Article
Development and Evaluation of Chromium- Modified Aluminide Diffusion Coating

Author: Ahmed Ali Moosa,Jaleel Kareem Ahmed, Ali Hubi Haleem
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2009 Volume: 17 Issue: 1 Pages: 308-321
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractIn this work nickel superalloy Inconel 600 was coated with two different types of coatings Cr modified aluminide coating this is called(Aluminizing- Chromizing) and Y-doped Cr modified aluminide coating this is called (Aluminizing- Chromizing- Yttriumizing) using pack cementation method. Diffusion coating was carried out in one step process by simultaneous aluminizing –chromizing process and by simultaneous aluminizing- chromizing- yttriumizing process using the conversion reaction of 10 wt.% Cr2O3, 10 wt.% Al, 2 wt.% NH4Cl, 4 wt% NaCl and 72 wt.% Al2O3 and 2% Y2O3 when required. The diffusion coating processes were carried out at 1050 oC for 8hrs. After diffusion coating the coating layer was found to be consisted of: -NiAl.Cyclic oxidation test in air was conducted on the Inconel 600 coated with Cr-modified aluminide coating and on the Inconel 600 alloy coated with Y-doped Cr modified aluminide coating in the temperature range 700- 1100 oC. The oxidation cycles include 10 hrs. at furnace temperature. The results indicate that Y-doped Cr modified aluminide coating is more effective in increasing the oxidation resistance of Inconel 600 alloy. The role of yttrium can be attributed to an improvement of the adherence of the oxide scales.

الخلاصة تم في هذا البحث طلاء سبيكة ذات أساس نيكل ( الانكونل 600) بنوعين من الطلاء : الأول طلاء الألمنيوم المدعم بالكروم و يدعى ( الألمنه – الكرمنة) والثاني طلاء الألمنيوم المدعم باليتريوم والكروم ويدعـى ( الألمنه – الكرمنة- التطعيم باليتريوم) بتقنية السمنته . جرى الطلاء الانتشاري آنيا لنوعي الطلاء من خلال التفاعل للمكونات التالية : 10 wt.% Cr2O3, 10 wt.% Al, 2 wt.% NH4Cl , 4 wt% NaCl ,72 wt.% Al2O3أما بالنسبة للنوع الثاني من الطلاء فيتم بإحلال فقط 2 wt.% Y2O3 من الألومينا. تمت عملية الطلاء الانتشاري بدرجة حرارة 1050 oC ولمدةhr. 8 . لقد وجد إن طبقة الطلاء الانتشاري تتكون من الطور -NiAl . جرى اختبار الأكسدة الدوري لسبيكة الانكونل 600 قبل وبعد الطلاء في مدى من درجات الحرارةoC ( 700 - 1100) وبمعدل 10hr للدورة الواحدة. أشارت النتائج إن تدعيم الألمنيوم باليتريوم والكروم أكثر كفاءة في زيادة مقاومة التأكسد لسبيكة الانكونل 600 , ويرجع ذلك إلى دور اليتريوم في تحسين التصاقية طبقة الأوكسيد الواقية.


Article
Oxidation of Simple and Pt-Modified Diffusion Coating on Inconel Alloy 600 in Air
أكسدة سبائك انكونيل - 600 المحورة بالطلاء الأنتشاري الالمنه - بلاتين

Authors: Ahmed Ali Moosa --- Hussein Al-Alqawie --- Khalil Al-Hatab
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2005 Volume: 24 Issue: 7 Pages: 909-922
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract


Article
Surface Modification of Multiwall Carbon Nanotubes for Metal Matrix Nan composite Applications
تهيئة سطوح انابيب الكاربون النانوية لملائمة تطبيقات المواد المتراكبة النانوية ذات الاساس المعدني

Authors: Ahmed Ali Moosa --- Abdul Qader Faisal --- Righdan Mohsen Namus
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 7 Part (A) Engineering Pages: 1859-1869
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

MWCNTs first functionalized by using two steps covalent functionalization process. Functionalized MWCNTs coated with copper by using electroless coating process. Three different groups of Cu/MWCNTs nanocomposites with (0.1, 0.5, 1, 2, 3 wt% MWCNTs) were prepared by means of powder technology. The first group contains multiwalled carbon nanotubes as received (Cu/MWCNTs), second group contains functionalized multiwalled carbon nanotubes (Cu/FMWCNTs) while the third group contains coated multiwalled carbon nanotubes (Cu/CMWCNTs). Comparison between these samples show that the coating of MWCNTs was remarkably improve hardness and wear resistance of copper nanocomposite. The improvement in mechanical properties is due to the enhancement in both adhesion with matrix and dispersion ability of MWCNTs. SEM, XRD, FTIR were used to characterize of coating process and Cu/MWCNTs nanocomposites.

في البداية تم توظيف انابيب الكاربون النانوية باستخدام التوظيف التساهمي وعلى مرحلتين. انابيب الكاربون النانوية الموظفة تم طلاءها بمعدن النحاس باستخدام (Electroless coating process). ثلاث مجاميع من المواد المتراكبة النانوية ذات الارضية النحاسية تم تحضيرها باستخدام تكنولوجيا المساحيق بنسب وزنية مختلفة من انابيب الكاربون النانوية. احتوت المجموعة الاولى على انابيب الكاربون النانوية كما هي واحتوت المجموعة الثانية على انابيب الكاربون النانوية الموظفة بينما احتوت المجموعة الثالثة على انابيب الكاربون النانوية المطلية. بينت المقارنة بيت هذه العينات ان عملية الطلاء قد حسنت وبشكل ملحوظ الصلادة ومقاومة البلا للمادة المتراكبة النانوية. ان التحسن في الخواص يمكن ارجاعه هنا الى زيادة كل من الالتصاق مع الارضية و قابلية التشتت لانابيب الكاربون النانوية. تم استخدام (SEM, XRD, FTIR) لتوصيف عملية الطلاء وكذلك لتوصيف المواد المتراكبة النانوية ذات الاساس المعدني.