Study The Effect of Thickness on The Structural and Optical constant of CdSe Thin Films
دراسة تاثير السمك على الخواص التركيبية والثوابت البصرية لاغشية سيلينايد الكادميوم (CdSe)الرقيقة

Authors: T.H.Mahmoud طاهر حمد محمود --- B.K.Hassun بشرى كاظم حسون --- S.A.Make سمير عطا مكي
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2017 Issue: 1 Pages: 249-264
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research , pure (CdSe) thin films with a different thickness ( 300 , 500 ,700 ,900) ± 20 nm was deposited on glass substrate in room temperature ( 300K ) with deposition rate (0.7±0.01) nm /sec by thermal evaporation under vacuum technique , and then studies their structure and optical properties .The resultant of the structural analysis showed that all films with all thickness prepared were polycrystalline in nature and have hexagonal type structure with atomic growth in three crystal orientation which it [002] , [102] and [103] with Preferred orientation along [002] plane for all Prepared films.The optical analysis measurement showed that all prepared films have absorption coefficient with a value larger than (∝ > 〖10〗^4 〖cm〗^(-1)) and this value was increased when increasing the film thickness especially in the visible range of electromagnetic spectrum , the optical energy gap was founded in the range ( 1.70 -1.72 ) eV.

تم في هذا البحث ترسيب اغشية سيلينايد الكادميوم النقية بطريقـــة التبخير الحراري فــي الفراغ عـلى قواعد من الزجاج بــدرجة حـرارة الغرفــــــة ( 300k) وبسمــك مـختلف 20 nm±) 900 ،700 ، 500 ، 300 ) وبـمعـدل تــرسيب sec / 0.7nm ووجد بـان الاغشيـة النـاتجة كـانت ذات جـودة عالية مــن حيــث تجانس الغشاء والتصاقيته بالارضيات الزجاجية، ودرسـت خواصها التركيبية والبصرية. اظهرت نتائـج الفحوصــات التركيبية بـان جميع الاغشيــة الرقيقة ,والمحضرة بسمك مختلف كانت متعددة التبلور ومـن النـوع السداسـي مع نمو ذري بثلاثة اتجاهات بلورية هـي [103] و[102] و[002] كان المميز والسائد منها في الاتجاه [002] وللنماذج المحضرة كافة .امـــا نتائج الفحوصات البصريــة فـقـد بــيـنت بـان مـعامـل الامتصـاص للاغـشية المحــضرة كـــان ذو قــيمة اكــبر من (〖cm〗^(-1) α >〖10〗^4 ) وان هـذه الـقيمة تـزداد بشكل عام بزيادة السمك لاسيما عند الطاقات الفوتونية الواطئة ، اما بالنسبة الى قيمة فجوة الطاقة البصرية فلقد كانت ضمن المدى eV(1.70-1.72) .


Article
The Effect of the (Se) percentage on Compositional, Morphological and structural properties of Bi2(Te1-xSex)3 thin films
تأثير نسبة (Se) على الخواص السطحية والتركيبية لاغشية Bi2(Te1-x Sex)3 الرقيقة

Loading...
Loading...
Abstract

Alloys of Bi2[Te1-x Sex]3 were prepared by melting technique with different values of Se percentage (x=0,0.1,0.3,0.5,0.7,0.9 and 1). Thin films of these alloys were prepared by using thermal evaporation technique under vacuum of 10-5 Torr on glass substrates, deposited at room temperature with a deposition rate (12nm/min) and a constant thickness (450±30 nm).The concentrations of the initial elements Bi, Te and Se in the Bi2 [Te1-x Sex]3 alloys with different values of Se percentage (x), were determined by XRF,The morphological and structural properties were determined by AFM and XRD techniques. AFM images of Bi2[Te1-x Sex]3 thin films show that the average diameter and the average surface roughness increase with the increase of the percentage of Se. The X–ray diffraction measurements for bulk and thin films of Bi2[Te1-xSex]3 have polycrystalline structure with rohmbohedral structure, with space group R3m, and a strong (015) preferred orientation, the crystallite increase with the increase of Se percentage .

تم تحضير سبائك المركب Bi2(Te1-x Sex)3 بعملية صهر المواد الاولية وفق نسب مختلفة لنسبة السيلينيوم (x=0 , 0.1 ,0.3 ,0.5 ,0.7,0.9 and 1). الاغشية الرقيقة لهذا المركب تم تحضيرها باستخدام تقنية التبخير الحراري تحت ضغط فراغ يصل الى 10-5 torr)) حيث تم ترسيب المادة على قواعد زجاجية نظيفة في درجة حرارة الغرفة بمعدل ترسيب((12nm/min بسمك ((450±30 nm. . قد تم التأكد من نسب المواد الأولية (Bi ,Te and Se) باستخدام جهاز فلورة الاشعة السينينة XRF , اما الخواص التركيبية للسبائك والاغشية الرقيقة لمركب Bi2(Te1-x Sex)3 باختلاف نسبة السيلينوم فيها بواسطة جهاز حيود الاشعة السينية XRD اما الخواص السطحية للاغشية الرقيقة تم فحصها باستعمال جهاز AFM وقد وجد ان اقطار الحبيبات تزداد بزيادة نسبة السيلينيوم فيها وكذلك يزداد معدل الخشونة فيها ان قياس حيود الاشعة السينية وجد ان السبائك والاغشية الرقيقة لها تركيب متعدد التبلور ذو تركيب سداسي وفسحة مجموعة R3m وكانت القمة السائدة والاقوى هي (015) وكذلك بينت ان حجم البلوريات يزداد بزيادة نسبة السيلينيوم في المركب .