Article
Preparation single layer of (MgO) as antireflection coating using PLD technique
تحضير غشاء مضاد للانعكاس احادي الطبقة من اوكسيد المغنسيوم باستخدام تقانة الترسيب بالليزر النبضي

Loading...
Loading...
Abstract

In this work preparation of antireflection coating with single layer of MgO using pulsed laser deposition (PLD) method which deposit on glass substrate with different thicknesses (90 and 100) nm annealed at temperature 500 K was done. The optical and structural properties (X-ray diffraction) have been determined. The optical reflectance was computed with the aid of MATLAB over the visible and near infrared region. Results shows that the best result obtained for optical performance of AR'Cs at 700 shots with thickness 90 nm nanostructure single layer AR'Cs and low reflection at wavelength 550 nm.

في هذا البحث تم تحضير طلاء مضاد للانعكاس احادي الطبقة لمادة اوكسيد المغنسيوم بطريقة الترسيب بالليزر النبضي. وعلى اساس من الزجاج وباسماك مختلفة 90-100 نانومتر وفي درجة حرارة التلدين (500) درجة كلفنية.تم دراسة الخصائص البصرية والتركيبية للطلاء. الانعكاسية حسبت بواسطة برنامج MATLABضمن المنطقة المرئية والقريبة من الحمراء, النتائج اظهرت ان الحصول على افضل اداء بصري للطلاء المضاد للانعكاس عند سمك الغشاء 90 نانومتر وبعدد نبضات 700 نبضة وباقل انعكاسية و كان بطول موجي 550 نانومتر.


Article
Linear Optical Properties of Bromocresol Green Dye Doped Poly Methyl Methacrylate Thin Films
الخواص البصرية الخطية لاغشية بولي مثيل ميثاكرلايت المطعمة بصبغة بروموكريسول الخضراء

Loading...
Loading...
Abstract

In this study, we investigated the effect of Bromocresol green dye (BCG) of the PMMA thin films optical properties. Films of Poly Methyl Methacrylate doped by 10% BCG doping ratio to prepared two concentrations 2x10-4 and 6x10-4 M of PMMA-BCG dye were deposited on glass substrate using free casting method at room temperature. The optical properties of the films were determined using UV-Visible absorbance and transmittance spectra at the 300 - 900 nm wavelength range. The linear absorption coefficient and the extinction coefficient were calculated. The results showed that the optical properties were increasing by increasing the dye concentration, while the optical energy gap was decreasing with the doping. Also from the linear optical properties result the PMMA-BGC thin films are a promised materials for nonlinear optics applications.

درسنا تاثير التطعيم بصبغة بروموكريسول الخضراء على الخواص البصرية الخطية لاغشية البوليمر (بولي مثيل ميثا اكريلايت). تم تحضير هذه الاغشية المكونة من بولي مثيل ميثا اكريلايت المطعم بنسبة 10% صبغة بروموكريسول الخضراء لتحضير تركيزين (2×10-4, 6×10-4 مولاري) من غشاء بولي مثيل ميثاكرلايت – بروموكريسول الخضراء بواسطة طريقة الصب الحر على الواح زجاجية بدرجة حرارة الغرفة). تم قياس الخواص البصرية الخطية من خلال قياس اطياف الامتصاص والنفاذية ضمن المدى الطيفي 300- 900 نانو متر, اذ تم حساب المعاملات البصرية مثل معامل الامتصاص، معامل الانكسار، معامل الخمود، وفجوة الطاقة. اظهرت النتائج بأن المعاملات البصرية الخطية تزداد بأزدياد نسبة التطعيم للصبغة فيما لاحظنا نقصان في فجوة الطاقة البصرية مع ازدياد نسبة التطعيم. كما اظهرت النتائج ايضا ان هذا المادة ممكن ان تكون مادة واعدة لتطبيقات البصريات اللاخطية


Article
Influence of substrates on the properties of cerium -doped CdO nanocrystalline thin films
تأثير قواعد الترسيب على خصائص اغشية اوكسيد الكادميوم النانوية CdO الرقيقة المشوبة بالسيريوم Ce

Loading...
Loading...
Abstract

Transparent thin films of CdO:Ce has been deposited on to glass and silicon substrates by spray pyrolysis technique for various concentrations of cerium (2, 4, and 6 Vol.%). CdO:Ce films were characterized using different techniques such as X-ray diffraction (XRD), atomic force microscopy(AFM) and optical properties. XRD analysis show that CdO films exhibit cubic crystal structure with (1 1 1) preferred orientation and the intensity of the peak increases with increasing's of Ce contain when deposited films on glass substrate, while for silicon substrate, the intensity of peaks decreases, the results reveal that the grain size of the prepared thin film is approximately (73.75-109.88) nm various with increased of cerium content. With a surface roughness of (0.871–16.2) nm as well as root mean square of (1.06-19.7) nm for glass substrate, while for silicon (84.79-107.48) nm, for a pure CdO and doped with Ce (2, 4, and 6 Vol.%). The 300-nm-thin CdO films showed that the optical energy band gap equal 2.6 eV, and increases with increasing doping until reaches a maximum value of 3.25 eV when doping levels 6 Vol.%.

تم ترسيب الاغشية الرقيقة الشفافة لـ CdO المشوبة بالسيريوم Ce على قواعد الزجاج والسيليكون بتقنية التحلل الكيميائي الحراري, وبنسب التشويب مختلفة مع السيريوم وكانت 2, 4, and 6 Vol.%)). تم التعرف على خصائص الاغشية باستخدام تقنية حيود الأشعة السينية (XRD) ومجهر القوى الذرية (AFM) وكذلك الخصائص البصرية. وبينت فحوصات حيود الاشعة السينية ان اغشية اوكسيد الكادميوم تمتلك تركيب بلوري مكعبي وباتجاه مفضل (111), وان شدة القمم تزداد مع زيادة تركيز السيريوم عند الترسيب على قواعد الزجاج, اما في حالة الترسيب على قواعد السليكون فان شدة القمم تقل. ومن خلال فحوصات مجهر القوى الذرية في حالة الترسيب على قواعد الزجاج وجد ان الحجم الحبيبي للأغشية المحضرة هي (73.75-109.88) nm, وان الخشونة السطحية هي تقريبا (0.871–16.2) nm وان (RMS) هو (1.06-19.7) nm, اما في حالة الترسيب على قواعد السيليكون تبين ان الحجم الحبيبي هو (84.79-107.48) nm للاغشية النقية والمشوبة. بينت الفحوصات البصرية ان الاغشية ذات سمك (300 nm) وتمتلك فجوة طاقة بصرية ((2.6 eV وان هذه القيمة تزداد مع زيادة نسب التشويب لتصل الى اعظم قيمة لها (3.25 eV) عند نسبة تشويب 6 Vol.%.


Article
Structural and Optical Properties of Ce-Cupric Oxide Thin Films
الخصائص التركيبية والبصرية لأغشية اوكسيد السيريوم-النحاس الرقيقة

Loading...
Loading...
Abstract

This work focuses discusses the structural and optical properties of Cerium- Cupric oxide thin film prepared on silicon and glass substrate by the spray pyrolysis technique at a temperature of 200,250,300 ̊C. The results of (XRD) tests showed that all the prepared films were of a polycrystalline installation and monoclinic crystal structure with a preferable direction was (11-1) of CuO. Morphology analysis studied by atomic force microscopy (AFM) and reveals that the grain size of the prepared thin film is approximately (64.69-101.26)nm , with a surface roughness of (0.238– 0.544) nm as well as root mean square of (0.280-0.636)nm for CuO Ce-doping, Optical characteristics were studied by UV/VIS Spectrophotometer at (300- 1100 nm) and observed that the transmission value was more than 80 % at the visible wavelength range. The direct energy gap (Eg) ranged between (1.70-3.00) eV at temperature 200 ̊C and then the values of the energy gap decreases with increasing temperature of substrate when, is measured by UV/VIS.

تم في هذا البحث مناقشة الخصائص التركيبية والبصرية لأغشية أوكسيد السيريوم- أوكسيد النحاس الرقيقة المرسبة على قواعد من السيليكون والزجاج بواسطة تقنية التحلل الكيميائي الحراري في درجات حرارة مختلفة ̊ C300،250، 200، وأظهرت نتائج حيود الاشعة السينية (XRD) أن جميع الاغشية المحضرة تمتلك تركيب متعدد التبلور (polycrystalline) أحادية الميل (monoclinic) وان الاتجاه المفضل هو (11-1). درست طبوغرافية السطح من خلال مجهر القوة الذرية (AFM) وقد تبين أن الحجم الحبيبي للأغشية الرقيقة المحضرة حوالي(64.69-101.26)nm ، مع خشونة السطح(0.238– 0.544) nm وكذلك متوسط الجذر التربيعي (RMS)(0.280-0.636)nm لأغشية أوكسيد النحاس- سيريوم الرقيقة المحضرة، وقد تمت دراسة الخصائص البصرية بواسطة ﻣﻄﯿﺎف اﻟﻨﻔﺎذﯾﺔ ﻟﻼﺷﻌﺔ اﻟﻤﺮﺋﯿﺔ –ﻓﻮق اﻟﺒﻨﻔﺴﺠﯿﺔ (UV-VIS)عند طول موجي ,(300 - 1100 nm) ولوحظ أن قيمة النفاذية كانت أكثر من 80% في نطاق الطول الموجي المرئي وان فجوة الطاقة المباشرة تمتلك قيم متدرجة بين (1.70-3.00) eV عند درجة حرارة C 200 ̊، ثم تنخفض قيم فجوة الطاقة مع زيادة درجة حرارة القاعدة.


Article
The Influence of RF power, pressure and substrate temperature on optical properties of RF Sputtered vanadium pentoxide thin films
تاثير الطاقة والضغط ودرجة حرارة الركيزة على الخصائص البصرية للاغشية الرقيقة لخامس اوكسيد الفاناديوم باستخدام الترذيذ بالترددات الراديوية

Authors: Ibrahim K. salman إبراهيم خلف سلمان --- N.K. Hassan نديم خالد حسن --- Mohammed K. Khalaf محمد خماس خلف
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 42-47
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The V2O5 films were deposited on glass substrates which produce using "radio frequency (RF)"power supply and Argon gas technique. The optical properties were investigated by, UV spectroscopy at "radio frequency" (RF) power ranging from 75 - 150 Watt and gas pressure, (0.03, 0.05 and 0.007 Torr), and substrate temperature (359, 373,473 and 573) K. The UV-Visible analysis shows that the average transmittance of all films in the range 40-65 %. When the thickness has been increased the transhumance was decreased from (65-40) %. The values of energy band gap were lowered from (3.02-2.9 eV) with the increase of thickness the films in relation to an increase in power, The energy gap decreased (2.8 - 2.7) eV with an increase in the pressure and substrate temperature respectively.

تم ترسيب أغشية رقيقة من خامس اكسيد الفاناديوم على ركائز زجاجية التي تنتج باستخدام طاقة التردد الراديوي وتقنية غاز الأرجون، وتم بحث الخواص البصرية بواسطة دراسة مطيافية مرئية فوق بنفسجية عند قدرة التردد الراديوي من 75 - 150 واط وضغط الغاز 0.03 تور، .050 تور و 0.007 تور، ودرجة حرارة الركيزة (359، 373، 473 و 573) كلفن. أظهر التحليل الطيفي المرئي و للأشعة فوق البنفسجية أن متوسط نفاذ جميع الأغشية يكمن في نطاق 40-65 ٪ و عندما زاد السمك انخفضت نسبة الانتقال مـــن (65 -40) %. و انخفضت فجوة النطاق الضوئي للغشاء من 3.02 إلى 2.9 الكترون فولت, مع زيادة سماكة الأغشية مقارنة بالزيادة في القدرة، من ناحية أخرى انخفضت فجوة النطاق من 2.8 إلى 2.7 الكترون فولت, مع زيادة الضغط ودرجة حرارة الركيزة على التوالي.


Article
The Effect of Al Doping on Structural, Electrical and Optical Properties of CdSe Films
تأثير تطعيم Al على الخواص التركيبية، الكهربائية والبصرية لأغشية CdSe

Authors: Suha A. Najim سهى عبد الله نجم --- Nawfal Y. Jamil نوفل يوسف جميل
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2018 Volume: 27 Issue: 3E Pages: 164-172
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

CdSe thin films were deposited on glass substrates by chemical bath deposition technique. The deposited CdSe thin films were annealed by thermal evaporation for (1h) at 250 ˚C. The samples were then coated with a different thicknesses of thin Al films (50, 100, 150, 200) Å by thermal evaporation method which then annealed at (1h,250˚C). The structural, optical, and electrical properties of deposited and doped samples were studied. The X-ray diffraction analysis showed that the films have polycrystalline structure of hexagonal type. From optical properties, the band gap energy of undoped CdSe thin film was 2 eV and it is decreased by increasing of Al doping. Electrical resistivity of the doped films showed a decrease with the increase of the Al concentration. The doped and undoped samples revealed that the conductivity was n-type

تم ترسيب أغشية CdSe الرقيقة على أرضية من الزجاج باستخدام تقنية الترسيب بالحمام الكيميائي Chemical Bath Deposition CBD)). أغشية CdSe الرقيقة المرسبة تم تلدينها بالتبخير الحراري لمدة ساعة عند 250 ˚C. العينات تم تطعيمها بغشاء من الألمنيوم الرقيق وبأسماك مختلفة Å(50, 100, 150, 200) بطريقة التبخير الحراري وبعدها تم تلدينها عند (1h, 250˚C). تم دراسة الخواص التركيبية، البصرية والكهربائية للنماذج المرسبة والمطعمة. من تحليل حيود الأشعة السينية تبين بان الأغشية تمتلك تركيبا متعدد البلورات من النوع السداسي (Hexagonal). ومن الخواص البصرية، وجد أن فجوة الطاقة لأغشية CdSe غير المطعمة 2 eV وإنها تقل مع زيادة التطعيم بالألمنيوم. المقاومية الكهربائية للأغشية المطعمة تبين أنها تقل مع زيادة تركيز Al. النماذج المطعمة وغير المطعمة أظهرت توصيلية من النوع السالب (n-type).


Article
Optical properties for prepared polyvinyl alcohol/ polyaniline/ ZnO nanocomposites
الخواص البصرية للمركب النانوي المحضر بولي فينل الكحول بولي انلين اوكسيد الزنك

Authors: Salma Mohamed سلمى محمد حسن --- Nawras Kareem نورس كريم علي
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 36 Pages: 181-189
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The optical energy gap and optical constants such as the reflective index, dielectric constant have been evaluated due to The optical transmission and UV-VIS absorption spectra have been recorded in the wavelength (200 - 1100 nm) for PVA/PANI polymer blends and PVA/PANI/ZnO nanocomposites with different concentrations of ZnO (0.02, 0.05, 0.07, 0.1and 0.2) wt %. The results indicate that the materials have allowed direct transition. The reflection index and dielectric constant are increase with wavelength.

تم حساب فجوة الطاقة البصرية والثوابت البصرية مثل الانعكاس وثابت العزل الحقيقي باستخدام أطياف الامتصاص الضوئية وأشعة فوق البنفسجية في الطول الموجي (200 - 1100nm ) للخلائط البوليمريه بولي فاينل الكحول/ بولي انلين ومتراكبات النانوبه بولي فاينل الكحول/بولي انلين/ أكسيد الزنك النانوي وبتراكيز مختلفه من ال ZnO (0.02، 0.05، 0.07، 0.1 و 0.2) %. نتائجنا تشير إلى أن المواد سمحت الانتقال المباشر و وجد زياده معامل الانكسار وثابت العزل مع الطول الموجي.


Article
Morphological and Optical Properties of In_2 O_3:Sn Thin Films Deposited by Spray Pyrolysis

Authors: Salam Amir Yousif --- Duha Ismail Khalil
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2018 Volume: 14 Issue: 02 Pages: 275-290
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The morphological and optical properties of indium tin oxide (ITO) thin films have been studied in this paper. Tin doped indium oxide thin films were deposited successfully on glass substrates at (450±10)℃ for various tin doping (0, 5, 10, 15, 20) % by spray pyrolysis technique. Atomic force microscopy has been used to study the surface morphology of In_2 O_3:Sn thin films. The optical properties were calculated by the absorbance and transmittance spectra in the wavelength interval (300-1000) nm. The optical constants such as (absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of dielectric constant and optical conductivity) have been calculated and discussed.


Article
Effect Of Thermal Annealing On The Optical Properties Of Thin Films Of Polymer Blend (PMMA:PVC:PS)

Author: Ali N. Sabbar 1*, Karar M.Talib2, and Hassan T. Badh1
Journal: Almuthanna Journal of Pure Science (MJPS) مجلة المثنى للعلوم الصرفة ISSN: 22263284 Year: 2018 Volume: 5 Issue: 1
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

In this paper, we report upon preparation and optical properties of the polymer blend(50%PMMA:25%PVC:25%PS) thin films. The thin films have been prepared with specific ratios using the castingtechnique at normal weather conditions. The films were subjected to heat treatment in varying temperatures for threehours. The results showed that increase thermal annealing temperature leads to decrease values of the direct and indirectenergy gap, but increase the extinction coefficient and optical conductivity. The refractive index, real and imaginarydielectric constants showed a heterogeneous behaviour. Thermal annealing by 80 oC and up leads to deformation thethin films.


Article
Synthesis and Optical Properties of Polystyrene Doped with DCM Thin Films

Author: Akeel Shaker Tuhaiwer
Journal: Almuthanna Journal of Pure Science (MJPS) مجلة المثنى للعلوم الصرفة ISSN: 22263284 Year: 2018 Volume: 5 Issue: 1
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

In the present work Polystyrene (PS) polymer doped with DCM laser dye thin films have been preparedon glass substrate using casting method. The final samples of PS doped with DCM thin films were treated withdifferent annealing temperatures at (30, 40, 50, 60) oC. Optical absorption and transmission spectra of the preparedthin films were recorded using UV-VIS double beam spectrometer in the wavelength range from 190 to 1100 nm.The results shown that the allowed direct electronic transitions energy gap increased from 2.08 up to 2.25e.V as thetemperature increasing from 30 to 60oC, whereas the allowed indirect electronic transition energy gap increase from2.02 up to 2.17 eV as the temperature increase from 30 to 60oC. The effect of temperature on the optical propertiessuch as Urbach’s energy, Refractive index, Extinction coefficient, Critical angle, Brewster angle, and Finessecoefficient of PS doped with DCM thin films also studied in this work.

Keywords

Optical properties --- PS --- DCM --- thin films --- cast method

Listing 1 - 10 of 36 << page
of 4
>>
Sort by
Narrow your search

Resource type

article (36)


Language

English (31)

Arabic (2)

Arabic and English (1)


Year
From To Submit

2018 (36)