Article
سلوك أنواع مختلفة من الاسمنت المحلي والمستورد كمادة انهاء

Author: جبار علي لفته
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 3 Pages: 603-616
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

That is absolutely necessary and the need for and use of cement in the end it became necessary to conduct laboratory tests for this article to find out its mandate despite the fact that there is control of the quality of materials produced for this article in the labs .So I saw of national duty and humanitarian study of the properties of some types of cement and give guidance for users to choose the best quality by conducting laboratory tests to this article, so I took four samples of cement, two local (bridge and north) and the other imported from (the UAE and the Gulf) has been conducting chemical analysis and physicist, as shown in the table (1) and (2) The research has included conducting several tests of cement mortar to select four different types of cement for three mixing ratio as shown in Table (3), namely, (1:1.5), (1:2), (1:3) and water to cement ratio w/c=40% were examined operator of the mortar soft (flow and stiffness) and density of wetlands and absorption of age (3) days and the dry density of age (1) days compressive strength and tensile at old (7,28)days which tests in three treatments (with air, water and oven) has been screening in the laboratory of concrete/at technical institute Musayib, Results show that(flow=700mm) and stiffness primary device Viket (12) minutes and hardening the final (27) min and this is identical to the specifications Iraq's number(5) for the years (1984), corresponding to the specification of the (BS-146-1973) and (ASTM-C595-1985) and the compressive strength of age (28) days with water treatment was better to have reached (28.31 Mpa) and tensile strength of age (28) days with water treatmenteqal (5 Mpaacoording toIraq number (5) for the year 1984. So investors and users are advised to make sure of the type and quality of cement used in order to get high workability, high strength and high durability

بالرغم من أن هنالك سيطرة نوعية للمواد المنتجة لهذه المادة في المعامل. ات ألمختبريه لهذه المادة لمعرفة صلاحياتها الوطني والإنساني دراسة خواص بعض أنواع الاسمنت وإعطاء التوجيه للمستخدمين لاختيارلذا رأيت من الواجب أن الضرورة القصوى والحاجة لمادة الاسمنت واستعمالها في الإنهاء أصبح من الضروري إجراء الفحوص أفضل نوعيه من خلال إجراء الفحوصات ألمختبريه لهذه المادة لذا أخذت أربع نماذج من الاسمنت اثنان محليه (الجسر والشمالي) والأخرى مستوردة من (الإماراتي و والخليجي) حيث تم أجراء التحليل الكيميائي و الفيزيائي وكما مبين بالجدول (1) و(2).وقد تضمن البحث أجراء عدة فحوصات مختبرية لمونة السمنت للأربع الأنواع من السمنت بثلاثة نسب خلط وكما مبين بالجدول(3) وهي (1.5:1) ,(2:1) ,(3:1) وثلاثة معالجات( بالهواء, بالماء, بالفرن) وتم الفحص بعمر(7,28 يوم) وتم فحص عامل التشغيل (اللقوام والأنسيابو فحص الامتصاص والكثافة الرطبه والكثافة الجافة بعمر يوم وفحص الانضغاط لمكعبات (5*5*cm5) وبعمر (28,7يوم) وفحص الشد النماذج الجافه وكانت نسبة الماء (w/c) لجميع الخلطات(40%) وتم الفحص في مختبر الخرسانة للقسم المدني/المعهد التقني المسيب وقد كانت النتائج الاسمنت المستورد (الخليجي) أفضل النتائج حيث بلغ الأنسياب (flow=700mm) والتصلب الابتدائي بجهاز فليكات (12) دقيقه و التصلب النهائي (27) دقيقه وهذا مطابق للمواصفات العراقية رقم (5) لعام (1984) والمطابق للمواصفات البريطانية القياسية (B.C-146-1973) ومطابق للمواصفات الامريكيه (ASTM-C595-1985) ومقاومة الانضغاط بعمر ( 28يوم) والمعالجة بالماء قد بلغت (28.31 Mpa) ومقاومة الشد بعمر (28يوم)والمعالجة بالماء بلغت (5Mpa) وكانت مطابقة للمواصفات العراقية القياسية (5) لعام1984.لذا ننصح المستثمرين والمستخدمين الاسمنت المستعمل من اجل الحصول على قابلية تشغيل عاليه ومقاومه عاليه ومتانة عالية .


Article
أنتاج بلاطات خرسانية عالية المقاومة بأستخدام برادة الحديد المحلية كبديل جزئي عن السمنت بإضافة الملدن S.B.R.

Author: جبار علي لفته
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 4 Pages: 749-758
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research includes production ties with high strength concrete by using iron filing . Resulting from remnants of refrigerator for laboratories civil , which passing from sieve (4.75)mm partial substitute for cement which was used four mixture of three ties of concret mixture (B=25%), miture (C=50%) ,mixture (D= 75%). As replacement by weight of cement..and compare with reference (Mix.A) . and the labrotatory test sample as flowing:- 1-Fresh concrete was examind by precipitation of concret and the results as flowing (Mix.B = 95 mm) , (Mix.C=90mm),(mixD=85mm) compare with (Mix.A) which gives (100mm) .2-Hardend concret was examend with comprsive strength cupice modelse (10*10*10)cm , the (Mix.B =48 mpa), (mix.C =43.5 mpa),(mix.D =39.25Mpa) compare with reference mixture (Mix.A) give (45 mpa) at (28 day).The strength increase at late time (60day), is reached (59.5Mpa) for mix .B , the Mix.C=51.25 Mpa , the Mix.D=40.15 compare with reference sample (A=52.45 Mpa). when modulus of rupture for ties with dimension (40*40*5)cm of (Mix.B=5.5 Mpa) , (Mix.C=4.5 Mpa)m(Mix.D=3.5 Mpa) compare with reference Mix (A) =(4.75 Mpa) at edge 28 day.3-The modulus of rupture for ties (40*40*5)cm shows the results samples mixture B=35Mpa lest mixture C= 45Mpa lest mixture D=3.25Mpa compare with reference (A=4.75)Mpa at age (28)days .All of these tests to increasing result with the percentage (50%) but decrease percentage (75%) because of reducing of cohesive of the steel mixture concrete these crush steel concrete have stiffness and hardness but have not cohesive.

يتضمن هذا البحث أنتاج بلاطات لخرسانة عالية المقاومة بأستخدام برادة الحديد الناتجة من بقايا البرادة للمعامل الأهلية والعابرة من منخل حجم (4.75 ملم) كبديل جزئي عن السمنت حيث أستخدم أربعة خلطات لثلاثة بلاطات خرسانية الخلطة (B: 25%), الخلطة (C:50%), الخلطة (D:75%) كنسبة وزنيه من السمنت ومقارنتها مع الخلطة المرجعية (A) .1-وتم فحص الخرسانة الطرية :- فحص الهطول للخرسانة الطرية كان مقداره للخلطة (B:95سم), الخلطة (C:90سم), الخلطة (D:85 سم) مقارنةً بالخلطة المرجعية ذات الهطول (100سم). 2-مقاومة الأنضغاط للنماذج لمكعبة (10*10*10) فقد أعطت الخلطة (B) نسبة أنضغاط مساوية ومقاربة للخلطة المرجعية وبعمر (28 يوم) بلغت(48) ميكاباسكال بينما أعطت الخلطة (C) مقاومة (43.5) ميكاباسكال وأعطت الخلطة (D) مقاومة 39.25)) ميكاباسكال مقارنة بالخلطة المرجعية التي أعطت (45) ميكاباسكال.3- مقاومة الشد فقد أعطت الخلطة (B) مقاومة (6.55) ميكاباسكال وهي أعلى نسبة تليها الخلطة (C) ثم الخلطة(D) مفقارنة بالخلطة المرجعية التي حققت مقاومة قدرها (5.65) ميكاباسكال.وقد أزدادت المقاومة بالأعمار المتأخرة وصلت الخلطة (B الى 59.5) ميكاباسكال وللخلطة (C الى 51.25) ميكاباسكال والخلطة (Dالى 40.15) مقارنةً بالخلطة المرجعية التي حققت أنضغاطاً (52.92) ميكاباسكال.4- فحص معايير الكسر للبلاطات بأبعاد (40*40*5) سم فأعطت البلاطات الخرسانية للخلطة (B) معامل كسر(5.30) ميكاباسكال بينما بلغ معايير الكسر للخلطة (C) (4.5) ميكاباسكال والخلطة (D=3.25) مقارنة بالخلطة المرجعية البالغة (4.75) ميكاباسكال وبعمر 28 يوم.جميع الفحوصات أعطت زيادة بالنتائج بنسبة أحلال (50%) وأنخفضت نسبة الأحلال الى (75%) بسبب قلة اللزوجة لخرسانة البرادة الناتجة لكون خرسانة البرادة تمتلك الصلادة والقوة لكن لاتمتلك اللزوجة.


Article
The effect Musayyib thermal power station waste water on some physical and chemical properties of the Euphrates River water
تأثير مخلفات محطة كهرباء المسيب الحرارية على بعض الخواص الفيزيائية والكيميائية لمياه نهر الفرات

Authors: Qais Hatem قيس حاتم محمد --- Ameer Hashim امير هاشم حسين --- Jabbar Ali جبار علي لفته
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2014 Volume: 7 Issue: 4 Pages: a221-236
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This research deals with analyzing for samples from Euphrates River before and after the power plant of Mussaibe. Standard methods are used to find electric conductivity, PH, turbidity, hardness, chloride, alkality, total suspended solid and total solid.The study takes twelve months during 2009, such that one sample was taken in the first day of the month represents the monthly value. The samples were taken from Euphrates river before the plant and after the the plant by 50m, 200m, 500m and 1000m from outflow of the plant.The study shows the effect of the plant on the properties that taken in the study. The study contains also effect the plant on the irrigation water properties (electric conductivity, total solid)

يتضمن البحث دراسة تحليلية لعينات من نهر الفرات قبل وبعد محطة كهرباء المسيب الحرارية. استخدمت طرق قياسية لتقدير كل من التوصيل الكهربائي، الأس الهيدروجيني، الكدرة، العسرة، الكلورايد، القاعدية، المواد الصلبة العالقة والمواد الصلبة الكلية.أجريت الدراسة لسنة واحدة وهي سنة 2009 حيث أخذت عينة واحدة في اليوم الأول من كل شهر مثلت القيم الشهرية. أخذت العينات قبل وبعد منطقة الطرح للنهر وعلى ابعاد 50م, 200م, 500م, 1000م.أظهرت الدراسة تأثر بعض الخواص التي تم قياسها بمياه المخلفات التي تطرحها المحطة. وتبين حدوث تغير في جميع الخواص وتميل هده الخواص الى العودة الى قيمها قبل المحطة كلما ابتعد النهر عن موقع الطرح. وتنطوي الدراسة على مقارنة بعض الخواص التي تم قياسها بمتطلبات مياه الري (خاصيتي التوصيل الكهربائي وكمية المواد الصلبة الكلية).

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

Arabic (3)


Year
From To Submit

2015 (1)

2014 (2)