Article
Preparation of NanoPorous Alumina by Anodization Method and Study of Their Structural Properties
تحضير الألومينا ذات المسامات النانومترية بطريقة الانودة ودراسة خصائصها التركيبية

Author: Ali J Addie علي جبر عداي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 5 Part (B) Scientific Pages: 176-185
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Highly ordered nanoporous alumina structures have been prepared by electrochemical anodization for high purity Al-foils, electrolyte cell parameters have controlled to obtain optimum preparation conditions. Anodization potential, current density and electrolyte concentration effects on the prepared porous layer, surface morphology have been studied by scanning electron microscope and energy dispersive x-ray spectroscopy have used to analyze chemical composition of the samples.Results of the SEM show that the pore size was about 20-80 nm and it depends strongly on the anodization potential & electrolyte concentration, the higher anodization potential can destroy the barrier layer & cause a hi-dissolution rate of aluminum in the electrolyte, while with low potential a porous layer cannot be obtained. The highest degree of order and hexagonal distribution of pores was obtained with anodization potential of 20 volts and 0.2M of the electrolyte concentration. Results of EDS confirm the formation of the aluminum oxide layer with traces of sulfur which belong to the electrolyte.

حضرت تراكيب اوكسيد الالمنيوم المسامية النانومترية ذات التنظيم العالي بالانودة الكهروكيميائية لرقائق الالمنيوم عالية النقاوة، وجرى التحكم بمعلمات الخلية الكهروكيميائية للحصول على أفضل معل مات تحضير. درست تأثيراتالجهد والتيار الكهربائي المار في الخلية وتركيز المحلول على خ صائص الطبقة المسامية المتكتم .ةنو التركيز على دراسة مورفولوجية السطوح المتكونة باستخدام المجهر الالكتروني الماسح ودراسة التركيب الكيم يائي باستخدام مطياف الاشعة ا..ينية.بينت نتائج تحليلات المجهر الالكتروني الماسح ان اقطار المسامات التي تم الحصول عليها تراوحت بين 20 و 80 نانومتر وهي تعتمد بشكل كبير على جهد الأنودةوتركيز المحاليل، و أدت زيادة الجهد الى تدمير طبقة الحاجز وحصول اذابة سريعة للألمنيوم وتكوين سطوح متاكلة غير مسامية، بينما ادت الجهود المنخفضة الى عدم تكون طبقة مسامية، وقد تم الحصول على درجة انتظام عالي وتوزيع سداسي للمسامات عند جهد انودة 20 فولت وتركيز محلول 0.2M ، فيما بينت تحليلات مطيافيةالاشعة السينية المشتتة للطاقة تكون طبقة اوكسيد الالمنيوم مع وجود نسب من تراكيز الكبريت التي تعود لللالالول لالالكترول يتي.


Article
تحسين الحماية التاكلية للفوالذ باستخدام طالءات المتراكب النانوي PMMA/TiO2

Authors: محمد عبيد كاظم --- علي جبر عداي --- محمد حسين علي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 4 Part (C) Pages: 57-65
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

في هذا البحث تم تحضير طالءات متراكب نانوي ذو أساس بوليمري من البولي مثيل ميثاكرياليت PMMA0, 0.5, 1.0, 1.5, 2.0 ( اضافة وبنسب 75 nm حبيبي حجم بمعدل النانوية التيتانيوم أوكسيد بدقائق مدعم%wt .)رسبت الطالءات على سطوح الواح من الفوالذ الكربوني باستخدام طريقة الغمر وتم تشخيص التركيبالكيميائي للطالءات المتراكبة باستخدام مطياف االشعة تحت الحمراء FTIR .إجري أختبار التآكل بواسطةالغمر في محاليل حامضية وملحية عند درجة حرارة الغرفة، وتم قياس مقدار الفقدان في الوزن وحساب معدلالتاكل كدالة لزمن التعرض كمعيار لتأثر الفوالذ الكربوني بوسطي التآكل المختلفين. أكدت النتائج إن مقاومةالتآكل لطالءات المتراكبات النانوية TiO2/PMMA تبدي تحسنا ملموسا مقارنة بطالءات البولي مثيلميثاكرياليت النقية في األوساط التآكلية الحامضية والملحية.


Article
Study of Microstructure and Mechanical Properties of Zr-Nano Powder by Microwave Sintering
دراسة الخصائص التركيبية والميكانيكية لمسحوق الزركونيا النانومتري الملبد باستخدام الموجات الدقيقة

Authors: Riyadh I.A رياض ابراهيم عطية --- Ali J.Addie علي جبر عداي --- Mohammed O.K.* محمد عبيد كاظم
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2012 Volume: 8 Issue: 3 - part 2 Pages: 174-181
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

In this research zirconium oxide samples have been prepared using microwave sintering and conventional sintering furnaces, and the effect of nano powder of zirconium oxide addition on micro-scale powder have been studied with respect to the structural and mechanical properties of the samples.The results showed that the prepared microwave samples have a fine structure with smaller grains and more uniformity, but the density of the samples are slightly higher for samples prepared in the traditional way, while the addition of the Nano-scale powder leads to obtain samples with higher density because of the low porosity. It also added the nanoparticles led to a marked improvement in the micro hardness of the samples.The results confirm that the addition of limited ratios of nanoparticles to micro-scale-powders of the same substance will lead to improvement in the microstructure and some mechanical properties that have been studied in this research.

في هذا البحث جرى تحضير نماذج اوكسيد الزركونيوم باستخدام تقنيتي التلبيد بالموجات الدقيقة والتلبيد بالافران التقليدية، كما تمت دراسة تاثير اضافة مسحوق اوكسيد الزركونيوم النانوي الى المسحوق المايكروي على الخصائص التركيبية والميكانيكية للنماذج. بينت النتائج ان البنية الدقيقة للنماذج المحضرة بالموجات الدقيقة تبدي تركيبا حبيبيا اصغر واكثر تجانس، الا ان كثافة النماذج تكون اعلى بقليل بالنسبة للنماذج المحضرة بالطريقة التقليدية، في حين ان اضافة المسحوق النانوي يؤدي الى الحصول على عينات ذوات كثافة اعلى وذلك بسبب انخفاض المسامية. كما ادت الاضافة النانوية الى حصول تحسن ملحوظ في الصلادة الدقيقة للعينات. تؤكد النتائج على ان اضافة نسب محدودة من المساحيق النانوية الى المساحيق المايكروية لنفس المادة تؤدي الى حصول تحسن في البنية الدقيقة وفي بعض الخصائص الميكانيكية التي تمت دراستها في البحث.


Article
Characterization of the Structural and Electrical Properties of Transparent Conductive Oxides Prepared by Sol-Gel Method
توصيف الخصائص التركيبية لأكاسيد موصلة شفافة محضرة بطريقة المحلول هلام

Authors: Ali J Addie علي جبر عداي --- Azhar I Hassan ازهار عناد جبر --- Saleema S Saad سليمة سالم سعد
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 6 Part (B) Scientific Pages: 209-216
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Nano crystalline powder of the System Cu-Al-O have been prepared by Sol-Gel technique, copper nitrate and aluminum nitrate have adopted as raw materials for the reaction, and subsequently solid state reactions have used to synthesize different compounds and phases at the calcination stage. Effects of calcination temperature and time in the range 800-1100oC and 1hr-6hr respectively have been investigated. XRD results show that the system have a multiphase and it depends on the calcination time and temperature, the higher the temperature and time the higher the percentage of the compound CuAlO2, whereas the SEM microscopy show that the Nano powder have particle size of 40nm, and Raman spectroscopy reveals the presence of Eg and A1g modes which belong to the structure CuAlO2. The work emphasize that the control of the technique parameters could provide high degree of control on the final required phases and structures.

حضرت مساحيق بلورية نانوية من النظام Cu-Al-O بتقنية المحلول هلام، وتم استخدام نترات النحاس ونترات الالمنيوم كمواد اولية في التفاعلات، كما اعتمدت تقنية تفاعلات الحالة الصلبة للحصول على مركبات واطوار مختلفة في مرحلة الكلسنة. جرى خلال البحث دراسة تأثير درجة حرارة الكلسنة التي تراوحت بين 088 و 0088 درجة مئوية وزمن الكلسنة الذي تراوح بين ساعة وست ساعات. بينت تحليلات حيود الاشعة السينية تكون عدد من المركبات والاطوار المختلفة في النظام وهي تعتمد بشكل كبير على درجة حرارة الكلسنة كما ان زيادة زمن الكلسنة يؤدي الى تحسن التركيب الطوري والبلوري وزيادة نسب تكون المركب CuAlO2 ، بينما بينت تحليلات المجهر الالكتروني الماسح ان المساحيق المتكونة تمتلك حجوم نانوية بحدود 40nm كما اكدت التحليلات الطيفية لمجهر رامان ظهور النمطين A1g و Eg اللذان يعودان للمركب CuAlO2 . وبذلك أكد البحث بان التحكم بمعلمات التقنية يمكن ان يوفر درجة عالية من التحكم بالأطوار والمكونات المطلوبة.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic (2)

Arabic and English (1)

English (1)


Year
From To Submit

2018 (1)

2016 (2)

2012 (1)