دراسة تأثير الضغط المسلط على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 باستخدام السباكة بالعصر

Author: د. فاروق منصور مهدي د. نجيب سلمان عبطان سعد رمضان احمد
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2013 Volume: 20 Issue: 4 Pages: 11-17
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This present study shows ,the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Alumium alloy A380 was studied .From fig(5) its clear that ,the microstructure of prepare casting samples consist of two phases hard eutectic (Al-Si) and Primary α-Al.The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84)MP

تم في هذا البحث دراسة تاثير الضغط المسلط ضمن المدى (10-84) ميكاباسكال خلال عملية السباكة بالعصر المباشر على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 من الخردة , تبين من خلال البنية المجهرية ان البنية تتكون من طورين هما طور اليوتكتك الصلد وطور الالمنيوم الاولي وكذلك وجدنا من خلال علاقة الضغط المسلط وكسر المساحة لطور اليوتكتك ان نسبة كسر المساحة تزداد عند الضغوط (68,84) ميكاباسكال بينما قلت هذه النسبة عند الضغوط (10,17,34) ميكاباسكال . ومن خلال دراسة العلاقة بين الضغط المسلط بمدياته الخمسة والكثافة الحقيقية نلاحظ زيادة الكثافة بزيادة الضغط المسلط (10-17) ميكاباسكال وكذلك عند الضغط (84) ميكاباسكال.