Article
PREPARATION OF HIGH PURITY MAGNESIUM OXIDE FROM SEA BITTERN RESIDUAL FROM NaCl PRODUCTION IN Al-BASRAH SALTERN, SOUTH IRAQ

Authors: Waleed R. Abdullah --- Alaa M. Kh. Mustafa
Journal: Iraqi Bulletin of Geology and Mining مجلة الجيولوجيا والتعدين العراقية ISSN: 18114539 Year: 2013 Volume: 9 Issue: 3 Pages: 129-146
Publisher: Ministry of Industry and Minerals وزارة الصناعة والمعادن

Loading...
Loading...
Abstract

In this study, light and dead-burned magnesia (MgO) were prepared from the sea-bittern residual from the production of NaCl; extracted from sea water (Arabian Gulf) in Al-Basrah saltern in the south of Iraq. Dead burned magnesia of pure and dense form assaying 96.8% MgO, with a bulk density of 3.7 gm/cm3 was prepared at optimum conditions, including pre-treatment of the sea bittern of 26 Baume with calcium chloride at a ratio of 1.05:1.00 (CaCl2:MgSO4) to remove calcium sulfate, addition of precipitant (dolime) at a molar ratio of 1:1 (CaO.MgO:MgCl2), and precipitation temperature of about 70 °C for 60 minutes. The precipitated Mg(OH)2 was subjected to calcination at 1000 °C for 60 minutes, whereby a milky soft powder of light-burned (active) magnesia was produced. Dead-burned (inactive) magnesia was then obtained by burning the light-burned magnesia at 1650 °C for 60 minutes. This study provides further benefit, of producing a high purity calcium sulfate (≥ 98%) as a byproduct of the MgO production.

تم في هذا البحث دراسة إنتاج مادة المغنيسيا الخفيفة ومطلقة الحرق، باستغلال المحلول المر المتخلف عن عملية إنتاج ملح الطعام المستخرج من مياه البحر )الخليج العربي) في مملحة البصرة، جنوب العراق، حيث أمكن تحضير مادة أوكسيد المغنيسيوم مطلقة الحرق وعالية النقاوة (96.8% MgO) وبكثافة كتلية 3.7 غم/سم3، بعد تثبيت الظروف المثلى لعملية التحضير والتي تضمنت: معاملة أولية للمحلول المر (كثافة 26 بوميه) بمادة كلوريد الكالسيوم وبنسبة 1.05:1.00 (CaCl2:MgSO4) للتخلص من كبريتات الكالسيوم ولتهيئة المحلول المر للمرحلة التالية. تضمنت المرحلة الثانية إضافة المادة المرسبة (الدولايم) الى المحلول المر وبنسبة مولية 1:1 (CaO.MgO:MgCl2) لترسيب هايدروكسيد المغنيسيوم، وتم التفاعل بدرجة حرارة 70 درجة مئوية لمدة ساعة كاملة. تم حرق هايدروكسيد المغنيسيوم الناتج من عملية الترسيب بدرجة حرارة 1000 درجة مئوية لمدة ساعة للحصول على مادة أوكسيد المغنيسيوم واطئ الحرق (النشط أو الفعال) وبإخضاع الأخيرة للحرق بدرجة حرارة 1650 درجة مئوية، تم الحصول على مادة المغنيسيا عالية الحرق (غير الفعالة). كما يوفر البحث إمكانية إنتاج كبريتات الكالسيوم النقية (≥ 98%) كمنتج عرضي لإنتاج أوكسيد المغنيسيوم.


Article
PRILIMINARY UPGRADING OF SILICA SAND FOR SILICON AND SILICONES INDUSTRIES FROM ARDHUMA, IRAQI WESTERN DESERT

Authors: Tanya V. Khachiek --- Ibtihal Kh. Fleah --- Alaa M.Kh. Mustafa
Journal: Iraqi Bulletin of Geology and Mining مجلة الجيولوجيا والتعدين العراقية ISSN: 18114539 Year: 2013 Volume: 9 Issue: 1 Pages: 75-84
Publisher: Ministry of Industry and Minerals وزارة الصناعة والمعادن

Loading...
Loading...
Abstract

In this research a preliminary beneficiation study was conducted on a sample from Ardhuma silica-sand deposit in the Iraqi Western Desert, to provide a raw material for silicon industries. The beneficiation processes applied were vibration screening (dry and wet), attrition scrubbing and magnetic separation (dry and wet). These techniques were used individually or in combination to upgrade the sand to produce quartz-sand meeting the requirements of Metallurgical-Silicon production. This would be the base material for silicon materials and Solar-Grade Silicon.Quartz-sand fulfills the requirements of the State Company for Mining Industries and Aquatic Insulation for the raw materials of MG-Silicon production, which was produced by applying one of the following beneficiation routs: The first consists of autogenesis grinding, dry screening on 150 µ, attrition scrubbing and wet screening on 150 µ. Whereas, the second includes autogenous grinding, dry screening on 150 µ and dry magnetic separation using magnetic field intensity of 16.5 Kilogauss.

تم في هذا البحث إجراء دراسة أولية لتنقية نموذج من خام رمال السليكا لمنطقة أرضمة الواقعة في الصحراء الغربية العراقية لإنتاج مادة أولية تستخدم في صناعة السليكون الميتالورجي، حيث طبق في هذا البحث عدد من عمليات المعالجة شملت الغربلة الجافة والرطبة، الرج والحك الميكانيكي الشديدين والفصل المغناطيسي الجاف والرطب. هذه التقنيات استخدمت بشكل منفرد أو بصورة متتالية (متعاقبة) لإنتاج رمال زجاج مطابقة لمواصفات المواد الأولية (الكوارتز) الداخلة في إنتاج السليكون الميتالورجي الذي يعتبر الأساس في الصناعات السليكونية والألواح الشمسية المستخدمة في توليد الطاقة.ولقد وجد أن بالإمكان إنتاج رمال كوارتز مطابقة لمواصفات الشركة العامة للصناعات التعدينية والعزل المائي الخاصة بالمواد الأولية الداخلة في صناعة السليكون الميتالورجي بإتباع أي من المسلكين التكنولوجيين التاليين: الأول يتضمن عملية طحن رملي ذاتي وغربلة جافة على غربال 150 مايكرون، ثم عملية الرج والحك الميكانيكي الشديدين وأخيراً غربلة رطبة على غربال 150 مايكرون. فيما يشمل المسلك الثاني عملية الطحن الرملي الذاتي والغربلة الجافة على غربال 150 مايكرون، ثم عملية الفصل المغناطيسي الجاف باستخدام شدة مجال مغناطيسي 16.5 كيلوگاوس.


Article
PREPARATION OF PRECIPITATED CALCIUM CARBONATE FROM WADI GHADAF LIMESTONE OF DAMMAM FORMATION
تحضير كاربونات الكالسيوم المترسبه من حجر الكلس لمنطقة وادي غدف

Authors: Wasan A. Muslim وسن عبد الكاظم مسلم --- Alaa M. Kh. Mustafa علاء محمد خليل مصطفى
Journal: Iraqi Bulletin of Geology and Mining مجلة الجيولوجيا والتعدين العراقية ISSN: 18114539 Year: 2015 Volume: 11 Issue: 2 Pages: 123-138
Publisher: Ministry of Industry and Minerals وزارة الصناعة والمعادن

Loading...
Loading...
Abstract

In view of the availability of a cheap and a high quality limestone raw material and the practical abilities to produce precipitated calcium carbonate (PCC) using the carbonation process route, this study was carried out with bench scale experiments. High purity limestone of Wadi Ghadaf (Dammam Formation), was calcined to produce quick lime which was converted to calcium hydroxide by slaking with water, the final stage comprised injection of CO2 gas into the slaked lime slurry. Calcium carbonate was precipitated as a high purity (99.5% CaCO3) white powder (95% brightness) with a particle size range of (6 – 12) microns. Conditions optimization was done through each stage of this study.

على ضوء توفر المادة الأولية المتمثلة بحجر الكلس بنقاوة جيدة وبسعر رخيص مع وجود الإمكانية العملية لتطبيق طريقة الكربنة، تم إجراء تجارب منضدية لتحضير كاربونات الكالسيوم المترسبه حيث تم أولاً حرق حجر الكلس من منطقة وادي غدف (تكوين الدمام) لإنتاج النورة الحية (أوكسيد الكالسيوم) التي تمت معاملتها بعد ذلك بالماء لإنتاج هيدروكسيد الكالسيوم وتبع ذلك ترسيب كاربونات الكالسيوم بحقن غاز ثاني أوكسيد الكاربون في لباب الهيدروكسيد، تم تثبيت الظروف المثلى لكل مرحلة من مراحل تحضير كاربونات الكالسيوم المترسبة والتي أعطت نتائج جيدة للمنتج من خلال نعومة تراوحت بين (6 - 12 مايكرون) ونقاوة عالية حوالي (99.5%) ودرجة بياض 95%.


Article
LABORATORY STUDY OF MgO PREPARATION FROM IRAQI DOLOMITE BY LEACH-PRECIPITATION – PYROHYDROLYSIS PROCESS
دراسة مختبرية لتحضير أوكسيد المغنيسيوم من الدولومايت العراقي بطريقة الإذابة – الترسيب – التحلل الحراري

Authors: Alaa M. Kh. Mustafa علاء محمد خليل مصطفى --- Dalya Kh. Al-Dahan داليا خالد حميد --- Tanya V. Khachik تانيا فاروجان خاجيك
Journal: Iraqi Bulletin of Geology and Mining مجلة الجيولوجيا والتعدين العراقية ISSN: 18114539 Year: 2014 Volume: 10 Issue: 3 Pages: 83-107
Publisher: Ministry of Industry and Minerals وزارة الصناعة والمعادن

Loading...
Loading...
Abstract

In this study, a three-process approach was applied for the extraction of Magnesia (MgO) from Iraqi dolomite. The first process comprises leaching of (– 2 mm) raw dolomite in 25% solid by 22% HCl aqueous solution for 10 minutes at room temperature, extracts 99.68% of MgO in the dolomite ore. The second process, which is a separation process, includes two-steps (hydration and carbonation) for the separation of calcium as Precipitated Calcium Carbonate (PCC, 1st stage) of 90.1% purity and a magnesium recovery of 92.8% as dissolved MgCl2. Hydration was carried out by adding 55% by weight ratio of calcined dolomite (dolime)/ leached dolomite at 70 °C for 60 minute; this was followed by carbonation of the slurry formed by CO2 gas at a pressure of 2 bars for 100 minutes at room temperature. The MgCl2 solution produced was subjected for evaporation to remove the dissolved Calcium Bicarbonate by precipitation as (PCC, 2nd stage) with a purity of 97%. The purified brine was further evaporated till dry salt of MgCl2.6H2O (Bischofite) was obtained, and then subjected for pyrohydrolysis, which was the third process, at 650 °C for 60 minutes. 22% HCl was regenerated with a product of 95.48% MgO purity after washing with water and drying.

تم في هذه الدراسة استخلاص المغنيسيا (MgO) من الدولومايت العراقي باعتماد طريقة مكونة من ثلاثة عمليات منفصلة ومتتالية. تضمنت العملية الأولى معاملة خام الدولومايت ذي الحجم الحبيبي ( mm2– ) مع حامض الهيدروكلوريك بتركيز 22% ونسبة صلب 25% لمدة 10 دقائق بدرجة حرارة الغرفة لاستخلاص مايقدر بـ 99.68% من MgO الموجود في خام الدولومايت. في حين شملت العملية الثانية مرحلتين [معاملة الدولومايت المكلسن (الدولايم) مع محلول الاستخلاص ومرحلة الكربنة] لفصل الكالسيوم بشكل كاربونات الكالسيوم المترسبة (PCC، المرحله الاولى) وبنقاوة 90.1% مع استرجاع 92.8% من المغنيسيوم في المحلول بشكل MgCl2الذائب. حيث أضيفت نسبة 55% وزنا من الدولايم الى الدولومايت المعامل بالحامض بدرجة حرارة °C 70 لمدة 60 دقيقة، اتبعت بحقن غاز CO2 في اللباب المتكون تحت ضغط 2 بار لمدة 100 دقيقة وبدرجة حرارة الغرفة. تم تبخير محلول MgCl2 الناتج للتخلص من بيكربونات الكالسيوم الذائبة وتحويلها الى راسب كربونات الكالسيوم المترسبة (PCC، المرحلة الثانية) وبنقاوة 97%. وقد تم تبخير المحلول الملحي المنقى لحين ظهور راسب MgCl2.6H2O الذي بدوره خضع لعملية التحلل المائي الحراري وهي العملية الثالثة والاخيرة بدرجة حرارة °C 650 لمدة 60 دقيقة. حيث أمكن استرجاع حامض HCl بتركيز 22% مع الحصول على راسب أوكسيد المغنيسيوم الناتج من التحلل الحراري بعد الغسل والتخفيف وبنقاوة 95.4%.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2015 (1)

2014 (1)

2013 (2)