Production Composite Materials by Fused Deposition Method
استخدام طريقة الغمرأو (التغطيس) لانتاج مواد متراكبة

Authors: نوال عزت عبد اللطيف --- اسراء عبد القادر
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2007 Volume: 25 Issue: suppl.of No.2 Pages: 44-60
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this research is to produce composite materials with ceramic basecovered by a layer of (Al) and its alloys by means of fused deposition technique.This technique represents new method and combines the powder technology withthe casting technique. Al2O3 poweder was used after having been pressed bydifferent pressure(58,117 and 176 MPa) in metal molds. The sintering process hasbeen preformed at 1100 o C for two hours. After that, the porosity percentage hasbeen measured and the samples were immersed in the molten metals heated to 700oC . Ultirnatly, these samples were heated to about 1000 o C by a furnace for half anhour. Then,the samples were cooled to 650 oC and examined by an opticalmicroscope and the scanning electron microscope. Moreover, the x-ray diffractionfor these sample has been employed to define the structure of the resultingcomposite as well as to define the resulting bond between the deposited metal layerand the ceramic matrix in addition to characterize the existing phases within thecomposite material.

يهدف البحث الى أنتاج مواد متراكبة ذات أساس من سيراميك مح اط بطبقة معدنية منوهي تقنية تجمع ( Fused deposition method) الالمنيوم اوسبائكه باستخدام طريقة التغطيسمابين تكنولوجيا المساحيق وتقنية السباكة . تم استخدام مسحوق الالومينا بعد أن تم كبسه في176,117,58 ) ثم أجراء عملية التلبيد )MPa قوالب معدنية تحت ضغوط كبس مختلفة1100 ) ولمدة ساعتين . وبعد حساب نسبة المسامية للنماذج OC) عند درجة حرارة (Sintering)700 O ) السيراميكية الملبدة تم غمرها بالمنصهرات المعدنية التي تم تسخينها الى درجة حرارة1000 ) ولمدة نصف ساعة. OC) وبعد عملية الغمر تم التسخين داخل الفرن الى درجة حرارة (C650 ). أجري الفحص المجهري بأستخدام المجهر OC ) بعدها تم تبريد المنصهر الى حرارةالضوئي والمجهر الالكتروني الماسح وكذلك الفحص بأستخدام حيود الأشعة السينية لمعرفةتراكيب المواد المتراكبة الناتجة أضافة الى الربط الناتج مابين طبقة المعدن المترسب والجسمالسيراميكي اضافة الى تحديد الاطوار المتكونة في المادة المتراكبة . اظهرت نتائج الفحصأمكانية نجاح عملية التغطيس بمنصهر سبيكة ( الالمنيوم – مغنيسيوم ) في الحصول على موادمتراكبة من السيراميك والمعدن وبشكل طبقات ،كما لوحظ أن قوة الربط مابين الجسم السيراميكيوالمعدن المترسب يعتمد على نسبة المغنيسيوم في المنصهر المعدني ،ويعتمد كذلك على تكوينالناتجة من تفاعل الالومينا مع المغنيسيوم والتي تؤدي الى زيادة MgOAl2O الأطوار الفقرية 3الربط مابين السيراميك والمعدن.


Article
STUDYING THE EFFECT OF REINFORCING BY SICP ON THE DRY SLIDING WEAR BEHAVIOR AND MECHANICAL PROPERTIES OF AL- 4% CU MATRIX ALLOY
دراسة تأثير التقوية بواسطة دقائق كربيد السليكون على البلى الانزلاقي الجاف والخواص الميكانيكية لسبيكة ذات أساس من المنيوم -4% نحاس

Author: Israa A. K. اسراء عبد القادر
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2013 Volume: 6 Issue: 2 Pages: 139-153
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research is devoted to study the effect of addition of different weight percent from SiCp ( 2, 4, 6, 8 ) to Al– 4 Cu alloy which have been fabricated by liquid metallurgy method on the dry sliding wear behavior and mechanical properties. Wear characteristics of Al–SiC composites have been investigated under dry sliding conditions and compared with base alloy. Dry sliding wear tests have been carried out using pin-on-disk wear test under normal applied loads 5, 10, 15 and 20 N and at different sliding velocity of (2.7, 3.7, 4.7) m/sec. It was also observed that the wear rate varies linearly with increases normal applied load but lower in composites as compared to the base material. The wear mechanism appears to be oxidative for both Al – Cu alloy and composites under the given conditions of load and sliding velocity as indicated by optical microscopic of the worn surfaces. Further, it was found from the experimentation that the wear rate decreases linearly with increasing weight percent of silicon carbide. The best results have been obtained at 8 % wt SiC . We also observed that the yield strength, tensile strength increases with increasing wt% of SiC , but the ductility decreases.

يهدف البحث إلى دراسة تأثير إضافة دقائق من كربيد السليكون بنسب مئوية وزنية مختلفة (2,4,6,8 ( على سلوك البلى الانزلاقي الجاف والخواص الميكانيكية لسبيكة ذات أساس المنيوم. وهذه المواد المتراكبة تم تصنيعها بطريقة (liquid metallurgy ) . إن اختبار البلى الانزلاقي الجاف تم إجراؤه باستخدام تقنية المسمار على القرص حيث تم تسليط أحمال 5,10,15,20 نيوتن وسرع انزلاقية مختلفةm/sec ( 2.7,3.7,4.7) . وقد تبين من النتائج ان معدل البلى يتغير خطيا " بشكل عام ,حيث ابدت المادة المتراكبة المقواة بدقائق كربيد السليكون وبنسبة 8 wt% أعلى مقاومة للبلى مقارنة" مع المواد المتراكبة الاخرى والسبيكة الأساس. إن آلية البلى تبدو اوكسيدية لكل من السبيكة الأساس والمواد المتراكبة عند تسليط احمال وسرع انزلاقية مختلفة . كما تبين من الفحص بالمجهر الضوئي للسطح المتضرر ان معدل البلى يتناقص بشكل خطي مع ازدياد النسب المئوية الوزنية لكربيد السليكون وقد أعطت المادة المتراكبة المقواة بنسبة 8wt% أعلى مقاومة للبلى . وقد تبين ان الصلادة , مقاومة الشد القصوى ومقاومة الخضوع تزداد مع ازدياد النسب المئوية الوزنية لكربيد السليكون , وبينما المطيلية تنخفض .


Article
EFFECT OF Ti AND Sn ADDITIONS ON MECHANICAL PROPERTIES OF ALUMINUM- SILICON - COPPER ALLOY
تأثير اضافة Ti و Sn على الخواص الميكانيكية لسبيكة الومنيوم – سليكون - نحاس

Authors: Muhammad A. Fakhri --- Israa A. Alkadir اسراء عبد القادر عزيز
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2016 Volume: 9 Issue: 4 Pages: 48-61
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research is devoted to study the effect of adding alloying elements (Ti and Sn) with different percentages (1, 3 and 5) wt% on the microstructure, mechanical properties, and dry sliding wear resistance of Al-6.9wt%Si-1.7%Cu alloy.The particle size of Ti powder is 200 µm, but the Sn adding as a small bits to the alloy. The microstructures were examined with optical microscope for the base alloy before and after adding alloying elements. This examination showed that the changing occurs on the morphology of grain, precipitated intermetallic compounds and other phases (TiAl, TiAl2, Al2Cu and β-Sn) determined by the x-ray diffraction. The mechanical properties studied in this research were the tensile strength, impact toughness, and hardness. The results depicted that the ơu, ơy and hardness increase with increasing the percentage of Ti, while they decrease with increase the percentage of Sn. On the other hand, the alloys with Ti additions revealed that El% decrease with increasing Ti additions, but El% increase with increasing the Sn addition to the base alloy. Also, the impact toughness, was examined, and it was found alloying element was lower than the base alloy for both elements (Ti and Sn). The pin-on-disk technique was used to determine the wear resistance for base alloy before and after adding the alloying elements. The wear resistance increased with increasing the percentage of the Sn, but it decreased with increasing the percentage of Ti at different applied loads (2.5, 5 and, 7.5) N at a constant sliding speed of (3.7) m/sec.