Dielectric behavior and AC electrical conductivity analysis of PMMA films
التوصيلية الكهربائية المتناوبة لأغشية PMMA

Authors: Ikhlas H.Shalal اخلاص هميم شلال --- Bushra A.Hasan بشرى عباس حسن
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2013 Volume: 11 Issue: 20 Pages: 47-57
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

PMMA films of different thickness (0.006, 0.0105, 0.0206, 0.0385 and 0.056cm) were synthesized by casting process. The temperature and frequency dependence of dielectric constant and AC electrical conductivity measurements at various frequencies (10kHz-10MHz) and temperatures (293-373K) were carried out. Few anomalies in dielectric studies were observed near 313 and 373 K respectively. These points were related to glass transitions temperature. The variation of activation energy and conduction behavior was studied .From the AC conduction studies, it is confirmed that the mechanism responsible for the conduction process is hopping of carriers. The variations of the dielectric constant and loss as function of frequency at different temperature was observed and the results were discussed. The calculated activation energy varied with the thickness, temperature, and applied frequency. Conductivity plots against frequency suggested that the response obeying the universal power law concerning the AC conductivity and dielectric behavior of polymer. The polarizability  increases with temperature but decreases with thickness indicating weekends and rising of intermolecular forces respectively.

حضرت أغشية من بولي مثيل اكرليت وبأسماك مختلفة بواسطة طريقة الصب.أجريت قياسات التوصيلية الكهربائية المتناوبة ( σa.c(w في مدى درجات الحرارة(293-373)K وفي مدى التردد (107-104Hz). لوحظ سلوك غير اعتيادي في دراسة معامل العزل والذي اعزي إلى درجة حرارة التحول الزجاجي .تم دراسة تغير سلوك التوصيل الكهربائي وتأثيره على طاقة التنشيط. أظهرت النتائج إن ميكانيكية التوصيل المسوؤلة عن التوصيل هي التنطط.القيم المحسوبة لطاقات التنشيط تغيرت مع السمك, التردد ودرجة الحرارة. علاقة التوصيل الكهربائي مع التردد آسية تؤكد التوصيل المتناوب والسلوك العزلي للبوليمروالاستقطابية ازدادت مع درجة الحرارة بينما تناقصت مع زيادة السمك والذي يشير إلى ضعف وزيادة قوى الترابط الجزيئي وعلى التوالي.


Article
The Effect of the (Se) percentage on Compositional, Morphological and structural properties of Bi2(Te1-xSex)3 thin films
تأثير نسبة (Se) على الخواص السطحية والتركيبية لاغشية Bi2(Te1-x Sex)3 الرقيقة

Loading...
Loading...
Abstract

Alloys of Bi2[Te1-x Sex]3 were prepared by melting technique with different values of Se percentage (x=0,0.1,0.3,0.5,0.7,0.9 and 1). Thin films of these alloys were prepared by using thermal evaporation technique under vacuum of 10-5 Torr on glass substrates, deposited at room temperature with a deposition rate (12nm/min) and a constant thickness (450±30 nm).The concentrations of the initial elements Bi, Te and Se in the Bi2 [Te1-x Sex]3 alloys with different values of Se percentage (x), were determined by XRF,The morphological and structural properties were determined by AFM and XRD techniques. AFM images of Bi2[Te1-x Sex]3 thin films show that the average diameter and the average surface roughness increase with the increase of the percentage of Se. The X–ray diffraction measurements for bulk and thin films of Bi2[Te1-xSex]3 have polycrystalline structure with rohmbohedral structure, with space group R3m, and a strong (015) preferred orientation, the crystallite increase with the increase of Se percentage .

تم تحضير سبائك المركب Bi2(Te1-x Sex)3 بعملية صهر المواد الاولية وفق نسب مختلفة لنسبة السيلينيوم (x=0 , 0.1 ,0.3 ,0.5 ,0.7,0.9 and 1). الاغشية الرقيقة لهذا المركب تم تحضيرها باستخدام تقنية التبخير الحراري تحت ضغط فراغ يصل الى 10-5 torr)) حيث تم ترسيب المادة على قواعد زجاجية نظيفة في درجة حرارة الغرفة بمعدل ترسيب((12nm/min بسمك ((450±30 nm. . قد تم التأكد من نسب المواد الأولية (Bi ,Te and Se) باستخدام جهاز فلورة الاشعة السينينة XRF , اما الخواص التركيبية للسبائك والاغشية الرقيقة لمركب Bi2(Te1-x Sex)3 باختلاف نسبة السيلينوم فيها بواسطة جهاز حيود الاشعة السينية XRD اما الخواص السطحية للاغشية الرقيقة تم فحصها باستعمال جهاز AFM وقد وجد ان اقطار الحبيبات تزداد بزيادة نسبة السيلينيوم فيها وكذلك يزداد معدل الخشونة فيها ان قياس حيود الاشعة السينية وجد ان السبائك والاغشية الرقيقة لها تركيب متعدد التبلور ذو تركيب سداسي وفسحة مجموعة R3m وكانت القمة السائدة والاقوى هي (015) وكذلك بينت ان حجم البلوريات يزداد بزيادة نسبة السيلينيوم في المركب .

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

Arabic and English (1)

English (1)


Year
From To Submit

2017 (1)

2013 (1)