Influence of Temperature on Fracture Toughness of Jute Fiber Reinforced Unsaturated Polyester Resin
تأثير درجة الحراره على متانه التكسير النوعيه لمتراكب راتنج البولي أستر غير المشبع المقواة بالياف الجوت

Author: Akram R. Jabur
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 17 Pages: 5481-5494
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Jute fiber reinforced unsaturated polyester resin composites (J/UP) weresubjected to low velocity impact tests in several Temperatures degree in order to study the effects of temperature variance on the intrinsic fracture toughness Gc impact properties. An investigation was conducted onto the effects of temperatures on impact resistance of jute fiber-reinforced unsaturated polyester resin composite. Impact tests were performed on the specimens at different temperatures. The temperatures were 27, 50, 75 and 100 Cº. The results reflect the influence of ambient temperature on impact toughness measurements. The resultsindicate an obvious correlation between the ambient temperatures and impact load, total absorbed energy and fracture toughness. The prepared specimens exhibited brittle fracture behavior with a lower peak load, lower impact energy and less time to fail compared with results at temperature higher Tg. The impact test results show that the total energy absorbed at 100 C° have higher energy when the composite behavior changed from brittle to ductilebehavior. The intrinsicfracture toughness is higher for specimens tested in 100 Cº and 75 Cº and shows ductile behavior; while specimens tested with temperature lower than Tg show brittle fracture and lower Gc.

عرضت عينات من راتنج البولي أستر غير المشبع المقواة بالياف الجوت لاختبارتالصدمه بسرعه واطئه في درجات حراريه مختلفه لغرض دراسة تأثير تغاير درجات الحراره البحث يتعرض لتأثير درجات الحراره × Gc على مواصفات متانه التكسر النوعيه بالصدمه أنجزت × على مقاومة الصدمه لمتراكبات راتنج البولي أستر غير المشبع المقوى بالياف الجوت درجات الحراره التي أجريت بها × فحوص الصدم على العينات بدرجات حراره مختلفه أن النتائج المستحصله تعكس تأثير درجه حرارة المحيط × 100 م° , 75 ,50, الفحوص هي 27 عرضت عينات من راتنج البولي أستر غير المشبع المقواة بالياف × على قياسات متانة الصدمالجوت لاختبارت الصدمه بسرعه واطئه في درجات حراريه مختلفه لغرض دراسة تأثير تغاير البحث يتعرض لتأثير × Gc درجات الحراره على مواصفات متانه التكسر النوعيه بالصدمه درجات الحراره على مقاومة الصدمه لمتراكبات راتنج البولي أستر غير المشبع المقوى بالياف درجات الحراره التي × أنجزت فحوص الصدم على العينات بدرجات حراره مختلفه × الجوت أن النتائج المستحصله تعكس تأثير درجه × 100 م° , 75 ,50, أجريت بها الفحوص هي 27 تتشير النتائج الى أرتباط وِاضحِ بين درجات × حرارة البيئيه على قياسات متانة الصدمالطاقه الممتصه الكلي ومتانة التكسير. أن العينات التي حضرت , الحرارة البيئيه وتحميل الصدم تبدي سلوك تكسير قصيفا" يرافقه قمم تحميل واطئه وطاقة صدم واطئه وتستغرق زمنا" أقل Tg للانهيار مقارنة" مع النتائج الحاصله للعينات في درجات حراريه أعلى من أن نتائج فحوص الصدم بينت أن الطاقه الكليه الممتصه بالفحص بدرجة حراره 100 م تستلزم طاقه أعلى عندما يتغاير سلوك المتراكب من القصيف الى المطيلي . أن متانة التكسير النوعيه تكون للعينات المفحوصه بدرجة حراره 100 و 75 م تكون أعلى وتظهر تظهر سلوكا" قصيفا" في Tg سلوكا" مطيليا" بينما العينات المفحوصه بدرجات حراره أقل من. Gc التكسر وأقل قيمه ل


Article
THERMAL DEGRADATION EFFECT ON THE FRACTURE TOUGHNESS OF GLASS FIBER REINFORCED UNSATURATED POLYESTER RESIN COMPOSITE
تأثير الآتلاف الح ا ررى على متانة التكسير لمت ا ركب البولي أستر الغير مشبع المقوى بالياف الزجاج

Author: Akram R. Jabur اكرم رحيم جبار
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 4 Pages: 709-719
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractSamples of FRP prepared by applied unsaturated polyester resin as matrix reinforced by one layerwoven glass fiber( 0º/90º), using hand lay up method. The prepared samples are subjected tothermal aging at 85 º C for different time in dryer oven up to 1200 hrs time and tested byunnotched sample impact tester to obtained the fracture toughness , polynomial relationshape oforder 5 found between Gc and Aging time decreasing Gc strongly to lower value .The Stress straintests for aged to specific time and without aging samples by tensile test show that sample agedthermally tend to brittle behavior and lost its mechanical properties as aging time increase, whilesample without aging show ductile behavior . FTIR analysis show decomposition of the polyesterby creating new free radical and observed new peak wave number in transmtion spectra due tofiber crystallization.

حضرت عينات من البوليمر المقوى بالالياف بأستخدام ا رتنج بوليمر البولي أستر الغير مشبع كقالب أم مقوى بطبقه90 ) وبأستخدام تقنية التشكيل اليدوى . العينات المحضره عرضت للتعتيق الح ا ررى ° واحده من الياف الزجاج المتعامده (° 0بدرجة ح ا ررة 85 م ولفت ا رت زمنيه مختلفه في فرن تجفيف ولزمن يصل الى 1200 ساعه كحد أقصى وفحصت العينات بجهازأقرب Gc فحص الصدم لعينات غير محززه لتحديد متانة الكسر حيث حصل منحني للعلاقه بين زمن التعتيق الح ا رري وبشده الى القيمه الاقل . أن أختبا ا رت Gc الى أن يكون ذو علاقه متعددة الحدود من الدرجه الخامسه. حيث تنخفض قيمةالشد لاستحصال العلاقه أجها د- أنفعال لعينا ت غير معرضه للتعتيق وأخرى معتقه ح ا رريا لمدد محدده ومختاره بينت أنالعينات المعتقه ح ا رريا" تميل للسلوك القصيف وتفقد خواصها الميكانيكيه بزياده فترة التعتيق الح ا رري :بينما العينات التي لمتعرض للتعتيق الح ا رري أبدت سلوكا" مطيليا" . أن تحاليل الطيف تحت الحم ا رء بينت تحللا" للبولي أستر بتخليق جذور حرهوملاحظة أمكانية حصول تبلورلالياف الزجاج من خلال ما ظهر من قمم جديده في العدد الموجي في طيف الامتصاص


Article
The Effect of Solvent Additions on theMechanical Properties of Epoxy
تأثير أضافة المذيبات على المواصفات الميكانيكية للايبوكسي

Authors: Khalid K. Abbass --- Akram R. Jabur --- Saad B. H. Farid
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 18 Pages: 5732-5743
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The effect of the TolueneC6H5CH3 and Acetone (CH3)2CO additions on themechanical properties of cured Epoxy is studied. Different weight percentages ofToluene (0, 4, 8, 10 & 14 wt%) and Acetone (0, 3, 5, 8 & 10 wt%) were usedunder curing temperatures (40°C and 60°C) for Toluene and 40°C for Acetonewith curing time of 24hrs. The results show improved mechanical properties(Young modulus and Fracture stress) for Epoxy samples cured at 40°C with theincrease of Toluene to a maximum of 8wt%, then these properties are degraded asthe Toluene percentage increase. In the contrary, the Epoxy samples cured at 60 °Cshows poorer properties with increased weight percentages of the Toluene.Epoxy samples thinned with different amount of Acetone solvent isprepared and cured. These samples show best mechanical properties at Acetoneaddition of 5wt%. Extra amounts of Acetone addition degrade the results. Themechanical properties, fracture morphology and FTIR spectra shows moreaggressive effect of the Acetone compared with Toluene as solven

الخلاصةعلى (CH3)2CO والاسيتون C6H5CH تمت دراسة تأثير أضافات التالوين 3المواصفات الميكانيكية للايبوكسي المعالج. وقد استخدمت نسب وزنية مختلفة من0) في درجتين , 3, 5, 8 & 10 wt%) 0, 4, 8 ) والاسيتون , 10 & 14 wt%) التالوينحرارتين للمعالجة الحراية للتالوين هما 40 و 60 درجة مئوية و 40 درجة مئويةللاسيتون ولمدة 24 ساعة. بينت النتائج تحسن المواصفات الميكانيكية (معامل يونك وجهدالكسر) للنماذج المعالجة بدرجة 40 مئوية مع زيادة نسبة التالوين حتى النسبة الوزنية%8 وبعدها بدأت تتراجع المواصفات مع زيادة نسبة التالوين. وعلى العكس من ذلك،ظهر ان النماذج المعالجة بدرجة حرارة 60 مئوية تعكس مواصفات ميكانيكية ضعيفة وتتراجعأكثر عند زيادة نسبة اضافة التالوين.حضرت نماذج من الايبوكسي مخففة بنسب مختلفة من الاسيتون. وكانت أفضلالمواصفات الميكانيكية لهذه النماذج عند النسبة الوزنية 5% للاسيتون. وعند زيادة هذه النسبةتتراجع هذه النتائج. وقد بينت نتائج المواصفات الميكانيكية والصور المجهرية لسطح الكسروكذلك فحوصات الاشعة تحت الحمراء تأثير أكثر حدة للاسيتون مقارنة التالوين كمذيب.


Article
Bi2-Xhgxsr2-Ybaycacu2o8/Ag Sheath HTSC Wires, (Hg, Ba) Substitution Effect on the Critical Temperature

Authors: Akram R. Jabur --- Matti N. Makadsi --- Mohammed S.Mehde
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 14 Part (A) Engineering Pages: 2650-2664
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Bi2-xHgxSr2-yBayCaCu2O8 High Temperature Superconductor (HTSC) has beenprepared as a pellet by solid state reaction with a certain substitution percentages (0,0.05 ,0.1) of Hg and Ba substitution instead of Bi and Sr respectively . Then, HTSCwires were fabricated from the prepared superconductor pellets using powder in tube(PIT) method utilizing silver as the tube material. The prepared wires are of three types;with monofilament MOF, 9 multifilament core 9MF and 81 filaments core(81MF).Several cycles of mechanical drawing and rolling process performed to the startingsilver tube of 0.4 cm diameter and 5 cm length to minimize the filament diameter. Theaverage filament diameter with 81MFC wire was about 25μm measured with an opticalmicroscope.Tc critical temperature for superconductivity is measured for the pellets and wiresusing four point probes techniques. These results show that the substation Bi by Hggive a rise to the superconductor to improve highly Tc , while substitution Sr with Balowers Tc .substitution of 0.05 , 0.1 Hg to the composition Bi2-xHgxSry-2BayCa1Cu2O8will raise the transition temperature (Tc) . Also substitution of Sr by Ba decreases thetransition temperature (Tc), Hg( 0.05 – 0.1 ) substitution still raise Tc after substitutionof Ba with (0.05 – 0.1). low – Tc phase (2212) , 2201 phase in B-2212 system and theaddition of Ag to silver sheaths and a small amount of impurity phases appear in theresult of XRD analysis.


Article
The Effect of PVP Addition on the Mechanical Properties Of [84%LLDPE: 15 %(( 100- X) %PP: X%PVP):1%Basalt Particle] Polymer Blend Composites.
دراسة تأثير أضافة (PVP) على الخواص الميكانيكيه للخليط البوليمري المتراكب: [84%LLDPE:15%((100-X)%PP:X%PVP):1%basalt particle]

Authors: Teeb A. Mohammed --- Akram R. Jabur --- Sihama E. salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 573-585
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Polymer blends composites were prepared according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with weight ratios selected for X values (0,4,8,12,16 %), as strips by double screw extruder and use press process the strips to prepare the samples according ASTM specification, the mechanical properties were studied for all theprepared samples which are (tensile, flexural, compression, impact, hardness, and creep tests). The results are as following:- results showed increment of mechanical properties as PVP ratio increases except elongation, furthermore the results recorded highest values of fracture strength, young modulus, compressive strength, flexural strength, maximum shear stress, flexural modulus and creep modulus at PVP 8% wt. which are (31.32MPa, 0.14GPa, 27.4MPa,24MPa, 0.6MPa, 1.08GPa and 0.558GPa) respectively.While the highest values of fracture toughness and hardness recorded at 12% wt. (1.4696Pa√m), and at 4% wt. (56.5) respectively.

حضرت المتراكبات ذات أساس الخليط البوليمري الثلاثي, وفق الصيغة [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] وبنسب وزنية مختارة لقيم x 16,12 ,8 ,4 ,0) %). وقد تم تحضيرها بشكل شرائط حضرت بعملية البثق بواسطة باثقة ثنائية اللولب واستخدمت عملية كبس الاشرطة لتحضير العينات وفق المواصفة القياسية (ASTM) , درست الفحوصات الميكانيكية للعينات المحضرة والمتمثلة ( فحص الشد والانحناء والانضغاط والصدمة والصلادة والزحف) أظهرت النتائج زيادة في الخصائص الميكانيكية مع زيادة نسبة PVP باستثناء المطيلية وعلاوة على ذلك سجلت النتائج أعلى قيم لمقاومة الشد, معامل الرونة, مقاومة الانضغاط ومقاوة الانحناء واعلى أجهاد قص ومعامل مرونة الانحناء ومعامل الزحف عند نسبة (8% wt) PVPوهي على الترتيب (31.32MPa , 0.14GPa , 0.6MPa , 27.4MPa , ( 0.558GPa , 1.08Gpaفي حين سجلت أعلى قيم لمتانة الصدمة وقيم الصلادة عند نسبةPVP 12% wt.)) (1.696 Pa√m) و 4%wt ((56.5 على الترتيب .


Article
Comparative Study of the Mechanical Properties of Two Groups Ternary Polymer Blends Composites
دراسة مقارنة للخواص الميكانيكيه لمجموعتين من الخلائط البوليمرية الثلاثية المتراكبة الخلاصة

Authors: Sihama E. salih --- Akram R. Jabur --- Teeb A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 7 Part (A) Engineering Pages: 1870-1886
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thermoplastic polymer blends composites were prepared as strips by double screw extruder. The prepared composites consists of two groups, the first group was prepared as ternary polymer blend according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with X values (0,4,8,12,16%).The second group was prepared with replacing the weight ratios for each of the LLDPE and PP according to formula [84%PP:15%((100-X)%LLDPE:X%PVP):1%B.P] with same X values. Mechanical properties for all prepared samples (tensile, flexural, compression, impact toughness, hardness and creep tests) were studied. The results of this research showed that the fracture strength, young modulus, compressive strength, flexural modulus and creep modulus for the two groups increase with increasing in PVP percentage and the highest values were at 8%PVP, while elongation decreases with addition PVP to the composites. Moreover flexural strength, shear stress and hardness values increase slightly with increasing in PVP percentage for both groups. In addition to that, the impact strength and fracture toughness for the second group samples were high and reach the maximum values (0.45 kJ/m²) at 4%PVP and (4.58 Pa√m) at 8%PVP respectively, as well as all results show that the second groups samples have better mechanical properties.

الخلائط البوليمرية اللدائنية المتراكبة تم تحضيرها بشكل شرائط بواسطة باثقة ثنائية اللولب .المتراكبات المحضرة تتكون من مجموعتين,المجموعة الاولى حضرتكمزيج بوليمري لدائني ثلاثيوطبقا الى الصيغة التالية [84% LLDPE: 15% ((100-X) %PP: X%PVP): 1%B.P]وعندقيم X (16,12,8,4,0). والمجموعة الثانية حضرت باستبدال النسب الوزنية لكل من LLDPE وPP فيما بينهما وحسب الصيغة التالية [84%PP:15((100-X)%LLDPE:X%PVP):1%B.P] وبنفس قيم X . تم دراسة الفحوصات الميكانيكية للعينات المحضرة والمتمثلة ( فحص الشد والانحناء والانضغاطومتانة الصدمة والصلادة والزحف)وبينت النتائج البحث ان كل من مقاومة الكسر ومعامل المرونة ومقاومة الانضغاط ومعامل مرونة الانحناء ومعامل الزحف لكلا المجموعتين تزداد بزيادة نسبة PVP في الخليط وسجلت أعلى قيم عند النسبة PVP(8%) بينما تناقصت قيم الاستطالة لكلا المجموعتين عند أضافة PVP للمتراكبات المحضرة ,أما قيم مقاومة الانحناء واجهاد القص والصلادةازدادت قليلاً مع زيادةنسبة PVP في المجموعتين الاولى والثانية.ومن خلال فحص مقاومة الصدمة لوحظ ان عينات المجموعة الثانية تمتلك اعلى قيم لمقاومة الصدمة ومتانة الكسر والبالغة (0.45 kJ/m²)عند نسبة %PVP 4و4.58 Pa√m)) عند نسبة 8%PVP على الترتيب. كما وبينت النتائج أن عينات المجموعة الثانية تمتلك خواص ميكانيكية افضل مما تمتلكها عينات المجموعة الأولى.

Keywords

polymer composites --- PVP --- PP --- LLDPE


Article
The Effects of Operating Parameters on The Morphology of Electrospun Polyvinyl alcohol Nanofibres

Authors: Akram R. Jabur --- Laith K. Abbas --- Safa M. Muhi Aldain
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Issue: المؤتمر العلمي الثالث لكلية العلوم Pages: 35-46
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

في هذا البحث تم تحضير انسجه من البولي فينيل الكحول بطريقة البرم الالكتروني حيث تم دراسة تأثير العوامل التشغيلية و منها الفولتية المسلطة , معدل التدفق للسائل البوليمري والمسافة بين الابرة الي الجامع.تم اجراء بعض الفحوصات الشاملة للانسجه البوليمرية النانويه تتضمن قطر الليف بالحسابات الاحصائية من صور المجهر الالكتروني الماسح.البولي فينيل الكحول تم اذابته في ماء مقطر بتركيز (10%). المحلول البوليمري برم الكترونيا في ظروف عملية مثل الفولتية المسطله (25,20,15,10,5) كيلوفولت, المسافة بين حافة الابرة والجامع (22,20,15,12,8,4) سم ومعدل التدفق (10,1,0.8,0.5,0.2) مل.ساعه- 1,القطر الداخلي للابرة المستخدمة (0.6 سم ),الجامع للالياف هو صفيحة المنيوم. عند الزيادة الفولتية العاليه المسلطه بثبوت الظروف الاخرى يلاحظ تزداد ان القوة الكهروستاتيكية الى ان تتجاوز الشد السطحي للبوليمرحيث يسمح نفث البوليمر للنفاذ من حافة الابرة ليصل الى الجامع.عند زيادة معدل التدفق مع ثبوت العوامل الاخرى, أن فولتية مسلطه عاليه بقيمة 25 كيلو فولت تنتج أفضل.بزيادة معدل تدفق السائل البوليمري يحصل زيادة كميات تدفق السائل البوليمري اما عند زيادة عالية جدا لمعدل التدفق تنتج الياف مسطحة .تاثير المسافة بين حافة الابرة والجامع بثبوت الظروف الاخريلاحظ معدل قطر الليف يقل تدريجيا من (857نانومتر) على مسافة (4 سم ) الى (600نانومتر) على مسافة (22سم), حيث ان المسافة الكبيرة تسمح للمذيب بوقت اطول للتبخربشكل كامل واستطاله اكثر للالياف.

In this research, the preparation of PVA membranes by electrospinning was studied. The influence of processing parameters, i.e., applied voltage, flow rate and spinneret-to-collector distance was investigated. More comprehensive characterizations of the nanofiber membranes, including fiber diameter, by statistical determination from (SEM) images. PVA was dissolved in distilled water at concentration (10% wt). The polymer solution was electrospun under processing conditions i.e., an applied voltage of (5,10,15,20,25) KV, a needle tip- collector distance of (4,8,12,15,20,22) cm, and a flow rate of (0.2,0.5,0.8,1,10) mL/hr, ,using orifice size of spinneret is (0.6 mm), stationary substrate set-up, aluminum collector .When the high voltage is increased with constant other parameters, the electrostatic force will increase until the polymer surface tension is overcome, allowing a charged jet of polymer to escape from the tip of needle and travel to the collector. The best applied voltage obtained is (25 KV).When the flow rate is increased with keeping other parameters constant, more polymer solution is ejected. Increasing the flow rate too high, more smooth flattened fibers and merged. In accordance with obtained results, the optimum solution flow rates were obtained to be (0.2ml/h) and (0.5ml/h).The effect of needle tip-collector distance, was studied by a series of experiments were carried out with constant other parameters. Shows that average fiber diameter have a slight decrease trend from (857 nm) at distances of (4cm) to (600nm) at distance of (22cm). Possibly the larger distances increase flight time of the jet, stretching of the solution so the solvent had enough time to evaporate completely.

Keywords


Article
Effect of NaCl Solution Addition on Improving Some of the Physical Properties of Nylon 6 Solutions used for Electro spinning Purpose

Authors: Fadhil A. Chayad --- Akram R. Jabur --- Noor M .Jalal
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 7 Part (A) Engineering Pages: 1265-1274
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Nylon 6 / (0.5, 1, 1.5, 2 and 2.5) wt. % NaCl solutions were prepared for electrospinning technique. The electrical conductivity of polymeric solutionincreases directly with NaCl concentration from 3.8 (mS/ cm) for pure nylon solution to 12.7 mS/cm at nylon 6/ 2.5 wt. % NaCl, and slight decreasing the viscosity and the surface tension of the solution . Increasing the polymeric solution conductivity cause more electrical charges carried by the electrospinning jet. Prepared films morphology tested by SEM and the average fibers diameters measured for each concentration. In this research, it was proved that the nanofibers film shows decreasing the average diameter by increasing NaCl concentration.


Article
Ambient Temperature Affect the Pore size of PVA Nanofibers Tissues
تأثير درجة حرارة المحيط على الحجم المسامي لانسجة الياف بولي فينال الكحول النانويه

Authors: Akram R. Jabur --- Laith K. Abbas --- Safa M. Muhi Aldain
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 6 Part (B) Scientific Pages: 1040-1047
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Electrospinning has recently emerged as a leading technique for generating biomimetic scaffolds made of synthetic and natural polymers for tissue engineering applications. PVA was dissolved in distilled water at concentration (10% wt). PVA 10% DW solution was prepared as biopolymeric materials for fabricating tissue engineered scaffolds by electrospinning, varying ambient temperature (25, 30, 35, 40, 45 and 50) ͦ C andinvestigated the ambient temperature effect on tissue nanofibers pore size. Scanning electron microscopy was utilized to profile the topography of individual electrospun fibers. Statistical measurements for each SEM images lead to measure the mean poresize of tissue obtained. Our results indicate that the average poresize of PVA fibertisues could be scaled down to mean values (132-300)nm smooth nanofibers without any beads, poresize decreased as ambient temperature increase to certain temperature at (40 °C) and retrain increasing at (45 and 50) °C temperature.

برز البرم الالكتروني حديثا" كتقنية رائده لتخليق سقالات محاكاة بايولوجيا مصنعه من بوليمرات صناعيه او طبيعيه لاستخدامات الهندسة النسيجيه . أذيب بولي فينال الكحول في ماء مقطر بتركيز 10% وزنيا" . حضر بولي فينال الكحول 10% من الماء المقطر كماده سائل بوليمر احيائي لتصنيع سقالات هنسة نسيجيه بالبرم الالكتروني , وبتغيير درجات حرارة المحيط (45,40,35,30,25 و( 50 ͦم° ودراسة تأثير تغيير درجة حرارة المحيط على حجم المسامي للانسجه الليفيه النانويه.أستخدم فحص المجهر الالكتروني الماسح لتحديد شكل وطوبوغرافية الالياف المبرمه الكترونيا .واجريت حسابات احصائيه من كل صور من صور المجهر الالكتروني الماسح المأخوذه للالياف لتحديد معدل حجم المسامات للنسيج المحضر والمفحوص . النتائج التي تم الحصول عليها تدل على أن معدل حجم المسامات للالياف أنسجه بولي فينال الكحول يمكن أن تتدرج الى قيمه ممتده بين (132-300) نانومتر لالياف ملساء دون حصول اي عقد , والحجم المسامي يتناقص بزيادة درجة حرارة المحيطه الى درجه حراره معينه هي 40 م° والتي بعدها يعود للتزايد عند درجات حراره (50, 45) م°.


Article
Fabrication and Characterization Membrane Prepared from Oxidized Multiwall Carbon Nanotube/Nylon 6 Composite
تصنيع وتوصيف غشاء محضر من متراكب انابيب الكاربون متعددة الجدران النانويه المؤكسده/نايلون

Authors: Akram R. Jabur --- Laith K. Abbas --- Saja A. Moosa
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2017 Issue: المؤتمر العلمي الخامس لكلية العلوم Pages: 200-212
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Mixed matrix nanofibres membranes were prepared, characterized, studied and evaluated for performance and properties in this research. Acid oxidized Multiwall carbon nanotubes MWCNTs embedded in Nylon 6 as matrix polymer were the materials used to create the prepared membranes. Through; the electrospinning process, the hydrophilicity of the membrane was enhanced by blending (MWCNTs) due to migration of functionalized MWCNTs into the membrane surface. Scanning electron microscopy SEM and morphology studies showed that average fiber diameters produced were about 72-193 nm and average pore size 183 - 226 nm . It was found that as fiber diameter decreases high porosity and small pore size will be created and increasing the amount of functionalized MWCNTs leads to increase of pure water flux. The MWCNT blended with Nylon 6 membranes showed better antibactericidal ability as compared to the neat Nylon 6 membranes. Water filter media with a high rejection ratio against heavy metal ions reached (80%) at (0.8 wt. % MWCNT) membrane. Addition of MWCNTs forms a membrane with high mechanical strength (4.158MPa) of Nylon/ 0.8 wt. % MWCNT.

في هذا البحث حضرت أغشية مخلوطه من البوليمر والياف نانويه وتم توصيفها ودراسة وتقييم أدائها وخصائصها,انابيب الكاربونيه النانويه المتعددة الجدران المؤكسده حمضيا" MWCNTs غمرت في بوليمرالنايلون 6 كمادة اساس حيث استخدمت هذه الانابيب لتحضير الغشاء. عززت خاصية ألفة الماء (تبللية) للاغشيه بخلط أنابيب الكاربون MWCNTs حيث يعزى لتكون رابط من انابيب االكاربون مفعل MWCNTs الى سطح الغشاء خلال عملية البرم الكهربائي. دراسة المورفولوجيه بالمجهر الالكتروني الماسح أظهرت أن معدل قطر الالياف المنتجه كان بحدود 139-72 نانومتر ومعدل حجم المسامات 183-226 نانومتر, وجدأن قطر الالياف ينقص بزيادة المساميه تكون مسامات بحجم صغير. زيادة اضافة انابيب الكانون النانوية المفعلة MWCNTs تؤدي الى زيادة كمية تدفق الماء النقي. أن أضافةMWCNT المخلوطة لأغشية النايلون6 أظهرت قدرة المضاده للبكتريا أفضل بالمقارنة مع الأغشية نايلون 6النقيه. أوساط تصفية المياه بارتفاع نسبة الرفض ضد ايونات المعادن الثقيلة وصلت (80٪) في غشاء (0.8 نسبه وزنيه٪ أنابيب الكاربون النانويه. أضافة الانابيب الكاربونيه الناونيه متعددة الطدران تمنح الاغشيه المحضره متانه ميكانيكه عاليةوصلت (4.158ميكاباسكال) لغشاءمن النايلون / بأضافة وزنيهبالوزن0.8 ٪ من الانابيب النانويه

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (12)


Year
From To Submit

2017 (3)

2016 (1)

2015 (2)

2014 (2)

2013 (1)

More...