Article
Structural and optical properties of Fe- doped ZnO thin films prepared by Sol–Gel spin coating process and their photocatalytic activities
دراسة الخصائص التركيبية والبصرية للأغشية الرقيقة النانوية ZnO المشوبة بالحديد المحضرة بواسطة طريقة محلول-جيلاتين وانشطتها بالتحفيز الضوئي

Loading...
Loading...
Abstract

Pure and Fe-doped zinc oxide nanocrystalline films were prepared via a sol–gel method using spin coating process. Pure and Fe-doped zinc oxide, containing 2 to 8 % Fe, were annealed at 500 ̊C for 2 h. The thin films were prepared and characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), field emission scanning electron microscopy (FE-SEM) and UV- visible spectroscopy. The XRD results showed that ZnO has hexagonal wurtzite structure and the Fe ions were well incorporated into the ZnO structure. As the Fe level increased from 2 wt% to 8 wt%, the crystallite size reduced in comparison with the pure ZnO. The transmittance spectra were then recorded at wavelengths ranging from 300 nm to 1000 nm. The optical band gap energy of spin-coated films also decreased as Fe doping concentration increased. In particular, their optical band gap energies were 3.75, 3.6, 3.5, 3.45 and 3.3 eV doping concentration of 0%, 2%, 4%, 6% and 8% Fe, respectively. The performance of the pure and doped ZnO thin films was examined for the photocatalytic activity using organic dyes (methyl orange, methyl blue, methyl violet). The samples ZnO with concentration of Fe showed increased photocatalytic activity with an optimal maximum performance at 0.8 wt%.

تم تحضير اغشية رقيقة لأوكسيد الزنك النقي و المشوبة بالحديد بواسطة طريقة محلول-جيلاتين. تم تلدين اغشية أوكسيد الزنك النقي و المشوبة التي تحتوي على 2 الى 8٪ من الحديد في درجة حرارة 500 درجة مئوية لمدة ساعتين. تم دراسة جميع الاغشية المحضرة باستخدام جهاز حيود الأشعة السينية (XRD)، مجهر القوة الذرية (AFM)، مجال الماسح الضوئي المجهر الإلكتروني (FESEM) ومطياف الطيف المرئي-الأشعة فوق البنفسجية. اظهرت نتائج حيود الاشعة السينية أن أغشية اوكسيد الزنك النقية والمشوبة له هيكل wurtzite سداسي وقد تم دمج أيونات الحديد بشكل جيد في بنية ZnO . وتبين كذلك ان الحجم البلوري يقل بزيادة تركيز الاشابة بالحديد من 2 ٪ إلى 8 ٪wt ، انخفض حجم البللورات مقارنةً بـ ZnO النقي. ثم تم تسجيل أطياف النفاذية عند أطوال موجية تتراوح بين 300 نانومتر إلى 1000 نانومتر. قد اظهرت نتائج قياس فجوة الطاقة البصرية انها تقل بزيادة تركيز الاشابة بالحديد حيث تراوحت قيم فجوة الطاقة 3.75 و 3.6 و 3.5 و 3.45 و 3.3 الكترون-فولت عند تركيز الاشابة 0٪ و 2٪ و 4٪ و 6٪ و 8٪ على التوالي. تم فحص أداء الأغشية الرقيقة ZnO النقية والمشوبة للنشاط التحفيزي باستخدام الصبغات العضوية (برتقالي الميثيل، ميثيل الأزرق، ميثيل البنفسج). وأظهرت عينات ZnO مع تركيز Fe زيادة النشاط التحفيزي مع أقصى قدر من الأداء الأمثل في 0.8wt ٪.


Article
Structural and Gas Sensing Characteristics of CuO-Doped ZnO Thin Films Papered by Pulsed-Laser Deposition

Authors: Mohammed A. Annaz --- Mazin H. Hasan
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2019 Volume: 15 Issue: 4 Pages: 3-9
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

In this work, pulsed-laser deposition was used to prepare zinc oxide (ZnO) thin films on glass and porous silicon substrates. These films were doped with different contents of copper oxide (CuO). The x-ray diffraction patterns showed peaks belonging to hexagonal ZnO structure only for the samples with CuO contents of 10, 30 and 50%, while the peaks belonging to cubic CuO structure were observed in the samples with partial CuO contents of 70 and 90%. As the CuO content was increased, the average roughness of the prepared surfaces was accordingly increased. The electrical measurements showed that all prepared samples were of n-type conductivity and the charge carrier concentration was decreasing with increasing partial content of CuO. The CuO-doped ZnO films deposited on porous silicon substrates were tested as gas sensors. The maximum sensitivity of 49% for NO2 gas was recorded at constant current of 15 mA and exposure time of 30 min for the sample of 10% CuO content at operation temperature of 200 °C.


Article
Gas Sensing of (SnO2)1-x(ZnO)x composite films associating with structural and electrical properties
التحسس الغازي لأغشية مركب (SnO2)1-x(ZnO)x مع الخصائص التركيبية والكهربائية

Loading...
Loading...
Abstract

Semiconductor-based gas sensors were prepared, using n-type tin oxide (SnO2) and tin oxide: zinc oxide composite [(SnO2)1-x(ZnO)x] at different atomic ratios (x) using pulsed laser deposition at room temperature, without any treatment. The prepared thin films were examined in order to obtain the optimum conditions for gas sensing applications, using X-ray diffraction, Hall effect measurements, and direct current conductivity. It was found that the optimum crystallinity and maximum electron density, corresponding to the minimum charge carrier mobility, appeared at 10% ZnO ratio. This sample has the optimum gas sensitivity was 358 % against 10% NO2 gas appeared at 473 K working temperature.

تم تحضير المتحسس الغازي المعتمد على شبه الموصل، باستخدام أوكسيد القصدير((SnO2 من النوع n و مزيج أوكسيد القصدير: أوكسيد الزنك (SnO2)1-x(ZnO)x عند نسب ذريةx مختلف باستخدام الترسيب بالليزر النبضي في درجة حرارة الغرفة، بدون اي معالجة. فحصت الأغشية الرقيقة المحضرة للوصول الى الظروف المثلى لتطبيقات المتحسس الغازي، باستخدام حيود الأشعة السينية، وقياسات تأثير هول، وتوصيلية التيار الكهربائي المباشر. وقد وجد أن درجة التبلور المثلى وكثافة الإلكترون القصوى، المقابلة لتحركية حاملات الشحنة الدنيا، تظهر عند النسبة %10 من ZnO. وكانت أعلى حساسية لغاز لثاني أوكسيد النيتروجين هي %358 عند تركيز 10% وعند درجة حرارة تشغيل473 كلفن.


Article
Effect of some nanoparticles on the stages biology of the southern cowpea beetle Callosobruchus maculatus (Fab.) (Coleoptera:Bruchidae)
تأثير بعض المواد النانوية في حيوية أطوار خنفساء اللوبيا الجنوبية Callosobruchus maculatus (Fab.) (Coleoptera:Bruchidae)

Authors: Adnan Mosa Mohammed --- Sarah Amer Aswd
Journal: JOURNAL OF EDUCATION AND SCIENCE مجلة التربية والعلم ISSN: 1812125X Year: 2019 Volume: 28 Issue: 3 Pages: 188-199
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Nano particle of Zinc oxide size (5nm) and (100nm) and silver nano Particle (100 nm) were used in This study at concentrations (100, 250, 500, 750 and 1000) ppm to know their effect on some biological aspects of the southern cowpea beetle Callosobruchus maculatus (Fab.) through treating the food of these insects (chick pea seeds) by these nanoparticles.The study proved that the above Particles had a significant effect on the parentage of eggs hatching as it reached 49.4% compared to 86.9% of control Also, the some treatment led to high at 1000 ppm concentration mortality percentage 98%. Moreover, the treatment had an effect on the pupa stage and on the period of insect development, which was elongated significantly in the treatments of the zinc oxide size (100 nm). The maximum period was 40.60 days at the concentration of 1000 ppm Which differed significantly from its comparative coefficient. The productivity of insect decreased significantly to 16.6%in zinc oxide nano Particle size (5 nm) clearly. This study showed that the treatments effected the vitality of the first-generation females as the percentage of egg hatching decreased to 50% more than that egg retention was observed on these females which reached to 50% at treatment of zinc oxide size (5 nanometer).


Article
Antimicrobial efficacy of silver, zinc oxide, and titanium dioxide nanoparticles incorporated in orthodontic bonding agent

Authors: Sarah Yousif Hailan --- Mustafa M. Al-Khatieeb
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2019 Volume: 31 Issue: 3 Pages: 10-16
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: One of the most important complications of fixed orthodontic treatment is formation of white spots, which are initial carious lesions. Addition of antimicrobial agents into orthodontic adhesive material might be wise solution for prevention of white spots formation. The aim of this study was to evaluate the antibacterial properties of orthodontic adhesive primer against S. Mutans after adding the three different types of nanoparticles (Ag, ZnO, or TiO2).Materials and methods: Discs were prepared using empty insulin syringe approximately 2 mm×2 mm rounded in shape specimens (40 discs) were divided into four groups (ten discs for each group): The first group was the control (made from primer only), the second group (10 discs made from primer and incorporation of Ag NPs), the third group (10 discs made from primer and incorporation of ZnO NPs), and the fourth group (10 discs made from primer and incorporation of TiO2 NPs). The antibacterial properties of orthodontic bonding agent after incorporation of (Ag, ZnO, or TiO2) nanoparticles were evaluated by disc diffusion test and viable count of mutans streptococci.Results: The results of this study showed that there were high significant differences between the all groups using ANOVA F-test, and the colony forming unit were 99×10³, 39.6×10³, 19.4×10³, 6.6×10³ CFU/mL respectively. Conclusion: The incorporation of these nanoparticles (Ag, ZnO, or TiO2) into Transbond ™ XT adhesive primer helps to enhance the antibacterial properties of primer against the S. mutans.


Article
Spectroscopic studying of plasma parameters for SnO2 doped ZnO prepared by pulse Nd:YAG laser deposition
دراسة طيفية لمعلمات البلازما لأوكسيد الزنك المشوبة بأوكسيد القصدير المحضرة بواسطة الترسيب بالليزرالنبضي Nd:YAG

Authors: Muna A. Essa منى احمد عيسى --- Kadhim A. Aadim كاظم عبد الواحد عادم
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2019 Volume: 17 Issue: 42 Pages: 125-135
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this work, plasma parameters such as (electron temperature (Te), electron density (ne), plasma frequency and Debye length (λD)) were studied by using spectral analysis techniques. The spectrum of the plasma was recorded with different energy values, SnO2 and ZnO anesthetized at a different ratio (X = 0.2, 0.4 and 0.6). Spectral study of this mixing in the air. The results showed electron density and electron temperature increase in zinc oxide: tin oxide alloy targets. It was located that the intensity of the lines increases in different laser peak powers when the laser peak power increases and then decreases when the force continues to increase.

في هذا العمل، تمت دراسة معلمات البلازما مثل (درجة حرارة الإلكترون(Te) ، كثافة الإلكترون(ne) , تردد البلازما وقطر كرة ديباي λD)) (باستخدام تقنيات التحليل للطيف الناتج من البلازما باستخدام مزيج من اوكسيد الزنك المشوب بأوكسيد القصدير وبنسب مختلفة ((X=0.2, 0.4, 0.6. تمت دراسة الطيف الناتج في الهواء. لوحظ من النتائج ان درجة حرارة الالكترون وكثافة الالكترون تزداد في المزيج بين اوكسيد الزنك وأوكسيد القصدير, لوحظ ان خطوط الطيف تزداد بزيادة طاقة الليزر ثم عندما تستمر الطاقة بالازدياد.


Article
Adsorption of Some Alephatic Dicarboxylic Acids on Zinc Oxide: A kinetic and Thermodynamic Study
امتزاز بعض الحوامض الاليفاتية ثنائية الكاربوكسيل على أوكسيد الزنك: دراسة حركية وثرموداينميكية

Author: Saddam. M. Al-Mahmoud صدام محمد المحمود
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2019 Volume: 16 Issue: 4 Pages: 892-897
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The adsorption of Malonic acid, Succinic acid, Adipic acid, and Azelaic acid from their aqueous solutions on zinc oxide surface were investigated. The adsorption efficiency was investigated using various factors such as adsorbent amount, contact time, initial concentration, and temperature. Optimum conditions for acids removal from its aqueous solutions were found to be adsorbent dose (0.2 g), equilibrium contact time (40 minutes), initial acids concentration (0.005 M). Variation of temperature as a function of adsorption efficiency showed that increasing the temperature would result in decreasing the adsorption ability. Kinetic modeling by applying the pseudo-second order model can provide a better fit of the data with a greater correlation coefficient, which indicates that the adsorption process follow the pseudo-second order kinetics. The negative values of Gibbs free energy and the enthalpy change confirm the spontaneous and exothermic nature of the adsorption process. A good ability of zinc oxide to remove aliphatic dicarboxylic acids from its aqueous solutions has been found, and the chain length of the acids has no significant effect on its adsorption.

الهدف من اجراء هذا البحث هو لدراسة ميكانيكية امتزاز حامض المالونيك، حامض السكسنيك، حامض الاديبيك، وحامض الازيلايك من محاليلها المائية على سطح أوكسيد الزنك. حيث تم دراسة كفاءة الامتزاز بالاستعانة بعدة عوامل مختلفة مثل كمية المادة المازة، زمن التماس، التركيز الابتدائي، ودرجة الحرارة. اظهرت النتائج ان الظروف المثلى اللازمة لإزالة الحوامض من محاليلها المائية هي كمية المادة المازة 0.2 غرام، وأفضل زمن للاتزان هو 40 دقيقة، والتركيز الابتدائي للحوامض كان 0.005 مولاري. كما أظهرت الدراسة ان زيادة درجة الحرارة تقلل من كفاءة الامتزاز. ومن خلال تطبيق النماذج الحركية على عملية الامتزاز وجد ان نموذج الرتبة الثانية الكاذبة يعطي علاقة خطية مع معامل ارتباط جيد. كما اشتملت الدراسة على حساب الدوال الثرموداينميكية، حيث أظهرت النتائج ان القيمة السالبة للطاقة الحرة لجبس والتغير في الانثالبي تؤكدان التلقائية والطبيعة الباعثة للحرارة لعملية الامتزاز. لقد وجد ان لاوكسيد الزنك قابلية جيدة على إزالة الحوامض الاليفاتية ثنائية الكاربوكسيل من محاليلها المائية، وان طول السلسلة للحوامض ليس له أي تأثير على امتزازها.


Article
Preparation and Study the Effect of Nano Zinc Oxide Particles Upon Some Mechanical and Thermal Properties of Epoxy Resin
تحضير ودراسة تأثير دقائق أوكسيد الزنك النانوية على بعض الخواص الميكانيكية والحرارية لراتنج الايبوكسي

Author: Kadhim N. Abed كاظم نوري عبد
Journal: kirkuk university journal for scientific studies مجلة جامعة كركوك - الدراسات العلمية ISSN: 19920849 / 26166801 Year: 2019 Volume: 14 Issue: 4 Pages: 109-130
Publisher: Kirkuk University جامعة كركوك

Loading...
Loading...
Abstract

Nanoparticles of zinc oxide are prepared by three different chemical methods. The first one includes mixing of zinc nitrate (hexa – H2O) with solution of sodium hydroxide (0.4N) at a ratio of (2:1) (sampleN1). In the second method, ammonium bicarbonate solution mixed with zinc sulfate (0.2M) at a ratio of (1:2) (sampleN2). The third method includes mixing of zinc nitrate (hexa – H2O) with sodium hydroxide (0.6N) at a ratio of (2:1) (sampleN3), were solution of starch added as fixing agent for nanoparticles. The nanoparticles examined by X– ray diffraction technique. in addition to transmission electronic microscope to determine the volume of nanoparticles. Composites are prepared by mixing nanoparticles of zinc oxide with epoxy resin. Mechanical properties measurement showed that the hardness value of the sample (EP+N3) was (103.38) due to Shore is better than the values of the other prepared samples (EP, EP+N2, EP+N1). Also, the composite (EP+N3) showed good compressive strength which was (163.71 MPa). The value of thermal conductivity of the mentioned composite was (6.41W m-1 0K-1) which indicates good thermal properties. However, the study showed that the Epoxy resin has a good response to form important composites with zinc oxide nanoparticles.

حضرت الدقائق النانوية لأوكسيد الزنك بثلاثة طرائق مختلفة، تضمنت الطريقة الأولى مزج محلول من نترات الزنك سداسية ماء التبلور مع محلول من هيدروكسيد الصوديوم (0.4N) بنسبة (1:2) (نموذج(N1 ، وتضمنت الطريقة الثانية مزج محلول من بيكربونات الأمونيوم مع محلول كبريتات الزنك (0.2 M) بنسبة (2:1) (نموذج N2) وأما الطريقة الثالثة فقد تم فيها مزج محلول من نترات الزنك سداسية ماء التبلور مع محلول من هيدروكسيد الصوديوم ((0.6N بنسبة (1:2) (نموذج N3) وباستخدام محلول من النشأ كعامل مثبت للدقائق النانوية. شخصت الدقائق النانوية المحضرة باستخدام تقنية حيود الأشعة السينية (XRD)، كما تم استخدام تقنية المكروسكوب الإلكتروني النافذTEM) ) لتحديد أحجام الجسيمات النانوية. تم تصنيع متراكبات نانوية من خلال مزج الدقائق النانوية لأوكسيد الزنك المحضرة بالطرائق الثلاثة مع راتنج الايبوكسي . تمت إضافة أوكسيد الزنك النانوي بنسب 2 % , 4% , 6% , 8% , 10%)) لكل متراكب من المتراكبات الثلاث وأجريت الاختبارات لكل واحد منها. اتضح من خلال الاختبارات الميكانيكية ان قيمة الصلادة بمقياس شور للمتراكب EP + N3 كانت افضل قياسا إلى مثيلاتها للمتراكبات الأخرى المحضرة EP + N2) , EP + N1 ,EP ) حيث بلغت قيمتها (103.38). بلغت قيمة مقاومة الانضغاط للمتراكب EP + N3)) (163.71 MPa). أما التوصيلية الحرارية فقد بلغت قيمتها للمتراكب المذكور ((6.41W m-1 0K-1 مما يدل على خواصه الحرارية الجيدة. لقد بينت الدراسة استجابة راتنج الايبوكسي لتكوين متراكبات مهمة مع جسيمات أوكسيد الزنك النانوية.


Article
Annealing Effects of Sprayed Techniques on the Optical Properties of ZnO Thin Films
آثار الصلب لتقنيات الرش على البصري خواص ZnO Thin Films

Author: Ameera J. Kadhm
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2019 Volume: 25 Issue: 105 العلمي Pages: 163-177
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Zinc Oxide (ZnO) thin films were prepared on glass subsetrate at a temperature of 673 K using the Chemical Spray Pyrolysis (CSP) technique and annealed at (723 and 773) K for 120 minutes. The results show that the absorbance and coefficient of absorption decreases with the high temperature of annealing, the band gap of direct transition and the index of refraction increases with higher annealing temperature as the photon energy increases within the range that is visible. The high infrared transmittance increases with the temperature of higher annealing. The value of the peak for all optical properties excluding transmittance shift / decrease. Results agree that thin film (723 and 773) K is appropriate as photocatalytic material.

تم تحضير الأغشية الرقيقة لأوكسيد الزنك (ZnO) على قواعد زجاجية عند درجة حرارة 673 كلفن باستخدام تقنية الرش الكيميائي الحراري CSP) كلفن وتلدينها عند (723 و 773) ك لمدة 120 دقيقة. أظهرت النتائج أن الامتصاصية ومعامل الامتصاص يتناقصان مع ارتفاع درجة حرارة التلدين ، ويزداد فجوة الطاقة الانتقال المباشر ويزداد معامل الانكسار مع ارتفاع درجة حرارة التلدين مع زيادة طاقة الفوتون ضمن المدى المرئي. تزداد نفاذية الأشعة تحت الحمراء المرتفعة مع ارتفاع درجة حرارة التلدين. تشير النتائج الى ا امكانية استخدام الاغشية الملدنة بدرجة (723 و 773) K كمواد تحفيزية ضوئية


Article
Studythe OpticalandStructural Propertiesfor Thin Film Zinc Oxide (ZNO) Producedby Pulsed Laser Deposition

Authors: Mohammed T. Hussein --- Mohammed Jawad H. Kadhimb
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 4 Pages: 223-229
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Zinc oxide (ZnO) was prepared by pulsed laser deposition(PLD) using Q-Switching Nd: YAG laser with 1064 nm, Repetition rate(f )= 6 Hz , and Energy(E) = 500 mJ at room temperature under vacuum condition with torr. The optical properties included the absorption coefficient, extinction coefficient, index of refractive for the films of ZnO was evaluated and the results are discussed. The energy band gap of thin film ZnO 3 (eV) at room temperature. The optical transition was found to be direct and allowed transition. Moreover, UV–visible spectra were used to evaluate the ZnO energy gap. FTIR spectra for ZnO used to presence of Zn-O bonding.

اغشيه اوكسيد الزنك المحضرة بتقنيه الترسيب بالليزر النبضي باستخدام ليزر النديميوم ياك Q-Switchingذو الطول الموجي((1.06µmومعدل تكرار(6Hz) ولطاقهليزر500 mJ))بتقنيه الفراغ ولضغط تورر في درجه حراره الغرفة . الخواص البصرية التي تتضمن معامل الامتصاصية ومعامل الخمود ومعامل الانكسار لأغشيه اوكسيد الزنك تم ايجادها ومناقشه النتائج . من طيف الامتصاصية لا وكسيد الزنك اظهرت النتائج بانه يمتلك فجوه طاقه مباشره مقدارها((3eV . استخدم طيف تحويل فورير للأشعة تحت الحمراء لبيان وجود الأصرة بين الزنك والاوكسجين.

Listing 1 - 10 of 10
Sort by
Narrow your search

Resource type

article (10)


Language

English (6)

Arabic (4)


Year
From To Submit

2019 (10)