research centers


Search results: Found 2

Listing 1 - 2 of 2
Sort by

Article
Treatment of Wastewater Associated With Crude Oil in Reservoirs
معالجة المياه المصاحبة للنفط الخام في الخزانات النفطية

Authors: Dr. Thamer J. Mohammed د. ثامر جاسم محمد --- Jasim M. Jasim جاسم محمد جاسم
Journal: Journal of Petroleum Research & Studies مجلة البحوث والدراسات النفطية ISSN: 22205381 Year: 2019 Issue: 23 Pages: E64-E85
Publisher: Ministry of Oil وزارة النفط

Loading...
Loading...
Abstract

The produced water or wastewater resulting from the oil reservoirs in Basrah Petroleum Company / Zubair 1 Warehouse causes very high pollution in the land. The aim of this study is to find possible ways to treat such produced water and to remove turbidity through coagulation, flocculation, sedimentation and adsorption. Experimental tests of the properties for natural produced water such as turbidity, pH, TDS, TSS, and oil content found out that oil content = 137 mg/L and turbidity = 122 NTU. The produced water is treated with two types of coagulant poly aluminum chloride, alum and with two other types of adsorbent (Bentonite, Zeolite (Cation and Anion)). The coagulation, flocculation and sedimentation experiments are performed using a Jar-test device and adsorption experiments , and a magnetic stirrer device are used at different times, speeds, and concentrations. It is found through the practical results that the best dosages of (poly aluminum chloride and alum) are (3, 35, 6.75, and 30) mg/L to obtain R% (96.3, 93, 99, and 98.9), respectively. It is found from the experimental results of adsorption that the best results of weight adsorbent, stirrer time and stirrer speed to obtain maximum removal efficiency are (6 gram anion zeolite ,15 minute and 920 rpm) R% (98 , 97.8 and 99.2), respectively .It is found that the best results are poor at different parameters, except when it is used (2) gram of bentonite obtained R% of turbidity weight, stirrer time and stirrer speed by bentonite and zeolite (cation and anion) were (2 gram) . Finally, it was found that removing the oil content by adsorption (97.8) is better than coagulation (96.3). And the results for removing turbidity by coagulation (99) is better than adsorption (97.4) .

تسبب المياه المنتجة او المياه العادمة الناتجة من الخزانات النفطية في شركة نفط البصرة / مستودع زبير1 نسبة عالية من التلوث في الأراضي الزراعية. تهدف هذه الدراسة الى ايجاد طرق ممكنة لمعالجة هذه المياه المنتجة وازالة التعكر من خلال التخثر - التلبد - الترسيب والامتزاز. لقد أثبتت الاختبارات التجريبية لخصائص المياه المنتجة الطبيعية من الموقع مثل التعكر، ودرجة الحموضة ، و TDS، و TSS، ومحتوى الزيت.حيث يبلغ محتوى الزيت (137 ملغم / لتر) والتعكر (122 وحدةNTU)، وتتم معالجة المياه المنتجة بنوعين من المخثرات (بولي المنيوم كلورايد والشب) مع نوعين اخرين من الممتزات هي (البنتونايت، الزيولايت (الموجبة والسالبة)). وقد أجريت تجارب التخثير- التلبيد والترسيب لـ (بولي المنيوم كلورايد و الشب) من خلال استخدام جهاز الجرة مختبريا وأجريت تجارب الامتزاز لـ (البنتونايت و الزيولايت) من خلال أستخدام جهاز محرك مغناطيسي في أوقات وسرع وتراكيز مختلفة. تبين من النتائج التجريبية باستخدام اختبار الجرة لإزالة محتوى الزيت والتعكر ان الجرعات الافضل لـ (بولي المنيوم كلورايد والشب) هي (3، 35 ، 6.75 و 30) ملغرام/ لتر بنسبة كفاءة إزالة (96.3، 93، 99 و 98.9) على التوالي . ايضا" تبين من النتائج التجريبية للامتزازالذي يستخدم لأزالة المحتوى النفطي ان افضل وزن، زمن التحريك وسرعة التحريك للممتزات هي (6 غرام زيولايت سالب، 15 دقيقة و 920 دورة في الدقيقة) بنسبة كفاءة إزالة (98، 97.8 و 99.2) على التوالي. وجد من النتائج التجريبية لعملية الامتزاز لإزالة التعكر أن أفضل النتائج رديئة في معايير مختلفة، إلا عند استخدامه (2) غرام من البنتونايت الذي تم الحصول عليه R٪ من وزن التعكر وزمن التحريك وسرعة التحريك بواسطة البنتونايت والزيولايت (الموجبة والسالبة) كانت (2 غرام). في النهاية، توضح النتائج العملية للطريقتين المذكورتين أعلاه أن إزالة محتوى الزيت عن طريق الامتزاز ((97.8 أفضل من التخثير (96.3). ونتائج إزالة التعكر بواسطة التخثير(99) أفضل من الامتزاز 97.4)).


Article
Use of Alum and Polyelectrolyte Coagulants in Mixing Water in Concrete Bunkers Building or Construction
إستخدام مخثرات الشب والبولي ألكتروليت في ماء الخلط للخلطات الخرسانية المستخدمة في إنشاء السواتر

Author: Ako Rashed Hama آكو رشيد حمه
Journal: Sulaimania Journal for Engineering Sciences مجلة السليمانية للعلوم الهندسية ISSN: 24101699/24156655 Year: 2019 Volume: 6 Issue: 1 Pages: 11-28
Publisher: university of Sulaimania جامعة السليمانية

Loading...
Loading...
Abstract

This paper examines the possibility of using water treatment plant’s sludge [WTP] in mixing water in preparing high strength concrete bunkers. The two main chemical coagulants used in Dokan WTP 70 km southwest of Sulaimani city in Iraq, are alum and polyelectrolyte and they produce a coagulant’s sludge which settled at the end of sedimentation process on the bottom of the clarifier tanks. In this study, the two chemical coagulants alum and polyelectrolyte used as a concrete additives. Samples of the raw water taken from the inlets and have been tested continuously for a time period of 12 months during summer and winter seasons especially at the beginning of the stratification periods of Dokan Lake (source of the treatment plant). The tests included jar tests and turbidity of the samples, then determining the optimum quantity of each of alum and polyelectrolytes. So the maximum amount of the alum was 15mg/L while for polyelectrolyte was 10mg/L. Those two maximum high values of rates of alum and polyelectrolytes and their hybrid mixing rates have been used in preparation 7 concrete prototype bunkers with dimensions of 80cm x 80cm x 15cm with an admixture rates of 15mg/L alum, 15mg/L polyelectrolyte, 10mg/L alum, 10mg/L polyelectrolyte , 10mg/L alum with 5 mg/L polyelectrolyte, 5 mg/L alum with 5 mg/L polyelectrolyte and zero mg/L for both of them (blank). Two different types of tests have been performed for the prepared concrete bunkers; the in-lab compression tests for the cube samples of the prototypes concrete and the outdoor field shouting test for the prepared concrete bunker prototypes using 12.7 mm gun fire bullets and a shooting 100m from the target. Concrete compression laboratory tests have been conducted for 7,21and 28days aged concrete prototype bunkers while the depth, length and the diameter of the cracks and punching of the bullet hitting locations on the targeted prototype concrete bunker were measured. The results of this research reveals that adding alum along either in 15mg/l or 10 mg/ l doses in the three aged concrete 7,21,and 28 days will affect inversly on the concrete compaction strength by a (1 – 8)% while adding the other mensioned doses (polyelectrolyte along with different doses 10mg/l or 15 mg/l and a hybird doses of alum 10mg/l mixed with polyelectrolite 10mg/l ,will help in increasing the concrete compression strength of the concrete by 3.5% to 12%. Through out the tests its clearly appeared that the optimum coagulant in increasing the capacity of the concrete is polyelectrolyte and with a dosage of 15mg/l and it helps to increase the capacity of the concrete to 9% at 7days , 11.5 % at 21days and 13% at 28days from the age of the concrete .The results showed that the penetration depth for all the seven concrete bunker prototypes, evaluates each prototype performance via their penetration depths, because the penetration depth of the bullet is the most important variable in selecting the best performance concrete bunker prototype among all of them. The results also showed that the minimum penetration was 1.7 cm of polyelectrolyte used coagulant prototype of 15mg/L, and the maximum ratio about 2.2cm for the concrete banker prototype containing 15 mg/L of polyelectrolyte coagulant in mixing water of the concrete mixture used in it. Also the smallest diameter as a result of shooting test was 10 cm for this prototype while the largest diameter was 20 cm for the bunker prototype containing 10 mg/L of polyelectrolyte coagulant in mixing water of the mixture used in it.

تم في هذه الدراسة إستخدام المياه الغنية بمادتي الشب والبولي ألكتروليت اللتين هما من اكثر المخثرات شائعة الإستخدام في محطات التصفية كمحطة دوكان لتصفة مياه الإسالة والواقعة جنوب شرق مدينة السليمانية اذ تم إستخدامها كماء خلط في الخلطات الخرسانية عالية المقاومة والمستخدمة في إنشاء السواتر الخرسانية اذ تم إستخدام جرعات مختلفة من الشب والبولي ألكتروليت بالإعتماد على القيم القصوى للإستهلاك في المحطة خلال فترة زمنية مقدارها سنة اذ بلغت 15 ملغ/ لتر من الشب و 10 ملغ/لتر من البولي ألكتروليت. تم إنشاء سبعة نماذج من السواتر الخرسانية بأبعاد 80 سم x80 سم x 15 سم. كانت نسب الاضافة للمواد المخثرة الكيميائية الى ماء الخلط 10 و 15 ملغ/ لتر من شب لوحدهما ، 10 و 15 ملغ/لتر من البولي ألكتروليت لوحدهما ، و 10 ملغ/لتر من شب مع 5 ملغ/لتر من البولي ألكتروليت معا ، 5 ملغ/لتر من الشب مع 5 ملغ/لتر من البولي ألكتروليت معا وكما تم مقارنة الخلطات الحاوية على هذه النماذج من ماء الخلط مع خلطة مرجعية ذات ماء خلط إعتيادي ) غير حاوي على الشب او البولي اليكتوليت( . استخدم نوعان من الفحوصات لغرض معرفة مدى تأثر مقاومة الخرسانة عند إضافة تلك المواد وهما فحص مقاومة الإنضغاط للمكعبات والفحص الموقعي بإستخدام الرمي من رشاش آلي ذو ذخيرة حية بعيار 12.7 ملم من موقع ثابت وعن مسافة ثابتة تبلغ 100 م. بينت النتائج بان إستخدام الشب في ماء الخلط تقلل من مقاومة الخرسانة للانضغاط بنسبة تراوحت من 1 ٪ الى 8 ٪ في المقابل لوحظ ان إستخدام البولي اليكتوليت بشكل منفرد في ماء الخلط او بشكل مركب مع الشب ادى الى زيادة مقاومة الإنضغاظ بنسبة تراوحت من ) 3.5 الى 13 ٪) اذ عند إضافة 15 ملغ/لتر من البولي اليكتروليت الى ماء الخلط , لوحظ بان نسبة الزيادة في مقاومة الإنضغلط بلغت ) 13 ، 11.5 و 9(٪ عند الأعمار ) 7 ، 21 و 28 ( يوما على التوالي كما أن نسب الزيادة هذه تمثل النسب الأعلى مقارنة بالبقية الخلطات.أظهرت نتائج ألرمي الحقلي على نماذج السواتر والتي تعتبر دليل آخر لمعرفة مدى تأثر النماذج بالمواد المخثرة الكيميائية المضافة كانت أقل قيمة مقاسة لعمق إختراق الذخيرة في النماذج الخرسانية بلغت 1.7 سم للنموذج التي يحتوي على 15 ملغ/لتر من البولي اليكترويت أما أعلى قيمة للعمق كانت 2.2 سم. كما ان أكبر قطر متأثر بالذخيرة كان 18 سم للنموذج الذي يحتوي على 15 ملغ/لتر من البولي أليكتروليت أما أضغرها فقد بلغ 10 سم عند النموذج الذي يحتوى على 15 ملغ/لتر من مادة الشب. بذلك يمكن القول بأن المواد المخثرة الكيمياوية تزيد من مقاومة الإنضغاط للخرسانة المستخدمة في السواتر الخرسانية.

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

English (2)


Year
From To Submit

2019 (2)