Article
Tensile and Buckling Analysis of Polymeric Composite Columns

Authors: Jawad Kadhim Oleiwi --- Emad Saadi Al- hassani --- Alaa Abd Mohammed
Journal: Basrah Journal for Engineering Science مجلة البصرة للعلوم الهندسية ISSN: Print: 18146120; Online: 23118385 Year: 2014 Volume: 14 Issue: 2 Pages: 176-188
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

This research studied the critical load of composite columns theoretical and numerical by using ANSYS14 package depended on experimental tensile properties of composite specimens. The composite specimens were prepared by hand lay-up technique made from unsaturated polyester reinforced with glass fibers with different fiber volume fraction Vf, aspect ratio (L/T), and angle of fibers for coarse and fine woven fibers.The critical load that obtained by using program (ANSYS 14) have also shown a good agreement with results that were obtained theoretically and the maximum difference was (0.7%).The results show that the maximum value of the critical load can be observed at Vf =11%, L/T = (3.5) and θ = (0º/90º) for fine woven fibers was (622.115N). Also its found the maximum critical load for coarse woven fibers can be observed at Vf %=8%, L/T=(3.5) and θ = (0º/90º) was (486.887N). Also the observed values of tensile properties and predicated values are scattered close to the (45˚) line.


Article
A study of the effect of acid immersion on some physical properties of ( Epoxy – MgO) composites
دراسة تأثير الغمر بالحامض على بعض الخواص الفيزيائية لمتراكبات (الايبوكسي - اوكسيد المغنيسيوم)

Authors: Rifqa A. Salman رفقة عامر سلمان --- Jinan M. H. Jabir جنان محمد حسن جابر --- Salma M. Hassan سلمى محمد حسن
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 26 Pages: 146-150
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study a polymeric composite material was prepared by hand lay-up technique from epoxy resin as a matrix and magnesium oxide (MgO) as a reinforcement with different weight fraction (5,10,15, and 20)% to resin. Then the prepared samples were immersed under normal condition in H2So4(1 M) solution, for periods ranging up to 10 weeks. The result revealed that the diffusion coefficient decreasing as the concentration of MgO increase. Also we studied Hardness for the prepared samples before and after immersion. The result revealed that the hardness values increase as the concentration of MgO increase, while the hardness for the samples after immersion in H2SO4 decreased as compared to those before immersion. In addition, the dielectric strength decreasing by increasing the MgO concentration with time immersion.

تم في هذه الدراسة تحضير مادة متراكبة ذات اساس بوليمري باستخدام تقنية القولبة اليدوية وقد حضرت المادة المتراكبة من راتنج الايبوكسي كمادة اساس مدعم بمسحوق اوكسيد المغنيسيوم (MgO) وبكسور وزنية مختلفة (5,10,15 and 20)% ثم غمر النماذج المحضرة بالظروف الاعتيادية بمحلول حامض الكبريتيك(H2SO4) وبتركيز (1M) لفترة تصل الى 10اسابيع. حيث اظهرت النتائج ان معامل الانتشار يقل بزيادة نسبة دقائق التدعيم المضافة(MgO) . وكذلك تم دراسة اختبار الصلادة للنماذج المحضرة قبل وبعد الغمر حيث اظهرت النتائج ان قيم الصلادة تزداد بزيادة الكسور الوزنية لاوكسيد المغنيسيوم كما ان قيم الصلادة للنماذج قبل الغمر تمتلك اعلى قيم مقارنة مع قيم الصلادة بعد الغمر. اما متانة العزل فاظهرت النتائج انها تقل بزيادة كل من الكسور الوزنية المضافة ومدة الغمر.


Article
Preparation and studying of some properties of polymer composites reinforced with natural and artificial fibers
تحضير ودراسة بعض الخواص لمتراكبات بوليمرية مسلحة بالياف طبيعية وصناعية

Authors: Awham M. Hameed أوهام محمد حميد --- Saad Ali Fouad سعد علي فؤاد
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 138-147
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This work concerns the thermal and sound insulation as well as the mechanical properties of polymer matrix composite reinforced with glass fibers. These fibers may have dangerous effect during handling, for example the glass fibers might cause some damage to the eyes, lungs and even skin. For this reason the present work, investigates the behavior of polymer composite reinforced with natural fibers (Plant fibers) as replacement to glass fibers. Unsaturated Polyester resin was used as matrix material reinforced with two types of fibers, one of them is artificial (Glass fibers) and the other type is natural (Jute, Fronds Palm and Reed Fibers) by hand lay-up technique. All fibers are untreated with any chemical solvent. The Percentage of mixing was (90 wt. %) of the matrix while the weight fraction of each type of fibers was fixed (10 wt. %). The mechanical tests included impact and flexural strength tests. The results showed that the impact strength and flexural strength of the composites reinforced with Jute fibers is higher than that of Glass fibers and other natural fibers. The coefficients of thermal conductivity of the composites were measured by Lee's disc apparatus, the results show that the thermal insulation of the composite reinforced with jute fibers is higher than that of glass fibers and other natural fibers.The acoustic insulation of the composites reinforced with Jute fibers showed excellent result in insulation compared with glass fibers and other natural fibers.

أهتمت العديد من البحوث في دراسة الخواص العزل الحراري والصوتي و الخواص الميكانيكية لمتراكبات بوليمرية مسلحة بالياف الزجاج علما بأن هذه الالياف لها مضار عند التعامل معها فهي قد تضر بالعينين والرئتين وكذلك الجلد لذا ارتأينا اجراء دراسة خواص لمتراكبات البوليمر المقواة بألياف طبيعية (نباتية) كبدائل عن الياف الزجاج ومقارنة خواص كليهما وتحديد النتائج.استخدم راتنج البولي استر غير المشبع كمادة اساس وتم تسلسحه مع نوعين من الالياف, صناعية (الياف الزجاج) وطبيعية (الياف الجوت, وسعف النخيل, والياف القصب) جميع الالياف استخدمت بدون معاملة كيميائية, بواسطة تقنية الصب اليدوي. الكسر الوزني للرتنج كانت 90% نسبة وزنية بينما كان الكسر الوزني لجميع للأياف ثابت وهو 10% نسبة وزنية, الاختبارات الميكانيكية الي تم اجرائها هي اختبار الصدمة بطريقة جاربي واختبار مقاومة الكسر لحساب قيمة مقاومة الصدمة ومقاومة الكسر لهذه المتراكبات, النتائج اضهرت ان المتراكبات المسلحة بالياف الجوت (الطبيعية) لها مقاومة صدمة ومقاومة كسر اعلى من الياف الزجاج والاياف الطبيعية الاخرى. كذلك تم اجراء فحص التوصيلية الحرارية لهذه المتراكبات باستخدام جهاز(قرص لي) واوضحت نتائج اختبار التوصيلية الحرارية بأن العزل احراري للمتراكبات المسلحة بألياف الجوت اعلى من المتراكبات المسلحة بألياف الزجاج وكذلك اعلى من الالياف الطبيعية الاخرى, بينما نتائج فحص العزل الصوتي للمتراكبات المسلحة بألياف الجوت كانت ممتازة مقارنة بالمتراكبات المسلحة بالياف الزجاج وكذلك المتراكبات المسلحة بالاياف الطبيعيه الاخرى.


Article
The Effect of Artificial Saliva on The Surface Roughness of Different Esthetic Archwires (An in Vitro Study)

Authors: NoorS. Muayad --- Nidhal H. Ghaib نضال حسين غايب
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2017 Volume: 29 Issue: 3 Pages: 106-112
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background:The demand for esthetic orthodontic appliances is increasing so that the esthetic orthodontic archwires were introduced. This in vitro study was designed to evaluate the surface roughness of fiber-reinforced polymer composite (FRPC) archwires compared to coated nickel-titanium (NiTi) archwires immersed in artificial saliva.Materials and Methods:Three types of esthetic orthodontic archwires were used: FRPC (Dentaurum), Teflon coated NiTi (Dentaurum) and epoxy coated NiTi (Orthotechnology). They were round (0.018 inch) in cross section and cut into pieces of 15 mm in length.Forty pieces from each type were divided into four groups; one group was left dry condition and the other three groups were immersed in artificial saliva (pH=6.75 ± 0.015) at 37ºC for 1, 14 and 28 days intervals. The AFM was used to evaluatesurface analysis of all samples.ANOVA, Kruskal-Wallis, LSD and Mann-Whitney U tests were used to identify and localize the source of differences among the groups.Results:At each immersion period, FRPC wires exhibited the highest Ra among the study groups, except at 28 days immersion period where the Teflon coatings were the roughest. On the other hand, the least rough surfaces were the epoxy coatings when compared to analogous esthetic archwires, except at 1 day immersion period where the Teflon coatings had the least roughness. However, statistically non-significant differences were found between Teflon and epoxy at the dry condition and the 1 day immersion.Conclusions:The epoxy coated archwires were the best and the most appropriate esthetic orthodontic alignment archwires in term of the least surface roughness initially and over the course of study period


Article
Preparation and Optical Characterization of Polymer Composites Reinforced by Natural Materials

Author: Aseel S. Jasim
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2016 Volume: 19 Issue: 1 Pages: 91-97
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Three groups of composite materials were prepared by using casting method from Unsaturated Polyester with volume fraction (70%) reinforced by Rice Husks with volume fraction (30%) (first group), the second group was prepared from Unsaturated Polyester with volume fraction (70%) reinforced by Rice Husks with volume fraction (15%) and by Palm Fibers with volume fraction (15%) (hybird composite) and the third group consist also of Unsaturated Polyester with volume fraction (70%) reinforced by Palm Fibers with volume fraction (30%), the length of palm fibers was (2-3) mm. Parameters such as absorbance (A), transmittance (T), reflectance(R), refractive index (n), extinction coefficient (k) , real (εr) and imaginary parts (εi) of dielectric constants, were studied in the spectral range (200-800) nm. The results show that the absorbance increases with increasing the ratio of Palm Fibers while the transmittance decreases, the hybrid composite has the best values of reflectance and the higher values of extinction coefficient, Refractive index, real and imaginary parts of dielectric constants were for samples containing ratios of Palm Fibers and the lower values were for those contain Rice Husks only.

تم في هذا البحث تحضير ثلاث مجاميع من المواد المتراكبة بطريقة الصب وبسمك (0.5) سم لجميع العينات المحضرة بأستخدام مادة البولي استر غير المشبع وبكسر حجمي 70% (الكسر الحجي للبولي استر غير المشبع ثابت في كافة العينات المحضرة) وتدعيمها بقشور الرز وبكسر حجمي 30% (المجموعة الاولى)، اما المجموعة الثانية فيكون التدعيم بألياف النخيل وبكسر حجمي 15% وقشور الرز وبكسر حجمي 15% أيضاً (مركب هجيني) و المجموعة الثالثة كانت مدعمة بألياف النخيل بكسر حجمي 30%، طول الياف النخيل المستخدمة في هذا البحث(2-3) ملم.درست الخواص البصرية من خلال قياس الامتصاصية، النفاذية، الانعكاسية للآطوال الموجية (200-800) نانومتر وتم تحديد معامل الخمود ومعامل الانكسار وثابت العزل الكهربائي بجزئيه الحقيقي والخيالي. وتم التوصل الى ان الامتصاصية تزداد بزيادة الكسر الحجمي لألياف النخيل على عكس النفاذية تقل مع زيادة الكسر الحجمي للألياف. اما (المتراكب الهجيني) فقد سجل أفضل القيم في الانعكاسية. ان قيم كل من معامل الخمود معامل الانكسار وثابت العزل بجزئيه الحقيقي والخيالي كانت اعلى في العينات التي تحتوي على نسب من ألياف النخيل من تلك التي تحتوي على قشور الرز فقط.


Article
STUDY THE EROSION WEAR BEHAVIOR FOR UNSATURATED POLYESTER RESIN COMPOSITES MATERIALS REINFORCED BY CARBON FIBERS WITH AL2O3 POWDER USING TAGUCHI METHO

Authors: Reem Alaa Mohammed --- Rajaa Kamil Majeed --- Dalia Mohammed Gomaa
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2017 Volume: 21 Issue: 5 Pages: 213-224
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

this research investigates the erosion wear behavior of polyester resin composites materials reinforced with 4% volume fraction carbon fiber and (2%, 4%, 6% and 8%) volume fraction Al2O3 powder. These specimens were fabricated by hand lay-up technique. Erosion wear behavior was studied at different variables, are angles impingement (30º, 60º, 90º), with dry silica sand particles size (350,425,600 µm) at 10 hour, stand-off distance (17 cm) and flow rate (35 L ∕min). In this research erosion testing were carried out according to ASTM G76 and study effect of parameters on erosion wear rate by using Taguchi orthogonal arrays L9. The results indicate that, the specimen (UP+4%C.F+8% Al2O3) has high value of true density than other specimens. Also the specimen (UP+4%C.F+8% Al2O3) has (0.00011 cm3/gm) better erosion rate resistance at variables (425 µm , 30 º ) as compare to other composite materials . The ANOVE analysis showed that filler content factor (Al2O3) powder more effect on erosion rate than other factors

في هذا البحث تم التقصي عن سلوك بلى التعرية لمواد متراكبة من رانتج البولي استر غير المشبع المقواة مع كسر حجمي4 % من الالياف الكاربون ومسحوق الالومينا بكسور حجمية (2%,4 %, 6% و 8%), صنعت هذة العينات بتقنية الصب الیدوي . تم دراسة سلوك بلى التعرية عند متغيرات مختلفة وكانت زاوية التصادم (30º, 60º, 90º) و حجم دقائق رمل السيكا الجافه 350,425,600 µm)) مايكرون عند 10 ساعات و مسافة التصادم (17cm ) و معدل جريان (35 L∕min) . في هذا البحث كان اختبار بلى التعرية وفقا (ASTM G76) و دراسة تأثير المتغيرات على معدل بلى التعرية بواسطة استخدام المصفوفات المتعامدة لتاكوجي L9 . اشارت النتائج ان عينة (UP+4%CF+8%Al2O3) تمتلك اعلى قيمة من الكثافة الحقيقية من العينات الاخرى . ايضا من النتائج يمكن ملاحظة ان العينة (UP+4%C.F+8% Al2O3) تمتلك (( 0.00011 cm3/gm) افضل مقاومة لتعرية عند المتغيرات (425 µm , 30 º ) كمقارنة مع المواد المتراكبة الاخرى . تحليل الانوفا اظهر بان عامل محتوى الحشوه لدقائق (Al2O3 ) هو الاكثر تاثيرا على معدل التعرية من العوامل الاخرى


Article
Mechanical Properties of Polymer Composite Reinforced by Agricultural Wastes
الخواص الميكانيكية لمتراكب بوليمري مدعم بالمخلفات الزراعية

Author: Bushra Hosni Musa بشرى حسني موسى محمد
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2017 Volume: 13 Issue: 4 - part 2 Pages: 212-224
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This study is concerned on prepare polymer composite from unsaturated polyester resin (UPE) reinforced with) 10%) weight fraction of broomcorn natural fibers (long and short) by using hand lay-up technique. The natural fibers treated with 0.5 normality of NaOH solution. Some mechanical properties such as (Impact strength, flexural strength and shore D hardness) have been studied. It was found that the impact strength increased when unsaturated polyester reinforced by treated long broomcorn fibers compared with short fiber and pure unsaturated polyester while, flexural strength and hardness values decreased of treated composite compared with pure unsaturated polyester.

تتركز هذه الدراسه على تحضير متراكب بوليمري من البولي استر غير المشبع (UPE) المدعم بكسر وزني مقداره ( 10%) من الياف مقشة الذرة الطبيعيه (الطويلة والقصيرة) باستخدام تقنية القولبة اليدوية ، وقد تمت معاملة الألياف الطبيعية بمحلول هيدروكسيد الصوديوم (Na OH) وبتركيز قدره (0.5) نورمالتي. ودرست بعض الخواص الميكانيكية مثل (مقاومة الصدمه ، متانة الانحناء وصلادة شور D ) على هذا المتراكب البوليمري. ومن خلال النتائج وجد أن مقاومة الصدمه تزداد عند التدعيم بالياف المقشة الطويلة المُعامله بالمقارنه مع الالياف القصيرة والبولي استر غير المشبع النقي بينما تقل متانة الانحناء والصلاده للمتراكب المُعامل مما هو عليه للبولي استر غير المشبع النقي .

Listing 11 - 17 of 17 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (17)


Language

English (14)

Arabic and English (2)

Arabic (1)


Year
From To Submit

2017 (4)

2016 (2)

2015 (2)

2014 (4)

2013 (3)

More...