Influence of the Polymer Styrene Butadiene Rubber on Some of Clay Brick Properties
تأثير البوليمر (Styrene Butadiene Rubber) على بعض خواص الطابوق

Authors: هدى كريم حسين --- حيدر عادل عبد الحميد --- قيس جواد فريح
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 1 Pages: 55-65
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the improvement of clay brick durability by using twomethods of treatment, the first one by coating with Styrene Butadiene Rubber(Polymer) solution and the other by submerging bricks in polymer solution forvarious periods.The results showed that using coating method causes a slight increase in thecompressive strength with a maximum percentage of 3.8% for both yellow andgreen brick in comparison with untreated bricks, while the compressive strengthfor the two types of the brick reduced when they treated using submergingmethod, the percentage of reduction increases by about 26% and 7% for yellowand green brick respectively at submerged period of 24 hours.The results also indicated that no efflorescence appears for all treated bricks(treated by coating and submerging methods for all periods) and a decrease inabsorption with maximum percentages of 26.8% and 14.5% for yellow and greenbricks respectively when the specimens submerged in polymer solution for 24hours. All the results were compared with tested samples untreated with polymersolution.


Article
INFLUENCE OF COOLING METHODS ON THE COMPRESSIVE STRENGTH AND ABSORPTION FOR THERMOSTONE EXPOSED TO FIRE
تأثير طرق التبريد على خواص التحمل والامتصاص للثرمستون المعرض لحالة حريق

Authors: قيس جواد فريح --- فيصل كاظم عبد الحسين --- اسيل شعبان منسي
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2012 Volume: 25 Issue: 1 Pages: A 81-A 93
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

The research included two tests, compressive strength and absorption on two different types of thermostone ,first type without finishing , second with juss and gypsum finishing, tests were done on these samples under regular and high degree of temperature (300,400,500)C° as heated samples were tested and left to cool in air and then in water to simulate the fire condition. Results showed, compressive strength of thermostone reduce with the percentage of changes in temperature and the finishing layers depending on the changes of cooling condition as percentage of reducing in compressive strength increased with the increasement of temperature for the samples without finishing , the higher percentage was 29% at temperature 500 C° and the existence of finishing layers reduces the effect of heat on compressive strength the percentage reduction was (51.8,15,19.8)% for temperature (300,400,500) C° respectively ,for cooling condition , the thermostone samples exposed to high heat after cooling in water showed a specific reduce in compressive strength in high percent comparing with heated samples which cooled with air . the results also showed the absorption percent for samples without finishes is higher than those samples after removing finishing with temperature (,400,500)C° was (7.95,6.43)% respectively, the absorption percent of thermostone was only measured, so there was no possibility to measure it at (300)C° that means the presence of finishing reduces water absorption of thermostone .

تضمن البحث فحصين هما فحص مقاومة الانضغاط وفحص الامتصاص على نوعين من نماذج الثرمستونالأول يكون بدون انهاءات والثاني مع الإنهاء بمادة الجص والبورك , حيث تم إجراء الفحوصات على هذه النماذج٥٠٠ ) م° حيث تفحص النماذج وهي ساخنة ، ٤٠٠ ، في درجة الحرارة الاعتيادية وفي درجات حرارة عالية ( ٣٠٠وعندما تكون بدرجة حرارة الغرفة بعد تركها لتبرد بالهواء و بعد تبريدها بالماء كمحاكاة لحالة الحريق.اظهرت النتائج ان مقاومة الانضغاط للثرمستون تنخفض بنسب تتغير بارتفاع درجة حرارة التسخين وبتغيرحالات الانهاء وبتغير حالة التبريد حيث زادت نسبة النقصان في مقاومة الانضغاط بارتفاع درجة الحرارة للنماذجبدون انهاء حيث كانت اعلى نسبة هي ٢٩ % عند درجة حرارة ٥٠٠ م° كما ان وجود الانهاء في البناء يقلل كثيرامن تاثير الحرارة على مقاومة الانضغاط حيث كانت نسبة النقصان ( ٥١،٨ و ١٥ و ١٩،٨ )% لدرجات الحرارة٥٠٠،٤٠٠،٣٠٠ ) على التوالي اما بالنسبة لحالة التبريد فان تبريد نماذج الثرمستون المعرضة للحرارة العالية )بالماء يؤدي إلى انخفاض في مقاومة الانضغاط بنسب اكبر مقارنة مع النماذج الساخنة و المبردة في الهواء. بينتالنتائج ايضا ان نسبة الامتصاص للنماذج بدون انهاء اكبر مما في حالة النمادج التي قيست بعد ازالة الانهاء بدرجاتحرارة ٤٠٠ و ٥٠٠ م° حيث كانت ( ٧،٩٥ و ٦،٤٣ )% على التوالي، اذ قيست نسبة الامتصاص للثرمستون فقط ولميكن ذلك ممكنا بدرجة حرارة ٣٠٠ م° مما يعني ان وجود الانهاءات يقلل من نسبة امتصاص الثرمستون للماء.الكلمات المرشدة: الثرمستون، تاثير درجة الحرارة على الثرمستون، الحريق


Article
The Effect of some Natural Admixtures on the setting Time of Iraqi Plaster of Parts
تحسين زمن التجمد للجص الفني العراقي بإستخدام مضافات طبيعية

Authors: قيس جواد فريح --- وليد عبد الرزاق القيسي --- لمى سعدي عبد الخالق
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2005 Volume: 24 Issue: 9 Pages: 380-394
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Keywords

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

Arabic (3)


Year
From To Submit

2012 (1)

2011 (1)

2005 (1)