Novel Co-Precipitation Method for Synthesis of Nanostructured Nickel Oxide in Accordance to PH: Structural and Optical Properties as an Active Optical Filter

Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: P16094042/ E25213407 Year: 2019 Volume: 32 Issue: 1 Pages: 1-6
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Low cost Co-Precipitation method was used for Preparation of novel nickel oxide (NiO)nano particle thin films with Simple, with two different PH values 6, 12 and its effect onstructural and optical properties as an active optical filter. Experimental results of structuralproperties X-ray diffraction (XRD) showed that both Nickel oxide nanoparticles with (PH=6and 12) have polycrystalline structure smaller average particle size about 8.5 nm for PH = 6 incomparison with PH = 12. Morphological studies using Scanning electron microscopy (SEM)and atomic force microscope (AFM) show uniform nano rod distribution for PH=6 withsmaller average diameter, average roughness as compared with NiO with PH=12 that showedlarger diameter, grain size, spherical shape with scope of excellent sensing applications due tohigh roughness. Optical properties results show blue shift for PH = 6 as compared withPH=12m leading to potential of optoelectronic applications and as active optical


Article
X-band Region Characterization of Neoprene Rubber Reinforced Cd-Zn Ferrite Composite Material
توصيف حزمة (X) لمطاط النيوبرين المدعم بمواد متراكبة من كادميوم- زنك فرايت

Authors: FirasA’aidNajim فراس عائد نجم --- Wissam Adel Hussien وسام عادل حسين
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2019 Volume: 11 Issue: 01 Pages: 120-127
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The compound was prepared from (ZnFe2O4) and (CdFe2O4)The process of mixing the ferrite compounds was done according to the formula (CdxZn1-xFe2O4),The resulted compound was (Cd0.7Zn0.3 Fe2O4). The compounds (ZnFe2O4) and (CdFe2O4) were prepared by Co-Precipitation method because this method gives a good homogeneity to the powder particles. XRD and FE-SEM were performed, the results showed that ferrites had a phase-shaped cube and an increase in the concentration of cadmium in the (CdxZn1-x Fe2O4)compound .This result showed an increase in the lattice constant, the rate of crystalline size and the distance between the crystalline surfaces,due to the fact that the ionic radius of the cadmium is greater than the ionic diameter of the zinc, which is (0.83 A°).The images of the electron microscope (FE-SEM) showed an increase in particle size with an increase of concentration of cadmium ferrite in relation to the compound (CdxZn1-x Fe2O4),The components of the ferrite structures prepared by EDS technique were verified, where the ferritecompound (Cd0.7Zn0.3Fe2O4) mixed with the Neoprene (Chloroprene Rubber) (CR) according to weight ratio of (3,6g)of ferrite, after the process of forming rubber paste. The VNA was investigated for (8-12 GHz). It was observed that the reflection coefficient was reduced by increasing the fraction of ferrite to (6g) and obtain highly absorbent materials .Where the material behavior varies according to the frequency, as well as the concentration ratio in the ferrite and the quantity of the ferrite with Chloroprene rubber (CR).ThePermeability of (Cd0.7Zn0.3Fe2O4) was calculated as a function of frequency.The real part of the amplitude showed the amount of energy from the external electric field stored in the material.

تم تحضير الفرايت ذو التركيب (Zn Fe2O4) و(Cd Fe2O4) ومن ثم تمت عملية خلط المركبات الفرايت حسب الصيغة (CdxZn1-xFe2O4) والحصول على المركب (Cd0.7Zn0.3Fe2O4) حيث تم تحضير المركبات الفرايتية (Zn Fe2O4)و(Cd Fe2O4) بطريقة ( Co-Precipitation Method ) لأنها تعطي تجانسا لجزيئات المسحوق. تم دراسة الخواص التركيبية للنماذج المحظرة حيث أظهرت النتائج ان الفرايت من نوع (الطري ) وان زيادة تركيز الكادميوم في المركب (CdxZn1-x Fe2O4) أدى الى زيادة كل من ثابت الشبيكة و معدل الحجمالبلوري والمسافة بين السطوح البلورية كلما ازداد فرايت الكادميوم ويرجع سبب ذلك لان نصف القطر الايوني للكادميوم اكبر من نصف القطر الايوني للخارصين الذي يبلغ (A°0.83) واظهرت صور المجهر الالكتروني ( FE-SEM) تزايد حجم الجسيمات مع زيادة تركيز فرايت الكادميوم بلنسبة للمركب (CdxZn1-x Fe2O4) وتم التحقق من العناصر المكونة للتراكيب الفرايتية المحضرة بواسطة تقنية (EDS) تمت عملية مزج المركب (Cd0.7Zn0.3Fe2O4) مع (GRT) (Neoprene Chloroprene Rubber) بإضافة (3,6) غم من الفرايت ,بعد عملية تكوين العجينة المطاط تم اجراء فحص( VNA ) للعينات ضمن حزمة X من الموجات الميكروية (8-12) GHz . لوحظ أن معامل الانعكاس قد انخفض عن طريق زيادة جزء الفريت إلى (g 6) والحصول على مواد شديدة الامتصاص .حيث يختلف سلوك المادة باختلاف التردد ، وكذلك نسبة التركيز في الفريت وكمية الفريت مع المطاط النيوبرين (CR). حيث تم احتساب نفاذية للمركب (Cd0.7Zn0.3Fe2O4) كدالة للتردد. تم حساب الجزء الحقيقي والجزء الخيالي من ثابت العزل كدالة للتردد في النطاق X . أظهر الجزء الحقيقي من السعة مقدار الطاقة من الحقل الكهربائي الخارجي المخزن في المادة.