STUDY THE EFFECT OF GERMANIUM AND SILICON ADDITIONS ON THERMAL PROPERTIES AND MICROSTRUCTURE OF PURE ALUMINUM
دراسة تأثير إضافة الجرمانيوم والسيلكون على الخواص الحرارية و البنية المجهرية للألمنيوم النقي

Loading...
Loading...
Abstract

In this study an experimental work has been conducted to show the effect of Ge and Si additions on the micro structure and thermal properties of pure Al, as the specific heat at constant volume (Cv), thermal conductivity (k), and thermal diffusivity .Six samples have been casted with different addition percentages of Ge and Si (10,20,30%).The results shows as the Ge addition percentage is increased, the alloy density is increased by (29.34%), the thermal conductivity is decreased by (20.85%),the specific heat is decreased by (19.4%) and thermal diffusivity is decreased by (24.1%). But as the Si addition percentage is increased cause decreasing the alloy density by (4.21%), the thermal conductivity by (7.3%),the specific heat by (6.7%) and increasing the thermal diffusivity by (3.7%).Through this study it was found that the best addition is 30% (Si) addition percentage for pure Al gives highest thermal properties (Cv,k, ) compared with the same addition percentage of (Ge) .and from micro structure , it was found the distribution of (Si) particle through (Al) . phase , for the (Ge) particle it was found the a glomeration of (Ge) particle is because the weak of the wetting property of (Ge) comparing with the (Si) particles

تم في هذا البحث تحقيق دراسة عملية لبيان تأثير إضافة عنصري الجرمانيوم والسيلكون على البيئة المجهرية والخواص الحرارية للألمنيوم النقي وهي السعة الحرارية النوعية بثبوت الحجم (Cv) ومعامل التوصيل الحراري (k) ومعامل الانتشار الحراري ( ). لقد تم تصنيع ستة سبائك معدنية وذلك بتغير نسب إضافة كل من الجرمانيوم والسيلكون على الألمنيوم النقي وكانت النسب هي (30%,20% و10%). بينت النتائج المستحصلة انه بزيادة نسب إضافة الجرمانيوم إلى الألمنيوم النقي تسبب زيادة كثافة السبيكة بنسبة (%29.34 ), ونقصان معامل التوصيل الحراري بنسبة (%20.85 ), ونقصان السعة الحرارية النوعية بنسبة (%19.4 ), وكذلك نقصان معامل الانتشار الحراري بنسبة (%24.1 ). وأظهرت الدراسة أيضا انه بزيادة نسب إضافة السيلكون إلى الألمنيوم النقي تؤدي إلى نقصان كثافة السبيكة بنسبة (%4.21 ), ونقصان معامل التوصيل الحراري بنسبة (%7.3 ), ونقصان السعة الحرارية النوعية بنسبة (%6.7), وكذلك زيادة معامل الانتشار الحراري بنسبة (%3.7 ). خلال هذه الدراسة وجد أن أفضل إضافة هي (30%Si) للألمنيوم النقي والتي أعطت أعلى خواص حرارية (,Cv,k ) مقارنة بسبيكة (Al-30% Ge).اما بالنسبة الى التركيب المجهري نلاحظ توزع دقائق السليكون خلال طور الالمنيوم النقي اما بالنسبة الى دقائق الجرمانيوم فنلاحظ تجميع هذه الدقائق على شكل مجاميع ويعود السبب الى ضعف قابلية الترطيب (wetting) مقارنة بدقائق السليكون.


Article
تأثير المعاملة الحرارية الايزوثيرمية السريعة والمحلولية (T6) على خواص السبيكة (A319) المنتجة بطريقة السباكة بالضغط

Authors: محمد مهنا متعب --- نجيب سلمان عبطان --- رائد نجيب رزوقي
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2015 Volume: 22 Issue: 2 Pages: 74-80
Publisher: Tikrit University جامعة تكريت


Article
دراسة بعض الخواص الفيزيائية و الميكانيكية لمادة متراكبة ذات اساس من الالمنيوم6063 مدعم بدقائق الزركونيا و المحضرة بتقانة ميتالورجيا المساحيق

Authors: نجيب سلمان عبطان --- رابحة صالح ياسين --- انمار ضيف مهدي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 3 Pages: 932-941
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is studying some physical properties (density , porosity & water absorption) and some mechanical properties (micro hardness Vickers , compression strength & wear resistance) of aluminum 6063 matrix composite material that reinforced by (2.5,5,7.5&10) wt.% of ZrO2 particles. Powder metallurgy technique is used in samples preparing. Samples were compacted by using cold uniaxial pressing then followed sintering process at 600 oC under inert gas.Results were showed improving in (wear resistance , compression strength & micro hardness Vickers) and increasing in (density , porosity & water absorption). Increase micro hardness (44.5 – 101.13), compression strength (36.1998 – 46.7) N/mm2 and decrease wear rate (9.5*exp(-8) – 4.8*exp(-8)) g/cm at time 30 min. with (0 – 10)% ZrO2. While increase apparent density (1.388 – 3.15) g/cm3 , apparent porosity (0.96 – 4.61)% and water absorption (0.699 – 2.09)% at (0 – 10)% ZrO2.

يهدف البحث الى دراسة بعض الخواص الفيزيائية (الكثافة و المسامية و قابلية إمتصاص الماء) و بعض الخواص الميكانيكية (صلادة فيكرز المايكروية و مقاومة الإنضغاط القطرية و مقاومة البلى) لمادة متراكبة ذات اساس من الالمنيوم 6063 مدعمة بنسب وزنية مختلفة (2.5,5,7.5&10) wt.% من دقائق الزركونيا. وقد تم إتباع تقانة ميتالورجيا المساحيق في تحضير العينات حيث تم كبس العينات على البارد بطريقة الكبس احادي الإتجاه بضغط 5 طن تلى ذلك تلبيد العينات بدرجة حرارة 600 مo في جو خامل.وقد اظهرت النتائج ان تدعيم الالمنيوم 6063 بدقائق الزركونيا تحسن من مقاومة البلى و مقاومة الإنضغاط و صلادة فيكرز المايكروية وكذلك زيادة في قيم الكثافة و المسامية و قابلية إمتصاص الماء . إذ تزداد الصلادة من (101.13 – 44.5) و مقاومة الإنضغاط القطرية من (46.7 – 36.1998) N/mm2و يقل معدل البلى من (4.8*exp(-8) – 9.5*exp(-8)) غم/سم عند زمن 30 دقيقة ومحتوى (0 – 10)% من الزركونيا. بينما تزداد الكثافة الظاهرية (3.15 – 1.388) غم/سم3 و المسامية الظاهرية (4.61 – 0.96)% و قابلية إمتصاص الماء (2.09 – 0.699)% عند محتوى (10 – 0)% من الزركونيا.


Article
Evaluation Of Future Performance of Northern Fatha Storage System
دراسة تأثير الضغط المسلط على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 باستخدام السباكة بالعصر

Author: د. فاروق منصور مهدي د. نجيب سلمان عبطان سعد رمضان احمد
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2013 Volume: 20 Issue: 4 Pages: 11-17
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This present study shows ,the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Alumium alloy A380 was studied .From fig(5) its clear that ,the microstructure of prepare casting samples consist of two phases hard eutectic (Al-Si) and Primary α-Al.The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84)MP

تم في هذا البحث دراسة تاثير الضغط المسلط ضمن المدى (10-84) ميكاباسكال خلال عملية السباكة بالعصر المباشر على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 من الخردة , تبين من خلال البنية المجهرية ان البنية تتكون من طورين هما طور اليوتكتك الصلد وطور الالمنيوم الاولي وكذلك وجدنا من خلال علاقة الضغط المسلط وكسر المساحة لطور اليوتكتك ان نسبة كسر المساحة تزداد عند الضغوط (68,84) ميكاباسكال بينما قلت هذه النسبة عند الضغوط (10,17,34) ميكاباسكال . ومن خلال دراسة العلاقة بين الضغط المسلط بمدياته الخمسة والكثافة الحقيقية نلاحظ زيادة الكثافة بزيادة الضغط المسلط (10-17) ميكاباسكال وكذلك عند الضغط (84) ميكاباسكال.