Manufacturing of composite (Ni-Al +Al2O3-ZrO2) by using Flame Thermal Spray Technique.
تصنيع مواد مركبة (Al-Ni+Al2O3+ZrO2) بتقنية الرش الحراري باللهب

Loading...
Loading...
Abstract

Flame Thermal Spray technique was used to produce matrix composite of ZrO2 (25%) reinforced with Alumina (25%) with (Al-Ni) (50)% have been spray into base substrate of stainless steel type (316L). All samples were grit blasted as initial preparation state and all spraying done at different distances from substrate (12, 14, 16,17, 18, 20) cmtest of stiffness, porosity and adhesion has been experienced on the compound layer which produced to study the effect of changing the spraying distance on the layer characteristic. All samples were heated at (950, 1050) ºC for(1/2hr). The results before and after heat treatment show that the optimum condition for spraying distance at (16 cm) and heat treatment at (1050 ºC) which are most effective to give best results especially hardness, porosity and adherence bond.

تم استخدام تقنية الرش الحراري باللهب في إنتاج مادة مركبة ذات أساس من الزركونيا نسبة 25% مقواه بدقائق سيراميكية من الألومينا نسبة 25% مع مادة رابطة من(Al-Ni) بنسبة 50% على قاعدة من سبيكة الفولاذ نوع (316L) بعد إن تم تهيئتها بطريقة التخشين بالعصف الحبيبي. أجريت عملية الرش باستخدام مسافات رش مختلفة (12,14,16,17,18,20) سم. اختبارات الصلادة, المسامية, وقوة التلاصق تم إجراءها على طبقة المادة المركبة المنتجة لدراسة تأثير تغير مسافة الرش على خواص الطبقة الناتجة. تم إجراء المعاملة الحرارية على العينات عند درجات حرارة ºC(950,1050) لمدة نصف ساعة. أكدت نتائج الاختبارات قبل وبعد المعاملة الحرارية بأن أفضل مسافة رش (16cm) والمعاملة الحرارية (1050ºC) حيث لهما تأثير كبير في تحسين خواص طبقات المادة المركبة المنتجة خاصة الصلادة, المسامية مع قوة التلاصق.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

Arabic (1)


Year
From To Submit

2018 (1)