Article
"STUDYING THE EFFECT OF NITRIC ACID ON REINFORCED AND UNREINFORCED UNSATURATED POLYESTER "
"دراسة تاثير حامض النتريك على البوليستر غير المشبع المقوى وغير المقوى

Loading...
Loading...
Abstract

Abstract:-The aim of this work is to study the effect of different concentrations of nitric acid (20%,40%,60)for each 100ml of distilled water on unsaturated polyester and composite material. The composite material consists of unsaturated polyester reinforced with powder of aluminum at (0.1, 0.25, 0.5)wt% for (2-10) days. Nitric acid affects on unsaturated polyester through: physical degradation which represents by yellowish of polymer, swelling, the formation of pits, and hydrolytic corrosion. The presence of aluminum powder will inhibit the molecules of solution from penetration into the cross-linked polymeric chains and consequently will decrease the swelling at 0.1 wt% but the reinforcement with greater ratios of aluminum powder will lead to increase in weight.

يهدف هذا البحث إلى دراسة تأثير التراكيز المختلفة لحامض النتريك ( 20لكل 100 مليلتر من الماء المقطر على مادة البوليستر غير المشبع ثم المادة المركبة المؤلفةمن أرضية من البوليستر غير المشبع المقوى بدقائق الألمنيوم بنسب وزنيه تتراوح بينولفترة زمنية بين 2 إلى 10 أيام. يؤثرحامض النتريك على البوليستر wt%(0.1,0.25,0.5)غير المقوى من خلال التحلل الفيزياوي الذي يمثل اصفرار البوليمروانتفاخه وتكوين النقر والتحلل المائي .ان وجود دقائق الألمنيوم يؤدي لإعاقة جزيئات المحلول من التغلغل إلىاماالتقوية wt% السلاسل البوليمرية المتشابكة وبالتالي يؤدي للتقليل من الانتفاخ عند 0.1بنسب اعلى من مسحوق الالمنيوم فتؤدي الى حدوث زيادة بالوزن.


Article
EFFECT OF REINFORCING BY DIFFERENT PERCENTAGE OF FIBERS ON MECHANICAL PROPERTIES OF VINYL ESTER RESIN
تأثير التقوية بنسب وزنية مختلفة من ألياف الزجاج على الخواص الميكانيكية لراتنج الفنيل أستر

Authors: علي إبراهيم الموسوي --- فائز جواد كاظم
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2011 Volume: 24 Issue: 3 Pages: A1-A7
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

يبين البحث الحالي دراسة بعض المفاهيم والخواص المهمة في تصنيع المواد المركبة المتقدمة المقواة بالألياف ، وتعد هذه المفاهيم مقدمة لبعض الخواص المهمة للمواد البولميرية المقواة بالألياف والمتعلقة بنسب مكوناتها من الألياف والمادة الأساس وبعض الخواص الميكانيكية (الشد ،الصدم ،الإنضغاط ،الإنثناء ،الصلادة وغيرها) . يهدف هذا البحث إلى دراسة تأثير إستخدام نسب وزنية مختلفة من الألياف في التقوية على الخواص الميكانيكية للمادة المركبة المكونة من راتنج الفنيل أستر المقوى بألياف الزجاج أحادية الإتجاه(°0) نوع -E ذات كثافة سطحية (2.6 g/cm3)، وقد شملت هذه الخواص كل من مقاومة الصدم والشد والإنضغاط والإنثناء والصلادة حيث تم في البداية إستخراج الخواص الميكانيكية لراتنج الفنيل أستر قبل تقويته بالألياف بعدها تم إضافة نسب وزنية مختلفة من ألياف الزجاج إلى الراتنج (%60,%40,%20) و دراسة تأثير ذلك على الخواص المذكورة .

In this proposal research , some aspects and important properties in manufacturing of advanced composite materials reinforced by fibers will be studied ,these aspects show as introduction to some important properties of polymeric composite materials reinforced by fibers related with its composition and some mechanical properties (Tension ,Impact, Compression, Flexural, Hardness, etc) .The objective of this research is to study the effect of using different reinforcement percentage of fibers on mechanical properties for composite material consist of vinyl ester resin reinforced by glass fibers(°0) (E) type with (2.6 g/cm3) density which included impact , tensile, compression , flexural strength , and hardness where we extracted the mechanical properties for vinyl ester resin before reinforced by fibers, then we reinforced the resin by different weight percentage from glass Fibers(20%,40%,60%) and studied its effect on the above mechanical properties .


Article
EFFECT OF ANTIMONY TRIOXIDE THERMAL CONDUCTIVITY FOR POLYMERIC MATERIAL REINFORCED BY GLASS FIBERS
تأثير ثالث أُوكسيد الأنتيمون على الموصلية الح ا ررية لمادة ب ولميري ة مقواة بألياف زجاجية

Loading...
Loading...
Abstract

Abstract .This research aimed to study the effect of flame retardant material additionnamely antimony trioxide (Sb2O3) on thermal conductivity of composite materialconsist of conbextra epoxy (EP-10) resin reinforced by chopped E–type glass fiberswith density (600g/cm2) .The effect of different percents of antimony trioxide (10%,20%,30%) on thermal conductivity was investigated by using Fourier equation tocalculate the thermal conductivity coefficient (k) for this composite material beforeand after addition of flame retardant material ,where the thermal conductivity valueimproved after added trioxide where it change from(0.35 W/m.ºC) before addedantimony trioxide to (0.4 W/m.ºC) after addition (30%) from oxide at temperature (50ºC) which the best value from oxide additive

الخلاصة .يهدف هذا البحث إلى د ا رسة تأثير إضافة مادة معيقة للّهب وهي ثالث أُوكسيد الأنتيمون )(EP- على الموصلية الح ا ررية لمادة مت ا ركبة مكونة من ا رتنج الإيبوكسي كونبكست ا ر Sb2O3 )600 ) . لقد g/cm ذات كثافة سطحية ( 2 (E-Glass) 10 المقوى بألياف الزجاج المقطعة نوع )30 %) إلى المادة المت ا ركبة , %20,% تم إضافة ثالث أُوكسيد الأنتيمون بنسب مختلفة ( 10النهائية وقياس مدى تأثر الموصلية الح ا ررية لهذه المادة عن طريق إستخدام معادلة فوريرللمادة المت ا ركبة قبل وبعد إضافة المادة (k) لحساب التغير في قيمة معامل التوصيل الح ا رريالمعيقة للّهب ، ومن خلال النتائج التي تم الحصول عليها تحسنت قيمة الموصلية الح ا ررية بعد0.35 ) قبل إضافة ثالث أُوكسيد W/m.ºC) إضافة الأُوكسيد الثلاثي إليها حيث تغيرت من(50 ºC) 0.4 ) بعد إضافة ( 30 %) من الأُوكسيد عند درجة ح ا ررة W/m.ºC) الأنتيمون إلىوهي أفضل قيمة للأُوكسيد المضاف .