Design and Manufactur of Solar Cell from ITO/ ZnO/ CdS/ CdTe by Thermal Vaporization Technique and Studying the Physical Properties
تصميم وتصنيع خلية شمسية من ITO/ ZnO/ CdS/ CdTe بتقنية التبخير الحراري ودراسة الخواص الفيزيائية

Loading...
Loading...
Abstract

In this research, (ITO, ZnO, CdS and CdTe) films had been prepared by thermal vaporization, where the films deposited on glass slides separately at (1350 °C) (XRD, AFM and UV) tests were done on the samples, and found that all films were multiple crystallization. And the ITO film was cubic structure at the favorite granular growth orientation (222). The results of X-Ray Diffraction showed that the film of Zinc Oxide was hexagonal structure at the favorite granular growth orientation (200). Also, the results showed that the CdS film was hexagonal structure at the favorite granular growth orientation (002). And the results showed that CdTe film was cubic structure at the favorite granular growth orientation (111). The results of Atomic Force Microscope (AFM).Were studied Also the absorption and transmittance spectra for all prepared films in wave length (

تم في هذا البحث تحضير اغشية (ITO, ZnO, CdS, CdTe) بطريقة التبخير الحراري في الفراغ حيث رسبت الاغشية على شرائح زجاجية كل على حده وقد تم اجراء فحوصات (XRD, AFM, UV-Vis) على العينات ووجد ان جميع الاغشية متعدد التبلور وان غشاء (ITO) ذو تركيب مكعبي عند اتجاه النمو الحبيبي المفضل (222) , كما اظهرت نتائج حيود الاشعة السينية ان غشاء اوكسيد الخارصين (ZnO) ذو تركيب سداسيا عند اتجاه النمو الحبيبي المفضل (200). اظهرت النتائج ايضا ان غشاء كبريتيد الكادميوم (CdS) ذو تركيب سداسي عند اتجاه النمو الحبيبي المفضل(002) , واظهرت النتائج ان غشاء تلوريد الكادميوم (CdTe) ذو تركيب مكعبي عند اتجاه النمو الحبيبي المفضل (111). وتم دراسة نتائج مجهر القوة الذرية Atomic Force Microscop(AFM) كذلك تم قياس اطياف الامتصاص والنفاذ لجميع الاغشية المحضرة كدالة للطول الموجي (λ) ضمن المدى (1100 – 300) نانومتر. وقد حسبت فجوة الطاقة البصرية (Eg) عن طريق طيف الامتصاص وكانت قيمتها لغشاء Indiume Tin Oxide(ITO) (3.50) الكترون- فولت ولغشاء اوكسيد الخارصين (ZnO) (3.70) الكترون- فولت ولغشاء كبريتيد الكادميوم (CdS) (2.40) الكترون– فولت والغشاء تلوريد الكادميوم(1.40) (CdTe) الكترون – فولت وتم كذلك ايجاد النفاذية(T) ومعامل الانكسار (n) للأغشية المرسبة.


Article
The Effect of Thickness and Annealing on Structural and Optical Properties of ZnO: Al Thin Films
تأثير السمك والتلدين على الخصائص التركيبية والبصرية لأغشية ZnO : Al

Author: Maysam Sh. Ahmed ميسم شهاب احمد
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2018 Volume: 27 Issue: 2A Pages: 108-124
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

ZnO: Al transparent conductive thin films was prepared by home-made chemical vapor deposition system at (500oC). Zinc acetate dehydrate precursor was used to obtain ZnO films and aluminum nitrate nonahydrate as a dopant source to prepare different thickness (0.539µm, 0.369µm, 0.227µm, 0.057µm) of ZnO: Al thin films. In this study the structural and optical properties of thin films were investigated. X-ray measurements revealed that films structure was polycrystalline of hexagonal quartzite type with preferential orientation along (002) direction. The surface morphology of the films was determined by atomic force microscope (AFM) and the measurements indicate an increase in the smoothness of the upper surfaces after annealing (2.93 nm-1.6nm), and the grain sizes of the sample was in the Nano metric scale. The effect of thickness and annealing time on optical properties of the films were investigated. From the measurements, it was found that the transmittance decrease with increasing thickness. On the other hand, the transmittance and the optical gap increase with increasing the annealing time for low thicknesses, while for the higher thicknesses, a little changes were observed

حضرت أغشية الاكاسيد الموصلة الشفافة (ZnO) المطعمة بالألمنيوم (Al) عند درجة حرارة (500 oC) بــاستخدام منظــومة الترسيب البخاري الكيميائـــي عنـد الضغط الجوي الاعتيادي (APCVD)، تــم استعمال مادة خـلات الخارصين المائية كمـادة أساس ونترات الالمنيوم المائية كمــادة تطعيم لتحضير أغشية (ZnO:Al) ولأسماك مختلفــة 0.539µm, 0.369µm, 0.227µm, 0.057µm))، تم دراسة الخصائص التركيبية والبصرية لهذه الأغشية. أظهرت قياسات الأشعة السينية ( XRD ) ان تركيب ZnO:Al متعدد التبلور ومن النوع السداسي وذو اتجاه مفضل للنمو (002). درست طوبوغرافية سطوح الأغشية المحضرة باستخدام مجهر القوة الذرية (AFM) وأظهرت نتائج الفحـص تناقصاً في خشـونة سطح الغشاء بعد التلدين من (2.93 nm-1.6nm) لنفس السمك وكذلك تناقصاً في الحجم الحبيبي ضمن المدى النانومتري. وتمت دراسة تأثير السمك والتلدين عند أزمان مختلفة على الخصائص البصرية. بينت نتائج القياسات البصرية إن النفاذية تقل بزيادة سمك الغشاء وتزداد بزيادة زمن التلدين عند الأسماك القليلة بينما عند الأسماك الأكبر يكون تأثيرها قليلاً. اما بالنسبة الى فجوة الطاقة البصرية فكذلك تزداد بزيادة زمن التلدين.