORTAR

Authors: Fadhil A. Rasin --- Laith K. Abbas --- Mohammed J. Kadhim
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 5 Pages: 159-170
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This study involves nano-materials addition and interaction with cement mortar behavior for many mortar samples under variable curing time with constant water to cement ratio (W/C = 0.5). In this research some properties such as (hardness and water absorption test), were affected by adding small ratios of nano-particles (SiO2 or Al2O3) as replacements to the Ordinary Portland Cement (OPC) / type (I). The percentages of nano materials additives replacement on the mixture of mortar include (1, 2, 3, 4 and 5%) for both nano materials with constant (W/C) ratio. Also the amount of the fine aggregate used was three times the amount of cement. The results showed that, the hardness of the mortars for both nano materials gives better properties than mortar without nano materials in all tests. Best enhancements in properties for mortars with nano silica were achieved with (3%) additives while were achieved with nano alumina at (2%) additives.

تتضمن الدراسة اضافة المواد النانوية وتداخلاتها مع سلوك مونة الاسمنت لكثير من العينات تحت تاثير اوقات متغيرة للمعالجة مع نسبة ثابة للماء وبنسبة (W/C = 0.5). في البحث الحالي بعض الخواص الميكانيكية(اختبارخاصية الصلادة) والفيزياوية (اختبار امتصاص الماء) ، تأثرت من خلال اضافة نسب صغيرة من جسيمات نانوية (SiO2 or AL2O3) وكأضافات الى الأسمنت البورتلاندي العادي (OPC) نوع (I). النسبة المئوية للمواد النانوية المضافة الى خليط من عينات مونة الاسمنت كانت (1، 2، 3، 4، 5%) لكلا المواد النانوية المضافة ، كما استخدم الركام الناعم بثلاثة أضعاف كمية من الاسمنت المستخدم. اضهرت النتائج تحسن وارتفاع صلادة مونة الاسمنت لكل العينات الحاوية على مواد نانوية بالمقارنة مع العينات بدون المواد النانوية المضافة ولكل الأختبارات. تم الوصول الى افضل تحسن في الخصائص للعينات المضاف اليها النانو السيليكا عند نسبة (3%) بالمقارنة مع العينات المضاف اليها النانو الومينا والذي تحقق بنسبة (2%) مواد نانوية مضافة.


Article
Study the Effects of Nano-Materials Addition on Some Mechanical Properties of Cement Mortar

Authors: F.A. Rasin --- L.K. Abbas --- M.J. Kadhim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 4 Part (A) Engineering Pages: 348-355
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research involves nano-materials addition and interaction with cement mortar behavior for many mortar samples under variable curing time with constant water to cement ratio (W/C = 0.5). Some mechanical properties such as (compressive and flexural strength tests), durability (by water absorption test) were studied. The effect on the (Al-Mass cement) Ordinary Portland Cement (OPC) type (I) by additives with small amounts of nano-particles (SiO2) and (Al2O3) were investigated in this research. The nano materials additives were added on the mixture of mortar with the percentages (1, 2, 3, 4 and 5%) for both nano materials with constant (W/C) ratio and also the amount of the fine aggregate used three times the amount of cement. The results shows that, the strength of the mortar consist both nano materials give better properties than mortar without nano materials in all tests. But nano silica additive gives good properties up to (3%) than mortar with nano alumina additive which give proprietress up to (2%).


Article
Study the Effect of Nano Ceramic Particles on Some Physical Properties of Acrylic Resins

Author: Q.A. Hamad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 2 Part (A) Engineering Pages: 124-129
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present research, study the effect of adding two different types of reinforcing particles, which included: nano-alumina (nano-Al2O3) and nano-silica (nano-SiO2), that added with different volume fractions of (1%, 2% and 3%), on some physical properties of composite prosthesis complete denture base materials by using self (cold) cure poly methyl methacrylate (PMMA) resin as new fluid resin matrix. In this research, the composite prosthetic dentures specimens consist of two groups were prepared by using (Hand Lay-Up) method according to the types of reinforced particles, which includes: the first group consists of PMMA resin reinforced by nano-alumina particles, and the second group consists of PMMA resin reinforced by nano-silica particles. The physical tests were performed on these specimens include (water absorption test and thermal behaviors test). The result of this study showed the values of (thermal conductivity and thermal diffusivity) properties increased with increasing the volume fraction of both (nano-Al2O3 and nano-SiO2) particles in PMMA complete denture base materials. While, the values of (water absorption and specific heat) properties decreased. In addition, the addition of (nano-Al2O3) particles has a noticeable effect on the all properties of composite material for prosthetic denture base specimens more than the (nano-SiO2) particles.


Article
COMPRESSIVE STRENGTH OF CONCRETE CONTAINING WATER ABSORPTION POLYMER BALLS (WAPB)
مقاومة انضغاط الخرسانة الحاوية على الكرات البوليمرية الممتصة للماء

Author: Ikram Faraoun Ahmed اكرام فرعون احم
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2017 Volume: 8 Issue: 2 Pages: 42-52
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Water absorbent polymers (WAP) are new component in producing building materials. They provide internal curing which reduces autogenous cracking, eliminates autogenous shrinkage, mortar strength increased, enhance early age strength to withstand strain, improve the durability, introduce higher early age compressive strength, have higher performance and reduce the effect of insufficient external curing. This research used different percent of polymer balls to choose the percent that provides good development in compressive strength with time for both water and air curing. The water absorption polymer balls in this research have the ability to absorb water and after usage in concrete they spill out the water (internal curing) and shrink leaving voids of their own diameter before shrinking, thus leads to have internal curing with air voids to reduce the samples weight .The required quantity of water for the mixes reduced due to the addition of water from the absorption polymers.

البوليمرات الممتصة للماء هي اسلوب جديد في انتاج المواد البنائية التي تحتفظ بالماء اذ تقدم معالجة داخلية والتي تقلل التشققات الذاتية وتقلل الا نكماش الذاتي وتزيد قوة المونة والخرسانة وتزيد الانفعال المبكر وتزيد مقاومة الانضغاط المبكرة وبالتالي تحسن الاداء العام وتقلل من تاثير المعالجة الخارجية. هذا البحث يستخدم نسب مختلفة من الكرات البوليمرية لاختيار النسبة المثلى التي تعطي تطور جيد لمقاومة الانضغاط مع الزمن للنماذج المعرضة للمعالجة بالماء وبالهواء .ان ) المستخدمة في هذا البحث لها القابلية على امتصاص الماء وبعد وضعها في الخلطات WAPBالكرات البوليمرية ( الكونكريتية تطرح هذا الماء (تعطي معالجة داخلية) وتنكمش تاركة فراغات داخل الخلطة الخرسانية بقدر قطر هذه الكرات قبل انكماشها مما يقلل من وزن النموذج ان كمية الماء المستخدمة لاجراء الخلطات الخرسانية تم تقليلها بما يتناسب واضافة الكرات البوليمرية الماصة للماء وحسب كمية الماء الذي ستطرحه هذه الكرات البوليمرية.


Article
Study of The Properties of Clay Brick Made with The Addition of Certain Additives

Author: Basim Thabit Al-Khafaji
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 5 Pages: 1539-1551
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This investigated is conducted to study the effect of adding of marble dust and polymer (Styrene Butadiene Rubber) on the properties of clay brick. Specimens manufactured from soil brought from ( al-Huda plant of brick) located in Hilla . The proportions of the components of this soil were (% 49,% 18,% 33) (Clay, Sand, Silt), respectively, marble dust and (SBR) were added with percentages (12, 24,36) for marble dust and (5, 10, 15) for( SBR) by weight of dry soil. The properties of brick product were studied in two case ,in the first percentage of addition ( water /soil) was (15) and the second was (27) , also studied the case of adding (SBR) without adding water with addition a constant percentage of (marble dust) for all proportions of (SBR ). All Specimens were burnt in the same ( al_Huda plant) at a temperature of (1000 ° C) after being dried natural for a period of (7 day), through practical results for all test observed that the marble dust and (SBR) when the (water / soil = 27%) have the negative effect for compressive strength but marble dust has the acceptable effect on properties (water absorption and efflorescence) . However when the ( w/s=15% ), the marble dust and ( SBR) have an obvious positive effect for all properties of clay brick especially at addition of marble dust in ( 36 percentage) and (15 percentage) for polymer (SBR).

تم إجراء هذا البحث لدراسة تأثير إضافة غبار الرخام والبوليمر (مطاط ستايرين البيوتاديين) على خصائص الطوب الطيني .صنعت النماذج بتربة تم جلبها من ( معمل طابوق الهدى) الواقع في الحلة0كانت نسب مكونات هذه التربة هي 33 )% ,18%, %49) (Clay,Sand,silt)على التوالي. تم اضافة غبار المرمر بنسب (12%24,% 36,%) و البوليمر SBR (0%,16%,20%,24%) من وزن التربة الجافة 0درست خواص الطابوق المنتج في حالة اضافة نسبتي الماء (15%) و(27%) و درست حالة اضافة نسب من (SBR ) بدون اضافة ماء خلط و باضافة نسبة ثابتة من (غبار المرمرMD ) لكافة نسب (SBR ) في نفس المعمل تم حرق النماذج بدرجة حرارة (1000مئوية) بعد ان جففت لمدة (7 يوم) جفاف طبيعي ، من خلال النتائج العملية لكل الفحوصات لوحظ ان لغبار المرمر ومحلول (SBR) عند نسبة( ماء/ التربة =27%) تاثير غير ايجابي على مقاومة الانضغاط ولكن لغبار المرمر(MD) تاثير مقبول للخواص ( الامتصاص والتزهر) اما عند النسبة (15% w/s= ) فان لكل من غبارالمرمر والبوليمر (SBR ) تاثير ايجابي واضح جدا على كل خواص الطابوق الطيني وخصوصا عند نسبة الاضافة (36%) لغبار المرمر و(15%) للبوليمر( SBR ).


Article
Study of Raw Materials for Manufacturing Perforated Clay Bricks (Chamchamal, and Qaradagh Regions in Sulaimani/ Iraq)
دراسة مواد أولية لتصنيع الطابوق الطيني المثقب (في مناطق جمجمال وقرداغ في السليمانية / العراق)

Author: Kamal Ahmad Rashed كمال أحمد رشيد
Journal: Sulaimania Journal for Engineering Sciences مجلة السليمانية للعلوم الهندسية ISSN: 24101699/24156655 Year: 2017 Volume: 4 Issue: 4 Pages: 51-67
Publisher: university of Sulaimania جامعة السليمانية

Loading...
Loading...
Abstract

There is no information about the optimum molding moisture content and molding pressure on the physical and mechanical properties of clay bricks. In this paper, the effect of moisture content and applied pressure during molding of brick samples for two selected locations of Sulaimani province in Iraq were studied. After firing the molded brick samples at a temperature of 1000oC, the physical and mechanical properties were studied from the following tests: firing shrinkage, water absorption, dry density and uniaxial compressive strength. The results indicate that the optimum moisture content for molding and manufacturing of clay bricks is within (0.6 to 0.7) of plastic limit of the raw materials. Also, it was found that the sufficient applied pressure during molding of clay bricks is 6 MPa.

لا توجد معلومات كافية حول تأثير الرطوبة والضغوط التي تستخدم أثناء الصب على الخصائص الفيزيائية والميكانيكية للطابوق الطيني. تم في هذا البحث دراسة تأثير نسبة الرطوبة والضغوط التي تستخدم أثناء صب عينات الطابوق في موقعين مختارين في محافظة السليمانية. وبعد حرق عينات من الطابوق المصبوب عند درجة حرارة ( 1000ە م )، تم التعرف على الخواص الفيزيائية والميكانيكية باستخدام الاختبارات التالية: الانكماش الحراری ، امتصاص الماء ، الكثافة الجافة وقوة الضغط ذو محورين. وتشير النتائج أن نسبة الرطوبة المثالية لحد اللدونة للمواد الخام أثناء صب وتصنيع الطابوق الطيني هي ( 0.6 - 0.7 ). اضافة الى ذلك فقد وجد أن الضغط الكافي أثناء صب الطابوق الطيني هو 6 ميجا باسكال.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (6)


Year
From To Submit

2017 (6)