Article
Effect Of Applied Load On Wear Behavior Of Some Copper Alloys
تاثير الحمل المسلط على سلوك البلى لبعض سبائك النحاس

Author: مكارم حازم عبدالكريم
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 1 Pages: 28-36
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research devoted to studying the properties of sliding wear ofthree groups of copper alloys chosen to this study. They are Brass (70/30),Silicon bronze and Silicon-Brass. These three groups have been examinedby using (pin on Disc) apparatus under different wear conditions includingapplied loads and disc hardness is constant (35HRC). This study wasconcluded that the wear rate was increased as the applied load and the wearbehavior was changed from mild wear into transition wear as the appliedload is increased. This research concludes that the alloy of Silicon-brass wasthe best alloy due to high wear resistance in comparison with the otheralloys.

Keywords


Article
Effect of Pb and Sn Adding on Dry Sliding Wear Behavior of á-Brass (70/30)
تأثير إضافة الرصاص والقصدير على سلوك البلى الانزلاقي الجاف لسبيكة البراص الفا (70/30)

Authors: منى خضير عباس --- مكارم حازم عبدالكريم --- ذكرى مهدي علي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 7 Pages: 258-268
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work is concerned with a study of dry sliding wear of α–Brass (70/30) withaddition of lead and tin(3%wt) for each one alloy. Three brass alloys were prepared bymelting and pouring in steel molds. A Pin -on-Disc technique was used. The effect ofapplied loads and sliding times on wear rate were examined. The results show that thewear rate increases with increasing applied loads and with increasing sliding time atconstant sliding speed (2.7m/s) while hardness of steel disc was 35 HRc .The results also show that the brass alloy containing 3% tin has morewear resistance than that of other brass alloys.

70 ) . وقد تم / يتناول هذا البحث دراسة البلى الانزلاقي الجاف لسبيكة البراص الفا ( 30تحضير سبيكتين من البراص باضافة عنصر الرصاص والقصدير بنسبة % 3 كل على حدة الى70 ). وقد تم تحضير هذه السبائك / 70 ) علاوة على السبيكة الاساس ( 30 / سبيكة البراص الفا ( 30الثلاث بعملية الصهر والصب في قوالب فولاذية. .واستخدمت تقنية المسمار على القرص لقياس(2.7 m/sec) معدل البلى عند تسليط احمال مختلفة وفترات انزلاق مختلفة مع تثبيت سرعة الانزلاق35 ) . وقد اظهرت النتائج ان معدل البلى يزداد مع زيادة الحمل HRc) وصلادة القرص الفولاذي( المسلط والفترة الزمنية للانزلاق. وكذلك اظهرت سبيكة البراص الحاوية على عنصر القصدير (% 3افضل مقاومة بلى مقارنة مع السبائك الاخرى.