دراسة تأثير السرعة الدورانية ودرجة حرارة الصب على مقاومة البلى والصلادة لسبيكة الالمنيوم (A380) المقواة بنسب حجمية مختلفة من دقائق الالومنيا

Authors: مهند عبدالخالق حميد --- نجيب عبطان سلمان --- فاروق منصور مهدي
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2016 Volume: 23 Issue: 4 Pages: 1-10
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In this study a cylindrical liner was produced by horizontal centrifugal casting process. The liner was composed from aluminum alloy (A380) matrix reinforced with alumina particles (Al 2O3)with grain size of (63−125)µ and volume percent of 10,15 and 20%. The die was rotated atdifferent speeds and its temperature was remained constant at (350)ºC. In this present study it was concluded that any increase in temperature difference between pouring and die temperature will reduce the surface defects. This study reveals that increasing the rotational speed refines the grain size but cause the alumina particles to be concentrated atthe outer surface. Finally it was found that the addition of alumina particles increases bothhardness and wear resistance of the alloy.


Article
Study the Effect of Rotational Speed and Pouring Temperature on the Wear Resistance and Hardness of Alloy (A380) Reinforced with Different Volume Fraction of Alumina Particles
دراسة تأثير السرعة الدورانية ودرجة حرارة الصب على مقاومة البلى والصلادة لسبيكة الألمنيوم (A380) المقواة بنسب حجمية مختلفة من دقائق الالومينا

Loading...
Loading...
Abstract

In this study a cylindrical liner was produced by horizontal centrifugal casting process. The liner was composed from aluminum alloy (A380) matrix reinforced with alumina particles (Al2O3) with grain size of (63−125)µ and volume percent of 10,15 and 20%. The die was rotated at different speeds and its temperature was remained constant at (350)ºC. In this present study it was concluded that any increase in temperature difference between pouring and die temperature will reduce the surface defects. This study reveals that increasing the rotational speed refines the grain size but cause the alumina particles to be concentrated at the outer surface. Finally it was found that the addition of alumina particles increases both hardness and wear resistance of the alloy.

في هذه الدراسة تم استخدام سباكة الطرد المركزي الأفقي لإنتاج بطانة اسطوانية لمحرك الاحتراق الداخلي مكونة من سبيكة الألمنيوم (A380) المقواة بدقائق الالومينا(Al2O3) يتراوح الحجم لدقائق الالومينا بين (63- 25) مايكرون وبنسب حجمية مختلفة (20,15,10)%. تم تثبيت درجة حرارة القالب عند درجة حرارة (350)°م والتدوير بسرع مختلفة. تم التوصل في هذا البحث إلى أن زيادة الفرق بين درجة حرارة الصب ودرجة حرارة القالب تؤدي إلى تقليل العيوب والفجوات السطحية كما تم التوصل إلى أن زيادة السرعة الدورانية للقالب قد أدت إلى تنعيم البنية المجهرية وتزداد النعومة بالاقتراب من السطح الخارجي إلا أنها تعمل على زيادة تركيز دقائق الالومينا المضافة عند السطح الخارجي للاسطوانة. توصلت الدراسة الحالية كذالك إلى أن دقائق الالومينا المضافة قد عملت على رفع قيم الصلادة وتحسين مقاومة البلى.