Mechanical, Thermal and Wear Characteristics of Polymer Composite Material Reinforced with Calcium Carbonate Powder
الخواص الميكانيكية والحرارية وخاصية البلى لمادة بوليميري متراكبة مدعمة بمسحوق كاربونات الكالسيوم

Authors: Aseel B. Al-Zubaidi --- Ahmed A. Al-Tabbakh --- HanaaA. Al-Qaessy --- Ragad N. Al-Kaseey
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (B) Scientific Pages: 519-532
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Quick mast–105 is a well-known epoxy-based adhesive used in fabric reinforcement, bonding of wooden parts and variety of metals. Its mechanical and thermal properties are still limiting factors for extended technological and industrial applications. Enhancement of mechanical, wear and thermal characteristics of this epoxy resin using a cheap filler of CaCO3powder is the focus of the present study. The mechanical properties are demonstrated in terms of the flexural modulus, hardness and impact strength of the reinforced cured compound while thermal properties are presented through thermo gravimetric analysis and thermal conductivity coefficient. Results show that addition of 15% by weight of CaCO3 to the epoxy resin improves the mechanical properties and the thermal resistance of the end product paving the way for wider applications in industry and technology. Wear characteristics show that the reinforced product is suitable for high-speed applications.

يعد ايبوكسيي (quick mast 105) من المواد الايبوكسية اللاصقة المعروفة والمستخدمة في مجال تدعيم النسائج ولصق الاجزاء الخشبية والمواد الاخرى . وتعتبر الخواص الميكانيكية والحرارية لهذا الايبوكسي من العوامل المحددة في مجال التطبيقات التكنولوجية والصناعية لهذه المادة . تهدف هذه الدراسة الى تحسين الصفات الميكانيكية والحرارية وخواص البلى لهذا الايبوكسي باستخدام مادة حشو رخيصة التكلفة من مسحوق كاربونات الكالسيوم . لقد تم في هذا البحث استعراض الخواص الميكانيكية من خلال دراسة معاملات الانحناء والصلابة ومقاومة الصدمة للعينات الايبوكسية المدعمة فيما تمت دراسة الخصائص الحرارية من خلال التصرف الحراري – الوزني ومعامل التوصيلية الحرارية للعينات المدعمة . وقد اوضحت النتائج ان اضافة كاربونات الكالسيوم بنسبة وزنية تعادل 15% من وزن الايبوكسي تؤدي الى تحسين الخواص الميكانيكية والحرارية للعينات المدعمة مفسحا المجال لاستخدامها في مجالات صناعية وتكنلوجية اوسع . اما دراسة خاصية البلى فقد بينت ان مادة الايبوكسي المدعمة مناسبة للتطبيقات عالية السرعة.


Article
Erosion Wear and Hardness of Glass Fiber / Epoxy with Nano and Micro TiO2 Hybride Composites

Authors: Amine Achour --- Shatha Riyad Ahmed --- Ahmed A. Al-Tabbakh --- Aseel Basim Al-Zubaidi
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2018 Volume: 00 Issue: 1 Pages: 43-51
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The objective of this research is to prepare and study (Glass Fiber / Epoxy) with nano and micro Titanium dioxide (TiO2) composites with different volume percentage of nano and micro TiO2 powder of 2%, 4%, and 6% volume fraction. Atomic force microscopy techniques was used to measure the grain size of nano TiO2 powder (average diameter was 46 nm) and particle size analyzer techniques was used. Erosive wear behavior of this composite under three different impingement angles of 30°, 60° and 90° and three angular silica sand abrasive particle sizes approximately 425, 600 and 850 μm and hardness (shore D) were studied. In general the erosion wear of micro composites have lower erosion resistance than other nano-based compounds. Erosion resistance increase as the volume fraction increase. Nano composites of GF / EP with TiO2 have many advantages over micro composites from the view point of wear and hardness tests. The worn surface features of unfilled and filled G-E composites were examined using scanning electron microscopy (SEM) and results indicates more severe damage to matrix and glass fiber in unfilled composite system as compared to TiO2 filled composites.


Article
Mechanical and thermal properties of cockles shell cementing material
دراسة الخواص الميكانيكية والحرارية لمادة مونة الاسمنت المدعمة بمسحوق قشور المحار

Loading...
Loading...
Abstract

Mortar of ordinary Portland cement was blended with cockles shell powder at different weight ratios to investigate the effect of powder admixture on their strength and thermal conductivity. Results showed that addition of cockles shell powder at 50% of mortar weight improves hardness and compressive strength notably and reduces the thermal conductivity of the end product. Results suggest the possibility to incorporate cockles shell powders as constituents in cement mortars for construction and plastering applications.

تم خلط مونة الاسمنت البورتلاندي العادي مع مسحوق قشور المحار بنسب وزنيه مختلفة لدراسة تأثير الخليط من مسحوق قشور المحار على قوة الاسمنت والتوصيل الحراري. وأظهرت النتائج أن إضافة مسحوق قشور المحار بنسبة 50٪ من وزن عينة مونة الاسمنت يحسن صلابة وقوة الانضغاطية ويقلل من التوصيل الحراري للمنتج النهائي. وتشير النتائج إلى إمكانية خلط في شكل مكونات لمونه الاسمنت للبناء والتطبيقات التجصيص.

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2018 (1)

2015 (1)

2014 (1)