Fabrication of Ceramic-Metal Functionally Graded Materials
تحضير المواد المتدرجة وظيفيا لـ (سيراميك – فلز)

Authors: Alaa A. Atiyah --- Saad. B. H. Farid --- Dheya N. Abdulamer
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 3 Part (A) Engineering Pages: 513-524
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

High order step wise functionally graded materials Al2O3-Ti are fabricated. These materials combine the high fracture toughness of Ti phase and the relatively low density of Al2O3 and stand for candidate materials for harsh mechanical and thermal environments. The techniques of powder technology are utilized to fabricate these materials that composed of five graded layers of Al2O3-Ti phases. Al2O3 increasing linearly across these layers (0, 25, 50, 75 and 100wt% respectively).The green specimens are composed of Al2O3-TiH2 layers and the sintered specimens are composed of graded Al2O3-Ti. Spark Plasma Sintering technique is utilized for sintering of the graded green specimens. The best sintering conditions is found at 1500°C for 30 minute of sintering that gives apparent density of 4.25 g/cm3, porosity of 1.28% and diametric expansion of 1.58%. Optical microscopy shows gradual transition of phases at the interface of the graded layers

تم تصينع مواد متدرجة من Al2O3-Ti بطبقات متسلسلة عديدة. تجمع هذه المواد بين مقاومة الكسـر العالية لطور Ti والكثافة المنخفضة نسبيا لطور Al2O3 وترشح هذه المواد كمواد منافسـة في الظروف الميكانيكية والحرارية القاسـية. تم استخدام تقنيات المساحيق لتصنيع هذه المواد والمؤلفة من خمســة طبقات متدرجة بنسب الاطوار Al2O3-Ti. تتزايد نسـبة الطور Al2O3 خطيا خلال الطبقات (0، 25، 50، و 100wt% على التوالي).تتكون النماذج الخضراء من طبقات من Al2O3-TiH2 وتكون النماذج بعد التلبيد مكونة من تدرج من Al2O3-Ti. تم تلبيد النماذج المتدرجة الخضراء باستخدام التلبيد بشرارة البلازما. ووجد ان أفضل ظروف للتلبيد هي في درجة حرارة التلبيد 1500°C لزمن تلبيد 30 دقيقة والذي ادى الى كثافة ضاهرية بمقدار 4.25 g/cm3 ومســـامية بمقدار 1.28% وتمدد قطري بمقدار 1.58%. وقد اظهرت فحوصات المجهر الضوئي تحول متدرج للاطوار على الحدود بين الطبقات المتدرجة.


Article
Retarding of Precipitation Hardening of Al-Cu Alloy by Cadimium Addition
تأخیر عملیة التصلید بالترسیب لسبیكة (ألمنیوم – نحاس) بواسطة إضافة ألكادمیوم

Authors: Sabreen Ali --- Alaa A. Atiyah --- Amin D. Thamir
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 16 Part (A) Engineering Pages: 2997-3006
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of the present work is to prepare a set of Al-Cu alloys with slowprecipitation hardening by aging. Present work results can be utilized during theimporting or exporting of such alloys at solution treatment conditions. In order toestablish this aim, a set of Al-4%Cu alloys have been prepared in the laboratory toinvestigate the effect of Cd-addition with the percentage varied from (0.1, 0.3 and0.5) weight percentage. The prepared alloys with different Cd additions weresubjected to a natural aging up to 60 days after solution treatment. As a result, thealloys showed an obvious retarding in the aging kinetics as the percentage of Cdadditionsincreasing. This retarding was found to be due to the trapping of thevacancies that resulted during the quenching step that resulted in delays of Gunier-Preston zones precipitation. SEM has been used in monitoring of microstructure aswell as optical microscopy


Article
Mechanical Characteristics of Prepared Functionally Graded Cylinder by Centrifugal Casting
الخصائص الميكانيكية لاسطوانة متدرجة وظيفيا بواسطة السباكة بالطرد المركزي

Authors: Marwan A. Madhloom --- Alaa A. Atiyah --- Ali H. Ataiw
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 6 Part (A) Engineering Pages: 1344-1368
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

It is hoped in this paper to use the concept of centrifuging to prepare thick hollow functionally graded cylinder of (Al-TiO2) alloy. In order to achieve this objective, a vertical centrifugal casting machine was designed and manufactured. The FG cylinders prepared have shown a reasonable linear and the graded hardness value across the thicknesses. FG cylinders exhibit a heterogeneous microstructure in which a high volume fraction of (TiO2) hard particles is clustered on the surface according to the value of pouring temperature and motor force that represented by the mold number of rotations per minutes. It was found that using of pouring temperature of (850˚C) and rotation speed of (2100 r.p.m) would make a better graded hardness value across the thickness especially when (TiO2 weight%) is (10%). It is also found that the clustering of (TiO2) will weaken the tensile strength of prepared materials but increasing the wear resistance. Results of X-ray diffraction analysis for cylinders prepared with pouring temperature conditions (850˚C) and rotation speed of (2100 r.p.m)shows the development of (TiAl) crystalline phase in all prepared FG cylinders and maximum noticeable intensity was foundin (7.5weight% of TiO2) FG cylinders.

تم في هذا البحث إستخدام مفهوم التطريد المركزي لتحضير أسطوانة سميكة مُجوّفة مُتدرّجة وظيفياً من سبيكة الألمنيوم- أوكسيد التيتانيوم. ولغرض تحضير هذا النوع من المَواد المُتدرّجة، تم تصميم وتصنيع ماكنة سباكة بالتطريد المركزي العمودي لهذا الغرض. أظهرت الأسطوانات المُتدرّجة وظيفياً المُحَضّرة بأستخدام ماكنة التطريد المركزي قيم صلادة مُتدرّجة بصوره خطيه عبر السمك. كما اظهرت هذه المواد بُنية مجهرية غير مُتجانسة وبكسر حجمي عالي من الدقائق الصلدة من أوكسيد التيتايوم التي تجمّعتْ بدورها على طول السطح إعتمادا على قيمة درجة حرارة الصب وقوة الطرد المركزي التي تم التعبير عنها بعدد دورات القالب لكل دقيقة. كما وُجِدَ أنّ استخدام درجة حرارة الصب (˚C850) وسرعة دوران (2100r.p.m) قد أعطى قيم صلادة مُتدرّجة بصوره خطيه خاصة عندما كانت نسبة أوكسيد التيتانيوم المضافه (%10). كما وُجِدَ أيضاً أن تجمّع أوكسيد التيتانيوم يُضعِف من مُقاومة الشد لكنهُ يزيد من مُقاومة البلى. ولقد أثبتتْ نتائج تحليل حيود الأشعة السينية للأسطوانات المُحَضّرة بدرجة حرارة الصب (˚C850) وسـرعــة دوران (2100r.p.m) وجود الطور البلوري ( (TiAlبكل العيّنات ولكن كانت أقصى شدة ملحوظة لهذا الطور بالأسطوانة المُتدرّجة ذات نسبة (7.5%) من أوكسيد التيتانيوم.