The Effect of Ag Doping on the Structural, Optical and Electrical Properties of CdSe Thin Films
تأثير التطعيم بالفضة على الخواص الكهربائية والبصرية التركيبية لأغشيه CdSe

Authors: Nawfal Y. Jamil نوفل يوسف جميل --- Ammar Y. Burjus عمار ياسين برجس --- Heba M.T. Khalil هبة محمد طاهر
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2018 Volume: 27 Issue: 3E Pages: 146-152
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

This work includes a study of the effect of Ag doping in CdSe on optical, structural and Electrical properties, through changing the ratio of the added Ag with (0, 1, 5, 10) % to the final prepared CdSe solution. Measurements of the transmittance, absorption of the prepared samples of CdSe for wave lengths in the band (400nm-750nm) is carried out. It is found that the band gap decreased (Eg=(1.97,1.92,168,152)eV) respectively as Ag concentration increased. X-ray diffraction (XRD) measurements shows that the deposited pure CdSe thin film is polycrystalline with hexagonal structure, whereas doped films with Ag shows cubic structure in the[111] direction. Electrical conductivity measurement of the films showed an increase with increasing the Ag concentration, also an increase in crystal alignment found.

يتضمن هذا البحث دراسة تأثير التطعيم بعنصر الفضة Ag لأغشية CdSe الرقيقة على الخواص التركيبية والبصرية والكهربائية وذلك من خلال تغيير نسب الحجوم الخاصة بنترات الفضة وبالنسب (0,1,5,10)% عند تحضير اغشية CdSe، وتضمن البحث اجراء قياسات النفوذية والامتصاصية للأطوال الموجية (400-750)nm وتم حساب قيمة طاقة الفجوة وقد وجد انها تتغير حسب القيم التالية (Eg=(1.97,1.92,1.68,1.52 )eV)، وهذا يعني ان قيمة فجوة الطاقة تقل مع زيادة تركيز Ag ومن قياسات حيود الاشعة السينية (XRD) لدراسة التركيب البلوري وجد بان التركيب من النوع المتعدد البلورات السداسي للنماذج التي لا تحتوي على عنصر الفضة اما في حالة النماذج المطعمة عنصر الفضة وجد التركيب من النوع المكعبي ويمتلك اتجاهيه مفضلة عند المستوي (111)، أظهرت قياسات التوصيلية الكهربائية زيادة جيدة في التوصيلية مع زيادة التركيز بعنصر الفضة، وكذلك زيادة في الرص البلوري


Article
The Effect of Al Doping on Structural, Electrical and Optical Properties of CdSe Films
تأثير تطعيم Al على الخواص التركيبية، الكهربائية والبصرية لأغشية CdSe

Authors: Suha A. Najim سهى عبد الله نجم --- Nawfal Y. Jamil نوفل يوسف جميل
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2018 Volume: 27 Issue: 3E Pages: 164-172
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

CdSe thin films were deposited on glass substrates by chemical bath deposition technique. The deposited CdSe thin films were annealed by thermal evaporation for (1h) at 250 ˚C. The samples were then coated with a different thicknesses of thin Al films (50, 100, 150, 200) Å by thermal evaporation method which then annealed at (1h,250˚C). The structural, optical, and electrical properties of deposited and doped samples were studied. The X-ray diffraction analysis showed that the films have polycrystalline structure of hexagonal type. From optical properties, the band gap energy of undoped CdSe thin film was 2 eV and it is decreased by increasing of Al doping. Electrical resistivity of the doped films showed a decrease with the increase of the Al concentration. The doped and undoped samples revealed that the conductivity was n-type

تم ترسيب أغشية CdSe الرقيقة على أرضية من الزجاج باستخدام تقنية الترسيب بالحمام الكيميائي Chemical Bath Deposition CBD)). أغشية CdSe الرقيقة المرسبة تم تلدينها بالتبخير الحراري لمدة ساعة عند 250 ˚C. العينات تم تطعيمها بغشاء من الألمنيوم الرقيق وبأسماك مختلفة Å(50, 100, 150, 200) بطريقة التبخير الحراري وبعدها تم تلدينها عند (1h, 250˚C). تم دراسة الخواص التركيبية، البصرية والكهربائية للنماذج المرسبة والمطعمة. من تحليل حيود الأشعة السينية تبين بان الأغشية تمتلك تركيبا متعدد البلورات من النوع السداسي (Hexagonal). ومن الخواص البصرية، وجد أن فجوة الطاقة لأغشية CdSe غير المطعمة 2 eV وإنها تقل مع زيادة التطعيم بالألمنيوم. المقاومية الكهربائية للأغشية المطعمة تبين أنها تقل مع زيادة تركيز Al. النماذج المطعمة وغير المطعمة أظهرت توصيلية من النوع السالب (n-type).


Article
The Effect of Cadmium Selenide Thin Film Thickness on Carbon Monoxide Gas Sensing Properties prepared by Plasma DC-Sputtering Technique

Author: Baha'a A. M. Al-Hilli
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2018 Volume: 59 Issue: 4C Pages: 2234-2241
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Cadmium Selenide (CdSe) thin films have been deposited on a glass substrate utilizing the plasma DC-sputtering method at room temperature at different deposition time in order to achieve different films thickness, and studied its sensitivity to the carbon monoxide CO gas which are show high response as the film thickness increases, the DC-conductivity and photoconductivity are also studied and which are increased too as the film thickness increases, that indicates the good semiconducting behavior at room temperature and light environments.