Study of Optical Properties for Polystyrene Composite Material
دراسة الخصائص البصرية لمادة البولي ستايرين المتراكب

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2011 Volume: 9 Issue: 2 Pages: 149-156
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The present study suggests the introduction of ceramic fillers cabable to react with polystyrene polymer (PS) through mixing .Thus filler material (kaolinite Kao) after washing by distill water and drying and toasting to powder with temperature degree (100°C) and surfactant process of bentonite have been done on them by using poly vinyl alcohol(PVA) and hybrid by adding quaternary ammonium compound (Thac) to onstruct ( hybrid clay) cbable to react with dissolved polystyrene in toluene(Toul) have been added also binder material Tris(hydroxyl methyl) methyl amine and anti-oxidant material(bis dimethyl benzyl) di phenyl amine and study of optical properties to this composite such as absorbance and transmittance and absorbance coefficient ,a calculation were carried out for measuring forbidden energy gap for direct and indirect allowed and forbidden ,also calculation of the optical constant carried out such as extinct coefficient refractive index , and real imaginary part of dielectric constant

تمت في هذه الدراسة ادخال مالئات سيراميكية لها القابلية على التفاعل مع بوليمر بولي ستايرين(PS) بطريقة الخلط فاضيفت المادة المالئة (كاؤولينKao) بعد غسلها بالماء المقطر وتجفيفها وحرقها بدرجة 100 مο ومن ثم تحفيزها بمادة بولي فاينيل الكحول(PVA) وتجفيفها ومن ثم تهجينها باضافة مركب الامونيوم الرباعي(Thac) لتكوين (طين مهجن) قادر على التفاعل مع البولي ستايرين المذاب في التلوين(Toul) ومن ثم اضافة مادة رابطة Tris(hydroxyl methyl) methyl amine ومادة مانع التاكسد(bis dimethyl benzyl) di phenyl amine للخليط وتم دراسة الخصائص البصرية لهذا المتراكب كالامتصاصية والنفاذية ومعامل الامتصاص ، وحسبت فجوة الطاقة البصرية للانتقال المباشر وغير المباشر المسموح والممنوع وتضمنت الحسابات البصرية ايضا حساب الثوابت البصرية كمعامل الخمود ومعامل الانكسار وكذلك تم حساب الجزء الحقيقي والخيالي لثابت العزل الكهربائي.

Keywords


Article
Studying Dielectric Properties of Polystyrene-Bentonite Composite and Effective Parameters
دراسة الخصائص الكهربائية لمتراكب بولي ستايرين - بنتونايت والعوامل المؤثرة فيها

Author: وسن كامل حسن
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2011 Volume: 3 Issue: 2 arabic Pages: 23-28
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Samples of composite material have been prepared by using raw material like poly styrene as matrix material,Bentonite Al-Suffra (filler material),Poly vinyl alcohol (binder material) with the state ratios in the research . After preparing Bentonite powder, it had been choose particle size smaller than (100 μm) and after conducting the toasting process to powder with different temperature degrees (100,200,300,400 οC) have been added to dissolved polystyrene material in tolouene with the state ratios and temperature degrees (70-80 οC) have been used also binder material poly vinyl alcohol (PVA) and have been studied dielectric properties for the material (Impedance, Loss factor,A.C.conductivity,Dielecric constant) and study of effect temperature , rate of filler and frequency in value of dielectric constant .

حضرت نماذج من المواد المتراكبة باستخدام المواد الأولية البولي ستايرين (مادة أساس) وبنتونايت الصفرة (مادة مالئة) وبولي فاينيل الكحول (مادة رابطة) وبالنسب المذكورة في البحث . بعد تهيئة مسحوق البنتونايت تم انتقاء حجم حبيبي اقل من(μm100) وبعد إجراء عملية التحميص للمسحوق بدرجات حرارية (οC 100,200,300,400) إضيفت إلى مادة البولي ستايرين المذابة باستخدام التولوين بنسب معينة وبدرجة حرارة (70-80 οC) مع استخدام مادة رابطة وهي كحول البولي فاينيل (PVA) و درست الخصائص الكهربائية لهذه المادة (الممانعة,عامل الفقد , التوصيلية المتناوبة , ثابت العزل) ودراسة تأثير كل من درجة الحرارة ونسبة المالئ والتردد في قيمة ثابت العزل الكهربائي .

Keywords


Article
A study of the effect of thickness and Gamma Ray on the optical properties of Polystyrene – Kaolinite Composite
دراسة تأثير السمك واشعة كاما على الخواص البصرية لمتراكب بولي ستايرين – كاؤولين

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 10 Issue: 1 Pages: 192-199
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

A study of the effect of thickness on the optical properties of Polystyrene – Kaolinite Composite of thickness (0.86,0.92,1.11) mm prepared by introduction of filler material (kaolinite) to matrix material (polystyrene) after toasting to powder with temperature degree(100 ͦ C)and drying and choose partical size (D<100 μm) and have been used also binder material poly vinyl chloride (PVC) and had been added to dissolved polymer matrix material in benzen with the state ratios and study of effect of thickness for samples after and befor irradiation γ- Ray irradiation from Co60of average energy (2.5 Mev) with radiation dose of (250 KGy) on optical properties for composite material and absorption increase but the transmission decrease as a data of waving length with increase the thickness, as well as it is found that the absorption coefficient of these samples increase with decrease thickness and also calculation of the optical constant carried out such as extinct coefficient , refractive index, reflectance ,real and imaginary part of dielectric constant after and befor irradiation.

تم في هذا البحث دراسة تأثير السمك على الخواص البصرية لمتراكب بولي ستايرين – كاؤولين بسمك mm(0.86،0.92،1.11) المحضرة بإدخال مادة مالئة (الكاؤولين) إلى المادة الأساس (بولي ستايرين) بعد حرقها بدرجة(100 ͦC) وتجفيفها وإعادة طحنها وانتقاء حجم حبيبي (D<100 μm) مع استخدام مادة رابطة هي بولي فاينيل الكحول P.V.C ومن ثم تمت إضافتها للمادة الأساس البوليميرية المذابة في البنزين بنسب معينة ودرس تأثير سمك العينات قبل وبعد تشعيعها بأشعة كاما المنبعثة من مصدرCo60 ذات معدل طاقة (2.5Mev) وبجرعة إشعاعية (250KGy) على الخواص البصرية للمادة المتراكبة حيث تزداد الامتصاصية وتقل النفاذية كدالة للطول الموجي بزيادة السمك بالإضافة إلى زيادة معامل الامتصاص مع نقصان السمك . وتضمنت الحسابات البصرية ايضاً حساب الثوابت البصرية كمعامل الخمود ومعامل الانكسار والانعكاسية كما حسب الجزء الحقيقي والخيالي لثابت العزل الكهربائي قبل التشعيع وبعده .

Keywords


Article
Study of some Mechanical properties for polymer Matrix Composite Material Reinforcement with ceramic fillers
دراسة بعض الخواص الميكانيكية لمادة متراكبة ذات أساس بوليمري بمالئات سيراميكيه

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2013 Volume: 11 Issue: 1 Pages: 126-133
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The present study suggests the introduction of ceramic fillers cabable to react with polystyrene polymer (PS) through mixing .Thus filler material (bentonite) after washing by distill water and drying and toasting with different temperature degrees (100,200,300,400 °C)and surfactant process have been done on them by using poly vinyl alcohol(PVA) and dryig and had been choose partical size smaller than (75 μm) and Polystyrene was dissolved in benzen and then the ceramic fillers was added to polystyrene solution with the state ratios and temperature degrees (70-80 °C)have been used surfactant material to polymer surface and anti-oxidant material and binder material , and the study of effects because of these additions upon mechanical material for composite .

تمت في هذه الدراسة ادخال مالئات سيراميكية لها القابلية على التفاعل مع بوليمر بولي ستايرين(PS) بطريقة الخلط الآلي فاضيفت المادة المالئة (البنتونايت) بعد غسلها بالماء المقطر وتجفيفها وتحميصها بدرجات حرارية مختلفة (100,200,300,400) °C ومن ثم تحفيزها بمادة بولي فاينيل الكحول(PVA) وتجفيفها ومن ثم تم انتقاء حجم حبيبي اقل من (75 um) وتم اذابة المادة البوليمريه ( البولي ستايرين ) باستخدام البنزين , ثم اضيفت لها المادة المالئه بنسب معينة وبدرجة حرارة (70-80 °C) كما تم استخدام مواد محفزة لسطح البوليمرومادة مانع التاكسد ومادة رابطة وتمت دراسة تاثير تلك المضافات في الخواص الميكانيكية للمتراكب.

Keywords


Article
Study of some Mechanical properties for polymer Matrix Composite Material Reinforcement with ceramic fillers
دراسة بعض الخواص الميكانيكية لمادة متراكبة ذات أساس بوليمري بمالئات سيراميكيه

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2013 Volume: 11 Issue: 1 Pages: 126
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The present study suggests the introduction of ceramic fillers cabable to react with polystyrene polymer (PS) through mixing .Thus filler material (bentonite) after washing by distill water and drying and toasting with different temperature degrees (100,200,300,400 °C)and surfactant process have been done on them by using poly vinyl alcohol(PVA) and dryig and had been choose partical size smaller than (75 μm) and Polystyrene was dissolved in benzen and then the ceramic fillers was added to polystyrene solution with the state ratios and temperature degrees (70-80 °C)have been used surfactant material to polymer surface and anti-oxidant material and binder material , and the study of effects because of these additions upon mechanical material for composite .

تمت في هذه الدراسة ادخال مالئات سيراميكية لها القابلية على التفاعل مع بوليمر بولي ستايرين(PS) بطريقة الخلط الآلي فاضيفت المادة المالئة (البنتونايت) بعد غسلها بالماء المقطر وتجفيفها وتحميصها بدرجات حرارية مختلفة (100,200,300,400) °C ومن ثم تحفيزها بمادة بولي فاينيل الكحول(PVA) وتجفيفها ومن ثم تم انتقاء حجم حبيبي اقل من (75 um) وتم اذابة المادة البوليمريه ( البولي ستايرين ) باستخدام البنزين , ثم اضيفت لها المادة المالئه بنسب معينة وبدرجة حرارة (70-80 °C) كما تم استخدام مواد محفزة لسطح البوليمرومادة مانع التاكسد ومادة رابطة وتمت دراسة تاثير تلك المضافات في الخواص الميكانيكية للمتراكب.

Keywords


Article
دراسة تأثير امتصاص الماء لمتراكب بولي ستايرين- بنتونايت

Author: وسن كامل حسن
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 5 Pages: 1590-1599
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Samples of composite materials have been prepared by using raw material like polystyrene as matrix material , Bentonite Al-Sufrra (Filler material), Poly vinyl alcohol (surfactant material to Bentonite)and using surfactant material to dissolved polymer surface with Anti-oxidant and binder material with the state ratios in the research .After preparing Bentonite powder , it had been choose particle size smaller than (100um)after conducting the toasting process to powder with different temperature degrees(200,300,400)οC and surfactant process of Bentonite have been done on them by using Poly vinyl Alcohol .These samples which have been treated by heat and surfactant by using Poly vinyl Alcohol have been added to dissolved polystyrene material in toluene with the state ratios and temperature degrees(70-80)οC have been used also surfactant materials to polymer surface and anti-oxidant material ,and the study of effects because of these additions upon water absorption of composite material and prepared samples of figure cubic as length (1cm) and thickness(2-4mm) for absorption technique and room temperature and had been measure weight any dry samples and then enter in the water and taked weights for (24 hour) after then out of water to measure of water weight absorbed and had been measure of maximum water amount absorbed (for limit satisfied) after(4 days) for different from sample to other and drew figures to explain for that ,also samples of prepared for use to thermal conductivity and dielectric constant and use befor and after to enter the water .

حضرت نماذج من المواد المتراكبة باستخدام المواد الاولية البولي ستايرين (مادة اساس) وبنتونايت الصفرة (مادة مالئة)وبولي فاينيل الكحول (مادة محفزة للبنتونايت) مع استخدام مادة محفزة لسطح البوليمر(POG) المذاب مع مادة مانع للتأكسدومع المادة الرابطة وبالنسب المذكورة في البحث .بعد تهيئة مسحوق البنتونايت تم انتقاء حجم حبيبي اقل من (100um) وبعد اجراء عملية التحميص بدرجات حرارية (200,300,400)οC اجريت عليها عملية تحفيز البنتونايت بأستخدام PVA .ان هذه العينات المعاملة حرارياً والمحفزة بأستخدام بولي فاينيل الكحول تم اضافتها الى مادة البولي ستايرين المذابة باستخدام التولوين بنسب معينة وبدرجة حرارة (70-80)οC كما تم استخدام مواد محفزة لسطح البوليمر ومادة مانع التأكسد ومادة رابطة وتمت دراسة تأثير تلك الاضافات على خاصية أمتصاصية الماء للمادة المتراكبة حيث حضرت عينات مكعبة الشكل بطول ضلع (1cm) وبسمك يتراوح بين (2-4mm) الخاصة بتقنية الامتصاص وبدرجة حرارة الغرفة وتم تثبيت وزن كل عينة وهي جافة ومن ثم غمرت في الماء واخذت اوزانها كل (24 ساعة) بعد اخراجها من الماء لحساب وزن الماء الممتص وتم قياس كمية الماء الممتص العظمى (عند حد الاشباع) بعد مرور (4 أيام) التي اختلفت من عينة لاخرى ورسمت المخططات التي توضح ذلك , كذلك حضرت نماذج قياس التوصيلية الحرارية وثابت العزل الكهربائي وقياس مقدارها قبل وبعد الغمر .

Keywords


Article
A study of sintering temperature effect on the thermal conductivity of Polystyrene – Bentonite Composite
دراسة تأثير درجة حرارة الحرق على التوصيلية الحرارية لمتراكب بولي ستايرين – بنتونايت

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2013 Volume: 11 Issue: 4 Pages: 233-241
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Samples of composite materials have been prepared by using raw material like poly styrene as matrix material , Bentonite AL-Sufrra (Filler material) ,poly vinyl alcohol (surfactant material to Bentonite) and using surfactant material to dissolved polymer surface with Anti-oxidant (bis dimethyl benzyl diphenyl amine) and binder material (Tris hydroxy methyl methyl amine) with different ratios.After preparing Bentonite powder, it had been choose particle size smaller than (75μm) after conducting the annealing process to powder with different temperature (100,200,300,400)°C and surfactant process of Bentonite have been done on them by using poly vinyl Alcohol.These samples which have been treated by heat and surfactant by using poly vinyl Alcohol have been added to dissolved poly styrene material in benzene with the state ratios and temperature degrees (70-80)°C have been used also surfactant materials to polymer surface and anti-oxidant material and binder material , and the study of effects because of these additions upon Thermal Conductivity.

تم تحضيرنماذج المواد المتراكبة باستخدام المواد الاولية , البولي ستايرين (مادة اساس) وبنتونايت الصفرة (مادة مالئة) وبولي فنيل الكحول (مادة محفزة للبنتونايت) مع استخدام مادة محفزة لسطح البوليمر (poly oxy glycols) المذاب مع مادة مانع التاكسد (bis dimethyl benzyl) di phenyl amine مع المادة الرابطة Tris(hydroxyl methyl) methyl amine وبنسب مختلفة .وبعد تهيئة مسحوق البنتونايت تم انتقاء حجم حبيبي اقل من (75 μm) بعد اجراء عملية التلدين للمسحوق بدرجات حرارة مختلفة (100,200,300,400) ͦ C اجريت عليها عملية تحفيز البنتونايت باستخدام بولي فانيل الكحول .إن هذه العينات المعاملة حراريا" والمحفزة باستخدام بولي فاينيل الكحول تم إضافتها إلى مادة البولي ستايرين المذابة باستخدام البنزين بنسب معينة وبدرجة حرارة C°(70-80) كما تم استخدام مواد محفزة لسطح البوليمر ومادة مانع التأكسد ومادة رابطة وتمت دراسة تأثير تلك المضافات في الخواص الحرارية

Keywords


Article
Effect of some mechanical properties on polyethelen - bentonite composite
تأثير بعض الخواص الميكانيكية على متراكب بولي اثيلين – بنتونايت

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2014 Volume: 12 Issue: 4 Pages: 85-97
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The research focuses on the preparation composite material containing Low Density Polyethelene (LDPE) and bentonite clay of grain size (75µm) ,followed by calcinations process at (300,500) ºC ,after that poly vinyl alcohol (PVA) solution prepared and used as a bonded layer covered the bentonite powder befor applied as a filler,pluger injection molding method were used to prepare samples which have filler percentage (2.5,5,7.5,10,12.5)% . Many tests have been done including: (Bending test,Impact,Hardness , Compression strength and Tension) .The research results showed that the values (Bending,Hardness,Compression Strength,Tensile) will increase with the increase of the filler percentage ,in the other hand the values of impact strength will be decrease with the increase of the filler percentage of the all samples used in this research .

تم في هذا البحث تحضير مادة متراكبة مكونة من راتنج البولي اثيلين واطيء الكثافة وطين البنتونايت ذو حجم حبيبي (75µm) واجريت عليه عملية تحميص بدرجات حرارية (300,500) ºC ثم عولج بمادة بولي فاينيل الكحول بوصفها طبقة رابطة لمادة الملء مع البوليمر وقد استعملت عملية الحقن المكبسي لتحضير عينات البحث بنسب وزنية (2.5,5,7.5,10,12.5)% ,اجريت مجموعة من الاختبارات شملت: (الانحناء ,الصدمة,الصلادة,الانضغاط,الشد) للعينات المحضرة.وقد اظهرت نتائج البحث ان قيم (الانحناء,الصلادة,الانضغاط,الشد) تزداد مع زيادة النسبة الوزنية لمادة التدعيم . اما مقاومة الصدمة فان قيمتها تقل مع الزيادة في النسبة الوزنية لمادة التدعيم ولجميع العينات المستعملة في البحث.

Keywords


Article
Effect of Iraqi Bentonite granules addition on physical characteristics for polystyrene
تأثير إضافة دقائق البنتونايت العراقي على الخصائص الفيزياوية للبولي ستايرين

Author: وسن كامل حسن
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Volume: 13 Issue: 1 Pages: 257-270
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Stydy in this research some of physical characterristics (bulk density , volume shrinkage , apparent porosity , water absorption , absorption , transmission , absorbance coefficient, extinct coefficient, refractive index , real and imaginary part of dielectric constant) for different percentages from Iraqi bentonite clay as a filler material for polystyrene polymer . Bentonite clay was prepared as a powder for partical size (75µm) after that surfactant of bentonite have been done on them by using poly vinyl alcohol and hybrid by adding quarternary ammonium compound to contract (hybrid clay) able to react with dissolved polystyrene in toluene. Experimentally, it was found through the measurement for samples , increasing of bentonite percentage lead to increasing of (bulk density , volume shrinkage) . also increasing of bentonite percentage lead to decreasing of (apparent porosity , water absorption) .The optical properties it was found that the values of the transmission and absorption coefficient for the prepared samples hare increased where as values the other optical properties hare decreased for polymer composite

تم في هذا البحث دراسة بعض الخصائص الفيزيائية (الكثافة الحجمية , التقلص الحجمي , المسامية المفتوحة , امتصاصية الماء,الامتصاصية , النفاذية , معامل الامتصاص , معامل انكسار , معامل خمود والجزء الحقيقي والخيالي لثابت العزل) لتراكيز مختلفة من دقائق البنتونايت العراقي كمادة عضوية لبوليمر البولي ستايرين حيث حضر مسحوق البنتونايت ذو حجم حبيبي (75 µm) ثم عولج بمادة بولي فاينيل الكحول ومن ثم تم تهجينها باضافة مركب الامونيوم الرباعي لتكوين (طين مهجن) قادر على التفاعل مع البولي ستايرين المذاب في التلوين . وجد عمليا من خلال القياسات ان قيم (الكثافة الحجمية , التقلص الحجمي) للنماذج تزداد مع زيادة نسبة البنتونايت المضافة . وقيست قيم (امتصاصية الماء , المسامية المفتوحة) فقد قلت بزيادة نسبة البنتونايت المضاف . اما الخواص البصرية فتزداد قيمتها كالنفاذية ومعامل الامتصاص للعينات المحضرة اما بعض الخواص البصرية المتبقية فتقل قيمها للمتراكب البوليمري .

Keywords


Article
دراسة الخواص البصرية الخطية وغير الخطية لمتراكب بولي فاينيل كلورايد - بنتونايت باستخدام تقانة المسح على المحور الثالث

Author: وسن كامل حسن
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 1 Pages: 368-377
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The spectral characteristics and nonlinear optical properties of composite poly vinyl cloride – b entonite have been determined. The spectral characteristics are studied by record fluorescence spectra and calculations were carried out to determine the linear optical constants such as absorption coefficient (αº) , extinct coefficient (k) , linear reflect coefficient (R) and linear refractive index (n) . The non linear optical properties were measured by Z- scan technique using He-Ne laser with (632.8 nm) wave length . The non linear refractive index and absorbtion coefficient are found in order of (1.9*10-7 cm2 /mWatt),( 0.1193cm /mWatt) respectively . These results show that the sample can be applied in non linear optics

تم في هذا البحث تحديد الخواص الطيفية والخواص البصرية اللاخطية لمتراكب بولي فاينيل كلورايد – بنتونايت. درست الخواص الطيفية بتسجيل اطياف الانبعاث وحساب الثوابت البصرية المتمثلة بمعامل الامتصاص الخطي (αº) ومعامل الخمود (k) ومعامل الانعكاس الخطي (R) ومعامل الانكسار الخطي(n) .اما الخواص البصرية اللاخطية فتم قياسها بواسطة تقانة المسح على المحور الثالث (Z – scan) باستخدام لليزر هيليوم – نيون عند الطول الموجي (632 nm). وقد وجد ان معامل الانكسار اللاخطي ومعامل الامتصاص اللاخطي يساوي( 1.9*10-7) سنتمتر مربع / ملي واط و (0.1193) سنتمتر / ملي واط على التوالي. هذه النتائج اظهرت ان العينة ذات الخواص البصرية الخطية وغير الخطية يمكن استخدامها في التطبيقات مجال الالكتروبصريات.

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

Arabic (7)

Arabic and English (3)

English (1)


Year
From To Submit

2015 (4)

2014 (1)

2013 (3)

2012 (2)

2011 (2)