Article
Study the Rates of Corrosion in Aluminium Reinforced By Silicon Carbide
دراسة معدلات التأكل لمكبوسات الالمنيوم المدعمة بمادة كاربيد السيليكون

Authors: محمد سعيد وحيد --- سدير موفق مجيد
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 18 Pages: 834-846
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work production of aluminium matrix composites with silicon carbide (α-SiC) as reinforcement material were fabricate, the particle sizes of (SiC) used were (500μm- 250 μm and125 μm), with weight percentage of (7.5% - 10% - 15%) from silicon carbide for eachparticle size. The single action pressing was used as one of P/M methods then followed by sintering process at temperature of 450 ºC. The samples subjected to the electrochemical corrosion test at room temperature.The medium of corrosion was solution of 3% weight (NaCl+distilled water)solution. It is found from the photograph microscopy and the results test that all samples which reinforced by(SiC) particles have a(craves or pit) which caused by the particles that act as a cathode sites , and when the size and the percentage of particles increase the Icorr through it also increase as shown in the result.

في هذا العمل حضرت مادة متراكبة ذات اساس من الالمنيوم وبأستخدام كاربيد السيليكون -250μm-125 μm) كمادة مدعمة, حيث تم اضافة دقائق كاربيد السيليكون بأحجام مقدارها 7.5 ) واستخدمت طريقة % -10%- 500 ) وبنسب اضافة وزنية مختلفة مقدارها (% 15 μm (Powder metallurgy) الكبس الاحادي للتصنيع كواحدة من طرق ميتالورجيا المساحيق 450 ومن ثم اجري فحص التأكل الكهروكيميائي تحت ºC بعد ذلك تم تلبيد النماذج بدرجة تاثير وسط ملحي بنسبة (% 3 ) وبدرجة حرارة الغرفة ولكل النماذج المصنعة . وجد من التصوير المجهري ونتائج الاختبار ان جميع النماذج المدعمة بدقائق كاربيد السيليكوننتيجة لكون ان الدقائق قد شكلت مواقع لحدوث تفاعل (Pitting) قد ظهر عليها التنقر او الحفر الاختزال وكلما زادت نسبتها وحجمها الدقائقي زادت قيمة التيار المار خلالها ويتبين ذلك من النتائج.


Article
The Mechanical Properties of Aluminum Matrix Composites
الخواص الميكانيكية لمتراكب ذات اساس من الالمنيوم

Authors: محمد سعيد وحيد --- سدير موفق مجيد
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 15 Pages: 517-523
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work is production of aluminum matrix composite by powder metallurgy method .The samples have done when aluminum powder was used as a matrix in purity of (9.99%) and silicon carbide(α-SiC) as reinforcement material, the particle sizes were used which (125μm) at weight percentage (7.5% - 10% - 15%) from silicon carbide for each particle size. The purpose is to improve the hardness and wear properties of matrix .It was found that the hardness is increased with increment of the amount of added particles, due to the hardness of silicon carbid particles. From the wear test, it is found that the wear resistance increase with increasing the weight percentage of SiC particles, but the wear rate increase when the applied load increase for all the particles size and additional percentage. Also, it is found that when the sliding velocity increases, the wear rate also increases, but the best results were found in samples reinforced with (SiC) particles

تم تصنيع مادة متراكبة ذات اساس من الالمنيوم باتباع ميتالورجيا المساحيق اذ استعمل كمادة (α - SiC) الالمنيوم بنقاوة (% 99.9 ) كمادة اساس معدنية , وكاربيد السيليكون نوع الفا . (15% -10%- 125 ) بنسب وزنية هي (% 7.5 m m) تدعيم وبحجم دقائقي مقداره ان الغاية الرئيسية هي تحسين خاصية مقاومة البلى والصلادة للمادة الاساس . حيث وجد ان الصلادة تظهر زيادة بقيمتها بزيادة نسبة اضافة دقائق كاربيد السيليكون لكون هذه الدقائق ذاتصلادة عالية. اما من فحص مقاومة البلى فلقد وجد ان مقاومة البلى تقل مع زيادة الحمل المسلط نتيجة زيادة قوة الاحتكاك و بالتالي زيادة التشوه الحاصل ما بين سطح العينة والقرص, وقد كانت اصغر مقاومة للبلى عند العينات غيرالمدعمة بدقائق كاربيد السيليكون الا ان اعلى مقاومة للبلى وجدت عندالعينات المدعمة بدقائق كاربيد السيليكون وتزداد بزيادة نسب اضافتها .اما تأثير سرعة الانزلاق على مقاومة البلى فقد وجد انها تزداد بزيادة نسبة اضافة دقائق كاربيد السيليكون الاان زيادة سرعة الانزلاق تؤدي الى زيادة معدلات البلى للمادة المتراكبة نتيجة زيادة الشغل والازاحة التي تتحركها العينة