Synthesized pure cobalt oxide nanostructure and doped with yttrium by hydrothermal method for photodetector applications
تحضير اوكسيد الكوبلت النانوية والمطعمة بالايتريوم المحضرة بطريقة الهيدروثرميل لتطبيقات الكاشف الضوئي

Authors: Suhad A. Hamdan سهاد عبد الكريم حمدان --- Iftikhar M. Ali افتخار محمود علي
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 40 Pages: 77-87
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, pure Co3O4 nano structure and doping with 4 %, and 6 % of Yttrium is successfully synthesized by hydrothermal method. The XRD examination, optical, electrical and photo sensing properties have been studied for pure and doped Co3O4 thin films. The X-ray diffraction (XRD) analysis shows that all films are polycrystalline in nature, having cubic structure. The optical properties indication that the optical energy gap follows allowed direct electronic transition calculated using Tauc equation and it increases for doped Co3O4. The photo sensing properties of thin films are studied as a function of time at different wavelengths to find the sensitivity for these lights. High photo sensitivity doped Co3O4 with 6% of Yttrium, is a 118.774% at wavelength 620 nm, while for pure Co3O4 films no sensitivity at the same wavelength. So, higher sensitivity is found for doping Co3O4 with fast rise and fall times less than 1s.

في هذا العمل تم تحضير Co3O4 النانوية التركيب النقية والمطعمة ب 4٪ و 6 ٪ يتتريوم بنجاح بطريقة الهيدروثرمل. تحليل الاشعة السينية والخصائص البصرية والخصائص الكهربائية وخصائص استشعار الضوء درست للاغشية المحضرة من Co3O4 النقي والمطعم بالايتريوم. اظهر تحليل الاشعة السينية كل الاغشية المحضرة متعددة التبلور في طبيعتها وتمتلك تركيب مكعب. تبين الخواص البصرية أن فجوة الطاقة الضوئية تتبع الانتقال الإلكتروني المباشر المحسوب باستخدام معادلة تاوس وتزداد مع تطعيم Co3O4. خصائص تحسسية الضوء للاغشية تم تحقق منها كدالة للزمن عند اطوال موجية مختلفة لايجاد التحسسية لهذه الاضواء.حساسية عالية للضوء عند تطعيم Co3O4 مع 6 ٪ من الإيتريوم، هي 118.774 ٪ عند الطول الموجي 620 نانومتر، في حين أنه لا توجد حساسية لافلام Co3O4 النقية عند نفس الطول الموجي. لذلك، يتم الحصول على حساسية أعلى لـ Co3O4 المطعم مع أوقات الصعود والهبوط السريع أقل من 1 ثانية.


Article
Enhancement of Hydrothermally Co3O4 Thin Films as H2S Gas Sensor by Loading Yttrium Element
تحسين اغشية رقيقة Co3O4 مائيا حراريا كمتحسس لغاز H2S عن طريق تحميل عنصر الإيتريوم

Authors: Suhad A. Hamdan سهاد عبد الكريم حمدان --- Iftikhar M. Ali افتخار محمود علي
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2019 Volume: 16 Issue: 1 Supplement Pages: 221-229
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The gas sensing properties of Co3O4 and Co3O4:Y nano structures were investigated. The films were synthesized using the hydrothermal method on a seeded layer. The XRD, SEM analysis and gas sensing properties were investigated for Co3O4 and Co3O4:Y thin films. XRD analysis shows that all films are polycrystalline in nature, having a cubic structure, and the crystallite size is (11.7)nm for cobalt oxide and (9.3)nm for the Co3O4:10%Y. The SEM analysis of thin films obviously indicates that Co3O4 possesses a nanosphere-like structure and a flower-like structure for Co3O4:Y.The sensitivity, response time and recovery time to a H2S reducing gas were tested at different operating temperatures. The resistance changes with exposure to the test gas. The results reveal that the Co3O4:10%Y possesses the highest sensitivity around 80% at a 100oC operating temperature when exposed to the reducing gas H2S with 0.8sec for both recovery and response times.

تمت دراسة الخصائص التحسسية للاغشية Co3O4 و Co3O4: Y النانوية . تم تحضير هذه الاغشية بطريقة مائية حرارية على طبقة البذرة. تم فحص الاشعة السينية XRD ومجهر المسح الالكتروني SEM وخصائص تحسسية الغاز درست للاغشية Co3O4 و Co3O4: Y النانوية. فحصXRD يظهر كل الافلام متعددة التبلور و تمتلك تركيب مكعب ومعدل الحجم البلوري لاوكسيد الكوبلت النقي 11.7 نانومتر ولاوكسيد الكوبلت المطعم Co3O4:10%Y 9.3 نانومتر. تحليل المجهر الالكتروني الماسح SEM تشير بوضوح الى Co3O4 تمتلك تركيب كروي و Co3O4: Y تمتلك تركيب نانوي يشبه الزهرة. تم اختبار التحسسية وزمن الاستجابة وزمن الاسترجاع للغاز المختزل H2S في درجات حرارة تشغيل مختلفة. المقاومة تتغير نتيجة التعرض الى غاز الاختبار. النتائج اظهرت Co3O4:10%Y تمتلك اعلى تحسسية حوالي 80% في درجة حرارة تشغيل 100درجة مئوية عند التعرض للغاز المختزل H2S وزمن استجابة واسترجاع 0.8 ثانية.


Article
Isotherm and pH Effect Studies of Tetracycline Drug Removal from Aqueous Solution Using Cobalt Oxide Surface

Authors: Asmaa A. Maryoosh --- Marwa A. Abed --- Dhifaf A. Abdul abass --- Ali Amer Waheb --- et al.
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2019 Volume: 22 Issue: 2 Pages: 12-18
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Tetracycline adsorption on the surface of cobalt oxide studied in this work to determine the appropriate conditions for increasing the efficiency of adsorption by changing the temperature, adsorbed dosages, concentration, contact time and pH. The results showed that the rate of adsorption decreased by increasing the temperature and concentration and at 45 minutes with 0.1 gm of Co3O4. The influence of pH on adsorption at pH (1.2, 6, 8) was studied and concentration with a linear range of (20-70 mg/l), the adsorption ratio decreased by increasing the concentration at the same pH. The point of zero charges pHzc calculated and found to be equal to 7.2. Both Langmuir and Freundlich isotherm studied. The result showed a good agreement with Freundlich linear model.