Article
Fabrication and characterization of Ag-BaF2/GaSb Schottky diode
" تصنيع ودراسة خصائص ثنائي شوتكي "Ag–BaF2-GaSb

Author: Abdulsamee Fawzi Abdulaziz عبدالسميع فوزي عبدالعزيز
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2017 Volume: 22 Issue: 6 Pages: 103-107
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The Ag-BaF2/GaSb Schottky diode measurement has been investigated by using voltage versus current (I-V) at different temperatures, voltage versus capacitance (C-V) and hotoelectric measurements on n-type GaSb carrier per cm-3, Current – voltage measurement were used to study the interface layer. Near ideal characteristics were observed for Ag-BaF2/GaSb contact with ideality factor values (1.21-1.451). The Schottky barrier height and donor concentration (Nd) have been obtained from C-V characteristics. Barrier height results from these methods were the same approximately with the results obtained from current – voltage measurement and were in the same range which suggests that the Fermi level is pinned in the lower half of the band gap. Photoelectric measurements were used for barrier height measurements by applying the fowler method. The surfaces of sample was analyses using scanning electron microscopy (SEM) and also the x-ray is used to investigate the reasons for the non-ideal behavior of Ga contacts and to study the surface of Ag-BaF2 layer on the air-cleaved n-GaSb surface.

فحصت قياسات ثنائي شوتكي باستخدام التيار- الفولتية، السعة– الفولتية وقياسات الكهروضوئية على انتيمون الكاليوم من النوع المانح (n-GaSb) عند درجات الحرارة المختلفة. استخدمت قياسات التيار- الفولتية في دراسة الطبقة البينية حيث لوحظت خصائص شبه مثالية لتماس شوتكيAg-BaF2-GaSb مع قيم عامل المثالية (1.21– 1.451). تم الحصول على ارتفاع حاجز شوتكي وتركيز الحاملات ((Nd من خصائص السعة–الفولتية (C-V). ارتفاع الحاجز(b) باستخدام هذه الطرق يشبه تقريبا النتائج الملحوظة من قياسات التيار-الفولتية وعند نفس المدى المقترح لمستوى فيرمي لأقل من نصف فجوة الطاقة. استخدمت قياسات الكهربائية الضوئية لقياس ارتفاع الحاجز بواسطة تطبيق نظرية فولير Fowler theory. أما مجهر الماسح الالكتروني والأشعة السينية (X-ray) فقد استخدمت لفحص السلوك غير المثالي لتماسات الكاليوم Ga ودراسة سطوح طبقاتAg-BaF2 على سطح انتيمون الكاليوم من النوع المانح (n-GaSb).


Article
Study structural, surface morphological and magnetic properties of Mn(1-x) Znx Fe2O4 by solid state reaction method
" دراسة الخواص التركيبية؛ ومورفولوجية السطح والخواص المغناطيسية لمركبات Mn(1-x) Znx Fe2O4 المحضرة بطريقة تفاعلات الحالة الصلبة"

Loading...
Loading...
Abstract

The powder of Mn-Zn ferrite having the chemical formula Mn(1-x)ZnxFe2O4 where x varies from 0, 0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by solid state Reaction method. The X-Ray Diffraction studies confirm the formation of spinel cubic structure. The particle size was calculated by X-ray broadening studies. Also the structural parameters like Lattice Constant, X-ray density, bulk density (d), Porosity (P), ionic radius (Ra , Rb) and anion parameter or the oxygen positional parameter for all the samples. The micro structural features of the samples were obtained using a Scanning Electron Microscopy (SEM). The magnetic properties of Mn(1-x)ZnxFe2O4 ferrites were strongly affected by the Zn content. The saturation magnetization increased. It may be due to relatively high orbital contribution of Mn2+ ions to magnetic moment, which gives large induced anisotropy.

تم تحضير مركبات المنغنيز- الخارصين ذات الصيغة الكيميائيةMn(1-x)ZnxFe2O4 حيث ان 0 ≤ x ≤ 0.5وذلك باستخدام طريقة تفاعلات الحالة الصلبة. تم حساب الحجم الحبيبي لجميع مركبات الفرايت المحضرة من حيود الأشعة السينية بعد التأكد من تشكيل الطور الأحادي ذو التركيب البلوري مغزلي الشكل. كما تم حساب ثابت الشبيكة والكثافة الظاهرية المحسوبة من حيود الأشعة السينية (ρx-ray), والكثافة الفيزياوية, ونصف القطر الايوني حيث وجد أنها تزداد مع زيادة تركيز نسبة الخارصين, بينما كانت المسامية تنقص مع زيادة تركيز الكادميوم. كما لوحظ صور التركيب الميكروي لجميع النماذج بواسطة مجهر الماسح الالكتروني. أما نتائج الفحوصات المغناطيسية فقد أظهرت تاثير نسبة الخارصين على زيادة المغناطيسية المشبعة. قد تكون نتيجة المساهمة النسبية للقيمة العاليا لاوربيتال العزم المغناطيسي لايون المنغنيز الذي يسبب زيادة الخواص المتباينة.