Study of Some Mechanical Properties for a Polymer Material Reinforcement with Chip or Powder Copper
دراسة بعض الخواص الميكانيكية لمادة بوليمرية مقواة برايش و مسحوق النحاس

Authors: علي حسين عتيوي --- ليث وضاح اسماعيل --- أسيل محمود عبد الله
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2012 Volume: 18 Issue: 5 Pages: 103-113
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this paper, chip and powder copper are used as reinforcing phase in polyester matrix to form composites. Mechanical properties such as flexural strength and impact test of polymer reinforcement copper (powder and chip) were done, the maximum flexural strength for the polymer reinforcement with copper (powder and chip) are(85.13 Mpa)and (50.08 Mpa) respectively was obtained, while the maximum observation energy of the impact test for the polymer reinforcement with copper (powder and chip) are (0.85 J) and (0.4 J) respectively.

في هذا البحث تم استخدم رايش ومسحوق النحاس لتقوية مادة البولي استر لانتاج مادة متراكبة. تم إجراء الفحوصات الميكانيكية مثل مقاومة الانحناء واختبار الصدمة لمادة البوليمرية المقواة برايش ومسحوق النحاس، وقد وجد ان أقصى مقاومة انحناء للمادة البوليمرية المقواة بالنحاس (المسحوق والرايش)هي(85.13 Mpa)و(50.08 Mpa)على التوالي، بينما أعلى طاقة ممتصة في فحص الصدمة للمادة البوليمرية المقواة بالنحاس (المسحوق والرايش) هي (0.85 J)و (0.4 J)على التوالي.


Article
A comparative Study on the Thermal Conductivity of Micro and Nano fluids by Using Silver and Zirconium Oxide
دراسة مقارنة بين التوصيل الحراري للموائع المايكروية والنانوية باستخدام الفضة وأوكسيد الزركونيوم

Authors: Layth W. Ismael مدرس ليث وضاح اسماعيل --- Dr. Khalid Faisal. Sultan د. خالد فيصل سلطان
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2014 Volume: 7 Issue: 2 Pages: 189-204
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

ABSTRACT In this article experimentally investigations have been carried out to study the effect of the size and type particles on the thermal conductivity of micro and nanofluids. The study investigated nanofluids and microfluids which containing silver (Ag) and zirconium oxide (Zr2O3) as well as in the size and type of micro and nanoparticles in distilled water as base fluid with different particles size and concentrations. The experimental results emphasized the enhancement of the thermal conductivity due to the nanoparticles presence in the fluid greater than microfluids, also shown the effect of the particle size and concentration on the thermal conductivity. It has been recognized that the addition of highly conductive particles can significantly increase the thermal conductivity of heat – transfer fluids. Particles in the micro and nano – size range have attracted the most interest because of their enhanced stability against sedimentation and, as a result, reduction in potential for clogging a flow system. Furthermore the results showed that, the obtained thermal conductivities doubtlessly revealed that size and type particles was a key factor affecting conductive heat transport in suspensions. The aim of this article is an experimental exploration of the thermal conductivity of micro – and nano – particles and Compared with them as well as type particles and the method used in this researcher know Lee's disc technique. These results show noticeable enhancement in the thermal conductivity were evaluated to be ( 7.66 %, 2.35 %) for the Ag, Zr2O3 – distilled water nanofluid while reaches to (3.23 %,1.02 %) for the Ag , Zr2O3 – distilled water micro fluids at the concentration of (0.05 vol. %) and at the room temperature. A good agreement was found between the experimental obtained data for this paper and other results from published papers.

يتضمن البحث الحالي دراسة عملية للموصلية الحرارية للموائع التي تحتوي على حبيبات نانوية وما يكروية مخلوطة مع المائع الاساسي وكذلك تأثير حجم ونوع الجزئيات. الدراسة تضمنت سوائل نانوية وما يكروية مكونة من فضة Ag وأوكسيد الزركونيوم Zr2O3 على شكل حبيبات نانوية وما يكروية مختلطة مع الماء النقي كمائع اساسي بكسور حجمية وتراكيز مختلفة. أكدت النتائج التجريبية تحسين الموصلية الحرارية بسبب وجود الجسيمات النانوية في المائع أكبر من الموائع الميكروية ، أظهرت أيضا تأثير حجم الجزيئات والتركيز على التوصيل الحراري. وقد تم الاعتراف بأن إضافة جزيئات يمكن أن تزيد بشكل كبير من الموصلية ا لحرارية في انتقال الحرارة بالموائع . الجزيئات ذات الحجم النانوي والميكروي اجتذبت قدر كبير من الاهتمام بسبب تحسين الأستقرارية ضد الترسيب وبالنتيجة ،الحد من احتمال انسداد التدفق بالنظام وعلاوة على ذلك أظهرت النتائج أن التوصيلات الحرارية التي تم الحصول عليها كشفت بلا شك أن حجم و نوع الجزيئات كان عاملا رئيسيا يؤثر على انتقال الحرارة بالتوصيل في الموائع الميكروية والنانوية . الهدف من هذه المقالة هو دراسة عملية في الموصلية الحرارية للجزئيات النانوية والميكروية و بالمقارنة بينهما ، فضلا عن نوع الجزيئات و الطريقة المستخدمة في هذا الباحث تعرف بتقنية قرص لي. كما بينت النتائج العملية تحسن ملحوظ في الموصلية الحرارية بسبب الحبيبات الما يكروية والنانوية المضافة الى المائع، كذلك بينت تأثير الحجم الحبيبي والتركيز على الموصلية الحرارية. النتائج بينت ايضا ان الموصلية الحرارية الى المواد النانوية تكون اكبر من الموصلية الحرارية للمواد المايكروية بسب صغر حجم الجزئيات النانوية بالمقارنة مع الحجم المايكروية. وان نسب التحسين في الموصلية الحرارية كانت (2.73,7.66%) الى المائع النانوي الفضة Ag وأوكسيد الزركونيوم Zr2O3 مع الماء النقي على التوالي . بينما كانت هذه النسب (1.02, 3.23%) الى المائع المايكروية الفضة Ag وأوكسيد الزركونيوم Zr2O3 مع الماء النقي وبتركيز (0.05%) وبدرجة حرارة الغرفة. وجد توافق جيد بين النتائج العملية المستحصلة من هذه الدراسة ونتائج اخرى في بحوث منشورة سابقة